CN105919161A - Cigarette filter stick capable of softening aroma - Google Patents
Cigarette filter stick capable of softening aroma Download PDFInfo
- Publication number
- CN105919161A CN105919161A CN201610361826.XA CN201610361826A CN105919161A CN 105919161 A CN105919161 A CN 105919161A CN 201610361826 A CN201610361826 A CN 201610361826A CN 105919161 A CN105919161 A CN 105919161A
- Authority
- CN
- China
- Prior art keywords
- parts
- cigarette filter
- prepared
- cigarette
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cigarette filter stick capable of softening the aroma. The cigarette filter stick is prepared from raw materials in parts by weight as follows: 5.8-7 parts of calcium stearate, 83-90 parts of polypropylene resin, 1.2-2 parts of polyvinyl alcohol, 0.7-1 part of dibenylidene sorbitol, 4.8-5 parts of silica gel, 2.5-3 parts of activated carbon, 35-40 parts of banana peels, 0.2-0.3 parts of an aluminate coupling agent and a proper amount of deionized water. The prepared cigarette filter stick can realize effects of reducing irritation, enriching the cigarette aroma and improving the remaining taste, is low in production cost, high in efficiency and good in molding effect, can reduce the danger of cigarettes and has the practical production significance and value.
Description
Technical field
The present invention relates to cigarette filter rod technical field, particularly relate to the cigarette filter rod of a kind of soft fragrance.
Background technology
The harmful substance that cigarette combustion produces, such as the N-nitrosamine in tar, benzopyrene, free radical etc., serious harm cigarette
The people's is healthy, and Chinese smoker is numerous, and Smoking is harmful to your health, must improve the safety of Medicated cigarette under existing conditions,
Inevitably cause the loss of fragrance matter, perfuming research to be carried out while reducing harmful substance, improve Medicated cigarette
Local flavor, meets consumer demand.Filter tip can with the harmful substance in effectively catching cigarette smoke, the most novel filter tip material
For reducing, cigarette smoke is coal-tar middle oil and other harmful components tool has very important significance in research.Adsorption technology subtracts at perfuming cigarette
Evil has important application, is added in filter tip after adsorbent essence, the requirement of perfuming can be met;Additionally add at filter tip
Add the adsorbent of suitable high absorption property, the CO in flue gas can be adsorbed.
In " application in perfuming cigarette harm reduction CO of the modified porous material " literary composition, author proposes to select delicate fragrance type spice two
Hydrogen actinidia lactone and geranyl acetone are applied research object, have selected aluminium silicate, montmorillonite and MCM-C41 for absorption storage perfume
Material, for presently, there are the fragrance material problem that release efficiency is the highest from these porous materials, by load glucose again
The method of high temperature cabonization is modified, and test result indicate that the adsorbent after carbonizing and modifying, and the acidic-group on its surface all increases,
Basic group all reduces, and the Desorption Activation Energy of Carbon on dihydroactinidiolide and geranyl acetone adsorbent after modification reduces,
Show that this method of modifying can effectively weaken adsorbent and show the adhesion with fragrance material, contribute to the slow release of fragrance material;
Reducing CO part, preparing the adsorbent of activated carbon supported copper the most respectively by different Cu source, testing and show to prepare
Two kinds of adsorbents all have preferably reduction CO effect.Although author is pretty good in perfuming harm reduction each side effect, but comprehensively real
Border effect and cost consideration, process is loaded down with trivial details, does not possess actual application, is unfavorable for large-scale promotion, and the present invention is from reality
Occurring, the filter stick material understanding China's tobacco business use is mainly cellulose diacetate and polypropylene fibre, diacetate fiber
Element fall Jiaozhuo is used substantially, comfortable taste, but its raw material sources are limited, and price is high, and complex manufacturing is seriously polluted, polypropylene
Fiber is cheap, and chemical stability is good, but owing to the polarity of this material is little, smooth surface, to the nicotine in flue gas and tar
Absorbability poor diacetate fiber so that it is only used in low-grade medicated cigarette, and polypropylene fibre is modified by the present invention,
Make fiber surface coarse, introduce functional group, strengthen its absorption and retain the performance of harmful ingredients in flue gas, reduce cost, economize on resources,
Invention is made to possess good Social benefit and economic benefit.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that the cigarette filter rod of a kind of soft fragrance.
