CN107034723A - Color ink jet printer paper and preparation method thereof - Google Patents
Color ink jet printer paper and preparation method thereof Download PDFInfo
- Publication number
- CN107034723A CN107034723A CN201710289242.0A CN201710289242A CN107034723A CN 107034723 A CN107034723 A CN 107034723A CN 201710289242 A CN201710289242 A CN 201710289242A CN 107034723 A CN107034723 A CN 107034723A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- ink jet
- jet printer
- color ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of color ink jet printer paper and preparation method thereof, the color ink jet printer paper includes the cellulose of 20~30 parts by weight, the hemicellulose of 15~25 parts by weight, the lignin of 10~20 parts by weight, the polyurethane of 5~10 parts by weight, the epoxy resin of 2~5 parts by weight, the chitosan quaternary ammonium salt of 2~3 parts by weight, the octadecyldimethylamine of 1~4 parts by weight, the wax of 4~6 parts by weight, the montmorillonite of 2~7 parts by weight, the pigment of 3~7 parts by weight, the surfactant of the staple fibre of 7~12 parts by weight and 2~5 parts by weight.Color ink jet printer paper can absorb ink in the present invention, and the ink droplet that also can be does not spread to periphery, and the image quality of air brushing image can be caused close to or up photographic picture effect, colour reproduction is true to nature, firm number of color, in bright gay color, front cover, has a sense of hierarchy at image clearly.Printing paper quality is high in addition, cost is low, absorbency is good, with certain intensity, is difficult fold.
Description
Technical field
The present invention relates to printing paper field, especially a kind of color ink jet printer paper and preparation method thereof.
Background technology
Color ink jet printer paper is the acceptor that ink jet printer nozzles spray ink, and image or text are recorded in the above
Word.Color ink jet printer paper is a kind of new recording sheet, because development is fast, also ununified quality standard.Use for reference international normal
There are corresponding quality testing scope and examination criteria in technical specification, the country, is beaten according to the color jet-ink that this standard production goes out
Printing paper quality is not less than same kind of products at abroad, but the market price can be lower than the like product of import by 20%~50%.Therefore, state
Producing color ink jet printer paper has the very strong market competitiveness.But the oil absorbency of color ink jet printer paper is poor at present,
And ink droplet can also spread to periphery.
The content of the invention
In view of this, it is an object of the invention to provide a kind of color ink jet printer paper and preparation method thereof, with good
Oil absorbency, and ink droplet do not spread to periphery.
To achieve these goals, the invention provides following technical scheme：
A kind of color ink jet printer paper, includes the raw material of following parts by weight：
Preferably, the pigment is cinnabar, carbon black, laterite, realgar, peacock green, gamboge, alizarin red, indigo-blue, titanium white, zinc
Barium white, lead chromate yellow or barba hispanica.
Preferably, the wax is paraffin, Tissuemat E, beeswax or vegetable wax.
Preferably, the staple fibre is alginate fibre, CUP, nitric acid ester fiber or soybean fiber.
Preferably, in addition to antiseptic, the antiseptic, the antiseptic includes N- (4- hydroxy 3-methoxybenzene first
Base) acrylamide and chitin.
Preferably, the surfactant is neopelex or triethanolamine soap.
Preferably, in addition to antistatic additive, the antistatic additive is dodecyldimethylammonium hydroxide inner salt or fatty alcohol polyoxy
Vinethene.
Present invention also offers a kind of above-mentioned preparation method of color ink jet printer paper, comprise the following steps：
It is beaten after cellulose, hemicellulose, lignin, surfactant are mixed, adds wooden polyurethane, asphalt mixtures modified by epoxy resin
Fat, chitosan quaternary ammonium salt, octadecyldimethylamine, wax, montmorillonite, pigment, staple fibre use beating crusher decentralized processing, then
It is put into ultrasonic disperse instrument and carries out ultrasonic disperse, obtains mixed slurry；By mixed slurry with being manufactured paper with pulp, being dried with oblique net paper machine, obtain
To color ink jet printer paper.
