CN204054823U - The ultraviolet clear anti-fog fenestrated membrane of a kind of obstruct - Google Patents
The ultraviolet clear anti-fog fenestrated membrane of a kind of obstruct Download PDFInfo
- Publication number
- CN204054823U CN204054823U CN201420447118.4U CN201420447118U CN204054823U CN 204054823 U CN204054823 U CN 204054823U CN 201420447118 U CN201420447118 U CN 201420447118U CN 204054823 U CN204054823 U CN 204054823U
- Authority
- CN
- China
- Prior art keywords
- ultraviolet
- fog
- sensitive adhesive
- adhesive layer
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to and a kind of intercepts ultraviolet clear anti-fog fenestrated membrane, and it is by anti-fog layer (1), first transparent polyester film or polyethylene film base material (2-1), first ultraviolet-resistant pressure-sensitive adhesive layer (3-1), second transparent polyester film or polyethylene film base material (2-2), second ultraviolet-resistant pressure-sensitive adhesive layer (3-2) and mould release membrance (4) forms and each layer is complex as a whole.The utility model fenestrated membrane can intercept ultraviolet lastingly, again can be antifog lastingly.
Description
Technical field
The utility model relates to the ultraviolet clear anti-fog fenestrated membrane of a kind of obstruct, is particularly suitable for being pasted onto the glass surface of building or the glass surface of automobile.
Background technology
Furniture in building, carpet, artistic pictures, the fabrics such as curtain or automotive trim meeting accelerated ageing under sunlight or strong artificial light shine, especially under ultraviolet lighting, can photooxidative degradation be produced and cause greatly shortening its service life, at present, there is uv-shielding capacity difference and the problem such as ageing-resistant performance is not good in most domestic fenestrated membrane product, namely fenestrated membrane is to ultraviolet rejection rate < 90%, and along with the continuous increase of service time, the outward appearance of fenestrated membrane and physical property also can decline gradually, and above-mentioned fenestrated membrane product relies on electrical heating method and use anti-fog coating to realize antifog, but the former respond well price is high, the wasting of resources is large, anti-fog coating is just sprayed on the surfaces such as glass by the latter, but can not solidify, therefore antifog persistence difference and use inconvenient.Therefore, be badly in need of exploitation one both endurable obstruct ultraviolets, and also have the fenestrated membrane of lasting anti-fog effect, so that the interior trim of available protecting building or automobile and ensure that occupant is healthy, the interference of fog to security can also be reduced.
Summary of the invention
The purpose of this utility model is: provide one efficiently can intercept ultraviolet, the ultraviolet clear anti-fog fenestrated membrane of obstruct that again can be antifog lastingly.
The technical scheme realizing the utility model object is: the ultraviolet clear anti-fog fenestrated membrane of a kind of obstruct, and its innovative point is,
It to be made up of anti-fog layer, first transparent polyester film or polyethylene film base material, first ultraviolet-resistant pressure-sensitive adhesive layer, second transparent polyester film or polyethylene film base material, second ultraviolet-resistant pressure-sensitive adhesive layer and mould release membrance and each layer is complex as a whole, described anti-fog layer ultraviolet light polymerization is combined on a surface of first transparent polyester film or polyethylene film base material, the heat cure of first ultraviolet-resistant pressure-sensitive adhesive layer be combined in first transparent polyester film or polyethylene film base material another on the surface, a surface recombination of second transparent polyester film or polyethylene film base material is at the outer surface of first ultraviolet-resistant pressure-sensitive adhesive layer, the heat cure of second ultraviolet-resistant pressure-sensitive adhesive layer be combined in second transparent polyester film or polyethylene film base material another on the surface, mould release membrance is compounded in the outer surface of second ultraviolet-resistant pressure-sensitive adhesive layer.
