CN105753416A - Novel early-strength and quick-drying tile adhesive concentrate - Google Patents
Novel early-strength and quick-drying tile adhesive concentrate Download PDFInfo
- Publication number
- CN105753416A CN105753416A CN201510533587.7A CN201510533587A CN105753416A CN 105753416 A CN105753416 A CN 105753416A CN 201510533587 A CN201510533587 A CN 201510533587A CN 105753416 A CN105753416 A CN 105753416A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- concentrate feed
- adhesive
- quick
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to novel early-strength and quick-drying tile adhesive concentrate.The tile adhesive concentrate at least comprises, by weight, 500-800 parts of sulphoaluminate cement clinker, 200-500 parts of high-strength gypsum, 1-100 parts of early strength agent, 40-120 parts of dispersible latex powder, 1-10 parts of retarder, 1-40 parts of water reducer and 5-20 parts of cellulose ether.The novel early-strength and quick-drying tile adhesive concentrate has the advantages that the sulphoaluminate cement clinker and Portland cement are used as the composite cement base materials, the composite cement base materials are coordinated with the additives such as the early strength agent and retarder, tile glue coagulation time is regulated, sufficient operation time is guaranteed, early strength and quick drying are achieved, the next joint filling can be performed immediately after tile adhering, construction time can be shortened, and the construction period can be shortened.
Description
Technical field
The present invention relates to a kind of ceramic tile adhesive concentrate feed, specifically a kind of novel morning strong quick-drying ceramic tile bond concentrate feed.
Background technology
Ceramic tile is one of important architectural constructional materials, and the method for traditional sticking brick is to be soaked a period of time in water by ceramic tile, ash concrete and sand is mixed into slurry by a certain percentage and is applied to the ceramic tile back side, then paste in basic unit.Along with people are more and more higher to the requirement of ceramic tile, the water absorption of ceramic tile is more and more lower, the phenomenon such as traditional method of attaching easily causes ceramic tile hollowing, come off.In order to stop hollowing, fall brick phenomenon, present sticking brick is then widely used glue for tile, and glue for tile is with ash concrete, quartz sand for main component, adds a kind of mixture of redispersible rubber powder and other additive.Glue for tile solves ceramic tile hollowing well, falls brick phenomenon, but its transport, storage cost significantly high.Early-strength quick-dry type ceramic tile adhesive concentrate feed, it is made up of multiple chemical admixture, glue for tile make consumption little, effect is notable, and conveniently transport, storage, as long as getting final product packing and selling after premix dry mortar factory mixs homogeneously according to a certain percentage with satisfactory ash concrete, quartz sand, be conducive to quality control.Utilize the ceramic tile adhesive that this concentrate feed produces to have early strong, quick-drying characteristic, be particularly suited for the occasions such as second-hand house quickly renovation.
Summary of the invention
For above-mentioned situation, the present invention provides a kind of novel morning strong quick-drying ceramic tile bond concentrate feed, Concentrated formulations is selected sulfur aluminum clinker, with portland cement as complex cement base material, mates the additive such as early strength agent, retarder, regulate the setting time of glue for tile, ensure sufficient operable time, there is early strong, quick-drying feature simultaneously, next step joint filling work after patch block, can be carried out at once, the engineering time can be shortened, save the duration.
To achieve these goals, technical scheme is as follows:
A kind of novel morning strong quick-drying ceramic tile bond concentrate feed, described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
Sulphoaluminate cement clinker 500-800
High strength gypsum 200-500
Early strength agent 1-100
Redispersible latex powder 40-120
Retarder 1-10
Water reducer 1-40
Cellulose ether 5-20
As the presently preferred embodiments, the calcium sulphoaluminate content in described sulphoaluminate cement clinker is more than 55%.
As the presently preferred embodiments, described early strength agent is one or more in lithium sulfate, lithium carbonate, calcium formate.
As the presently preferred embodiments, described redispersible latex powder is one or both in ethylene-vinyl acetate copolymer, acrylic compounds latex powder.
As the presently preferred embodiments, described retarder is one or more in boric acid, sodium gluconate, tartaric acid.
As the presently preferred embodiments, described water reducer be polycarboxylic acid series high efficiency water reducing agent, naphthalene sulfonate high efficiency water reducing agent one or both.
As the presently preferred embodiments, described cellulose ether be hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether one or both, the viscosity 2000-75000mPa S of cellulose ether.
