CN105949642A - Plastic floor with high anti-dirty performance and preparation method of plastic floor - Google Patents
Plastic floor with high anti-dirty performance and preparation method of plastic floor Download PDFInfo
- Publication number
- CN105949642A CN105949642A CN201610316133.9A CN201610316133A CN105949642A CN 105949642 A CN105949642 A CN 105949642A CN 201610316133 A CN201610316133 A CN 201610316133A CN 105949642 A CN105949642 A CN 105949642A
- Authority
- CN
- China
- Prior art keywords
- mixing
- plastic floor
- roll
- parts
- strong
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plastic floor with high anti-dirty performance. The plastic floor comprises raw materials in parts by weight as follows: 55-65 parts of amorphous polyethylene terephthalate, 45-55 parts of PVC (polyvinyl chloride), 30-40 parts of a polyurethane emulsion, 30-40 parts of 2-chloroethyl vinyl ether, 25-35 parts of methylene diphenyl diisocyanate, 20-30 parts of dioctyl phthalate, 15-25 parts of a silicone-acrylic emulsion, 5-15 parts of fumed silica, 5-10 parts of chitin, 5-10 parts of barium stearate, 3-5 parts of an anti-aging agent and 3-5 parts of a cross-linking agent. The plastic floor has excellent anti-dirty performance. The invention further discloses a preparation method of the plastic floor.
Description
Technical field
The present invention relates to plastic material technical field, be specifically related to strong plastic floor of a kind of soil resistance and preparation method thereof。
Background technology
At present, the floor mainly used in repairs profession is timber floor and marble floor.But, it is easily deformed during the use of timber floor, ftractures, also need periodically to maintain, be heated after making moist and can produce various problem of appearance, the most also having the carcinogen such as methanol is release.The major defect of marble floor is to lay trouble, and processing charges is high, is easily broken, typically can not dismantle.
In order to avoid the problem in above-mentioned application, people have turned one's attention to plastic floor, and plastic floor is pavement more novel in current world building material industry, have that pattern is many, construction simple and fast, light weight, the corrosion-resistant and advantage such as go mouldy.Nowadays, plastic floor is applied in daily life more and more widely, as in market, airport, hospital, the occasion such as factory, usage amount increases the most increasingly.But plastic floor is due to mainly polymeric material, in use becomes easily infected by dirt, and should not remove, serves adverse effect to the application band of plastic floor.Therefore, it is badly in need of developing the strong plastic floor of a kind of antifouling capacity to solve the problems referred to above。
Summary of the invention
For solving above-mentioned technical problem, the present invention provides plastic floor that a kind of soil resistance is strong and preparation method thereof, by using specified raw material to be combined, coordinate corresponding production technology, having obtained a kind of Novel plastic floor, its antifouling capacity is excellent, has a good application prospect.
The purpose of the present invention can be achieved through the following technical solutions:
The plastic floor that a kind of soil resistance is strong, is prepared by the raw materials in: amorphization polyethylene terephthalate
55-65
Part,
PVC45-55
Part, polyaminoester emulsion
30-40
Part, ethylene
(2-
Chloroethyl
)
Ether
30-40
Part, methyl diphenylene diisocyanate
25-35
Part, o-phthalic acid dibutyl ester
20-30
Part, silicone acrylic emulsion
15-25
Part, gas-phase silica
5-15
Part, chitin
5-10
Part, barium stearate
5-10
Part, age resistor
3-5
Part, cross-linking agent
3-5
Part.
Preferably, described age resistor is selected from age resistor
CPPD
, age resistor
H
, age resistor
AW
In one or more.
Preferably, one or more in benzoyl peroxide, tetraisocyanate, trimethoxy silane of described cross-linking agent.
The preparation method of the plastic floor that described soil resistance is strong, comprises the following steps:
(
1
) weigh each raw material according to weight portion;
(
2
) by amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate join in muller, are warming up to
160-170
DEG C, carry out the most mixing, mixing time
30-50
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester, silicone acrylic emulsion again, it is cooled to
130-150
DEG C, it is mixing to carry out secondary, mixing time
20-30
Minute;
(
4
) the most backward mixing roll adds gas-phase silica, chitin, barium stearate, age resistor, cross-linking agent, it is warming up to
180-200
DEG C, carry out three times mixing, mixing time
60-80
Minute;
(
5
) material mixing through three times is cooled to
60-70
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
155-165
DEG C, middle roll temperature is
170-180
DEG C, lower roll temperatures is
150-160
DEG C, cooling, molding, obtain finished product subsequently.
