CN105859966B - 一种含有锌元素的高吸水性树脂及其制备方法 - Google Patents
一种含有锌元素的高吸水性树脂及其制备方法 Download PDFInfo
- Publication number
- CN105859966B CN105859966B CN201610234763.1A CN201610234763A CN105859966B CN 105859966 B CN105859966 B CN 105859966B CN 201610234763 A CN201610234763 A CN 201610234763A CN 105859966 B CN105859966 B CN 105859966B
- Authority
- CN
- China
- Prior art keywords
- starch
- ficiency
- zinc
- acrylic acid
- graft copolymerization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种含有锌元素的高吸水性树脂及其制备方法。该方法包括如下步骤:(1)制备包含有锌元素的淀粉糊;(2)用强碱中和丙烯酸;(3)在生物酶催化引发下,淀粉与丙烯酸进行接枝共聚反应;(4)将步骤(3)中所得接枝共聚产物干燥并粉碎,即得产品。本发明以生物酶为催化引发剂制备淀粉接枝共聚丙烯酸高吸水性树脂,制备工艺具有反应条件温和、反应过程易控以及绿色环保无污染等优点。通过该方法制得的吸水树脂具有淀粉接枝率高、吸水率高、生物降解性能好等特性,并且由于包含有微量元素锌,又能够很好地解决在沙地、瘠薄山地或雨水冲刷较重的土壤上栽种植物的“小叶病”问题。
Description
技术领域
本发明涉及生物酶催化及功能高分子材料领域,具体涉及一种含有锌元素的高吸水性树脂及其制备方法。更具体地,涉及一种以生物酶为催化引发剂制备的含有锌元素的高吸水性树脂及其制备方法。
背景技术
高吸水性树脂是一类含有羧基、羟基等强亲水性官能团,并具有空间网络结构的功能高分子聚合物。它通过水合作用能迅速地吸收几十倍乃至千倍自身重量的水,也能吸收几十倍至百倍的食盐水、血液和尿液等液体。作为一种新型功能高分子材料,高吸水性树脂具有吸水量大和保水性强的特点,它完全不同于传统的吸水材料(如海绵、纸、棉等),在农林、园艺、水土保持、医疗、化妆品和建材等领域有着广泛的用途。
淀粉是一种天然高分子化合物,具有来源广泛、价格低廉、可再生等优异特性。将淀粉与丙烯酸接枝共聚,可以制备出具有高吸水特性,易于生物降解且环境友好的吸水树脂。公开号为CN102093513A的专利提供了一种马铃薯淀粉接枝丙烯酸制备吸水树脂的方法,所制得的可降解环保型吸水树脂的蒸馏水吸水率为300~1200g/g,5.0%氯化钠水溶液的吸水率为35~125g/g;公开号为CN103073684A的专利将淀粉加入海藻酸钠与丙烯酸的聚合体系,制备了一种淀粉/丙烯酸复合高吸水树脂,吸水倍率在890~960g/g,吸生理盐水的倍率在98~110g/g;公开号为CN104193900A的专利将糊化的小麦淀粉糊与丙烯酸钠接枝共聚,并向该体系加入黑曲霉菌悬液或枯草芽孢杆菌悬液,制备了一种多孔淀粉系高吸水树脂,该吸水树脂具有吸水速率高、生物降解性强、耐盐性强等优点。由此可见,淀粉高吸水性树脂以其优良的特性,已经得到了材料开发者们的广泛关注。