In the ultraviolet clear anti-fog fenestrated membrane of the obstruct of technique scheme, described obstruct ultraviolet clear anti-fog fenestrated membrane thickness is 72 ~ 444 μm, and wherein, the thickness of anti-fog layer is 1 ~ 5 μm; The thickness of first transparent polyester film or polyethylene film base material is 20 ~ 175 μm; The thickness of first ultraviolet-resistant pressure-sensitive adhesive layer is 6 ~ 25 μm; The thickness of second transparent polyester film or polyethylene film base material is 20 ~ 175 μm; The thickness of second ultraviolet-resistant pressure-sensitive adhesive layer is 6 ~ 25 μm; The thickness of mould release membrance is 19 ~ 39 μm.
In the ultraviolet clear anti-fog fenestrated membrane of the obstruct of technique scheme, the thickness of described first ultraviolet-resistant pressure-sensitive adhesive layer is identical with the thickness of second ultraviolet-resistant pressure-sensitive adhesive layer, or different.
In the ultraviolet clear anti-fog fenestrated membrane of the obstruct of technique scheme, the thickness of described first transparent polyester film or polyethylene film base material is identical with the thickness of second transparent polyester film or polyethylene film base material, or different.
Technique effect of the present utility model is: the ultraviolet clear anti-fog fenestrated membrane of obstruct of the present utility model has composite construction, it to be made up of anti-fog layer, first transparent polyester film or polyethylene film base material, first ultraviolet-resistant pressure-sensitive adhesive layer, second transparent polyester film or polyethylene film base material, second ultraviolet-resistant pressure-sensitive adhesive layer and release film layer and each layer is complex as a whole, and each layer has mutual synergy.First ultraviolet-resistant pressure-sensitive adhesive layer and second ultraviolet-resistant pressure-sensitive adhesive layer of the ultraviolet clear anti-fog fenestrated membrane of obstruct of the present utility model are all by benzophenone type ultraviolet absorbent, benzotriazole ultraviolet absorber, acrylic acid adhesive, heat cure obtains on the surface that the mixed material of curing agent and solvent is coated in first transparent polyester film or polyethylene film base material respectively and on a surface of second transparent polyester film or polyethylene film base material, due to select benzophenone with the composite use of the ultraviolet absorber of benzotriazole and with consumption appropriate be suitable for other component coordinate, under each component is mutually collaborative, make first ultraviolet-resistant pressure-sensitive adhesive layer being formed and second ultraviolet-resistant pressure-sensitive adhesive layer all can the high molecular energy of quencher excitation state effectively and have the ability of enough seizure free radical Sum decomposition hydrogen peroxide, therefore, effectively can slow down the photodegradation of ultraviolet light and there is lasting ultraviolet-resistant effect, fenestrated membrane life cycle is made to obtain corresponding prolongation, and the antifogging agent composition of described anti-fog layer coordinates owing to have selected suitable hydrophilic heat cure solvent type acrylic resin SAA901 with other suitable components, under each component is mutually collaborative, surface after the curing of coating that this antifogging agent composition is formed is hydrophilic, little with the contact angle of water, therefore, very thin moisture film can be formed on this surface and mist can not be tied, thus producing anti-fog effect.Show according to great many of experiments, the antifogging agent composition of described anti-fog layer and the contact angle of water reach less than 6.5 °, and antifog persistence is good, antifogly reach more than 1 year; The ultraviolet-resistant rate of the ultraviolet clear anti-fog fenestrated membrane of obstruct of the present utility model reaches more than 99%, and ultraviolet-resistant performance is lasting; In addition, the preparation method of obstruct of the present utility model ultraviolet clear anti-fog fenestrated membrane is simple to operation, combine firmly between each layer, use very convenient, during use, after being peeled off by the outermost layer of mould release membrance, be pasted onto vehicle glass or glass of building surface, can ultraviolet be intercepted, antifogly lastingly can go back safety again.
Accompanying drawing explanation
Fig. 1 is the structural representation that the utility model intercepts ultraviolet clear anti-fog fenestrated membrane;
Fig. 2 is the chemical structural formula that the utility model intercepts ultraviolet clear anti-fog fenestrated membrane benzophenone type ultraviolet absorbent 2,2', 4,4'-used tetrahydroxybenzophenone;
Fig. 3 is the chemical structural formula that the utility model intercepts ultraviolet clear anti-fog fenestrated membrane benzotriazole used ultraviolet absorber 2-(the chloro-2H-124 Triazole of 5--2-base)-6-(1,1-dimethyl ethyl)-4-methylphenol.