The present invention is achieved by the following technical solutions:
The cigarette filter rod of a kind of soft fragrance, is made up of the raw material of following weight portion: calcium stearate 5.8-7, polypropylene tree
Fat 83-90, polyvinyl alcohol 1.2-2, dibenzal sorbitol 0.7-1, silica gel 4.8-5, activated carbon 2.5-3, Pericarpium Musae 35-40, aluminum
Acid esters coupling agent 0.2-0.3, deionized water are appropriate.
The cigarette filter rod of described a kind of soft fragrance, is made up of step in detail below:
(1) being added to after being cleaned up by Pericarpium Musae in agitator, quickly stir pulping, rotating speed is 1800-2000 rev/min, then
Deliver in high-pressure sterilizing pot sterilizing 60-90min at 121 DEG C, after natural cooling, add the silicon dioxide of Fructus Musae latex quality 3-5%
With the stearic acid of 0.5-1%, liter high-temperature is to adding aluminate coupling agent when 35-40 DEG C, mix homogeneously is placed under nitrogen atmosphere
Calcine 1-2 at 200-225 DEG C, pulverize standby after cooling;
(2) calcium stearate is added in the Oleum Terebinthinae of 15-18 times amount, is evenly stirred until dissolving, be subsequently adding the polypropylene tree of 40%
Fat mixes, and heated and stirred is completely dissolved to polypropylene, adds polyvinyl alcohol and two benzal Pyrusussuriensiss when temperature is cooled to 40-55 DEG C
Alcohol, ultrasonic disperse is uniform, is then added to pelletize in double screw extruder and makes master batch, by washing with alcohol post-drying for several times and residue
Acrylic resin blending and modifying to make modified polypropene standby;
(3) modified polypropene prepared by silica gel, activated carbon and step (2) is respectively placed in baking oven drying, drains moisture, cooling
After modified polypropene is cut into granule, the melt blending 20min in banbury by modified polypropylene particles and activated carbon granule, so
Rear addition silica gel continues 30min is blended, and cuts into the granule of uniform particle sizes after taking out cooling, be placed on capillary rheometer
In, make mixing precursor, precursor is clamped on fixture, add in hot tank at the environment of 170-180 DEG C, with the speed of 10mm/min
Uniform Tension makes fiber;
(4) load essence on product step (1) prepared, be coated in modification prepared by step (3) by binding agent compound poly-
On tacryl, after drying, conventionally make cigarette filter rod.
The invention have the advantage that the present invention pollutes for the reduction that economizes on resources, select polypropylene fibre to replace two acetic acid fine
Tie up as cigarette filter rod, use calcium stearate etc. to polypropylene modification to improve the shortcoming of polypropylene fibre so that it is surface goes out
Existing hole, crack and groove increase its specific surface area, and also use porous and poromerics silica gel, activated carbon to change polypropylene
Property so that it is become capillary polypropylene material, improve its adsorptivity further, and the means using solid phase to stretch make fiber,
Avoid the impact on polypropylene fibre absorption property of the electrostatic spinning intermediate ion liquid, improve safety, and in medicated cigarette
Harmful substance plays good crown_interception, also utilizes discarded Pericarpium Musae as adsorbing material, asepsis environment-protecting, economizes on resources,
And to its mixed and modified stability that improve material and mechanical property, and it is good to carry fragrance energy, does not affect mouthfeel, it is possible to band
Come good suction impression, cigarette filter rod prepared by the present invention, it is possible to playing reduction stimulates, enriches the work that cigarette is fragrant, improve pleasant impression
With, become to produce low cost, efficiency is high, good forming effect, and can the hazardness of Medicated cigarette, there is actual production meaning and value.
Detailed description of the invention
The cigarette filter rod of a kind of soft fragrance, is made up of the raw material of following weight portion (kilogram): calcium stearate 5.8,
Acrylic resin 83, polyvinyl alcohol 1.2, dibenzal sorbitol 0.7, silica gel 4.8, activated carbon 2.5, Pericarpium Musae 35, Aluminate are even
Connection agent 0.2, deionized water is appropriate.
