CN105838301A - Special sealant for high capacity batteries and preparation process thereof - Google Patents
Special sealant for high capacity batteries and preparation process thereof Download PDFInfo
- Publication number
- CN105838301A CN105838301A CN201610248740.6A CN201610248740A CN105838301A CN 105838301 A CN105838301 A CN 105838301A CN 201610248740 A CN201610248740 A CN 201610248740A CN 105838301 A CN105838301 A CN 105838301A
- Authority
- CN
- China
- Prior art keywords
- adds
- parts
- reactor
- mixed
- fried
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a special sealant for high capacity batteries and a preparation method thereof. The sealant is prepared from the following components: vegetable oil, potassium permanganate, methanol, ethylene glycol, pentaerythritol, sulfolane, alkylphenol ethoxylates, ethanolamine, zinc naphthenate, low grade ether, epoxy organosilicone, a toughening agent, a coupling agent, a curing agent, ethyl cyanoacetate, solid formaldehyde, piperidine, cyclohexane, ethyl acetate, phosphorus pentoxide, sulfur dioxide, hydroquinone, E-42 epoxy resin, a phenolic aldehyde-nitrile-butadiene rubber copolymer, acetone, ethylenediamine, fried common coltsfoot flower, stir-fried platycodon root, fried white silkworm, unibract fritillary bulb, fried opium poppy capsule, fried scorpion and scented tea. When used for sealing plastic surfaces, the sealant has an insulating function on the one hand and a sealing function on the other hand. The sealant prepared by utilizing the method is non-toxic and harmless, furthest ensures leakage of harmful substances of batteries, is also simple in process and low in cost and has excellent properties, a wide range of application, good stability, strong waterproofness, high bonding strength and strong practicability.
Description
Technical field:
The present invention designs a kind of battery auxiliary material preparation technology, is specifically related to a kind of high-capacity battery Special seal
Glue and preparation technology thereof.
Background technology:
Chemical industry is to develop the most rapid mainstay of the national economy industry modern times, and fine chemistry industry tail
Gas important component part, has obtained the development advanced by leaps and bounds, the clothing, food, lodging and transportion--basic necessities of life of the unresolved mankind in 20th century
And the energy, resource and environment problem make significant contribution;
Needing specialty glue for battery parcel glue, glue is development of modern industry and human living standard's raising
Requisite important materials, adhesive and bonding technology are with the incomparable extraordinary work of other connected modes
Skill, plays great effect in modern economy, modern national defense, modern science and technology.
Summary of the invention:
The technical problem to be solved is to overcome the defect of prior art, it is provided that a kind of high power capacity
Battery special seal gum and preparation technology thereof.
The technical problem to be solved realizes by the following technical solutions.
High-capacity battery special seal gum, it is characterised in that: it is prepared from the following components, vegetable oil 36-44
Part, potassium permanganate 4-6 part, methyl alcohol 9-11 part, ethylene glycol 9-11 part, pentaerythrite 4-6 part, sulfolane
9-11 part, APES 4-6 part, monoethanolamine 9-11 part, zinc naphthenate 19-21 part, rudimentary
Ether 6-10 part, epoxy organosilicon 50-60 part, toughener 10-15 part, coupling agent 1-2 part, curing agent 2-3
Part, ethyl cyanoacetate 100-150 part, solid formaldehyde 50-60 part, piperidines 2-3 part, hexamethylene 2-5 part,
Ethyl acetate 1-3 part, phosphorus pentoxide 2-5 part, sulfur dioxide 1-2 part, hydroquinones 1-3 part, E-42
Epoxy resin 89-99 part, phenolic aldehyde-nitrile rubber copolymer 89-99 part, acetone 66-75 part, ethylenediamine 10-15
Part, honey-fried FLOS FARFARAE 10-12 part, fry balloonflower root 5-8 part, process stiff silkworm 10-12 part, Bulbus Fritillariae Cirrhosae 3-5 part, process small-mouthed jar
Grain shell 3-5 part, process scorpio 1-2 part, jasmine tea 4-5 grain.