Detailed description of the invention
Below in conjunction with drawings and Examples, the utility model is further described in detail, but not limited.
Embodiment is raw materials used, unless otherwise indicated, is commercially available industrial goods, can be buied by commercial channel.
As shown in Figure 1, to the ultraviolet clear anti-fog fenestrated membrane of obstruct of the present utility model it to be made up of anti-fog layer 1, first transparent polyester film or polyethylene film base material 2-1, first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, second transparent polyester film or polyethylene film base material 2-2, second ultraviolet-resistant pressure-sensitive adhesive layer 3-2 and mould release membrance 4 and each layer is complex as a whole, described anti-fog layer 1 ultraviolet light polymerization is combined on a surface of first transparent polyester film or polyethylene film base material 2-1, first ultraviolet-resistant pressure-sensitive adhesive layer 3-1 heat cure be combined in first transparent polyester film or polyethylene film base material 2-1 another on the surface, the surface recombination of second transparent polyester film or polyethylene film base material 2-2 is at the outer surface of first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, second ultraviolet-resistant pressure-sensitive adhesive layer 3-2 heat cure be combined in second transparent polyester film or polyethylene film base material 2-2 another on the surface, mould release membrance 4 is compounded in the outer surface of second ultraviolet-resistant pressure-sensitive adhesive layer 3-2.
Described obstruct ultraviolet clear anti-fog fenestrated membrane thickness is 72 ~ 444 μm, and wherein, the thickness of anti-fog layer 1 is 1 ~ 5 μm; The thickness of first transparent polyester film or polyethylene film base material 2-1 is 20 ~ 175 μm; The thickness of first ultraviolet-resistant pressure-sensitive adhesive layer 3-1 is 6 ~ 25 μm; The thickness of second transparent polyester film or polyethylene film base material 2-2 is 20 ~ 175 μm; The thickness of second ultraviolet-resistant pressure-sensitive adhesive layer 3-2 is 6 ~ 25 μm; The thickness of mould release membrance 4 is 19 ~ 39 μm.
The thickness of described first ultraviolet-resistant pressure-sensitive adhesive layer 3-1 is identical with the thickness of second ultraviolet-resistant pressure-sensitive adhesive layer 3-2, or different.
The thickness of described first transparent polyester film or polyethylene film base material 2-1 is identical with the thickness of second transparent polyester film or polyethylene film base material 2-2, or different.
Embodiment preparation intercepts ultraviolet clear anti-fog fenestrated membrane
Concrete operations are as follows:
(A) raw material is prepared
1. base material is prepared
Thickness is first transparent polyester film base material 2-1 of 23 μm; Prepare second transparent polyester film base material 2-2 that thickness is 36 μm; Prepare the mould release membrance 4 that thickness is 23 μm;
2. preparation forms the antifogging agent composition A ~ C of anti-fog layer
The antifogging agent composition forming anti-fog layer is by hydrophilic heat cure solvent type acrylic resin SAA901 9 ~ 14 wt%, propylene glycol monomethyl ether 55 ~ 76 wt%, dimethyl formamide 3 ~ 10 wt%, catalyst triethylene diamine 1 ~ 5 wt%, levelling agent BYK-333 1 ~ 5 wt%, isopropyl alcohol 5 ~ 26 wt%, ethanol 5 ~ 24 wt% mixes formation, wherein, each component sum forming the antifogging agent composition of anti-fog layer is 100 wt%, specifically fills a prescription in table 1.
Take each component by table 1 formula ratio and put into container, at environment temperature is 18 ~ 28 DEG C, is uniformly mixed the antifogging agent composition A ~ C that can obtain respectively and form anti-fog layer, packages spare.