A kind of color ink jet printer paper that the present invention is provided and preparation method thereof, the color ink jet printer paper includes 20~
The cellulose of 30 parts by weight, the hemicellulose of 15~25 parts by weight, the lignin of 10~20 parts by weight, 5~10 weight
The polyurethane of number, the epoxy resin of 2~5 parts by weight, the chitosan quaternary ammonium salt of 2~3 parts by weight, 1~4 parts by weight
Octadecyldimethylamine, the wax of 4~6 parts by weight, the montmorillonite of 2~7 parts by weight, the pigment of 3~7 parts by weight, 7~
The surfactant of the staple fibre of 12 parts by weight and 2~5 parts by weight.Color ink jet printer paper can absorb in the present invention
Ink, the ink droplet that also can be is not spread to periphery, and the image quality of air brushing image can be caused close to or up photographic picture
Effect, colour reproduction is true to nature, firm number of color, in bright gay color, front cover, image clearly, has a sense of hierarchy.Other printing paper quality height,
Cost is low, absorbency is good, with certain intensity, is difficult fold.
Embodiment
The invention provides a kind of color ink jet printer paper, include the raw material of following parts by weight：
In above-mentioned technical proposal, color ink jet printer paper can absorb ink, and the ink droplet that also can be does not spread to periphery,
The image quality of air brushing image can be caused close to or up photographic picture effect again, colour reproduction is true to nature, firm number of color, and color is fresh
Bright, front cover, image clearly, has a sense of hierarchy.Printing paper quality is high in addition, cost is low, absorbency is good, with certain intensity, no
Easy fold.
In the present invention, the parts by weight of cellulose are 20~30 parts；In an embodiment of the present invention, the weight of cellulose
Number is 23~27 parts；In other embodiments, the parts by weight of cellulose are 24~26 parts.
In the present invention, the parts by weight of hemicellulose are 15~25 parts；In an embodiment of the present invention, hemicellulose
Parts by weight are 17~23 parts；In other embodiments, the parts by weight of hemicellulose are 19~21 parts.
In the present invention, the parts by weight of lignin are 10~20 parts；In an embodiment of the present invention, the weight of lignin
Number is 12~18 parts；In other embodiments, the parts by weight of lignin are 14~16 parts.
Polyurethane and epoxy resin can improve the quality of printing paper.In the present invention, the parts by weight of polyurethane be 5~
10 parts；In an embodiment of the present invention, the parts by weight of polyurethane are 6~9 parts；In other embodiments, the weight of polyurethane
Number is 7~8 parts.
In the present invention, the parts by weight of epoxy resin are 2~5 parts；In an embodiment of the present invention, the weight of epoxy resin
It is 2.5~4.5 parts to measure number；In other embodiments, the parts by weight of epoxy resin are 3~4 parts.
The fastness of chitosan quaternary ammonium salt and octadecyldimethylamine to improve pigment and printing paper so that colour spray
Black printing paper uniform in color.In the present invention, the parts by weight of chitosan quaternary ammonium salt are 2~3 parts；In embodiments of the invention
In, the parts by weight of chitosan quaternary ammonium salt are 2.2~2.8 parts；In other embodiments, the parts by weight of chitosan quaternary ammonium salt are
2.4~2.6 parts.
In the present invention, the parts by weight of octadecyldimethylamine are 1~4 part；In an embodiment of the present invention, ten eight
The parts by weight of Alkyl Dimethylamine are 1.5~3.5 parts；In other embodiments, the parts by weight of octadecyldimethylamine
For 2~3 parts.
Printing ink absorption of the wax to improve printing paper.In an embodiment of the present invention, wax is paraffin, Tissuemat E, honeybee
Wax or vegetable wax.
In the present invention, the parts by weight of wax are 4~6 parts；In an embodiment of the present invention, the parts by weight of wax are 4.4
~5.6 parts；In other embodiments, the parts by weight of wax are 4.8~5.2 parts.
Montmorillonite is to improve the roughness of printing paper, so as to improve the printing definition of printing paper.In the present invention, cover
The parts by weight for taking off soil are 2~7 parts；In an embodiment of the present invention, the parts by weight of montmorillonite are 3~6 parts；In other implementations
In example, the parts by weight of montmorillonite are 4~5 parts.
In an embodiment of the present invention, pigment be cinnabar, carbon black, laterite, realgar, peacock green, gamboge, alizarin red, it is indigo-blue,
Titanium white, lithopone, lead chromate yellow or barba hispanica.
