CN105784587A - 一种自粘改性沥青防水卷材粘接强度的测试方法 - Google Patents

一种自粘改性沥青防水卷材粘接强度的测试方法 Download PDF

Info

Publication number
CN105784587A
CN105784587A CN201610132815.4A CN201610132815A CN105784587A CN 105784587 A CN105784587 A CN 105784587A CN 201610132815 A CN201610132815 A CN 201610132815A CN 105784587 A CN105784587 A CN 105784587A
Authority
CN
China
Prior art keywords
self
modified asphalt
cement
testing
asphalt waterproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610132815.4A
Other languages
English (en)
Inventor
汪良
刘金景
吴士玮
刘欢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YUEYANG ORIENTAL YUHONG WATERPROOF TECHNOLOGY Co Ltd
Original Assignee
YUEYANG ORIENTAL YUHONG WATERPROOF TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YUEYANG ORIENTAL YUHONG WATERPROOF TECHNOLOGY Co Ltd filed Critical YUEYANG ORIENTAL YUHONG WATERPROOF TECHNOLOGY Co Ltd
Priority to CN201610132815.4A priority Critical patent/CN105784587A/zh
Publication of CN105784587A publication Critical patent/CN105784587A/zh
Pending legal-status Critical Current

Abstract

一种自粘改性沥青防水卷材粘接强度的测试方法，包括以下步骤：(1)采用水泥模块模具制作水泥模块，所述水泥模块成型长×宽×高尺寸为100～120mm×50～60mm×50～60mm；(2)将沥青基基层处理剂涂刷在水泥块表面；(3)将裁好的自粘改性沥青防水卷材粘贴在涂刷有基层处理剂的水泥块表面；(4)采用拉力机测试卷材粘接强度。本发明通过沥青基基层处理剂实现自粘改性沥青防水卷材与水泥模块的粘接，提高了测试方法对实际施工应用的粘接强度的适用性，并通过水泥模块模具、压辊挤压、拉力机测试等过程控制，提高粘接强度测试的准确性及可控性，提高实验室测试结果对建筑工地实际防水应用的指导价值。