Table 1
Note 1:SAA901 is the product grade of Xi'an Naviation Sanwo Chemical Co., Ltd.; Propylene glycol monomethyl ether, dimethyl methylamine, triethylene diamine are Shanghai Experimental Reagent Co., Ltd.'s product; BYK-333 is the product grade of German Bi Ke chemical company; Isopropyl alcohol and ethanol are from Changzhou Asource Chemical Co., Ltd.;
Note 2:SAA901 properties of product: outward appearance is colourless transparent liquid, and its solid is divided into 44.5 ± 1wt%(150 DEG C of mensuration), viscosity is 5 ± 0.5cps/25 DEG C;
Note 3: above-mentioned raw materials used also can be replaced by the equivalents of different factory;
3. the mixed material D ~ F of formation first ultraviolet-resistant pressure-sensitive adhesive layer and second ultraviolet-resistant pressure-sensitive adhesive layer is prepared
The mixed material forming first ultraviolet-resistant pressure-sensitive adhesive layer and second ultraviolet-resistant pressure-sensitive adhesive layer is all by benzophenone type ultraviolet absorbent 0.2 ~ 2.0wt%, benzotriazole ultraviolet absorber 0.2 ~ 2.0wt%, solvent ethyl acetate 20 ~ 35 wt%, solvent toluene 10 ~ 25wt%, acrylic acid adhesive 50 ~ 65wt%, curing agent 0.5 ~ 2.0 wt% forms, and above-mentioned each component sum is 100 wt%, specifically fills a prescription in table 2.
Each component is taken by table 2 formula ratio, at environment temperature is 18 ~ 28 DEG C, in container, first benzophenone type ultraviolet absorbent, benzotriazole ultraviolet absorber mixed with solvent ethyl acetate and toluene and stir 12 ~ 18 minutes, adding acrylic acid adhesive stirs after 18 ~ 22 minutes, add after curing agent stirs 12 ~ 18 minutes again, measuring viscosity with rotation viscometer or Cai's grace cup is 30 ~ 300 centipoises, mixed material D ~ the F forming ultraviolet-resistant pressure-sensitive adhesive layer can be obtained respectively, package spare.
Table 2
Note 1: benzophenone type ultraviolet absorbent SUV1 is 2,2', 4,4'-tetrahydroxybenzophenone, as shown in Figure 2, benzotriazole ultraviolet absorber CBT is 2-(the chloro-2H-124 Triazole of 5--2-base)-6-(1,1-dimethyl ethyl)-4-methylphenol to its chemical structural formula, its chemical structural formula as shown in Figure 3, and the two be Shanghai Zhi Xian Chemical Co., Ltd. produce; Ethyl acetate and toluene are from Changzhou Asource Chemical Co., Ltd.;
Note 2: above-mentioned raw materials used also can be replaced by the equivalents of different factory;
(B) preparation intercepts ultraviolet clear anti-fog fenestrated membrane
1. preparation intercepts ultraviolet clear anti-fog fenestrated membrane A
On a surface of transparent polyester film base material 2-1, after coating forms the antifogging agent composition A of anti-fog layer 1, temperature 80 ~ 150 DEG C, anti-fog layer 1 is obtained after heat cure, after applying at another of transparent polyester film base material 2-1 mixed material D forming ultraviolet-resistant pressure-sensitive adhesive layer on the surface, temperature 80 ~ 130 DEG C, place 10 ~ 120 seconds Post RDBMS and obtain first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, the surface recombination of transparent polyester film base material 2-2 is at the outer surface of first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, apply the mixed material of the mixed material E forming ultraviolet-resistant pressure-sensitive adhesive layer on the surface at another of transparent polyester film base material 2-2 after, temperature 80 ~ 130 DEG C, place 10 ~ 120 seconds Post RDBMS and obtain second ultraviolet-resistant pressure-sensitive adhesive layer 3-2, again mould release membrance 4 is compounded in second ultraviolet-resistant pressure-sensitive adhesive layer 3-2 outer surface, thus obtain obstruct ultraviolet clear anti-fog fenestrated membrane A(that each layer is complex as a whole as shown in Figure 1).
