CN105803135A - 一种皮革保护镀膜剂及其制备方法 - Google Patents
一种皮革保护镀膜剂及其制备方法 Download PDFInfo
- Publication number
- CN105803135A CN105803135A CN201610355686.5A CN201610355686A CN105803135A CN 105803135 A CN105803135 A CN 105803135A CN 201610355686 A CN201610355686 A CN 201610355686A CN 105803135 A CN105803135 A CN 105803135A
- Authority
- CN
- China
- Prior art keywords
- leather
- agent
- coating agent
- film coating
- protection film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及日用品技术领域,具体公开了一种皮革保护镀膜剂及其制备方法。所述的镀膜剂包含巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、水。本发明所述的皮革保护镀膜剂隔污、防水、耐摩擦性能好;此外,本发明所述的皮革保护镀膜剂能在皮革表面形成一层保护层,脏污轻易粘附不住,清洁更省力,延长皮革使用寿命。
Description
技术领域
本发明涉及日用品技术领域,具体涉及一种皮革保护镀膜剂及其制备方法。
背景技术
无论在皮鞋生产或皮衣、皮沙发制作过程中所使用的主要材料都是皮革(也叫天然皮革),是由动物皮制成的,称为天然革(是真皮)。真皮在经过制革工艺中一系列的物理化学和机械加工后,转变成一种固定的耐用的物质,被称为皮革,简称革。
皮革是人类早期文化中即存在的产物,皮革属于天然产物,来源有限,更其珍贵。在日常生活中皮革与高贵似乎具有同样的意义,一双高档的皮鞋不仅看它的品牌、款式、制作工艺,更重要的是天然皮革制品自身的美丽,以皮革销售对象而言的鞋类皮革,远远超出其他。
皮革护理是指对真皮制品,如对皮衣、皮沙发、皮椅、皮包、皮袋、皮鞋等的清洁、保养、上光、抛光、补色、镀膜等一系列护理工作。现有皮革护理过程中使用的皮革镀膜剂大多是由有机有机硅乳液或固体蜡制成,现有的这类皮革镀膜剂存在不干、发粘或太硬易龟裂,不易施工操作,不耐脏污,光泽不持久等缺陷。
发明内容
本发明所要解决的技术问题是,为了克服现有技术中存在的上述不足,提供一种皮革保护镀膜剂。
本发明所要解决的上述技术问题通过以下技术方案予以实现:
一种皮革保护镀膜剂,包含如下成分:巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、水。
优选地,所述的皮革保护镀膜剂,还包括防腐剂。
优选地,所述的皮革保护镀膜剂,包含如下重量百分比的成分:巴西蜡乳液30~40%,聚氨酯20~30%,有机硅乳液1~5%,流平剂1~10%,渗透剂10~20%,水10~20%。
进一步优选地,所述的皮革保护镀膜剂,包含如下重量百分比的成分:巴西蜡乳液30~35%,聚氨酯20~25%,有机硅乳液1~3%,流平剂5~10%,渗透剂10~15%,水10~20%。
最优选地,所述的皮革保护镀膜剂,包含如下重量百分比的成分:巴西蜡乳液32%,聚氨酯25%,有机硅乳液1.5%,流平剂8%,渗透剂13%,余量为水。
优选地,所述的皮革保护镀膜剂,还包含重量百分比为1~5%的防腐剂。
进一步优选地的,所述的皮革保护镀膜剂,还包含重量百分比为1~3%的防腐剂。
优选地,所述的水为去离子水。
一种皮革保护镀膜剂的制备方法,其步骤为:在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、以及水,搅拌15~50min即得。
一种皮革保护镀膜剂的制备方法,其步骤为:在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、水以及防腐剂,搅拌15~50min即得。
有益效果:(1)本发明提供了一种全新配方的皮革保护镀膜剂;(2)所述的皮革保护镀膜剂隔污、防水、耐摩擦性能好;(3)此外,本发明所述的皮革保护镀膜剂能在皮革表面形成一层保护层,脏污轻易粘附不住,清洁更省力,延长皮革使用寿命。
具体实施方式
以下结合具体实施例来进一步解释本发明,但实施例对本发明不做任何形式的限定。
实施例1一种皮革保护镀膜剂
配方:巴西蜡乳液32%,环保型聚氨酯25%,有机硅乳液1.5%,流平剂8%,渗透剂13%,防腐剂3%,余量为去离子水。所述的流平剂为氟改性丙烯酸酯流平剂;所述的渗透剂为脂肪醇聚氧乙烯醚。
制备方法:在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、去离子水以及防腐剂,搅拌20min即得。
实施例2一种皮革保护镀膜剂
配方:巴西蜡乳液30%,环保型聚氨酯20%,有机硅乳液1%,流平剂5%,渗透剂10%,防腐剂1%,余量为去离子水。所述的流平剂为氟改性丙烯酸酯流平剂;所述的渗透剂为脂肪醇聚氧乙烯醚。
制备方法:在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、去离子水以及防腐剂,搅拌20min即得。
实施例3一种皮革保护镀膜剂
配方:巴西蜡乳液35%,环保型聚氨酯25%,有机硅乳液3%,流平剂10%,渗透剂15%,防腐剂3%,余量为去离子水。所述的流平剂为氟改性丙烯酸酯流平剂;所述的渗透剂为脂肪醇聚氧乙烯醚。
制备方法:在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、去离子水以及防腐剂,搅拌20min即得。
实施例4耐酒精擦拭试验
方法如下:
1.用消毒酒精代替清扫用酒精或化妆品中所含酒精,对皮革镀膜表面的耐酒精性进行检测。
2.试验用器材:
2.1砝码:1000
2.2.按日本药局法D-96里所规定的消毒用酒精(76.9-81.4%).