Description

一种自粘改性沥青防水卷材粘接强度的测试方法
技术领域
本发明涉及一种防水卷材粘接强度的测试方法，具体涉及一种自粘改性沥青防水卷材粘接强度的测试方法。
背景技术
目前，自粘改性沥青防水卷材粘接强度的测试方法，在实验室采用的是自粘改性沥青防水卷材与铝板的粘接强度测试，而在实际的施工应用中，自粘改性沥青防水卷材是通过沥青基基层处理剂与水泥基层进行粘接强度测试。因此，由于铝板与基层处理剂材料性能存在巨大差异，采用铝板进行的粘接强度测试并不能完全反应实际施工时的粘接强度。如果按照铝板进行的粘接强度测试结果进行自粘改性沥青防水卷材的研发及生产，所得到的材料并不一定适用于施工过程中与沥青基基层处理剂的粘接。
基于这种现象，亟待探索一种模拟施工应用的方法进行自粘改性沥青防水卷材粘接性能的测试，可更好的反应材料的真实性能。
发明内容
本发明所要解决的技术问题是，提供一种自粘改性沥青防水卷材粘接强度的测试方法，可有效的评价自粘改性沥青防水卷材的粘接强度，提高自粘改性沥青防水卷材粘接性评估与研究的可靠性。
本发明解决其技术问题采用的技术方案是，一种自粘改性沥青防水卷材粘接强度的测试方法，主要包括以下步骤：
(1)采用水泥模块模具制作水泥模块，所述水泥模块成型长×宽×高尺寸为100～120mm×50～60mm×50～60mm；
(2)将沥青基基层处理剂涂刷在水泥块表面；
(3)将裁好的自粘改性沥青防水卷材粘贴在涂刷有基层处理剂的水泥块表面；
(4)采用拉力机测试卷材粘接强度。
进一步，步骤(1)中，所述水泥模块由42.5普通硅酸盐水泥，中砂，水按照质量比为1∶2∶0.4成型，水泥模块成型长×宽×高尺寸为100mm×50mm×50mm，且下表面为平整面，作为粘接面使用。
进一步，步骤(2)中，将沥青基基层处理剂涂刷在水泥模块光滑表面，然后将水泥模块置于标准养护条件下养护30min。
进一步，步骤(3)中，将自粘改性沥青防水卷材粘接在水泥模块表面，粘接面积为100mm×50mm，选用质量为2kg、宽度50～60mm的压辊反复滚压三次粘合面，最后将完成粘接的水泥模块置于标准养护条件下养护24h。
本发明通过沥青基基层处理剂实现自粘改性沥青防水卷材与水泥模块的粘接，提高了测试方法对实际施工应用的粘接强度的适用性，并通过水泥模块模具、压辊挤压、拉力机测试等过程控制，提高粘接强度测试的准确性及可控性，降低了实验室与实际使用中因测试方法不同造成的结果差异。
附图说明
图1为本发明制样结构图(其中，a为自粘改性沥青防水卷材，b为沥青基基层处理剂，c为水泥模块)。
具体实施方式
下面结合实施例和附图对本发明进一步加以说明。
实施例1：自粘改性沥青防水卷材粘接强度的测试方法
在实验室中采取模拟实际施工的方法实现，包括以下实施步骤：
(1)采用水泥模具将42.5普通硅酸盐水泥，中砂，水按质量比为1∶2∶0.4制作成型长×宽×高尺寸为100mm×50mm×50mm水泥模块c，且下表面为平整面，作为粘接面使用。
(2)将沥青基基层处理剂b涂刷在水泥模块光滑表面，然后将水泥模块置于标准养护条件下(温度18～22℃，相对湿度不小于90％)养护30min。
(3)将裁好的自粘改性沥青防水卷材a粘贴在涂刷有基层处理剂的水泥块表面，粘接面积为100mm×50mm；然后采用质量为2kg、宽度50～60mm的压辊反复滚压三次粘合面；接着将完成粘接的水泥模块置于标准养护条件下(温度18～22℃，相对湿度不小于90％)养护24h。
(4)采用拉力机测试自粘改性沥青防水卷材的粘接强度。
采用实施例1的测试方法，自粘改性沥青防水卷材的粘接强度测试比铝板测试法更能接近建筑工地实际使用情况，以更好的表征自粘改性沥青防水卷材与基层的粘接牢固性，更好的表征防水性能。

Claims (4)

1.一种自粘改性沥青防水卷材粘接强度的测试方法，其特征在于，包括以下步骤：
(1)采用水泥模块模具制作水泥模块，所述水泥模块成型长×宽×高尺寸为100～120mm×50～60mm×50～60mm；
(2)将沥青基基层处理剂涂刷在水泥块表面；
(3)将裁好的自粘改性沥青防水卷材粘贴在涂刷有基层处理剂的水泥块表面；
(4)采用拉力机测试卷材粘接强度。
2.根据权利要求1所述的自粘改性沥青防水卷材粘接强度的测试方法，其特征在于，步骤(1)中，所述水泥模块由42.5普通硅酸盐水泥，中砂，水按照质量比为1∶2∶0.4成型，水泥模块成型长×宽×高尺寸为100mm×50mm×50mm，且下表面为平整面。
3.根据权利要求1或2所述的自粘改性沥青防水卷材粘接强度的测试方法，其特征在于，步骤(2)中，将沥青基基层处理剂涂刷在水泥模块光滑表面，然后将水泥模块置于标准养护条件下养护30min。
4.根据权利要求1～3之一所述的自粘改性沥青防水卷材粘接强度的测试方法，其特征在于，步骤(3)中，将自粘改性沥青防水卷材粘接在水泥模块表面，粘接面积为100mm×50mm，选用质量为2kg、宽度50～60mm的压辊反复滚压三次粘合面，最后将完成粘接的水泥模块置于标准养护条件下养护24h。
CN201610132815.4A 2016-03-09 2016-03-09 一种自粘改性沥青防水卷材粘接强度的测试方法 Pending CN105784587A (zh)