然而,目前针对淀粉接枝丙烯酸高吸水性树脂的开发和利用,多数采用铈盐、过硫酸盐、锰盐、溴酸盐等化学物质以及J射线作为催化引发剂,这些化学物质作为催化引发剂存在反应不易控制、均聚物含量高和化学污染问题;J射线催化引发存在设备投入大,运行成本高,安全环保要求严等问题。
除此之外,锌是影响植物生长发育的一种重要微量元素。在沙地、瘠薄山地或雨水冲刷较重的土壤中,含锌盐少且易流失;在碱性土壤中锌盐常转化为难溶状态,不易被植物吸收;另外,土壤过湿,通气不好,也会降低根吸收锌的能力,这些情况都可以引起植物发生缺锌症状。锌影响到植株体内生长素的合成,所以植物缺锌时,植株矮小,叶片分化受阻,而且畸形生长,很多植物幼苗缺锌时,会发生“小叶病”,有时呈簇生状,叶片脉间失绿黄化,有褐色斑点,并逐渐扩大成棕褐色的坏死斑点。林木和果树缺锌时,表现发芽较晚,新梢节间缩短,数月后可出现枯梢或病枝枯死现象。幼树缺锌,根系发育不良,老树则有根系腐烂现象。患病果树上的花显著变小,不易坐果,果实小而畸形。
因此,提供一种含有锌元素的高吸水性树脂也是当前较为迫切的问题。
发明内容
本发明的一个目的是针对上述问题提供一种含有锌元素的高吸水性树脂及其制备方法。具体地,本发明提供一种以生物酶为引发剂制备的含有锌元素的高吸水性树脂及其制备方法。以生物酶催化引发具有反应条件温和、反应过程易控以及绿色环保无污染等优点,制得淀粉接枝率高、吸水率高、生物降解性能好的淀粉接枝丙烯酸高吸水性树脂。同时,由于该高吸水性树脂包含有微量元素锌,所以能够很好地解决当前在沙地、瘠薄山地或雨水冲刷较重的土壤上种植的植物中普遍存在“小叶病”的问题。
为实现上述目的,根据本发明的一个方面,提供了一种含有锌元素的高吸水性树脂的制备方法,所述制备方法的步骤包括:
(1)制备包含有锌元素的淀粉糊;
(2)用强碱中和丙烯酸;
(3)在生物酶催化引发下,淀粉与丙烯酸进行接枝共聚反应;
(4)将步骤(3)中所得接枝共聚产物干燥并粉碎,即得产品。
优选地,步骤(1)所述锌元素选自七水硫酸锌、一水硫酸锌、碱式硫酸锌、氯化锌、磷酸锌、碱式碳酸锌、木质素碳酸锌、环烷酸锌和乙二胺四乙酸锌钠等的一种或多种,优选七水硫酸锌或氯化锌或乙二胺四乙酸锌钠。
优选地,步骤(1)制备包含有锌元素的淀粉糊是将含有锌元素的物质溶于水中并加入淀粉,升温糊化一定时间后,降至室温,制得1%~15%淀粉糊。所述淀粉为谷类、薯类、豆类或根茎类淀粉中的一种或多种,且优选为糯淀粉或蜡质淀粉;所述淀粉糊化温度为60~100℃,优选为85~95℃;所述糊化保温时间为不小于0.5h,优选为1h。
优选地,步骤(2)中的中和丙烯酸所用的强碱为氢氧化钠或氢氧化钾,优选为20%~50%氢氧化钠;所述丙烯酸的中和度为50%~95%;优选为在冰浴下中和度为70%~90%。
优选地,步骤(3)为将步骤(1)所得淀粉糊与步骤(2)所得中和丙烯酸混合,升温并保温,然后依次加入生物酶,双氧水,N,N’–亚甲基双丙烯酰胺,在氮气保护下保温一定时间,在生物酶催化引发下使淀粉和丙烯酸进行接枝共聚反应。
优选地,步骤(3)中生物酶催化引发剂为辣根过氧化物酶、大豆过氧化物酶、亚铁血红素酶或氨基酸氧化酶,优选为辣根过氧化物酶。
优选地,淀粉与丙烯酸质量之比为1∶10~1∶3;锌元素含量为0.05%~0.5%;
生物酶量为0.05%~2%;双氧水量为0.1%~2%;N,N’–亚甲基双丙烯酰胺为0.01%~1%。
优选地,接枝共聚反应温度为10~40℃,接枝共聚反应时间为1~10h;接枝共聚反应温度优选为25~35℃,接枝共聚反应时间优选为3~7h。
优选地,接枝共聚产物的干燥温度为70~200℃,干燥时间为3~10h。
