CN105801138A - 电石炉口用长寿命耐冲刷浇注料 - Google Patents

电石炉口用长寿命耐冲刷浇注料 Download PDF

Info

Publication number
CN105801138A
CN105801138A CN201610118903.9A CN201610118903A CN105801138A CN 105801138 A CN105801138 A CN 105801138A CN 201610118903 A CN201610118903 A CN 201610118903A CN 105801138 A CN105801138 A CN 105801138A
Authority
CN
China
Prior art keywords
parts
life
long
erosion
furnace mouth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610118903.9A
Other languages
English (en)
Inventor
闫祖宁
刘丽君
曹宏光
闫业玉
李德慨
李海君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lvliang Yaojindao Metallurgical Materials Engineering Technology Co Ltd
Original Assignee
Lvliang Yaojindao Metallurgical Materials Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lvliang Yaojindao Metallurgical Materials Engineering Technology Co Ltd filed Critical Lvliang Yaojindao Metallurgical Materials Engineering Technology Co Ltd
Priority to CN201610118903.9A priority Critical patent/CN105801138A/zh
Publication of CN105801138A publication Critical patent/CN105801138A/zh
Pending legal-status Critical Current

Abstract

本发明具体为一种电石炉口用长寿命耐冲刷浇注料，解决了现有的氮化硅接合碳化硅砖作为电石炉口材料成本高寿命低的问题。电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉10~25份、硅微粉3~5份、球沥青1~2份、碳化硅5~8份、纯铝酸钙水泥3~5份、铝矾土熟料60~70份。本发明的电石炉口用长寿命耐冲刷浇注料具有较高的抗剥落、抗渣侵、抗热振性能，可以完美取代氮化硅结合碳化硅砖，不但可以将使用成本降低50%，而且可以将使用寿命提高30%。

Description

电石炉口用长寿命耐冲刷浇注料
技术领域
本发明涉及电石炉口用到的高温耐火材料，具体为一种电石炉口用长寿命耐冲刷浇注料。
背景技术
电炉熔炼法是电石生产工艺的一种，是由焦炭与氧化钙置于2200℃左右的电石炉中熔炼，生成碳化钙。生成的电石由电石炉口排出，电石炉口一般采用氮化硅接合碳化硅砖进行铺设，虽然保证了电石炉口的性能要求，但使用成本高、使用寿命低。
发明内容
本发明为了解决现有的氮化硅接合碳化硅砖作为电石炉口材料成本高寿命低的问题，提供了一种电石炉口用长寿命耐冲刷浇注料。
本发明是采用如下技术方案实现的：电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉10~25份、硅微粉3~5份、球沥青1~2份、碳化硅5~8份、纯铝酸钙水泥3~5份、铝矾土熟料60~70份，水4.5~5份。
浇注料具有加工容易、施工简单、成本低等优点，且使用寿命相对较长，因此是氮化硅结合碳化硅砖的可靠替代品。本发明中加入锆刚玉微粉，有效提高了浇注料的热震稳定性能、抗侵蚀性能等。
本发明的有益效果如下：利用优选的高铝骨料配方配成电石炉口用长寿命耐冲刷浇注料，解决了现有材料性能不足的问题。本发明的电石炉口用长寿命耐冲刷浇注料具有较高的抗剥落、抗渣侵、热震稳定性能，可以取代氮化硅结合碳化硅砖，不但可以将使用成本降低50%，而且可以将使用寿命提高30%。
具体实施方式
电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉10~25份、硅微粉3~5份、球沥青1~2份、碳化硅5~8份、纯铝酸钙水泥3~5份、铝矾土熟料60~70份，水4.5~5份。
实施例1
电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉10份、硅微粉4份、球沥青2份、碳化硅6份、纯铝酸钙水泥3份、铝矾土熟料65份，水4.5份。
实施例2
电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉15份、硅微粉5份、球沥青1份、碳化硅7份、纯铝酸钙水泥4份、铝矾土熟料70份，水4.7份。
实施例3
电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉20份、硅微粉3份、球沥青2份、碳化硅2份、纯铝酸钙水泥5份、铝矾土熟料60份，水5份。
实施例4
电石炉口用长寿命耐冲刷浇注料，是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉15份、硅微粉4份、球沥青1份、碳化硅5份、纯铝酸钙水泥5份、铝矾土熟料70份，水4.9份。

Claims (1)

1.一种电石炉口用长寿命耐冲刷浇注料，其特征在于：是由高铝骨料混合后加水配成，高铝骨料中各组份的配方具体为锆刚玉微粉10~25份、硅微粉3~5份、球沥青1~2份、碳化硅5~8份、纯铝酸钙水泥3~5份、铝矾土熟料60~70份，水4.5~5份。
CN201610118903.9A 2016-03-03 2016-03-03 电石炉口用长寿命耐冲刷浇注料 Pending CN105801138A (zh)