CN105834367A - 一种铸造用纸质浇道管制备工艺 - Google Patents

一种铸造用纸质浇道管制备工艺 Download PDF

Info

Publication number
CN105834367A
CN105834367A CN201610314468.7A CN201610314468A CN105834367A CN 105834367 A CN105834367 A CN 105834367A CN 201610314468 A CN201610314468 A CN 201610314468A CN 105834367 A CN105834367 A CN 105834367A
Authority
CN
China
Prior art keywords
paper
parts
casting
tube
pouring channel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610314468.7A
Other languages
English (en)
Inventor
姚伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Weiyan Environmental Protection Technology Co Ltd
Original Assignee
Huzhou Weiyan Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Weiyan Environmental Protection Technology Co Ltd filed Critical Huzhou Weiyan Environmental Protection Technology Co Ltd
Priority to CN201610314468.7A priority Critical patent/CN105834367A/zh
Publication of CN105834367A publication Critical patent/CN105834367A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铸造用纸质浇道管的制备工艺：（1）将废纸碎浆；（2）按照重量份数，废纸浆70份，刚玉粉8‑10份，铝矾土粉10‑12份，粘结剂10份，草木灰0.5份，搅拌均匀；（3）将调好的浆放入成型机，成圆管状；（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；（5）高温烘干；（6）烘干的纸浆管表面用防护涂料喷涂处理；（7）烘干或晾干即可装箱出厂。本发明的工艺其制备简单，性能优良，尤其是强度大大提高。

Description

一种铸造用纸质浇道管制备工艺
技术领域
本发明属于金属铸造行业的铸造辅助材料领域，特别涉及一种铸造用纸质浇道管制备工艺。
背景技术
铸造用环保耐火管（纤维管）主要用于重工业中的铸造企业，该产品用在铸造模具与型砂的连接通道，铁水在1600℃左右的温度通过该管道流到型腔内冷却成形，用该产品的目的是隔离型砂，防止铁液在高温情况下将型砂带入型腔，造成铸件质量不合格，用该产品为了提高铸件质量、降低废品率。对于耐火管的要求，就是在接触高温铁液的那几秒或几分钟内，能耐高温就可。
申请号201510723033.3公开了一种铸造用纸质浇道管。所述铸造用纸质浇道管采用下述原料制成，包括：有机纤维、无机纤维、烧结耐火材料、粘结剂、防水防潮剂、增强剂、助滤剂及助熔剂，本发明还公开了一种铸造用纸质浇道管的制造方法。本发明提供的铸造用纸质浇道管及其制造方法是依照纸浆模塑工艺技术制成的铸造用纸质浇道管与一直以来所使用耐火材料陶瓷浇道管部件相比具有重量轻、易于操作、铸件浇铸后废弃物少且易于处理、省工、省时、节能环保、不污染环境、环境保护友好等优点。
但是其仍存在制作复杂，强度不够高的缺点，本发明旨在提供一种铸造用纸质浇道管制备工艺，其制备简单，性能优良，尤其是强度大大提高。
发明内容
本发明针对现有技术存在的缺陷，目的在于提供一种铸造用纸质浇道管制备工艺，其制备简单，性能优良，尤其是强度大大提高。
本发明的目的可以通过以下技术方案实现：
一种铸造用纸质浇道管的制备工艺，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉8-10份，铝矾土粉10-12份，粘结剂10份，草木灰0.5份，搅拌均匀；
所述粘结剂为粘土；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
本发明的有益之处在于：
（1）现有的陶管主要使用原材料有铝矾土（AL2O3）、陶土，先将所用原材料搅拌，通过制管机挤压成型，然后烘干，最后放入窑炉通过1300℃的高温烧制而成，我们的窑炉是用煤气转换炉，生成煤气而燃烧加温的，又要用到煤。铝矾土、陶土及煤都是矿产资源，虽然我国的矿产资源丰富，但资源总有枯竭的一天。而纤维管主要使用原材料是废纸及附属材料，可以将废纸等废弃材料变废为宝，在全世界都提倡节能降耗的今天，我们也要积极行动起来尽自己的一份力量，为我们的后代留下一点资源。
（2）陶管的壁厚厚，单个重量重，在运输成本上就高于纤维管，使用的时候，陶管要用胶带固定连接，并且陶管是陶瓷制品，易碎，在运输及使用过程中一不小心就会破碎，而纤维管壁薄，重量轻，又是纸质材料为主，有韧性，不易破损，在使用时两头带子口，一套便可使用。
（3）对于使用厂家，型砂要再生利用，陶管是陶土烧制而成，壁厚、坚硬，需要从型砂中筛选分离，而残留的小颗粒，将会严重磨损型砂再生设备，大大提高设备维修成本。而纤维管的使用，通过铁液的高温融化， 减少了型砂的筛选分离步骤，减少了外来硬物对砂再生设备的磨损，降低了设备的维修成本。
（4）相比于现有技术的纸质浇道管制备工艺，其制备简单，性能优良，尤其是强度大大提高。
具体实施方式
实施例 1 ：
一种铸造用纸质浇道管的制备工艺，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉8份，铝矾土粉12份，粘结剂10份，草木灰0.5份，搅拌均匀；
所述粘结剂为粘土；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
结果：相比于201510723033.3公开的铸造用纸质浇道管，其强度提高了31%。
实施例 2 ：
一种铸造用纸质浇道管的制备工艺，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉10份，铝矾土粉10份，粘结剂10份，草木灰0.5份，搅拌均匀；
所述粘结剂为粘土；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
结果：相比于201510723033.3公开的铸造用纸质浇道管，其强度提高了55%。
实施例 3 ：
一种铸造用纸质浇道管的制备工艺，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉9份，铝矾土粉11份，粘结剂10份，草木灰0.5份，搅拌均匀；
所述粘结剂为粘土；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
结果：相比于201510723033.3公开的铸造用纸质浇道管，其强度提高了40%。
实施例 4 ：
一种铸造用纸质浇道管的制备工艺，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉10份，铝矾土粉11份，粘结剂10份，草木灰0.5份，搅拌均匀；
所述粘结剂为粘土；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
结果：相比于201510723033.3公开的铸造用纸质浇道管，其强度提高了50%。
实施例 5 ：
一种铸造用纸质浇道管的制备工艺，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉8份，铝矾土粉12份，粘结剂10份，草木灰0.5份，搅拌均匀；
所述粘结剂为粘土；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
结果：相比于201510723033.3公开的铸造用纸质浇道管，其强度提高了36%。
可见，本发明提供了一种铸造用纸质浇道管制备工艺，其制备简单，性能优良，尤其是强度大大提高。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (3)

1.一种铸造用纸质浇道管的制备方法，其特征在于步骤如下：
（1）将废纸碎浆；
（2）按照重量份数，废纸浆70份，刚玉粉8-10份，铝矾土粉10-12份，粘结剂10份，草木灰0.5份，搅拌均匀；
（3）将调好的浆放入成型机，成圆管状；
（4）将成圆管状的纸浆毛坏放入整形模具，热压整形；
（5）高温烘干；
（6）烘干的纸浆管表面用防护涂料喷涂处理；
（7）烘干或晾干即可装箱出厂。
2.权利要求1所述的铸造用纸质浇道管的制备方法，其特征在于：
所述粘结剂为粘土。
3.权利要求1-2任一项所述的铸造用纸质浇道管的制备方法制备得到的纸质浇道管。
CN201610314468.7A 2016-05-13 2016-05-13 一种铸造用纸质浇道管制备工艺 Pending CN105834367A (zh)