High-capacity battery special seal gum comprises the following steps and is prepared from:
1) selection one is with the reactor of agitator, then adds in formula important in reactor
Stirring opened by vegetable oil;
2) by the potassium permanganate in raw material, sulfolane, APES, monoethanolamine, aphthenic acids
Zinc and rudimentary ether, all add in reactor, after being stirred and heated to 60-80 DEG C, and isothermal reaction 2-4h;
3) after above-mentioned steps reaction terminates, reactor is cooled to 20-25 DEG C, by the Ji Wusi in raw material
Alcohol, methyl alcohol and ethylene glycol are added thereto, and stand 5-10h, obtain auxiliary material one after stirring;
4) E-42 epoxy resin and acetone are mixed;
5) mixed solvent and phenolic aldehyde-nitrile rubber copolymer are joined in bottle, stirring;
6) it is heated to 81-86 DEG C, adds MMA, continue stirring 1 hour;
7) intermixture is mixed in the ratio of 30:1 in the environment of ethylenediamine early-60 DEG C to 60 DEG C,
Stir;
8) cool to room temperature again, obtain auxiliary material two;
9) take epoxy organosilicon, after toughener, coupling agent mixing be completely dissolved, add curing agent and make half
Finished product glue;
10) take solid formaldehyde, piperidines adds in a flask, heating simultaneously, and stirring is dissolved, then will
It puts in reactor, and reactor is warming up to 90 DEG C, adds ethyl cyanoacetate, heats 2 hours, then
Recycling design methyl alcohol, to temperature 120 DEG C, stops heating, adds hexamethylene, ethyl acetate mixing, backflow
Dehydration, temperature rises to 125 DEG C, and discharging obtains condensation polymer;
11) condensation polymer and semi-finished product glue being mixed, proportion is 100:20-50, adds 5-10 part accelerator,
Being warming up to 90 DEG C, heating duration i.e. can get copolymerization adhesive in 1 hour;
12) take 1-2 part phosphorus pentoxide and add copolymerization adhesive, be heated to 190 DEG C-200 DEG C, vacuum
Crack under 0.1MPa, obtain crude monomer;
13) in crude monomer, remaining phosphorus pentoxide, hydroquinones, sulfur dioxide are added, in reaction
Stirring in still, temperature control 80-100 DEG C, vacuum be that to collect cut under 0.1MPa be the product of 70-80 DEG C
Product, obtain essence monomer;
14) take essence monomer adding mass fraction is the dioctyl phthalate of 1%-2%, lucite powder
Mixture, obtains moment adhesive;
15) by the honey-fried FLOS FARFARAE in constitutive material, fry balloonflower root, process stiff silkworm, Bulbus Fritillariae Cirrhosae, process pappy shell and
Processing scorpio, put in cucurbit, add the clear water of 5 times, boiling, the water to cucurbit is evaporated, and collects
Steam, steam liquefies again;Being put into by jasmine tea in boiling water simultaneously and soak, the water yield is 300ml, soaks
5-8 minute, cross drainage, obtain jasmine tea water;Again the steam collected is mixed with jasmine tea water, mixed
Liquid;
16) taking 20% auxiliary material one to mix with 40% mixed liquor, the moment adhesive taking twice 20% adds mixing,
Being heated to 60 DEG C, heating duration 10 minutes, during then cooling is placed in the auxiliary material two of 60%;
17) moment adhesive with 80% mixes the most again, cooling, obtains fluid sealant.
The invention has the beneficial effects as follows: the glue of cell sealing, for sealed plastic surface, on the one hand play
Insulating effect, another plays the effect of sealing, and the fluid sealant utilizing this law to prepare is nontoxic, maximum journey
Degree ensure that the leakage of battery harmful substance, and technique is simple simultaneously, and property favorable rates is honest and clean, of many uses, stable
Property good, water-resistance is strong, and adhesion strength is high, practical.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Specific embodiment 1: high-capacity battery special seal gum, is prepared from the following components, vegetable oil
36 parts, 4 parts of potassium permanganate, methyl alcohol 9 parts, ethylene glycol 9 parts, pentaerythrite 4 parts, sulfolane 9 parts, alkyl
Phenol polyethenoxy ether 4 parts, monoethanolamine 9 parts, zinc naphthenate 19 parts, 6 parts of rudimentary ether, epoxy organosilicon 50 parts,
Toughener 10 parts, coupling agent 1 part, 2 parts of curing agent, ethyl cyanoacetate 100 parts, solid formaldehyde 50 parts, piperazine
Pyridine 2 parts, hexamethylene 2 parts, 1 part of ethyl acetate, phosphorus pentoxide 2 parts, sulfur dioxide 1 part, hydroquinones
1 part, E-42 epoxy resin 89 parts, phenolic aldehyde-nitrile rubber copolymer 89 parts, 66 parts of acetone, ethylenediamine 10
Part, honey-fried FLOS FARFARAE 10 parts, fry balloonflower root 5 parts, process stiff silkworm 10 parts, Bulbus Fritillariae Cirrhosae 3 parts, process pappy shell 3 parts, process
Scorpio 1 part, jasmine tea 4.