根据本发明的另一方面,还提供了一种淀粉接枝丙烯酸高吸水性树脂,其中,锌元素的含量为0.05%~0.5%。
本发明的有益效果为:本发明以生物酶为引发剂所制备淀粉接枝丙烯酸高吸水性树脂,具有淀粉接枝率高、吸水率高、生物降解能力强等优异特性。而且,由于加入了微量元素锌,可使得本发明的含有锌的高吸水性树脂能够很好地解决当前在沙地、瘠薄山地或雨水冲刷较重的土壤上种植的植物中普遍存在的“小叶病”的问题。本发明提供的制备方法操作工艺简单,具有反应条件温和、反应易控以及绿色环保无污染等优点。通过本发明提供的方法所制备的淀粉接枝丙烯酸高吸水性树脂具有较高的吸水率,吸水率在1000~2300g/g。
具体实施方式
下述实施例对本发明进行详细地说明,但仅在于说明本发明而不对本发明构成限制。在不背离本发明精神和实质的前提下,对本发明所作的修饰或者替换,均属于本发明的范畴d
实施例1
(1)将470.4mg七水硫酸锌(ZnSO4·7H2O)溶解于95g水中,加入5g糯玉米淀粉,在80℃下糊化0.5至1h,待温度降至室温,制得5%的糯玉米淀粉糊。此外,可使用1%~15%之间任意浓度的糯玉米淀粉糊。
(2)称取20g丙烯酸,冰浴下加入30%氢氧化钠35g中和丙烯酸。
(3)将步骤(1)所得到的糯玉米淀粉糊和步骤(2)所得到的中和丙烯酸混合,搅拌状态下,依次加入2.5mL辣根过氧化物酶、2.5mL双氧水、0.010g N,N’–亚甲基双丙烯酰胺,在氮气保护下,在30℃下恒温反应5h。
(4)将步骤(3)所得产物取出,烘干并粉碎,即得糯玉米淀粉接枝丙烯酸高吸水性树脂。
在制得的含有锌的高吸水性树脂中,锌元素的含量为0.1%。
通过常规吸水率的测定实验,测得该吸水树脂的平衡吸水率为1700g/g。
此外,将上述制得的含有锌的高吸水性树脂应用于在沙地、瘠薄山地或雨水冲刷较重的土壤处,可以很好地防治或治愈在这些土地上生长的植物的“小叶病”的病症。
需要说明的是,除七水硫酸锌(ZnSO4·7H2O)之外,可以使用适应量的一水硫酸锌、碱式硫酸锌、氯化锌、磷酸锌、碱式碳酸锌、木质素碳酸锌、环烷酸锌和乙二胺四乙酸锌钠等中的一种或多种。并且,除糯玉米淀粉之外,可以使用其他谷类、薯类、豆类或根茎类淀粉中的一种或多种糯淀粉或蜡质淀粉。
实施例2
(1)将632.6mg螯合态锌,例如,乙二胺四乙酸锌钠溶解于95g水中,加入5g马铃薯淀粉,在95℃下糊化0.5至1h,待温度降至室温,制得5%的马铃薯淀粉糊。此外,可使用1%~15%之间任意浓度的马铃薯淀粉糊。
(2)称取20g丙烯酸,冰浴下加入30%氢氧化钠35g中和丙烯酸。
(3)将步骤(1)所得到的马铃薯淀粉糊和步骤(2)所得到的中和丙烯酸混合,搅拌状态下,依次加入3.5mL辣根过氧化物酶、3.5mL双氧水、0.010g N,N’–亚甲基双丙烯酰胺,在氮气保护下,在25℃下恒温反应9h。
(4)将步骤(3)所得产物取出,烘干并粉碎,即得马铃薯淀粉接枝丙烯酸高吸水性树脂。
在制得的含有锌的高吸水性树脂中,锌元素的含量为0.3%。
通过常规吸水率的测定实验,测得该吸水树脂的平衡吸水率为2050g/g。
此外,将上述制得的含有锌元素的高吸水性树脂应用于在沙地、瘠薄山地或雨水冲刷较重的土壤处,可以很好地防治或治愈在这些土地上生长的植物的“小叶病”的病症。
需要说明的是,除螯合态锌,如乙二胺四乙酸锌钠之外,可以使用适应量的七水硫酸锌、一水硫酸锌、碱式硫酸锌、氯化锌、磷酸锌、碱式碳酸锌、木质素碳酸锌和环烷酸锌等中的一种或多种。并且,除马铃薯淀粉之外,可以使用其他谷类、薯类、豆类或根茎类淀粉中的一种或多种糯淀粉或蜡质淀粉。