Preferably, described step (
5
In), the upper roll temperature of tri-roll press machine is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
℃。
Compared with prior art, it has the beneficial effect that the present invention
(
1
) present invention plastic floor with amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate are main component, by adding o-phthalic acid dibutyl ester, silicone acrylic emulsion, gas-phase silica, chitin, barium stearate, age resistor, cross-linking agent, be aided with that three stages are mixing, roll, cool down, the technique such as molding so that the plastic floor being prepared from possesses the antifouling property of excellence.
(
2
) the plastic floor cheaper starting materials of the present invention, technique is simple, is suitable to heavy industrialization and uses, practical.
Detailed description of the invention
Below in conjunction with specific embodiment, the technical scheme of invention is described in detail.
Embodiment
1
(
1
) weigh amorphization polyethylene terephthalate according to weight portion
55
Part,
PVC45
Part, polyaminoester emulsion
30
Part, ethylene
(2-
Chloroethyl
)
Ether
30
Part, methyl diphenylene diisocyanate
25
Part, o-phthalic acid dibutyl ester
20
Part, silicone acrylic emulsion
15
Part, gas-phase silica
5
Part, chitin
5
Part, barium stearate
5
Part, age resistor
CPPD 3
Part, benzoyl peroxide
3
Part;
(
2
) by amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate join in muller, are warming up to
160
DEG C, carry out the most mixing, mixing time
30
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester, silicone acrylic emulsion again, it is cooled to
130
DEG C, it is mixing to carry out secondary, mixing time
20
Minute;
(
4
) the most backward mixing roll adds gas-phase silica, chitin, barium stearate, age resistor
CPPD
, benzoyl peroxide, be warming up to
180
DEG C, carry out three times mixing, mixing time
60
Minute;
(
5
) material mixing through three times is cooled to
60
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
DEG C, cooling, molding, obtain finished product subsequently.
The performance test results such as table of the plastic floor that prepared soil resistance is strong
1
Shown in.
Embodiment
2
(
1
) weigh amorphization polyethylene terephthalate according to weight portion
60
Part,
PVC50
Part, polyaminoester emulsion
35
Part, ethylene
(2-
Chloroethyl
)
Ether
35
Part, methyl diphenylene diisocyanate
30
Part, o-phthalic acid dibutyl ester
25
Part, silicone acrylic emulsion
20
Part, gas-phase silica
10
Part, chitin
8
Part, barium stearate
8
Part, age resistor
H 4
Part, tetraisocyanate
4
Part;
(
2
) by amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate join in muller, are warming up to
165
DEG C, carry out the most mixing, mixing time
40
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester, silicone acrylic emulsion again, it is cooled to
140
DEG C, it is mixing to carry out secondary, mixing time
25
Minute;
(
4
) the most backward mixing roll adds gas-phase silica, chitin, barium stearate, age resistor
H
, tetraisocyanate, be warming up to
190
DEG C, carry out three times mixing, mixing time
70
Minute;
(
5
) material mixing through three times is cooled to
65
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
DEG C, cooling, molding, obtain finished product subsequently.
The performance test results such as table of the plastic floor that prepared soil resistance is strong
1
Shown in.