Specific embodiment 2: high-capacity battery special seal gum, is prepared from the following components, vegetable oil
44 parts, 6 parts of potassium permanganate, methyl alcohol 11 parts, ethylene glycol 11 parts, pentaerythrite 6 parts, sulfolane 11 parts,
APES 6 parts, monoethanolamine 11 parts, zinc naphthenate 21 parts, 10 parts of rudimentary ether, epoxy are organic
Silicon 60 parts, toughener 15 parts, coupling agent 2 parts, 3 parts of curing agent, ethyl cyanoacetate 150 parts, solid formaldehyde
60 parts, piperidines 3 parts, hexamethylene 5 parts, 3 parts of ethyl acetate, phosphorus pentoxide 5 parts, sulfur dioxide 2 parts,
Hydroquinones 3 parts, E-42 epoxy resin 99 parts, phenolic aldehyde-nitrile rubber copolymer 99 parts, 75 parts of acetone,
Ethylenediamine 15 parts, honey-fried FLOS FARFARAE 12 parts, fry balloonflower root 8 parts, process stiff silkworm 12 parts, Bulbus Fritillariae Cirrhosae 5 parts, process opium poppy
5 parts of shell, process scorpio 2 parts, jasmine tea 5.
Its preparation method includes:
1) selection one is with the reactor of agitator, then adds in formula important in reactor
Stirring opened by vegetable oil;
2) by the potassium permanganate in raw material, sulfolane, APES, monoethanolamine, aphthenic acids
Zinc and rudimentary ether, all add in reactor, after being stirred and heated to 60-80 DEG C, and isothermal reaction 2-4h;
3) until above-mentioned steps reaction terminate after, reactor is cooled to 20-25 DEG C, by the pentaerythrite in raw material,
Methyl alcohol and ethylene glycol are added thereto, and stand 5-10h, obtain auxiliary material one after stirring;
4) E-42 epoxy resin and acetone are mixed;
5) mixed solvent and phenolic aldehyde-nitrile rubber copolymer are joined in bottle, stirring;
6) it is heated to 81-86 DEG C, adds MMA, continue stirring 1 hour;
7) intermixture is mixed in the ratio of 30:1 in the environment of ethylenediamine early-60 DEG C to 60 DEG C, fill
Divide and stir;
8) cool to room temperature again, obtain auxiliary material two;
9) take epoxy organosilicon, after toughener, coupling agent mixing be completely dissolved, add curing agent and make half
Finished product glue;
10) take solid formaldehyde, piperidines adds in a flask, heating simultaneously, and stirring is dissolved, then by it
Put in reactor, reactor is warming up to 90 DEG C, add ethyl cyanoacetate, heat 2 hours, so
Rear recycling design methyl alcohol, to temperature 120 DEG C, stops heating, adds hexamethylene, ethyl acetate mixing,
Reflux dewatering, temperature rises to 125 DEG C, and discharging obtains condensation polymer;
11) condensation polymer and semi-finished product glue being mixed, proportion is 100:20-50, adds 5-10 part accelerator,
Being warming up to 90 DEG C, heating duration i.e. can get copolymerization adhesive in 1 hour;
12) take 1-2 part phosphorus pentoxide and add copolymerization adhesive, be heated to 190 DEG C-200 DEG C, vacuum
Crack under 0.1MPa, obtain crude monomer;
13) in crude monomer, remaining phosphorus pentoxide, hydroquinones, sulfur dioxide are added, at reactor
Interior stirring, temperature control 80-100 DEG C, vacuum be under 0.1MPa collect cut be 70-80 DEG C
Product, obtains essence monomer;
14) take essence monomer adding mass fraction is the dioctyl phthalate of 1%-2%, lucite powder
Mixture, obtains moment adhesive;
15) by the honey-fried FLOS FARFARAE in constitutive material, fry balloonflower root, process stiff silkworm, Bulbus Fritillariae Cirrhosae, process pappy shell and process
Scorpio, puts in cucurbit, adds the clear water of 5 times, boiling, and the water to cucurbit is evaporated, and receives
Collection steam, steam liquefies again;Being put into by jasmine tea in boiling water simultaneously and soak, the water yield is 300ml,
Soak 5-8 minute, cross drainage, obtain jasmine tea water;Again the steam collected is mixed with jasmine tea water,
Obtain mixed liquor;
16) taking 20% auxiliary material one to mix with 40% mixed liquor, the moment adhesive taking twice 20% adds mixing,
Being heated to 60 DEG C, heating duration 10 minutes, during then cooling is placed in the auxiliary material two of 60%;
17) moment adhesive with 80% mixes the most again, cooling, obtains fluid sealant.