2.3.纱布
2.4.胶头滴管
3.试验方法:
3.1.将纱布迭成8层,5mm2见方后,固定在砝码头上,用滴管在纱布上滴酒精0.5ml。
3.2.砝码与测试面垂直,砝码头接触测试面,手臂以水平方向以2秒1个往返的速度在皮革镀膜表层往返摩擦。
4.判断标准:
1.皮革涂膜的表面状况良好,原则上纱布上不能有涂料的颜色和成份.
2.涂膜面状态(擦痕)和纱布上所染涂料颜色,成分的状态都为OK时,方为合格.如其中有一条NG都为不合格。
实验结果:分别实验实施例1、2和3制备得到的皮革保护镀膜剂各100批,其合格率分别为100%、97%和99%
实施例5耐干湿擦试验
(一).试验片之制作:
1.依脱色试验之型别分成A、B两试片,每种各取二试片。
2.试片:裁取长22cm,宽3cm,之长条形试片。
(二).试验步骤:
试验种类分干试验和湿润试验。
2.1干试验:
①将试样和摩擦用皮革,应先在标准状态(1)放置4小时上。
注(1):JISL0801的6.(1)条规定。
②使用摩擦试验机时,试样固定在试验台上,摩擦用皮革固定在头端,向下压力为2N(4),在试样100mm间以每分钟30次的速度往复运动摩擦100次。
注(4):摩擦头质量约200g。
2.2湿润试验:摩擦用皮革先用蒸馏水湿润成为大约100%的湿润状态,用其摩擦标准状态的试样,然后在不超过60℃温度下干燥。
(三).试验结果之处理:
1.将细布置于污染用灰色标旁,以目视观察比较细布污染比例情况。
2.与灰色标比对可判定耐磨擦染色坚牢度之等级。
3.记录干式、湿式受测条件之污染等级。
4.判定是否合乎本厂验收标准。
(四).试验结果之判定:
比较皮革未受污染部份及已受试验片污染部分色泽之污染比例情况与灰色标何种等级之比例相近,即为该试验片之耐磨擦染色坚牢度之等级。
(五).检验标准:
摩擦用皮革的沾色判定,按JISL0801中第9条(染色牢度的判定)的规定执行。
依试验结果分下列判定
A优良:湿布试验在皮革上不留颜色。
B尚佳:湿布试验在皮革上有留色,但在干布试验后皮革上不留颜色。
C不良:干布试验后皮革留有颜色。
实验结果:分别实验实施例1、2和3制备得到的皮革保护镀膜剂各100批,其中实施例1的优良率为99%,实施例2的优良率为95%,实施例3的优良率为97%。
Claims (10)
1.一种皮革保护镀膜剂,其特征在于,包含如下成分:巴西蜡乳液、
聚氨酯、有机硅乳液、流平剂、渗透剂、水。
2.根据权利要求1所述的皮革保护镀膜剂,其特征在于,还包括防腐剂。
3.根据权利要求1所述的皮革保护镀膜剂,其特征在于,包含如下重量百分比的成分:巴西蜡乳液30~40%,聚氨酯20~30%,有机硅乳液1~5%,流平剂1~10%,渗透剂10~20%,水10~20%。
4.根据权利要求3所述的皮革保护镀膜剂,其特征在于,包含如下重量百分比的成分:巴西蜡乳液30~35%,聚氨酯20~25%,有机硅乳液1~3%,流平剂5~10%,渗透剂10~15%,水10~20%。
5.根据权利要求4所述的皮革保护镀膜剂,其特征在于,包含如下重量百分比的成分:巴西蜡乳液32%,聚氨酯25%,有机硅乳液1.5%,流平剂8%,渗透剂13%,余量为水。
6.根据权利要求3所述的皮革保护镀膜剂,其特征在于,还包含重量百分比为1~5%的防腐剂。
7.根据权利要求6所述的皮革保护镀膜剂,其特征在于,还包含重量百分比为1~3%的防腐剂。
8.根据权利要求1~7任一项所述的皮革保护镀膜剂,其特征在于,所述的水为去离子水。
9.权利要求1~6任一项所述的皮革保护镀膜剂的制备方法,其特征在于,在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、以及水,搅拌15~50min即得。
10.权利要求1~6任一项所述的皮革保护镀膜剂的制备方法,其特征在于,在分散搅拌机中依次加入巴西蜡乳液、聚氨酯、有机硅乳液、流平剂、渗透剂、水以及防腐剂,搅拌15~50min即得。