Embodiment
3
(
1
) weigh amorphization polyethylene terephthalate according to weight portion
65
Part,
PVC55
Part, polyaminoester emulsion
40
Part, ethylene
(2-
Chloroethyl
)
Ether
40
Part, methyl diphenylene diisocyanate
35
Part, o-phthalic acid dibutyl ester
30
Part, silicone acrylic emulsion
25
Part, gas-phase silica
15
Part, chitin
10
Part, barium stearate
10
Part, age resistor
AW 5
Part, trimethoxy silane
5
Part;
(
2
) by amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate join in muller, are warming up to
170
DEG C, carry out the most mixing, mixing time
50
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester, silicone acrylic emulsion again, it is cooled to
150
DEG C, it is mixing to carry out secondary, mixing time
30
Minute;
(
4
) the most backward mixing roll adds gas-phase silica, chitin, barium stearate, age resistor
AW
, trimethoxy silane, be warming up to
200
DEG C, carry out three times mixing, mixing time
80
Minute;
(
5
) material mixing through three times is cooled to
70
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
DEG C, cooling, molding, obtain finished product subsequently.
The performance test results such as table of the plastic floor that prepared soil resistance is strong
1
Shown in.
Embodiment
4
(
1
) weigh amorphization polyethylene terephthalate according to weight portion
55
Part,
PVC55
Part, polyaminoester emulsion
30
Part, ethylene
(2-
Chloroethyl
)
Ether
40
Part, methyl diphenylene diisocyanate
25
Part, o-phthalic acid dibutyl ester
30
Part, silicone acrylic emulsion
15
Part, gas-phase silica
15
Part, chitin
5
Part, barium stearate
10
Part, age resistor
CPPD 3
Part, trimethoxy silane
5
Part;
(
2
) by amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate join in muller, are warming up to
160
DEG C, carry out the most mixing, mixing time
50
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester, silicone acrylic emulsion again, it is cooled to
150
DEG C, it is mixing to carry out secondary, mixing time
20
Minute;
(
4
) the most backward mixing roll adds gas-phase silica, chitin, barium stearate, age resistor
CPPD
, trimethoxy silane, be warming up to
200
DEG C, carry out three times mixing, mixing time
60
Minute;
(
5
) material mixing through three times is cooled to
60
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
DEG C, cooling, molding, obtain finished product subsequently.
The performance test results such as table of the plastic floor that prepared soil resistance is strong
1
Shown in.
Comparative example
1
(
1
) weigh amorphization polyethylene terephthalate according to weight portion
55
Part,
PVC45
Part, ethylene
(2-
Chloroethyl
)
Ether
30
Part, methyl diphenylene diisocyanate
25
Part, o-phthalic acid dibutyl ester
20
Part, gas-phase silica
5
Part, chitin
5
Part, barium stearate
5
Part, age resistor
CPPD 3
Part, benzoyl peroxide
3
Part;
(
2
) by amorphization polyethylene terephthalate,
PVC
, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate join in muller, are warming up to
160
DEG C, carry out the most mixing, mixing time
30
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester again, it is cooled to
130
DEG C, it is mixing to carry out secondary, mixing time
20
Minute;
(
4
) the most backward mixing roll adds gas-phase silica, chitin, barium stearate, age resistor
CPPD
, benzoyl peroxide, be warming up to
180
DEG C, carry out three times mixing, mixing time
60
Minute;
(
5
) material mixing through three times is cooled to
60
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
DEG C, cooling, molding, obtain finished product subsequently.
The performance test results such as table of the plastic floor that prepared soil resistance is strong
1
Shown in.
Comparative example
2
(
1
) weigh amorphization polyethylene terephthalate according to weight portion
65
Part,
PVC55
Part, polyaminoester emulsion
40
Part, methyl diphenylene diisocyanate
35
Part, o-phthalic acid dibutyl ester
30
Part, silicone acrylic emulsion
25
Part, chitin
10
Part, barium stearate
10
Part, age resistor
AW 5
Part, trimethoxy silane
5
Part;
(
2
) by amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, methyl diphenylene diisocyanate join in muller, be warming up to
170
DEG C, carry out the most mixing, mixing time
50
Minute;
(
3
) in mixing roll, add o-phthalic acid dibutyl ester, silicone acrylic emulsion again, it is cooled to
150
DEG C, it is mixing to carry out secondary, mixing time
30
Minute;
(
4
) the most backward mixing roll adds chitin, barium stearate, age resistor
AW
, trimethoxy silane, be warming up to
200
DEG C, carry out three times mixing, mixing time
80
Minute;
(
5
) material mixing through three times is cooled to
70
DEG C, use tri-roll press machine to roll subsequently, wherein going up roll temperature is
160
DEG C, middle roll temperature is
175
DEG C, lower roll temperatures is
155
DEG C, cooling, molding, obtain finished product subsequently.
