CN105839454A - Rapidly-cured release film - Google Patents
Rapidly-cured release film Download PDFInfo
- Publication number
- CN105839454A CN105839454A CN201610127830.XA CN201610127830A CN105839454A CN 105839454 A CN105839454 A CN 105839454A CN 201610127830 A CN201610127830 A CN 201610127830A CN 105839454 A CN105839454 A CN 105839454A
- Authority
- CN
- China
- Prior art keywords
- coating
- film
- cloudy surface
- mould release
- rapidly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rapidly-cured release film. The rapidly-cured release film comprises a raw paper layer; the upper surface and lower surface of raw paper layer are respectively coated with a PE film and a PET film; and a matt antistatic coating is formed by coating of a matt antistatic agent which comprises silica particles, acrylic polyol with an average molecular weight of 500 to 2000, polyoxyalkylene series polyol resin with an average molecular weight of 200 to 2500, polyethylene glycol, cyclomethyl siloxane and 1-hydroxycyclohexylphenyl ketone-photoinitiator 184, wherein peak values occur when the particle sizes of the silica particles are in ranges of 0.1 to 2 [mu]m and 1.5 to 5 [mu]m according to size distribution results determined by using a laser diffraction-scattering method, and the average particle size of the particle sizes is 0.4 [mu]m or below. The rapidly-cured release film provided by the invention overcomes the problems that bonding force between a coating film layer and a release agent coating is low and peel strength is not stable and has especially superior capability in absorbing water in the form of bound water.
Description
Technical field
The present invention relates to a kind of mould release membrance, particularly to a kind of cloudy surface antistatic agent for mould release membrance.
Background technology
Release paper, also known as release paper, separate paper, is mainly used in the surface being covered in adhesive tape for protecting the glue of tape surface
Adhesive layer.Existing release paper is usually at one layer of leaching membrane layer of surface film of release paper ground paper layer that (material of employing mainly has
Polyethylene), then obtain release paper the surface of leaching membrane layer one layer of mould release coating (material of employing is mainly silicone oil) of coating.
But owing to leaching membrane layer flatness is high, poor adhesive force between mould release coating and leaching membrane layer, when release paper be coated with high viscosity
When the pad pasting of binding agent attaches, the binding agent that the mould release coating being easily caused in release paper is attached power bigger is taken away, thus
Local surfaces at pad pasting forms the mould release coating area being difficult to clean out, and destroys pure, concordance that pad pasting is overall.And
And owing to production process electrostatic is excessive, cause the local out-of-flatness of release coating layer, not only affect product peeling force stability, and
Easily produce electrostatic spark and cause fire.
Summary of the invention
It is an object of the present invention to provide a kind of fast setting mould release membrance, this fast setting mould release membrance had both solved the film of mould release membrance
Layer is the highest with mould release coating binding force, peeling force is unstable, improves again film surface anti-static performance, and also improves simultaneously
Scratch resistance performance.
For reaching above-mentioned purpose, the technical solution used in the present invention is: a kind of fast setting mould release membrance, described mould release membrance bag
Including upper and lower surface film respectively has the original paper layer of PE film and PET film, another surface-coated of the PET film of original paper layer to have cloudy surface
Anti-static coating, this another surface-coated of cloudy surface anti-static coating has mould release coating;Described cloudy surface anti-static coating is with release
The roughness on the surface of agent coating layer touch is 2.83 μm~3.32 μm, and it is protruding that this another surface of mould release coating has several
Portion;
Described cloudy surface anti-static coating is formed by the coating of cloudy surface antistatic agent, and this cloudy surface antistatic agent is by following masses percentage composition
Component composition:
Silica granule 3.8%,
Mean molecule quantity is the acrylic polyol 27.2% of 500 ~ 2000,
Mean molecule quantity is the resin 36.8% of the polyoxyalkylene series polyhydric alcohol of 200 ~ 2500,
Polyethylene Glycol 18.5%,
Cyclomethicone 6.2%,
1-hydroxycyclohexyl phenyl ketone-light trigger 184 7.5%;
The particle diameter of described silica granule be in the particle size distribution measured by laser diffraction and scattering method particle diameter 0.1 ~ 2 μm and 1.5 ~
It is respectively provided with peak value in the range of 5 μm and mean diameter is 4 μm or following.
In technique scheme, further improved plan is as follows:
In such scheme, described cloudy surface antistatic agent uses ultra-violet bands to be 280nm ~ 350nm, and illumination is 1200mW/cm2,
Described cloudy surface anti-static coating is irradiated, makes described component at the work of 1-hydroxycyclohexyl phenyl ketone-light trigger 184
Carry out polyreaction under with and obtain cloudy surface anti-static coating.
