CN105936708A - Heat-resistant insulating PVC wire and cable material - Google Patents
Heat-resistant insulating PVC wire and cable material Download PDFInfo
- Publication number
- CN105936708A CN105936708A CN201610436923.0A CN201610436923A CN105936708A CN 105936708 A CN105936708 A CN 105936708A CN 201610436923 A CN201610436923 A CN 201610436923A CN 105936708 A CN105936708 A CN 105936708A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable material
- high temperature
- diphenol propane
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a heat-resistant insulating PVC wire and cable material, which comprises the following raw materials (by weight): 80-100 parts of PVC resin, 25-30 parts of trioctyl trimellitate, 6-7 parts of calcined clay, 0.4-0.6 part of paraffin, 3-6 parts of ammonium polyphosphate, 0.7-0.9 part of diphenol propane, 1.0-1.4 parts of stearate, 2-3 parts of dicapryl phthalate and 0.4-0.6 part of diphenol propane. The PVC resin adopts SG-2 type polyvinyl chloride resin produced and manufactured by a suspension polymerization method. The product of the invention has good heat resistant and high temperature resistant properties, mechanical property, electric insulation performance and processability, and also has excellent heat resistance, flame resistance and dampproofing and waterproofing performance.
Description
Technical field
The present invention relates to technical field of electric wires and cables, specifically a kind of high temperature insulation level PVC cable material.
Background technology
Electric wire in order to transmit electricity (magnetic) can, information and realize electromagnetic energy conversion wire product, the electric wire of broad sense
Being also referred to simply as cable, the cable of narrow sense refers to insulated cable, and it may be defined as: the aggregation being made up of following part;One
Or many insulated wire cores, and the clad that each of which is likely to be of, total protective layer and outer jacket.
Electric wire description is various, has wide range of applications, use voltage at 1kV and following more, in the face of special occasions
The most derivative new product, such as fire-resistant cable, flame-retardant cable, low smoke and zero halogen/low-smoke low-halogen cable, mouse termite-proof, anti-
The wear-resisting cable of cable, oil resistant, medical cable, agricultural cable, mining cable, thin-walled electric wire etc..
Electric wire is widely used in industry-by-industry, must develop along with the most information-based, and the effect of electric wire is the most prominent
Go out, in industry and people are lived, all play very important role.In consideration of it, the present invention proposes a kind of high temperature insulation
Level PVC cable material.
Summary of the invention
The technical problem to be solved is to provide a kind of high temperature insulation level PVC cable material.The present invention to solve
Technical problem certainly realizes by the following technical solutions:
A kind of high temperature insulation level PVC cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 80-100 part,
Trioctyl trimellitate (TOTM) 25-30 part, calcinated argil 6-7 part, paraffin 0.4-0.6 part, APP 3-6 part, diphenylol
Propane 0.7-0.9 part, stearate 1.0-1.4 part, di-sec-octyl phthalate 2-3 part and diphenol propane 0.4-0.6
Part.
Further, currently preferred raw material components is: polyvinyl chloride resin 90 parts, trioctyl trimellitate (TOTM) 28 parts, calcining pottery
6.5 parts of soil, 0.5 part of paraffin, APP 4.5 parts, diphenol propane 0.8 part, stearate 1.2 parts, adjacent benzene two
Formic acid di-sec-octyl 2.5 parts and diphenol propane 0.5 part.
Further, described polyvinyl chloride resin uses the SG-2 model Corvic that suspension polymerization is manufactured.
Compared with prior art, the present invention has good heat resisting performance, mechanical performance, electrical insulation properties and processing
Performance, also has thermostability, anti-flammability and the waterproof and dampproof property of excellence simultaneously.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below to this
Invention is expanded on further.
Embodiment 1
A kind of high temperature insulation level PVC cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 80 parts, partially
Benzenetricarboxylic acid three monooctyl ester 25 parts, calcinated argil 6 parts, 0.4 part of paraffin, APP 3 parts, diphenol propane 0.7 part,
Stearate 1.0 parts, di-sec-octyl phthalate 2 parts and diphenol propane 0.4 part.
Further, described polyvinyl chloride resin uses the SG-2 model Corvic that suspension polymerization is manufactured.
Embodiment 2
A kind of high temperature insulation level PVC cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 90 parts, partially
Benzenetricarboxylic acid three monooctyl ester 28 parts, calcinated argil 6.5 parts, 0.5 part of paraffin, APP 4.5 parts, diphenol propane 0.8
Part, stearate 1.2 parts, di-sec-octyl phthalate 2.5 parts and diphenol propane 0.5 part.
Further, described polyvinyl chloride resin uses the SG-2 model Corvic that suspension polymerization is manufactured.
Embodiment 3
A kind of high temperature insulation level PVC cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 100 parts,
Trioctyl trimellitate (TOTM) 30 parts, calcinated argil 7 parts, 0.6 part of paraffin, APP 6 parts, diphenol propane 0.9 part,
Stearate 1.4 parts, di-sec-octyl phthalate 3 parts and diphenol propane 0.6 part.
Further, described polyvinyl chloride resin uses the SG-2 model Corvic that suspension polymerization is manufactured.
The present invention has good mechanical performance, electrical insulation properties and a processing characteristics, also have simultaneously excellence thermostability,
Anti-flammability and waterproof and dampproof property.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.The technical staff of the industry
It should be appreciated that the present invention is not limited by step embodiment, the simply present invention's described in step embodiment and description is former
Reason, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these change and change
Enter to both fall within scope of the claimed invention.Claimed scope is by appending claims and equivalent thereof
Define.
Claims (3)
1. a high temperature insulation level PVC cable material, it is characterised in that: include following raw material and parts by weight of component: PVC
Resin 80-100 part, trioctyl trimellitate (TOTM) 25-30 part, calcinated argil 6-7 part, paraffin 0.4-0.6 part, APP
3-6 part, diphenol propane 0.7-0.9 part, stearate 1.0-1.4 part, di-sec-octyl phthalate 2-3 part and diphenol
Base propane 0.4-0.6 part.
A kind of high temperature insulation level PVC cable material the most according to claim 1, it is characterised in that: preferably raw material
Component is: polyvinyl chloride resin 90 parts, trioctyl trimellitate (TOTM) 28 parts, calcinated argil 6.5 parts, 0.5 part of paraffin, APP
4.5 parts, diphenol propane 0.8 part, stearate 1.2 parts, di-sec-octyl phthalate 2.5 parts and diphenol propane 0.5
Part.
A kind of high temperature insulation level PVC cable material the most according to claim 1, it is characterised in that: described PVC
Resin uses the SG-2 model Corvic that suspension polymerization is manufactured.