The performance test results such as table of the plastic floor that prepared soil resistance is strong
1
Shown in.
By embodiment
1-4
And comparative example
1-2
The strong plastic floor of soil resistance test respectively its antifouling property (floor to be measured is immersed respectively coloured dirt liquid,
12 h
Rear cleaning, observing effect), hardness, environmental-protecting performance.
Table
1
Soil resistance | Shore hardness | Volatilization gas environmental effect | |
Embodiment 1 | Without vestige | 87 | Atomic weak |
Embodiment 2 | Without vestige | 79 | Atomic weak |
Embodiment 3 | Without vestige | 91 | Atomic weak |
Embodiment 4 | Without vestige | 75 | Atomic weak |
Comparative example 1 | Vestige is obvious | 52 | Atomic weak |
Comparative example 2 | Vestige is obvious | 50 | Atomic weak |
The present invention with amorphization polyethylene terephthalate,
PVC
, polyaminoester emulsion, ethylene
(2-
Chloroethyl
)
Ether, methyl diphenylene diisocyanate are main component, by adding o-phthalic acid dibutyl ester, silicone acrylic emulsion, gas-phase silica, chitin, barium stearate, age resistor, cross-linking agent, be aided with that three stages are mixing, roll, cool down, the technique such as molding, the plastic floor being prepared from is made to possess the antifouling property of excellence, hardness height, health environment-friendly simultaneously, application prospect is good, has good social benefit.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical fields, the most in like manner it is included in the scope of patent protection of the present invention。
Claims (5)
1. the plastic floor that a soil resistance is strong, it is characterised in that: it is prepared by the raw materials in: amorphization polyethylene terephthalate 55-65 part, PVC45-55 part, polyaminoester emulsion 30-40 part, ethylene (2-chloroethyl) ether 30-40 part, methyl diphenylene diisocyanate 25-35 part, o-phthalic acid dibutyl ester 20-30 part, silicone acrylic emulsion 15-25 part, gas-phase silica 5-15 part, chitin 5-10 part, barium stearate 5-10 part, age resistor 3-5 part, cross-linking agent 3-5 part.
The plastic floor that soil resistance the most according to claim 1 is strong, it is characterised in that: one or more in age resistor CPPD, antioxidant H, antioxidant A W of described age resistor.
The plastic floor that soil resistance the most according to claim 1 is strong, it is characterised in that: one or more in benzoyl peroxide, tetraisocyanate, trimethoxy silane of described cross-linking agent.
4. according to the preparation method of the strong plastic floor of the arbitrary described soil resistance of claims 1 to 3, it is characterised in that comprise the following steps:
(1) each raw material is weighed according to weight portion;
(2) amorphization polyethylene terephthalate, PVC, polyaminoester emulsion, ethylene (2-chloroethyl) ether, methyl diphenylene diisocyanate are joined in muller, it is warming up to 160-170 DEG C, carry out the most mixing, mixing time 30-50 minute;
(3) adding o-phthalic acid dibutyl ester, silicone acrylic emulsion again in mixing roll, be cooled to 130-150 DEG C, it is mixing to carry out secondary, mixing time 20-30 minute;
(4) in the most backward mixing roll add gas-phase silica, chitin, barium stearate, age resistor, cross-linking agent, be warming up to 180-200 DEG C, carry out three times mixing, mixing time 60-80 minute;
(5) material mixing through three times being cooled to 60-70 DEG C, use tri-roll press machine to roll subsequently, wherein go up roll temperature and be 155-165 DEG C, middle roll temperature is 170-180 DEG C, and lower roll temperatures is 150-160 DEG C, and cooling, molding, obtain finished product subsequently.
The preparation method of the plastic floor that soil resistance the most according to claim 4 is strong, it is characterised in that in described step (5), the upper roll temperature of tri-roll press machine is 160 DEG C, middle roll temperature is 175 DEG C, and lower roll temperatures is 155 DEG C.