CN105735034A - Efficient ink adsorption copy paper and preparing method thereof - Google Patents
Efficient ink adsorption copy paper and preparing method thereof Download PDFInfo
- Publication number
- CN105735034A CN105735034A CN201610092348.7A CN201610092348A CN105735034A CN 105735034 A CN105735034 A CN 105735034A CN 201610092348 A CN201610092348 A CN 201610092348A CN 105735034 A CN105735034 A CN 105735034A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- copy paper
- pulp
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses efficient ink adsorption copy paper and a preparing method thereof. The efficient ink adsorption copy paper is prepared from, by weight, 20-35 parts of bleached broad leaf pulp, 2-6 parts of sodium polyacrylate, 2-7 parts of powdered ink adhesive agent, 1-3 parts of water retaining resin, 16-33 parts of reed pulp, 1-10 parts of vinylon binder, 21-43 parts of wood pulp, 2-6 parts of dispersing agents, 5-12 parts of synthetic resin, 0.5-2 parts of brightening agent, 1-15 parts of titanium dioxide, 0.6-2.3 parts of polyvinyl acetate emulsion, 0.3-2 parts of white nano pigment paste, 1-2 parts of curing agent and 0.7-3.8 parts of cross-linking agent. Reed pulp, wood pulp and bleached broad leaf pulp are used as main materials for preparing the paper, and vinylon binder, titanium dioxide, cross-linking agent and various dispersing agents are adopted too, so that the prepared efficient ink adsorption copy paper is high in static bending intensity, small in deformation during printing or copying, high in color fastness and color saturation stability, and capable of well adsorbing ink. Meanwhile, by adding the powdered ink adhesive agent and the brightening agent, the ink adsorption effect and the brightness of the paper are improved.
Description
Technical field
The present invention relates to a kind of efficiently blotting copy paper and preparation method thereof.
Background technology
Traditional copy paper production technology generally uses bleached chemical softwood pulp to be primary raw material, or adds
Bleaching straw pulp uses calcium carbonate or Pulvis Talci to be filler, and such copy paper MOR is low, prints or multiple
During print, deformation is big, easy warpage, can not well adsorb ink simultaneously, and color fastness is bad, printed drawings picture element
It is poor to measure, the saturated poor stability of color.
Summary of the invention
It is high that the technical problem to be solved is to provide a kind of MOR, deforms little when printing or duplicate,
Can well adsorb ink, color fastness is good, the efficient blotting copy paper of the saturated good stability of color.
For solving the problems referred to above, the present invention is achieved through the following technical solutions: a kind of efficiently blotting is multiple
Printing paper, this efficient blotting copy paper is made up of following weight composition: bleaching broad-leaved slurry 20-35 part,
Sodium polyacrylate 2-6 part, powdered ink adhesive agent 2-7 part, solid water resin 1-3 part, reed pulp 16-33 part, dimension
Synthetic fibre binding agent 1-10 part, wood pulp 21-43 part, dispersant 2-6 part, synthetic resin 5-12 part, brightening agent
0.5-2 part, titanium dioxide 1-15 part, polyvinyl acetate emulsion 0.6-2.3 part, white nano dye slurry 0.3-2
Part, firming agent 1-2 part and cross-linking agent 0.7-3.8 part.
Another technical problem to be solved by this invention is to provide the preparation method of a kind of efficient blotting copy paper,
The present invention is achieved through the following technical solutions: the preparation process of described efficient blotting copy paper is such as
Under:
1) bleaching broad-leaved slurry 20-35 part, reed pulp 16-33 part, polyvinyl binding agent 1-10 are extracted by weight ratio
Part, wood pulp 21-43 part and titanium dioxide 1-15 part mix homogeneously add beater;
2) in the beater of step 1, dispersant 2-6 part, synthetic resin 5-12 part and brightening agent 0.5-2 are added
Part, making beating dispersion 30 minutes;
3) oleo stock after making beating dispersion is added sodium polyacrylate 2-6 part, powdered ink adhesive agent 2-7 part, consolidates
Water-resin 1-3 part, polyvinyl acetate emulsion 0.6-2.3 part, white nano dye are starched 0.3-2 part, are consolidated
Agent 1-2 part and cross-linking agent 0.7-3.8 part, be modulated into the slurry that pH value is 7.0-9.0;
4) oven temperature is adjusted to 65 DEG C-75 DEG C;
5) slurry of molding in step 3 is uniformly coated on drying plate;
6) slurry after extraction step 5 tiling is dried in being placed on baking oven and is finished product.