实施例3:
(1)将131.9mg氯化锌溶解于95g水中,加入5g藕淀粉糊,在90℃下糊化0.5至1h,待温度降至室温,制得5%的藕淀粉糊。此外,可使用1%~15%之间任意浓度的藕淀粉糊。
(2)称取20g丙烯酸,冰浴下加入30%氢氧化钠30g中和丙烯酸。
(3)将步骤(1)所得到的藕淀粉糊和步骤(2)所得到的中和丙烯酸混合,搅拌状态下,依次加入4mL辣根过氧化物酶、4mL双氧水、0.010g N,N’–亚甲基双丙烯酰胺,在氮气保护下,在35℃下恒温反应3h。
(4)将步骤(3)所得产物取出,烘干并粉碎,即得藕淀粉接枝丙烯酸高吸水性树脂。
在制得的含有锌元素的高吸水性树脂中,锌元素含量为0.25%。
通过常规吸水率的测定实验,测得该吸水树脂的平衡吸水率为1800g/g。
此外,将上述制得的含有锌元素的高吸水性树脂应用于在沙地、瘠薄山地或雨水冲刷较重的土壤处,可以很好地防治或治愈在这些土地上生长的植物的“小叶病”的病症。
需要说明的是,除氯化锌之外,可以使用适应量的七水硫酸锌、一水硫酸锌、碱式硫酸锌、氯化锌、磷酸锌、碱式碳酸锌、木质素碳酸锌、环烷酸锌和螯合态锌,如乙二胺四乙酸锌钠等中的一种或多种。并且,除藕淀粉之外,可以使用其他谷类、薯类、豆类或根茎类淀粉中的一种或多种糯淀粉或蜡质淀粉。
Claims (8)
1.一种含有锌元素的高吸水性树脂的制备方法,其特征在于,所述制备方法的步骤包括:
(1)制备包含有锌元素的淀粉糊,所述淀粉糊化温度为60~100℃;
步骤(1)所述锌元素选自七水硫酸锌、一水硫酸锌、碱式硫酸锌、氯化锌、磷酸锌、碱式碳酸锌、木质素碳酸锌、环烷酸锌和乙二胺四乙酸锌钠等的一种或多种;
步骤(1)制备包含有锌元素的淀粉糊是将含有锌元素的物质溶于水中并加入淀粉,升温糊化一定时间后,降至室温,制得1%~15%淀粉糊;
(2)用强碱中和丙烯酸;
(3)在生物酶催化引发下,淀粉与丙烯酸进行接枝共聚反应,接枝共聚反应温度为25~35℃,接枝共聚反应时间为3~7h;
具体为:将步骤(1)所得淀粉糊与步骤(2)所得中和丙烯酸混合,升温并保温,然后依次加入辣根过氧化物酶、双氧水、N,N’–亚甲基双丙烯酰胺,在氮气保护下保温一定时间,在辣根过氧化物酶催化引发下使淀粉和丙烯酸进行接枝共聚反应;
(4)将步骤(3)中所得接枝共聚产物干燥并粉碎,即得产品。
2.根据权利要求1所述的方法,其特征在于,所述锌元素选自七水硫酸锌或氯化锌或乙二胺四乙酸锌钠。
3.根据权利要求1或2所述的方法,其特征在于,所述淀粉为谷类、薯类、豆类中的一种或多种;所述淀粉糊化温度为85~95℃;所述糊化保温时间为不小于0.5h。
4.根据权利要求1或2所述的方法,其特征在于,步骤(2)中的中和丙烯酸所用的强碱为氢氧化钠或氢氧化钾;所述丙烯酸的中和度为50%~95%。
5.根据权利要求1所述的方法,其特征在于,淀粉与丙烯酸质量之比为1∶10~1∶3;
锌元素含量为0.05%~0.5%;
生物酶量为0.05%~2%;
双氧水量为0.1%~2%;
N,N’–亚甲基双丙烯酰胺为0.01%~1%。
6.根据权利要求4所述的方法,其特征在于,接枝共聚反应温度为10~40℃,接枝共聚反应时间为1~10h。
7.根据权利要求1或2所述的方法,其特征在于,接枝共聚产物的干燥温度为70~200℃,干燥时间为3~10h。
8.一种通过权利要求1-7中的任一项所述的方法制备得到的淀粉接枝丙烯酸高吸水性树脂,其中,锌元素的含量为0.05%~0.5%。