In the present invention, the parts by weight of pigment are 3~7 parts；In an embodiment of the present invention, the parts by weight of pigment are
4~6 parts；In other embodiments, the parts by weight of pigment are 4.5~5.5 parts.
Folding strength of the staple fibre to improve printing paper；In an embodiment of the present invention, staple fibre be alginate fibre,
CUP, nitric acid ester fiber or soybean fiber.
In the present invention, the parts by weight of staple fibre are 7~12 parts；In an embodiment of the present invention, staple fibre
Parts by weight are 8~11 parts；In other embodiments, the parts by weight of staple fibre are 9~10 parts.
In an embodiment of the present invention, surfactant is neopelex or triethanolamine soap.
In the present invention, the parts by weight of surfactant are 2~5 parts；In an embodiment of the present invention, surfactant
Parts by weight be 2.5~4.5 parts；In other embodiments, the parts by weight of surfactant are 3~4 parts.
In an embodiment of the present invention, in order that obtaining printing paper has antistatic property, antistatic additive is dodecyl two
Methyl betaine or AEO；In other embodiments, anlistatig parts by weight are 1~2 part.
In an embodiment of the present invention, in order that obtaining printing paper has antibiotic property, antiseptic includes N- (4- hydroxyls -3-
Mehtoxybenzyl) acrylamide and chitin；In other embodiments, the parts by weight of antiseptic are 0.5~1 part.
It should be noted that in antiseptic N- (4- hydroxy 3-methoxybenzene methyls) acrylamides and chitin quality
Than for (1.2~1.8)：(0.5~0.8).
Present invention also offers a kind of preparation method of color ink jet printer paper, comprise the following steps：
It is beaten after cellulose, hemicellulose, lignin, surfactant are mixed, adds wooden polyurethane, asphalt mixtures modified by epoxy resin
Fat, chitosan quaternary ammonium salt, octadecyldimethylamine, wax, montmorillonite, pigment, staple fibre use beating crusher decentralized processing, then
It is put into ultrasonic disperse instrument and carries out ultrasonic disperse, obtains mixed slurry；By mixed slurry with being manufactured paper with pulp, being dried with oblique net paper machine, obtain
To color ink jet printer paper.
Wherein, cellulose, hemicellulose, lignin, polyurethane, epoxy resin, chitosan quaternary ammonium salt, hexadecyldimethylamine
Base amine, wax, montmorillonite, pigment, staple fibre, surfactant are same as above, will not be repeated here.
Above-mentioned technical proposal, manufacturing process is simple, and manufacturing cost is low, and the color ink jet printer paper quality of production is good, intensity
Height, color consistency is good.
In order to further illustrate the present invention, the color ink jet printer paper and its system provided with reference to embodiment the present invention
Preparation Method is described in detail.
Embodiment 1
Color ink jet printer paper is counted including following material by weight：24 parts of cellulose, 17 parts of hemicellulose, lignin
12 parts, 8 parts of polyurethane, 3 parts of epoxy resin, 2 parts of chitosan quaternary ammonium salt, 1.5 parts of octadecyldimethylamine, 4.4 parts of paraffin, cover
De- 3 parts of soil, 6 parts of titanium white, 8 parts of alginate fibre, 2.5 parts of neopelex；
It is beaten after cellulose, hemicellulose, lignin, neopelex are mixed, adds wooden polyurethane, ring
Oxygen tree fat, chitosan quaternary ammonium salt, octadecyldimethylamine, paraffin, montmorillonite, titanium white, alginate fibre are scattered using beating crusher
Processing, then be put into ultrasonic disperse instrument and carry out ultrasonic disperse, obtain mixed slurry；By mixed slurry with being manufactured paper with pulp with oblique net paper machine,
Drying, obtains color ink jet printer paper.