The present invention efficient blotting copy paper provides the benefit that: use reed time prepared by described efficient blotting copy paper
Slurry, wood pulp and bleaching broad-leaved slurry for main material, collocation polyvinyl binding agent, titanium dioxide, cross-linking agent and each simultaneously
Plant dispersant, make the efficient blotting copy paper MOR made high, deform little when printing or duplicate, can be very
Good absorption ink, color fastness is good, the saturated good stability of color;With the addition of powdered ink adhesive agent simultaneously and brighten
Agent, improves the white luminance of blotting effect and paper.
Detailed description of the invention
Following example are used for illustrating the present invention, but are not limited to the scope of the present invention.
Embodiment 1
A kind of efficiently blotting copy paper of the present invention, this efficient blotting copy paper is to be become by following weight
Part composition: bleaching broad-leaved starch 20 parts, sodium polyacrylate 2 parts, powdered ink adhesive agent 2 parts, solid water resin 1 part,
Reed pulp 16 parts, polyvinyl binding agent 1 part, wood pulp 21 parts, dispersant 2 parts, synthetic resin 5 parts, brighten
Agent 0.5 part, titanium dioxide 1 part, polyvinyl acetate emulsion 0.6 part, white nano dye starch 0.3 part,
1 part of firming agent and cross-linking agent 0.7 part.
The preparation process of described efficient blotting copy paper is as follows:
1) 20 parts of bleaching broad-leaved slurry, reed pulp 16 parts, polyvinyl binding agent 1 part, wood are extracted by weight ratio
Starch 21 parts and 1 part of mix homogeneously of titanium dioxide adds beater;
2) in the beater of step 1, dispersant 2 parts, synthetic resin 5 parts and 0.5 part of brightening agent are added,
Making beating dispersion 30 minutes;
3) oleo stock after making beating dispersion adds sodium polyacrylate 2 parts, powdered ink adhesive agent 2 parts, solid water tree
1 part of fat, polyvinyl acetate emulsion 0.6 part, white nano dye starch 0.3 part, 1 part of firming agent and friendship
Connection agent 0.7 part, is modulated into the slurry that pH value is 7.0-9.0;
4) oven temperature is adjusted to 65 DEG C-75 DEG C;
5) slurry of molding in step 3 is uniformly coated on drying plate;
6) slurry after extraction step 5 tiling is dried in being placed on baking oven and is finished product.
Embodiment 2
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: bleaching broad-leaved starch 35 parts, sodium polyacrylate 6 parts, powdered ink adhesive agent 7 parts, solid water resin 3 parts,
Reed pulp 33 parts, polyvinyl binding agent 10 parts, wood pulp 43 parts, dispersant 6 parts, synthetic resin 12 parts, increasing
White agent 2 parts, titanium dioxide 15 parts, polyvinyl acetate emulsion 2.3 parts, white nano dye are starched 2 parts, are consolidated
Agent 2 parts and cross-linking agent 3.8 parts.
Embodiment 3
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: bleaching broad-leaved starch 28 parts, sodium polyacrylate 4 parts, powdered ink adhesive agent 4 parts, solid water resin 2 parts,
Reed pulp 25 parts, polyvinyl binding agent 5 parts, wood pulp 31 parts, dispersant 4 parts, synthetic resin 8 parts, brighten
Agent 1 part, titanium dioxide 7 parts, polyvinyl acetate emulsion 1.5 parts, white nano dye starch 1 part, solidification
Agent 1.5 parts and cross-linking agent 2 parts.
Embodiment 4
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: bleaching broad-leaved starch 23 parts, sodium polyacrylate 3 parts, powdered ink adhesive agent 3 parts, solid water resin 1.5 parts,
Reed pulp 21 parts, polyvinyl binding agent 2 parts, wood pulp 24 parts, dispersant 2.5 parts, synthetic resin 6 parts, increasing
White agent 0.8 part, titanium dioxide 3 parts, polyvinyl acetate emulsion 0.9 part, white nano dye starch 0.5 part,
1.3 parts of firming agent and cross-linking agent 1 part.