Owing to technique scheme is used, the present invention compared with prior art has following advantages and an effect:
1, fast setting mould release membrance of the present invention, it uses the acrylic polyol that mean molecule quantity is 500 ~ 2000 of certain content
With after the polyurethane resin of the resin polymerization of the polyoxyalkylene series polyhydric alcohol that mean molecule quantity is 200 ~ 2500 and with ring first
Radical siloxane mix, mean molecule quantity be 500 ~ 2000 acrylic polyol and mean molecule quantity be the polyoxygenated of 200 ~ 2500
Chain in the resin of alkene series polyhydric alcohol improves film surface anti-static performance, and also improves scratch resistance performance simultaneously;It is polynary
Alcohol acrylate monomer has the mean molecule quantity of 500 ~ 2000, if molecular weight is less than 500, the wearability of film tends to reducing,
If mean molecule quantity is more than 2000, during film-forming, the suitability is deteriorated.If polyalcohol acrylate monomer is specifically for second two
Alcohol, it is contemplated that water absorbing capacity, the Polyethylene Glycol that the present invention selects mean molecule quantity to be 200 ~ 1000, make use of its superior absorption
In conjunction with the ability of water, further increase anti-static effect.Owing to this acrylic polyol monomer has especially advantageous suction
Receiving the ability of the water combining water form, have anti-static effect, polyalcohol acrylate monomer all can use this monomer.
2, first the present invention is coated with cloudy surface anti-static coating to the surface of thin layer, passes through formula through cloudy surface anti-static coating
With the surface after PROCESS FOR TREATMENT, there is some uniform concaveconvex structures and anti-static effect, be then coated with at this surface silicon-coating mould release
Layer coating, the bottom surface of silicon mould release coating coating is penetrated at the notch on described cloudy surface anti-static coating surface in the liquid state, silicon from
Type agent coating coating is after solidification by being fixedly linked with cloudy surface anti-static coating at notch, therefore, adhesion more firmly, can
Lean on.And owing to antistatic processes, the impact that silicone oil coating instability is brought by electrostatic can be eliminated, release peeling force can be the most steady
Fixed, also avoid the generation of production process electrostatic spark.
3, the present invention uses light trigger 1-hydroxycyclohexyl phenyl ketone cause, mainly consider that it at wave band is
320-400nm ultraviolet light irradiate under, can instantaneous solidification film forming, can reach deep cure, there is good planarization and intensity.Institute
Stating light trigger is 1-hydroxycyclohexyl phenyl ketone-light trigger 184, is the ultraviolet initiator of a kind of efficient non yellowing,
For causing the UV polyreaction of unsaturated prepolymerization system, its mass content is 5~10 %.
4, fast setting mould release membrance of the present invention, described silica granule be particle diameter be the grain measured by laser diffraction and scattering method
In degree distribution, particle diameter is respectively provided with peak value in the range of 0.1 ~ 2 μm and 1.5 ~ 5 μm and mean diameter is 4 μm or following silicon
Stone granule, had both substantially increased atomized surface effect, in turn ensure that solidification effect.
5, the power of medium ultraviolet light of the present invention uses 1200mW/cm2If mainly power is less than 1200mW/cm2, film is the completeest
All solidstate, wearability reduces;If if power is higher than 1200mW/cm2, affecting film flatness, the suitability declines.Use ultraviolet ripple
Section is 320 ~ 400nm, and illumination is 1200mW/cm2, described cloudy surface coating agent is irradiated, makes described component special in the present invention
It being set for obtaining cloudy surface coating for carrying out polyreaction under the effect of the 1-hydroxycyclohexyl phenyl ketone of light trigger, thickness is 4 ~
10 μm, have an anti-static effect, then obtain cloudy surface release layer in one layer of mould release coating of surface-coated of described cloudy surface coating.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Embodiment: a kind of fast setting mould release membrance, described mould release membrance includes that upper and lower surface film respectively has PE film and PET
The original paper layer of film, another surface-coated of the PET film of original paper layer has cloudy surface anti-static coating, this another surface of cloudy surface anti-static coating
It is coated with mould release coating;The roughness on the surface of described cloudy surface anti-static coating and mould release coating layer touch be 2.83 μm~
3.32 μm, this another surface of mould release coating has several lobe;
Described cloudy surface anti-static coating is formed by the coating of cloudy surface antistatic agent, and this cloudy surface antistatic agent is by following masses percentage composition
Component composition:
Silica granule 3.8%,
Mean molecule quantity is the acrylic polyol 27.2% of 500 ~ 2000,
Mean molecule quantity is resin 36.8 % of the polyoxyalkylene series polyhydric alcohol of 200 ~ 2500,
Polyethylene Glycol 18.5%,
Cyclomethicone 6.2%,
1-hydroxycyclohexyl phenyl ketone-light trigger 184 7.5%;
The particle diameter of described silica granule be in the particle size distribution measured by laser diffraction and scattering method particle diameter 0.1 ~ 2 μm and 1.5 ~
It is respectively provided with peak value in the range of 5 μm and mean diameter is 4 μm or following.