2. preparation intercepts ultraviolet clear anti-fog fenestrated membrane B
On a surface of transparent polyester film base material 2-1, after coating forms the antifogging agent composition B of anti-fog layer 1, temperature 80 ~ 150 DEG C, anti-fog layer 1 is obtained after heat cure, after applying at another of transparent polyester film base material 2-1 mixed material D forming ultraviolet-resistant pressure-sensitive adhesive layer on the surface, temperature 80 ~ 130 DEG C, place 10 ~ 120 seconds Post RDBMS and obtain first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, the surface recombination of transparent polyester film base material 2-2 is at the outer surface of first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, apply the mixed material of the mixed material F forming ultraviolet-resistant pressure-sensitive adhesive layer on the surface at another of transparent polyester film base material 2-2 after, temperature 80 ~ 130 DEG C, place 10 ~ 120 seconds Post RDBMS and obtain second ultraviolet-resistant pressure-sensitive adhesive layer 3-2, again mould release membrance 4 is compounded in second ultraviolet-resistant pressure-sensitive adhesive layer 3-2 outer surface, thus obtain obstruct ultraviolet clear anti-fog fenestrated membrane B(that each layer is complex as a whole as shown in Figure 1).
3. preparation intercepts ultraviolet clear anti-fog fenestrated membrane C
On a surface of transparent polyester film base material 2-1, after coating forms the antifogging agent composition C of anti-fog layer 1, temperature 80 ~ 150 DEG C, anti-fog layer 1 is obtained after heat cure, after applying at another of transparent polyester film base material 2-1 mixed material E forming ultraviolet-resistant pressure-sensitive adhesive layer on the surface, temperature 80 ~ 130 DEG C, place 10 ~ 120 seconds Post RDBMS and obtain first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, the surface recombination of transparent polyester film base material 2-2 is at the outer surface of first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, apply the mixed material of the mixed material F forming ultraviolet-resistant pressure-sensitive adhesive layer on the surface at another of transparent polyester film base material 2-2 after, temperature 80 ~ 130 DEG C, place 10 ~ 120 seconds Post RDBMS and obtain second ultraviolet-resistant pressure-sensitive adhesive layer 3-2, again mould release membrance 4 is compounded in second ultraviolet-resistant pressure-sensitive adhesive layer 3-2 outer surface, thus obtain obstruct ultraviolet clear anti-fog fenestrated membrane C(that each layer is complex as a whole as shown in Figure 1).
When the mixed material of the antifogging agent composition of coating formation anti-fog layer 1, the mixed material forming first ultraviolet-resistant pressure-sensitive adhesive layer 3-1, formation second ultraviolet-resistant pressure-sensitive adhesive layer 3-2, adopt jetting type to be coated with, or scraper type is coated with.
(C) the ultraviolet clear anti-fog fenestrated membrane performance of obstruct is detected
The performance of the obstruct of above-mentioned preparation ultraviolet clear anti-fog fenestrated membrane A ~ C is detected, the results are shown in Table 3.
Table 3
Note: in table 3, every data be the utility model as follows embodiment obtained intercept ultraviolet clear anti-fog fenestrated membrane A ~ C carry out detect obtain:
1. water contact angle: use Japanese G-1 type contact angle instrument to test at the position, three, left, center, right of the anti-fog surface (i.e. anti-fog layer 1) intercepting ultraviolet clear anti-fog fenestrated membrane, get the mean value of three site tests data;
2. light transmittance: adopt the solar film transmission measurement instrument (model LS103) that Lin Shang Science and Technology Ltd. of Shenzhen produces, carries out with reference to ASTM D1003 standard method;
3. anti-fog properties: under room temperature, it is above the water surface of 60 DEG C that the anti-fog surface (i.e. anti-fog layer 1) intercepting ultraviolet clear anti-fog fenestrated membrane is placed in water temperature, its fenestrated membrane anti-fog surface (i.e. anti-fog layer 1) and water surface distance are 10cm, observe anti-fog layer 1 surface intercepting ultraviolet clear anti-fog fenestrated membrane, whether hazed in 1 hour;
4. resistance to water: ultraviolet for obstruct clear anti-fog fenestrated membrane is placed in respectively 0 DEG C, 20 DEG C, 40 DEG C water after 48 hours, observes the coating damage situation of the anti-fog layer 1 intercepting ultraviolet clear anti-fog fenestrated membrane;
5. ultraviolet-resistant rate: adopt Japanese Shimadzu UV-3600 type spectrophotometer to test, with reference to standard GB/T/T 2680;
6. peel strength: with reference to standard GB/T/T 2792;
7. hardness: with reference to standard GB/T/T 6739.