Novel morning strong quick-drying ceramic tile bond concentrate feed preparation technology, it is characterised in that comprise the following steps:
One, first according to match ratio precise, the additives such as cellulose ether, redispersable latex powder, water reducer, retarder, early strength agent are weighed；
Two, by above-mentioned match ratio precise, after sulphoaluminate cement clinker, high strength gypsum are weighed, add load weighted additive in step one, in advance after hand operated mixing, place into JC/T681-2005 planetary cement mortar mixer stirring at low speed proportioning material, stir 10-20 minute, until mix homogeneously obtains concentrate feed.
A kind of preparation method of the ceramic tile adhesive composite by early strong quick-dry type concentrate feed:
According to 1 part of concentrate feed, 2 part of 42.5 portland cement, the ratio of 5 part of 60 ~ 140 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, namely it is available for the adhesive of sticking brick.
The using method of a kind of ceramic tile adhesive composite by early strong quick-dry type concentrate feed, it is characterised in that comprise the following steps:
One, guarantee that all of basal plane structurally firm, dry, clean, nothing moves, also without oils, oils and fats, paraffin and other fouling products；Paint basal plane must expose more than at least 75% clean basal plane；Body of wall moisture content is not less than 20%；
Two, mix according to adhesive and clear water proportionally 1:0.24, by electric blender, adhesive and clear water are stirred well to uniformly without caking paste；
Three, after the material after stirring being stood 5-10 minute, then stir 1-2 minute a little；
Four, with the suitable notched scraper adhesive that application step three is prepared on basal plane；
Five, on the position have been coated with adhesive, pressure ceramic tile is rubbed, it is ensured that ceramic tile and adhesive have better stickup, and hollowing does not occur under ceramic tile；
Six, wipe, with sponge or wet cloth, the adhesive material that ceramic tile surface stays；
Seven, after waiting 4 hours, can arranging joint filling, the concrete time appropriately adjusts depending on weather, execution conditions difference.
The invention have the advantage that the present invention selects sulfur aluminum clinker in Concentrated formulations, with portland cement as complex cement base material, the coupling additive such as early strength agent, retarder, regulate the setting time of glue for tile, ensure sufficient operable time, there is early strong, quick-drying feature simultaneously, next step joint filling work after patch block, can be carried out at once, the engineering time can be shortened, save the duration.Inventive formulation can be compound in sticking brick, convenient transport, storage with portland cement, quartz sand.And the proportioning regulating concentrate feed with portland cement, quartz sand can be passed through, obtain the glue for tile of varying strength, in order to paste different types of ceramic tile.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be easy to understand, the present invention is expanded on further.
Embodiment 1:
A kind of novel morning strong quick-drying ceramic tile bond concentrate feed, described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
According to 1 part of concentrate feed, 1 part of 52.5 portland cement, the ratio of 1 part of 60 ~ 120 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, namely it is available for the adhesive of sticking brick.
The ceramic tile bond of embodiment 1 preparation is carried out performance Indexs measure, as shown in the table:
Embodiment 2:
A kind of novel morning strong quick-drying ceramic tile bond concentrate feed, described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
According to 1 part of concentrate feed, 1 part of 52.5 portland cement, the ratio of 1 part of 60 ~ 120 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, namely it is available for the adhesive of sticking brick.
Embodiment 3:
A kind of novel morning strong quick-drying ceramic tile bond concentrate feed, described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
According to 1 part of concentrate feed, 1 part of 52.5 portland cement, the ratio of 1 part of 60 ~ 120 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, namely it is available for the adhesive of sticking brick.
Embodiment 4:
A kind of novel morning strong quick-drying ceramic tile bond concentrate feed, described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
According to 1 part of concentrate feed, 1 part of 52.5 portland cement, the ratio of 1 part of 60 ~ 120 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, namely it is available for the adhesive of sticking brick.
Embodiment 5:
A kind of novel morning strong quick-drying ceramic tile bond concentrate feed, described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
According to 1 part of concentrate feed, 1 part of 52.5 portland cement, the ratio of 1 part of 60 ~ 120 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, namely it is available for the adhesive of sticking brick.