Above-mentioned cloudy surface antistatic agent uses ultra-violet bands to be 280nm ~ 350nm, and illumination is 1200mW/cm2, to described mist
Face anti-static coating is irradiated, and makes described component carry out under the effect of 1-hydroxycyclohexyl phenyl ketone-light trigger 184
Polyreaction obtains cloudy surface anti-static coating.
Performance indications are as shown in table 1:
Table 1
(1), ocular estimate: the existence of outward appearance, transparency and crackle is evaluated by visual observation.No problem film
Being rated as satisfactory (O), problematic film is rated as unsatisfactory (X);
(2), private seal by release aspect private seal 10 times, be qualified without delustring, delustring is defective;
(3), hundred lattice test cross-cut testers tests without coming off for qualified products, come off for substandard product;
(4), peel off voltage roller and adhesive tape crimping (1 kilogram back and forth, speed 0.3m/min), in release face, thereafter, is used hands
Quickly peel off (10m/min), read adhesive tape with electrostatic field tester (model: SIMCO FMX-003) and glue the stripping of release face
The maximum of electrostatic pressure, electrostatic pressure is qualified products less than 0.3KV, and electrostatic pressure is substandard product more than 0.3KV;
(5), two, face of surface resistance value sheet resistance tester G parallel copper electrodes be placed in the arbitrary place of sample surfaces, press black
Color A key, waits about 30 seconds, resistance at LED display test, and ambient temperature and humidity is noted down.Display surface resistance < 1.0E+10
Ω/sq, (65%RH, 23 DEG C) is qualified;Display surface resistance > 1.0E+10 Ω/sq, (65%RH, 23 DEG C) is defective.
(6) wearability test is at the 500g/cm of steel wire face (#0000)2The pressure that adds hard conating face is rubbed after 30 times,
To not having scar to be denoted as O, it is denoted as X to there being scar.
(7) pencil hardness test evaluates the pencil hardness of hard coating film according to GB/T 6739-2006.
Above-described embodiment, only for technology design and the feature of the explanation present invention, its object is to allow person skilled in the art
Scholar will appreciate that present disclosure and implements according to this, can not limit the scope of the invention with this.All according to the present invention
The equivalence that spirit is made changes or modifies, and all should contain within protection scope of the present invention.
Claims (1)
1. a fast setting mould release membrance, it is characterised in that: include that upper and lower surface film respectively has PE film and PET film
Original paper layer, another surface-coated of the PET film of original paper layer has cloudy surface anti-static coating, this another surface-coated of cloudy surface anti-static coating
There is mould release coating;Described cloudy surface anti-static coating is 2.83 μm~3.32 μ with the roughness on the surface of mould release coating layer touch
M, this another surface of mould release coating has several lobe;
Described cloudy surface anti-static coating is formed by the coating of cloudy surface antistatic agent, and this cloudy surface antistatic agent is by following masses percentage composition
Component composition:
Silica granule 3.8%,
Mean molecule quantity is the acrylic polyol 27.2% of 500 ~ 2000,
Mean molecule quantity is resin 36.8 % of the polyoxyalkylene series polyhydric alcohol of 200 ~ 2500,
Polyethylene Glycol 18.5%,
Cyclomethicone 6.2%,
1-hydroxycyclohexyl phenyl ketone-light trigger 184 7.5%;
The particle diameter of described silica granule be in the particle size distribution measured by laser diffraction and scattering method particle diameter 0.1 ~ 2 μm and 1.5 ~
It is respectively provided with peak value in the range of 5 μm and mean diameter is 4 μm or following;
Described cloudy surface antistatic agent uses ultra-violet bands to be 280nm ~ 350nm, and illumination is 1200mW/cm2, described cloudy surface is prevented
Electrostatic coating is irradiated, and makes described component be polymerized under the effect of 1-hydroxycyclohexyl phenyl ketone-light trigger 184
Reaction obtains cloudy surface anti-static coating.