Embodiment 5
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: bleaching broad-leaved starch 31 parts, sodium polyacrylate 5 parts, powdered ink adhesive agent 6 parts, solid water resin 2.5 parts,
Reed pulp 31 parts, polyvinyl binding agent 8 parts, wood pulp 41 parts, dispersant 5 parts, synthetic resin 10 parts, brighten
Agent 1.7 parts, titanium dioxide 12 parts, polyvinyl acetate emulsion 2 parts, white nano dye are starched 1.6 parts, are consolidated
Agent 1.8 parts and cross-linking agent 3.3 parts.
Embodiment 6
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: 24 parts of bleaching broad-leaved slurry, sodium polyacrylate 3.3 parts, powdered ink adhesive agent 4.2 parts, solid water resin 1.5
Part, reed pulp 22 parts, polyvinyl binding agent 7.8 parts, wood pulp 29 parts, dispersant 3.6 parts, synthetic resin 7.3
Part, 1.3 parts of brightening agent, titanium dioxide 11 parts, polyvinyl acetate emulsion 1.6 parts, white nano dye slurry
0.6 part, 1.3 parts of firming agent and cross-linking agent 2.2 parts.
Embodiment 7
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: 25 parts of bleaching broad-leaved slurry, sodium polyacrylate 4.6 parts, powdered ink adhesive agent 2.5 parts, solid water resin 2.1
Part, reed pulp 19 parts, polyvinyl binding agent 3.5 parts, wood pulp 35 parts, dispersant 3 parts, synthetic resin 11 parts,
0.8 part of brightening agent, titanium dioxide 4 parts, polyvinyl acetate emulsion 2 parts, white nano dye starch 1.5 parts,
2 parts of firming agent and cross-linking agent 3 parts.
Embodiment 8
Its difference from Example 1 is, this efficient blotting copy paper is by following weight composition
Composition: bleaching broad-leaved starch 30 parts, sodium polyacrylate 5 parts, powdered ink adhesive agent 5 parts, solid water resin 2 parts,
Reed pulp 25 parts, polyvinyl binding agent 5 parts, wood pulp 30 parts, dispersant 5 parts, synthetic resin 10 parts, brighten
Agent 1 part, titanium dioxide 10 parts, polyvinyl acetate emulsion 1 part, white nano dye slurry 1 part, firming agent
1.5 parts and cross-linking agent 2 parts.
The present invention is not limited to above-mentioned preferred forms, anyone draw under the enlightenment of the present invention other are any
Product as same or like with the present invention, within all falling within protection scope of the present invention.
Claims (2)
1. an efficient blotting copy paper, it is characterised in that: this efficient blotting copy paper is by following weight portion
Proportioning composition form: bleaching broad-leaved slurry 20-35 part, sodium polyacrylate 2-6 part, powdered ink adhesive agent 2-7 part,
Solid water resin 1-3 part, reed pulp 16-33 part, polyvinyl binding agent 1-10 part, wood pulp 21-43 part, dispersant
2-6 part, synthetic resin 5-12 part, brightening agent 0.5-2 part, titanium dioxide 1-15 part, polyvinyl acetate breast
Liquid 0.6-2.3 part, white nano dye slurry 0.3-2 part, firming agent 1-2 part and cross-linking agent 0.7-3.8 part.
2. the preparation method of the efficient blotting copy paper prepared described in claim 1, it is characterised in that:
The method comprises the following steps:
1) bleaching broad-leaved slurry 20-35 part, reed pulp 16-33 part, polyvinyl binding agent 1-10 are extracted by weight ratio
Part, wood pulp 21-43 part and titanium dioxide 1-15 part mix homogeneously add beater;
2) in the beater of step 1, dispersant 2-6 part, synthetic resin 5-12 part and brightening agent 0.5-2 are added
Part, making beating dispersion 30 minutes;
3) oleo stock after making beating dispersion is added sodium polyacrylate 2-6 part, powdered ink adhesive agent 2-7 part, consolidates
Water-resin 1-3 part, polyvinyl acetate emulsion 0.6-2.3 part, white nano dye are starched 0.3-2 part, are consolidated
Agent 1-2 part and cross-linking agent 0.7-3.8 part, be modulated into the slurry that pH value is 7.0-9.0;
4) oven temperature is adjusted to 65 DEG C-75 DEG C;
5) slurry of molding in step 3 is uniformly coated on drying plate;
6) slurry after extraction step 5 tiling is dried in being placed on baking oven and is finished product.