A kind of by the using method of early ceramic tile adhesive prepared by strong quick-dry type concentrate feed, it is characterised in that to comprise the following steps:
One, guarantee that all of basal plane structurally firm, dry, clean, nothing moves, also without oils, oils and fats, paraffin and other fouling products；Paint basal plane must expose more than at least 75% clean basal plane；Body of wall moisture content is not less than 20%；
Two, mix according to adhesive and clear water proportionally 1:0.24, by electric blender, adhesive and clear water are stirred well to uniformly without caking paste；
Three, after the material after stirring being stood 5-10 minute, then stir 1-2 minute a little；
Four, with the suitable notched scraper adhesive that application step three is prepared on basal plane；
Five, on the position have been coated with adhesive, pressure ceramic tile is rubbed, it is ensured that ceramic tile and adhesive have better stickup, and hollowing does not occur under ceramic tile；
Six, wipe, with sponge or wet cloth, the adhesive material that ceramic tile surface stays；
Seven, after waiting 4 hours, can arranging joint filling, the concrete time appropriately adjusts depending on weather, execution conditions difference.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; simply principles of the invention described in above-described embodiment and description; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements both fall within claimed the scope of the present invention.The protection domain of application claims is defined by appending claims and equivalent thereof.
Claims (9)
1. one kind novel morning strong quick-drying ceramic tile bond concentrate feed, it is characterised in that described glue for tile concentrate feed at least includes following component, and the mass fraction specific gravity range of each component and component is respectively as follows:
Sulphoaluminate cement clinker 500-800
High strength gypsum 200-500
Early strength agent 1-100
Redispersible latex powder 40-120
Retarder 1-10
Water reducer 1-40
Cellulose ether 5-20.
2. strong quick-drying ceramic tile bond concentrate feed novel morning according to claim 1, it is characterised in that the calcium sulphoaluminate content in described sulphoaluminate cement clinker is more than 55%.
3. strong quick-drying ceramic tile bond concentrate feed novel morning according to claim 1, it is characterised in that described early strength agent is one or more in lithium sulfate, lithium carbonate, calcium formate.
4. strong quick-drying ceramic tile bond concentrate feed novel morning according to claim 1, it is characterised in that described retarder is one or more in boric acid, sodium gluconate, tartaric acid.
5. strong quick-drying ceramic tile bond concentrate feed novel morning according to claim 1, it is characterised in that described water reducer be polycarboxylic acid series high efficiency water reducing agent, naphthalene sulfonate high efficiency water reducing agent one or both.
6. strong quick-drying ceramic tile bond concentrate feed novel morning according to claim 1, it is characterised in that described cellulose ether be hydroxypropyl methyl cellulose ether, ethoxyl methyl cellulose ether one or both, the viscosity 2000-75000mPa S of cellulose ether.
7. the preparation technology of strong quick-drying ceramic tile bond concentrate feed novel morning, it is characterised in that comprise the following steps:
One, first according to match ratio precise, the additives such as cellulose ether, redispersable latex powder, water reducer, retarder, early strength agent are weighed；
Two, by above-mentioned match ratio precise, after sulphoaluminate cement clinker, high strength gypsum are weighed, add load weighted additive in step one, in advance after hand operated mixing, place into JC/T681-2005 planetary cement mortar mixer stirring at low speed proportioning material, stir 10-20 minute, until mix homogeneously obtains concentrate feed.
8. one kind by the preparation method of the composite ceramic tile adhesive of early strong quick-dry type concentrate feed, it is characterized in that, according to 1 part of concentrate feed, 2 part of 42.5 portland cement, the ratio of 5 part of 60 ~ 140 order quartz sand, concentrate feed, portland cement, quartz sand are put into JC/T681-2005 planetary cement mortar mixer stirring at low speed 10-20 minute, until mix homogeneously, is namely available for the adhesive of sticking brick.
9. one kind by the using method of the composite ceramic tile adhesive of early strong quick-dry type concentrate feed, it is characterised in that comprise the following steps:
One, guarantee that all of basal plane structurally firm, dry, clean, nothing moves, also without oils, oils and fats, paraffin and other fouling products；Paint basal plane must expose more than at least 75% clean basal plane；Body of wall moisture content is not less than 20%；
Two, mix according to adhesive and clear water proportionally 1:0.24, by electric blender, adhesive and clear water are stirred well to uniformly without caking paste；
Three, after the material after stirring being stood 5-10 minute, then stir 1-2 minute a little；
Four, with the suitable notched scraper adhesive that application step three is prepared on basal plane；
Five, on the position have been coated with adhesive, pressure ceramic tile is rubbed, it is ensured that ceramic tile and adhesive have better stickup, and hollowing does not occur under ceramic tile；
Six, wipe, with sponge or wet cloth, the adhesive material that ceramic tile surface stays；
Seven, after waiting 4 hours, can arranging joint filling, the concrete time appropriately adjusts depending on weather, execution conditions difference.