The general principle of the present invention, principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. high-capacity battery special seal gum, it is characterised in that: it is prepared from the following components, vegetable oil
36-44 part, potassium permanganate 4-6 part, methyl alcohol 9-11 part, ethylene glycol 9-11 part, pentaerythrite 4-6 part, ring
Fourth sulfone 9-11 part, APES 4-6 part, monoethanolamine 9-11 part, zinc naphthenate 19-21 part,
Rudimentary ether 6-10 part, epoxy organosilicon 50-60 part, toughener 10-15 part, coupling agent 1-2 part, curing agent
2-3 part, ethyl cyanoacetate 100-150 part, solid formaldehyde 50-60 part, piperidines 2-3 part, hexamethylene 2-5 part,
Ethyl acetate 1-3 part, phosphorus pentoxide 2-5 part, sulfur dioxide 1-2 part, hydroquinones 1-3 part, E-42
Epoxy resin 89-99 part, phenolic aldehyde-nitrile rubber copolymer 89-99 part, acetone 66-75 part, ethylenediamine 10-15
Part, honey-fried FLOS FARFARAE 10-12 part, fry balloonflower root 5-8 part, process stiff silkworm 10-12 part, Bulbus Fritillariae Cirrhosae 3-5 part, process small-mouthed jar
Grain shell 3-5 part, process scorpio 1-2 part, jasmine tea 4-5 grain.
2. according to the high-capacity battery special seal gum described in claim 1, it is characterised in that: include
Following steps are prepared from:
1) selection one is with the reactor of agitator, then adds in formula important in reactor
Stirring opened by vegetable oil;
2) by the potassium permanganate in raw material, sulfolane, APES, monoethanolamine, aphthenic acids
Zinc and rudimentary ether, all add in reactor, after being stirred and heated to 60-80 DEG C, and isothermal reaction 2-4h;
3) after above-mentioned steps reaction terminates, reactor is cooled to 20-25 DEG C, by the Ji Wusi in raw material
Alcohol, methyl alcohol and ethylene glycol are added thereto, and stand 5-10h, obtain auxiliary material one after stirring;
4) E-42 epoxy resin and acetone are mixed;
5) mixed solvent and phenolic aldehyde-nitrile rubber copolymer are joined in bottle, stirring;
6) it is heated to 81-86 DEG C, adds MMA, continue stirring 1 hour;
7) intermixture is mixed in the ratio of 30:1 in the environment of ethylenediamine early-60 DEG C to 60 DEG C,
Stir;
8) cool to room temperature again, obtain auxiliary material two;
9) take epoxy organosilicon, after toughener, coupling agent mixing be completely dissolved, add curing agent and make half
Finished product glue;
10) take solid formaldehyde, piperidines adds in a flask, heating simultaneously, and stirring is dissolved, then will
It puts in reactor, and reactor is warming up to 90 DEG C, adds ethyl cyanoacetate, heats 2 hours, then
Recycling design methyl alcohol, to temperature 120 DEG C, stops heating, adds hexamethylene, ethyl acetate mixing, backflow
Dehydration, temperature rises to 125 DEG C, and discharging obtains condensation polymer;
11) condensation polymer and semi-finished product glue being mixed, proportion is 100:20-50, adds 5-10 part accelerator,
Being warming up to 90 DEG C, heating duration i.e. can get copolymerization adhesive in 1 hour;
12) take 1-2 part phosphorus pentoxide and add copolymerization adhesive, be heated to 190 DEG C-200 DEG C, vacuum
Crack under 0.1MPa, obtain crude monomer;
13) in crude monomer, remaining phosphorus pentoxide, hydroquinones, sulfur dioxide are added, in reaction
Stirring in still, temperature control 80-100 DEG C, vacuum be that to collect cut under 0.1MPa be the product of 70-80 DEG C
Product, obtain essence monomer;
14) take essence monomer adding mass fraction is the dioctyl phthalate of 1%-2%, lucite powder
Mixture, obtains moment adhesive;
15) by the honey-fried FLOS FARFARAE in constitutive material, fry balloonflower root, process stiff silkworm, Bulbus Fritillariae Cirrhosae, process pappy shell and
Processing scorpio, put in cucurbit, add the clear water of 5 times, boiling, the water to cucurbit is evaporated, and collects
Steam, steam liquefies again;Being put into by jasmine tea in boiling water simultaneously and soak, the water yield is 300ml, soaks
5-8 minute, cross drainage, obtain jasmine tea water;Again the steam collected is mixed with jasmine tea water, mixed
Liquid;
16) taking 20% auxiliary material one to mix with 40% mixed liquor, the moment adhesive taking twice 20% adds mixing,
Being heated to 60 DEG C, heating duration 10 minutes, during then cooling is placed in the auxiliary material two of 60%;
17) moment adhesive with 80% mixes the most again, cooling, obtains fluid sealant.