The cigarette filter rod of described a kind of soft fragrance, is made up of step in detail below:
(1) being added to after being cleaned up by Pericarpium Musae in agitator, quickly stir pulping, rotating speed is 1800 revs/min, is then delivered to height
In pressure autoclave, sterilizing 60min at 121 DEG C, adds silicon dioxide and the tristearin of 0.5% of Fructus Musae latex quality 3% after natural cooling
Acid, rises high-temperature and is placed at lower 200 DEG C of nitrogen atmosphere calcining 1 to addition aluminate coupling agent when 35 DEG C, mix homogeneously, cool down
Rear pulverizing is standby;
(2) calcium stearate is added in the Oleum Terebinthinae of 15 times amount, is evenly stirred until dissolving, be subsequently adding the acrylic resin of 40%
Mixing, heated and stirred is completely dissolved to polypropylene, adds polyvinyl alcohol and dibenzal sorbitol when temperature is cooled to 40 DEG C, super
Sound is uniformly dispersed, and is then added to pelletize in double screw extruder and makes master batch, by washing with alcohol post-drying for several times and remaining poly-
It is standby that allyl resin blending and modifying makes modified polypropene;
(3) modified polypropene prepared by silica gel, activated carbon and step (2) is respectively placed in baking oven drying, drains moisture, cooling
After modified polypropene is cut into granule, the melt blending 20min in banbury by modified polypropylene particles and activated carbon granule, so
Rear addition silica gel continues 30min is blended, and cuts into the granule of uniform particle sizes after taking out cooling, be placed on capillary rheometer
In, to make mixing precursor, precursor is clamped on fixture, add in hot tank at the environment of 170 DEG C, the speed with 10mm/min is uniform
Fiber is made in stretching;
(4) load essence on product step (1) prepared, be coated in modification prepared by step (3) by binding agent compound poly-
On tacryl, after drying, conventionally make cigarette filter rod.
Cigarette sample is prepared, with the Medicated cigarette only adding polypropylene fibre as compareing, with reference to ISO's and GB according to embodiment
Method detects, and test result is as follows:
Comparison Medicated cigarette:
Puff number (mouth /): 8.1;TPM (mg/ props up): 14.45;Nicotine (mg/ props up): 1.15;Tar (mg/ props up):
9.5;Cd reduction rate (%): 14.5;Pb reduction rate (%): 14.6;CO(mg/ props up): 11.5;
Test Medicated cigarette:
Puff number (mouth /): 7.9;TPM (mg/ props up): 11.53;Nicotine (mg/ props up): 1.08;Tar (mg/ props up):
9.1;Cd reduction rate (%): 21.14;Pb reduction rate (%): 21.12;CO(mg/ props up): 10.2.
Claims (2)
1. the cigarette filter rod of a soft fragrance, it is characterised in that be made up of the raw material of following weight portion: calcium stearate
5.8-7, acrylic resin 83-90, polyvinyl alcohol 1.2-2, dibenzal sorbitol 0.7-1, silica gel 4.8-5, activated carbon 2.5-3,
Pericarpium Musae 35-40, aluminate coupling agent 0.2-0.3, deionized water are appropriate.
The cigarette filter rod of a kind of soft fragrance, it is characterised in that by the preparation system of step in detail below
Become:
(1) being added to after being cleaned up by Pericarpium Musae in agitator, quickly stir pulping, rotating speed is 1800-2000 rev/min, then
Deliver in high-pressure sterilizing pot sterilizing 60-90min at 121 DEG C, after natural cooling, add the silicon dioxide of Fructus Musae latex quality 3-5%
With the stearic acid of 0.5-1%, liter high-temperature is to adding aluminate coupling agent when 35-40 DEG C, mix homogeneously is placed under nitrogen atmosphere
Calcine 1-2 at 200-225 DEG C, pulverize standby after cooling;
(2) calcium stearate is added in the Oleum Terebinthinae of 15-18 times amount, is evenly stirred until dissolving, be subsequently adding the polypropylene tree of 40%
Fat mixes, and heated and stirred is completely dissolved to polypropylene, adds polyvinyl alcohol and two benzal Pyrusussuriensiss when temperature is cooled to 40-55 DEG C
Alcohol, ultrasonic disperse is uniform, is then added to pelletize in double screw extruder and makes master batch, by washing with alcohol post-drying for several times and residue
Acrylic resin blending and modifying to make modified polypropene standby;
(3) modified polypropene prepared by silica gel, activated carbon and step (2) is respectively placed in baking oven drying, drains moisture, cooling
After modified polypropene is cut into granule, the melt blending 20min in banbury by modified polypropylene particles and activated carbon granule, so
Rear addition silica gel continues 30min is blended, and cuts into the granule of uniform particle sizes after taking out cooling, be placed on capillary rheometer
In, make mixing precursor, precursor is clamped on fixture, add in hot tank at the environment of 170-180 DEG C, with the speed of 10mm/min
Uniform Tension makes fiber;
(4) load essence on product step (1) prepared, be coated in modification prepared by step (3) by binding agent compound poly-
On tacryl, after drying, conventionally make cigarette filter rod.