CN105834403A - 推土铲铸造方法 - Google Patents
推土铲铸造方法 Download PDFInfo
- Publication number
- CN105834403A CN105834403A CN201610355420.0A CN201610355420A CN105834403A CN 105834403 A CN105834403 A CN 105834403A CN 201610355420 A CN201610355420 A CN 201610355420A CN 105834403 A CN105834403 A CN 105834403A
- Authority
- CN
- China
- Prior art keywords
- die
- mould
- tialn
- cast
- casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种推土铲铸造方法,先制备耐高温模具,然后将熔融状态的TiAlN浇铸在模具内表面,旋转模具待TiAlN分布均匀后将冷却模具,在模具内表面形成TiAlN层,最后向模具内浇铸铸铁,铸铁水填充满模具后继续对模具进行加热,待TiAlN层微融时将模具迅速冷却。本发明简化现有工艺,在铸造的同时在铸件表面制备出高硬度高耐磨性的涂层,一次成型,节约了生产时间和生产成本。
Description
技术领域
本发明涉及工程机械领域,具体是一种推土铲铸造方法。
背景技术
推土机是一种工程车辆,前方装有大型的金属推土铲,使用时放下推土铲,向前铲削并推送泥、沙及石块等,推土刀位置和角度可以调整。推土机能单独完成挖土、运土和卸土工作,具有操作灵活、转动方便、所需工作面小、行驶速度快等特点。其主要适用于一至三类土的浅挖短运,如场地清理或平整,开挖深度不大的基坑以及回填,推筑高度不大的路基等。
由于推土机的工作特性,推土铲不仅需要很高的硬度,还需要具有极高的耐磨性能。现在的推土铲制造过程中,通常是直接整体铸造出推土铲,然后在推土铲表面进行处理,增加高硬度高耐磨性的涂层,从而提高推土铲的使用寿命。
发明内容
本发明为了简化现有工艺,在铸造的同时在铸件表面制备出高硬度高耐磨性的涂层,一次成型,节约了生产时间和生产成本。
本发明一种推土铲铸造方法,包括以下步骤:
1)制备耐高温模具;
2)将熔融状态的TiAlN(氮铝化钛)浇铸在模具内表面,旋转模具待TiAlN分布均匀后将冷却模具,在模具内表面形成TiAlN层;
3)向模具内浇铸铸铁,铸铁水填充满模具后继续对模具进行加热,待TiAlN层微融时将模具迅速冷却;
4)脱模后对铸件表面进行初步打磨,去除明显的凸起和孔洞。
由于融化TiAlN需要较高温度,故模具无法使用普通的金属模具,步骤1)所述的耐高温模具为采用失蜡法制备的陶瓷模具。
本发明有益效果在于:简化现有工艺,在铸造的同时在铸件表面制备出高硬度高耐磨性的涂层,一次成型,节约了生产时间和生产成本。
具体实施方式
下面结合具体实施方式对本发明做进一步说明。
本发明提供了一种推土铲铸造方法,包括以下步骤:
1)制备耐高温模具;
2)将熔融状态的TiAlN(氮铝化钛)浇铸在模具内表面,旋转模具待TiAlN分布均匀后将冷却模具,在模具内表面形成TiAlN层;
3)向模具内浇铸铸铁,铸铁水填充满模具后继续对模具进行加热,待TiAlN层微融时将模具迅速冷却;
4)脱模后对铸件表面进行初步打磨,去除明显的凸起和孔洞。
由于融化TiAlN需要较高温度,故模具无法使用普通的金属模具,步骤1)所述的耐高温模具为采用失蜡法制备的陶瓷模具。
本发明具体应用途径很多,以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以作出若干改进,这些改进也应视为本发明的保护范围。
Claims (2)
1.一种推土铲铸造方法,其特征在于包括以下步骤:
1)制备耐高温模具;
2)将熔融状态的TiAlN浇铸在模具内表面,旋转模具待TiAlN分布均匀后将冷却模具,在模具内表面形成TiAlN层;
3)向模具内浇铸铸铁,铸铁水填充满模具后继续对模具进行加热,待TiAlN层微融时将模具迅速冷却;
4)脱模后对铸件表面进行初步打磨,去除明显的凸起和孔洞。
2.根据权利要求1所述的推土铲铸造方法,其特征在于:步骤1)所述的耐高温模具为采用失蜡法制备的陶瓷模具。