CN105906890A - 提高车用橡胶部件耐磨性能的方法 - Google Patents

提高车用橡胶部件耐磨性能的方法 Download PDF

Info

Publication number
CN105906890A
CN105906890A CN201610449143.XA CN201610449143A CN105906890A CN 105906890 A CN105906890 A CN 105906890A CN 201610449143 A CN201610449143 A CN 201610449143A CN 105906890 A CN105906890 A CN 105906890A
Authority
CN
China
Prior art keywords
parts
rubber component
rubber components
wear resistance
carbon black
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610449143.XA
Other languages
English (en)
Inventor
陈永亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU ZHONGPEI RUBBER PARTS MANUFACTURING Co Ltd
Original Assignee
LIUZHOU ZHONGPEI RUBBER PARTS MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU ZHONGPEI RUBBER PARTS MANUFACTURING Co Ltd filed Critical LIUZHOU ZHONGPEI RUBBER PARTS MANUFACTURING Co Ltd
Priority to CN201610449143.XA priority Critical patent/CN105906890A/zh
Publication of CN105906890A publication Critical patent/CN105906890A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种提高车用橡胶部件耐磨性能的方法,属于车用橡胶制造技术领域。本发明包括在橡胶部件的制备过程中加入占橡胶部件质量10%~15%的添加剂;其中,该添加剂按重量份计,由松香20份~30份、石油1份~5份、富马酸5份~8份以及炭黑5份~8份组成。本发明主要是通过在橡胶部件的制备过程中加入一定量的、由松香、石油、富马酸以及炭黑按特定比例组成的添加剂,从而提高橡胶部件的耐磨性能。

Description

提高车用橡胶部件耐磨性能的方法
技术领域
本发明属于汽车橡胶配件制造技术领域,尤其涉及一种提高车用橡胶部件耐磨性能的方法。
背景技术
汽车工业已成为我国国民经济的支柱产业,其发展影响并带动着相关产业特别是橡胶零配件工业的发展。汽车橡胶配件在汽车工业中占有非常重要的位置,其产品性能和品质直接影响着整车的质量。因此,为了适应汽车工业的发展,国内外均投入了大量的资金和人力对汽车用橡胶配件从材料、产品结构、装备和加工工艺等方面进行大量的工作。
发明内容
本发明所要解决的技术问题是提供一种提高车用橡胶部件耐磨性能的方法。
为了解决上述技术问题,本发明所采用的技术方案是:
在橡胶部件的制备过程中加入占橡胶部件质量10%~15%的添加剂;其中,该添加剂按重量份计,由松香20份~30份、石油1份~5份、富马酸5份~8份以及炭黑5份~8份组成。
由于采用上述技术方案,本发明具有如下有益效果:
本发明主要是通过在橡胶部件的制备过程中加入一定量的、由松香、石油、富马酸以及炭黑按特定比例组成的添加剂,从而提高橡胶部件的耐磨性能。
具体实施方式
以下结合具体实例对本发明作进一步详述:
实施例1
提高车用橡胶部件耐磨性能的方法如下:
在橡胶部件的制备过程中加入占橡胶部件质量10%的添加剂;其中,该添加剂按重量份计,由松香20份、石油1份、富马酸5份以及炭黑8份组成。
经测试发现,本实施例制得的车用橡胶部件的阿克隆磨耗仅为0.0045 cm3·(1.61km)-1
实施例2
提高车用橡胶部件耐磨性能的方法如下:
在橡胶部件的制备过程中加入占橡胶部件质量15%的添加剂;其中,该添加剂按重量份计,由松香30份、石油5份、富马酸8份以及炭黑6份组成。
经测试发现,本实施例制得的车用橡胶部件的阿克隆磨耗仅为0.0044cm3·(1.61km)-1
实施例3
提高车用橡胶部件耐磨性能的方法如下:
在橡胶部件的制备过程中加入占橡胶部件质量12%的添加剂;其中,该添加剂按重量份计,由松香25份、石油3份、富马酸7份以及炭黑5份组成。
经测试发现,本实施例制得的车用橡胶部件的阿克隆磨耗仅为0.0046 cm3·(1.61km)-1

Claims (1)

1.一种提高车用橡胶部件耐磨性能的方法,其特征在于:在橡胶部件的制备过程中加入占橡胶部件质量10%~15%的添加剂;其中,该添加剂按重量份计,由松香20份~30份、石油1份~5份、富马酸5份~8份以及炭黑5份~8份组成。
CN201610449143.XA 2016-06-21 2016-06-21 提高车用橡胶部件耐磨性能的方法 Pending CN105906890A (zh)