As can be seen from table 3 testing result, the ultraviolet clear anti-fog fenestrated membrane of obstruct of the present utility model, can be antifog lastingly, and ultraviolet-resistant rate > 99%.Its product light transmission, hardness, peel strength all meet user's requirement.
Use the ultraviolet clear anti-fog fenestrated membrane of obstruct of the present utility model very simple, as long as according to after concrete size cutting, after being peeled off by the outermost layer of mould release membrance 4, be pasted onto glass surface.The glass such as building, automobile is pasted after the utility model intercepts ultraviolet clear anti-fog fenestrated membrane, can play very well and intercept ultraviolet, effect antifog lastingly.
Claims (4)
1. intercept a ultraviolet clear anti-fog fenestrated membrane, it is characterized in that,
It is by anti-fog layer (1), first transparent polyester film or polyethylene film base material (2-1), first ultraviolet-resistant pressure-sensitive adhesive layer (3-1), second transparent polyester film or polyethylene film base material (2-2), second ultraviolet-resistant pressure-sensitive adhesive layer (3-2) and mould release membrance (4) forms and each layer is complex as a whole, described anti-fog layer (1) heat cure is combined on a surface of first transparent polyester film or polyethylene film base material (2-1), the heat cure of first ultraviolet-resistant pressure-sensitive adhesive layer (3-1) be combined in first transparent polyester film or polyethylene film base material (2-1) another on the surface, a surface recombination of second transparent polyester film or polyethylene film base material (2-2) is at the outer surface of first ultraviolet-resistant pressure-sensitive adhesive layer (3-1), the heat cure of second ultraviolet-resistant pressure-sensitive adhesive layer (3-2) be combined in second transparent polyester film or polyethylene film base material (2-2) another on the surface, mould release membrance (4) is compounded in the outer surface of second ultraviolet-resistant pressure-sensitive adhesive layer (3-2).
2. the ultraviolet clear anti-fog fenestrated membrane of obstruct according to claim 1, is characterized in that, described obstruct ultraviolet clear anti-fog fenestrated membrane thickness is 72 ~ 444 μm, and wherein, the thickness of anti-fog layer (1) is 1 ~ 5 μm; The thickness of first transparent polyester film or polyethylene film base material (2-1) is 20 ~ 175 μm; The thickness of first ultraviolet-resistant pressure-sensitive adhesive layer (3-1) is 6 ~ 25 μm; The thickness of second transparent polyester film or polyethylene film base material (2-2) is 20 ~ 175 μm; The thickness of second ultraviolet-resistant pressure-sensitive adhesive layer (3-2) is 6 ~ 25 μm; The thickness of mould release membrance (4) is 19 ~ 39 μm.
3. the ultraviolet clear anti-fog fenestrated membrane of obstruct according to claim 2, is characterized in that, the thickness of described first ultraviolet-resistant pressure-sensitive adhesive layer (3-1) is identical with the thickness of second ultraviolet-resistant pressure-sensitive adhesive layer (3-2), or different.
4. the ultraviolet clear anti-fog fenestrated membrane of obstruct according to claim 2, it is characterized in that, the thickness of described first transparent polyester film or polyethylene film base material (2-1) is identical with the thickness of second transparent polyester film or polyethylene film base material (2-2), or different.