CN105921744B - 一种金属打印抑制剂 - Google Patents

一种金属打印抑制剂 Download PDF

Info

Publication number
CN105921744B
CN105921744B CN201610294340.9A CN201610294340A CN105921744B CN 105921744 B CN105921744 B CN 105921744B CN 201610294340 A CN201610294340 A CN 201610294340A CN 105921744 B CN105921744 B CN 105921744B
Authority
CN
China
Prior art keywords
inhibitor
sintering
parts
metallic print
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610294340.9A
Other languages
English (en)
Other versions
CN105921744A (zh
Inventor
张靖
金良
黄少威
包海峰
叶宇柔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Wisdom Dimensional Molding Technology Co Ltd
Original Assignee
Guangdong Wisdom Dimensional Molding Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Wisdom Dimensional Molding Technology Co Ltd filed Critical Guangdong Wisdom Dimensional Molding Technology Co Ltd
Priority to CN201610294340.9A priority Critical patent/CN105921744B/zh
Publication of CN105921744A publication Critical patent/CN105921744A/zh
Application granted granted Critical
Publication of CN105921744B publication Critical patent/CN105921744B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种金属打印抑制剂，由下列质量份数的组份组成：硝酸镁35‑45份，氯化镁0‑15份，水55‑65份。本发明的用途是：采用喷头将本发明制备的金属打印抑制剂喷射在金属粉末上，在烧结的过程中抑制该抑制剂溶液影响到区域的烧结。

Description

一种金属打印抑制剂
技术领域
本发明涉及3D打印技术领域，尤其是一种金属打印抑制剂。
背景技术
选择性抑制烧结技术分为两个过程：成形过程和烧结过程。金属打印的原材料为金属粉末，采用逐层铺粉的方式堆叠成形。
成形过程：抑制剂的溶液被选择性的逐层喷射在零件的轮廓之上，描画图形的轮廓。
烧结过程：坯件被送入烧结炉烧结，抑制剂作用成分在这个过程中产生抑制作用，未喷洒抑制剂的区域粉末会被完全烧结。逐层打印完成后，多余的粉末被去除，打印的坯件被送入烧结炉烧结。
不同粉末的烧结温度不同，从铜合金大约800 到不锈钢大约1200的烧结温度。选择的抑制剂的作用成分如果有很高的烧结温度，那么这种抑制剂就可以用于更多的金属粉末材料的烧结抑制。如果单位体积的溶液能够产生更多的抑制作用成分，那么这种作用成分可以更全面的覆盖在粉末的表面，从而抑制作用也会更有效。
发明内容
本发明的目的是提供一种具有高溶解度、抑制作用成分具有高烧结温度的金属烧结的抑制剂，特别是用于选择性抑制烧结过程。
为实现上述目的，本发明所采用的技术方案是：
一种金属打印抑制剂，由下列质量份数的组份组成：
硝酸镁35-45 份，氯化镁0-15份，水 55-65份。
上述金属打印抑制剂的制备方法是： 0-15份氯化镁，35-45份硝酸镁， 55-65份水，形成盐水混合物，即为金属打印抑制剂。
本发明的用途是：采用喷头将本发明制备的金属打印抑制剂喷射在金属粉末上，在烧结的过程中抑制该抑制剂溶液影响到区域的烧结。
本发明的反应机理是：
抑制剂一开始是以液体的形式存在的，在打印模型时，将抑制剂喷射到物体表面粘接起来，等模型打印完成后放到高温炉里面进行烧结，烧结过程中，抑制剂分解产生的抑制作用成分为氧化镁，而氧化镁的熔点为2852，具有很高的烧结温度；两种盐具有高溶解度，因而在烧结的过程中会产生足够的氧化镁颗粒以覆盖在粉末的表面，从而阻止区域粉末的烧结。
附图说明
附图1为附着于H13粉末表面的氧化镁的示意图。
具体实施方式
下面给出若干实施例对本发明作进一步的详细说明：
实施例1：
采用H13工具钢粉末，粉末颗粒度为45微米，
取50g Mg(NO3)2·6H2O的盐溶于100g去离子水中，添加入合适的表面活性剂，形成混合溶液；
将该溶液逐层喷印在H13工具钢粉末层，喷印的区域为零件的轮廓线，层厚为100微米。
将打印的零件移入真空烧结炉烧结，烧结的温度设定为：
25~800, 升温速率为10/分钟
800~1200，升温速率为5/分钟
1200保温60分钟
1200到800，降温速率为10/分钟
800~400，降温速率为20/分钟
而后随炉冷却。
实验表明在喷射了抑制剂的区域粉末烧结被有效抑制，SEM观察的结果如附图1所示。

Claims (1)

1.一种金属打印抑制剂，其特征在于，由下列质量份数的组份组成：
硝酸镁35-45份，氯化镁0-15份，水55-65份。
CN201610294340.9A 2016-05-03 2016-05-03 一种金属打印抑制剂 Active CN105921744B (zh)