Embodiment 2
Color ink jet printer paper is counted including following material by weight：23 parts of cellulose, 25 parts of hemicellulose, lignin
10 parts, 7 parts of polyurethane, 2.5 parts of epoxy resin, 2.2 parts of chitosan quaternary ammonium salt, 1 part of octadecyldimethylamine, 5.6 parts of paraffin,
4 parts of montmorillonite, indigo-blue 7 parts, 7 parts of alginate fibre, 2 parts of triethanolamine soap；
It is beaten after cellulose, hemicellulose, lignin, triethanolamine soap are mixed, adds wooden polyurethane, asphalt mixtures modified by epoxy resin
Fat, chitosan quaternary ammonium salt, octadecyldimethylamine, paraffin, montmorillonite, indigo-blue, alginate fibre use beating crusher decentralized processing,
It is put into again in ultrasonic disperse instrument and carries out ultrasonic disperse, obtains mixed slurry；By mixed slurry with being manufactured paper with pulp, dried with oblique net paper machine,
Obtain color ink jet printer paper.
Embodiment 3
Color ink jet printer paper is counted including following material by weight：26 parts of cellulose, 21 parts of hemicellulose, lignin
16 parts, 9 parts of polyurethane, 4.5 parts of epoxy resin, 2.4 parts of chitosan quaternary ammonium salt, 2.5 parts of octadecyldimethylamine, Tissuemat E
5.2 parts, 6 parts of montmorillonite, 4.5 parts of gamboge, 11 parts of CUP, 3 parts of neopelex；
It is beaten after cellulose, hemicellulose, lignin, neopelex are mixed, adds wooden polyurethane, ring
Oxygen tree fat, chitosan quaternary ammonium salt, octadecyldimethylamine, Tissuemat E, montmorillonite, gamboge, CUP use beating crusher
Decentralized processing, then be put into ultrasonic disperse instrument and carry out ultrasonic disperse, obtain mixed slurry；Mixed slurry is copied with oblique net paper machine
Make, dry, obtain color ink jet printer paper.
Embodiment 4
Color ink jet printer paper is counted including following material by weight：20 parts of cellulose, 23 parts of hemicellulose, lignin
18 parts, 5 parts of polyurethane, 2 parts of epoxy resin, 2.6 parts of chitosan quaternary ammonium salt, 4 parts of octadecyldimethylamine, 6 parts of beeswax, cover de-
7 parts of soil, 5.5 parts of peacock green, 10 parts of CUP, 4 parts of triethanolamine soap；
It is beaten after cellulose, hemicellulose, lignin, triethanolamine soap are mixed, adds wooden polyurethane, asphalt mixtures modified by epoxy resin
Fat, chitosan quaternary ammonium salt, octadecyldimethylamine, beeswax, montmorillonite, peacock green, CUP use the scattered place of beating crusher
Reason, then be put into ultrasonic disperse instrument and carry out ultrasonic disperse, obtain mixed slurry；By mixed slurry with being manufactured paper with pulp, dried with oblique net paper machine
It is dry, obtain color ink jet printer paper.
Embodiment 5
Color ink jet printer paper is counted including following material by weight：30 parts of cellulose, 15 parts of hemicellulose, lignin
20 parts, 6 parts of polyurethane, 5 parts of epoxy resin, 2.8 parts of chitosan quaternary ammonium salt, 3.5 parts of octadecyldimethylamine, 4 parts of vegetable wax,
5 parts of montmorillonite, 3 parts of realgar, 12 parts of nitric acid ester fiber, 4.5 parts of neopelex；
It is beaten after cellulose, hemicellulose, lignin, neopelex are mixed, adds wooden polyurethane, ring
Oxygen tree fat, chitosan quaternary ammonium salt, octadecyldimethylamine, vegetable wax, montmorillonite, realgar, nitric acid ester fiber use beating crusher
Decentralized processing, then be put into ultrasonic disperse instrument and carry out ultrasonic disperse, obtain mixed slurry；Mixed slurry is copied with oblique net paper machine
Make, dry, obtain color ink jet printer paper.
Embodiment 6
Color ink jet printer paper is counted including following material by weight：27 parts of cellulose, 15 parts of hemicellulose, lignin
14 parts, 10 parts of polyurethane, 4 parts of epoxy resin, 3 parts of chitosan quaternary ammonium salt, 3 parts of octadecyldimethylamine, 4.8 parts of vegetable wax,
2 parts of montmorillonite, 4 parts of laterite, 9 parts of nitric acid ester fiber, 5 parts of triethanolamine soap；
It is beaten after cellulose, hemicellulose, lignin, triethanolamine soap are mixed, adds wooden polyurethane, asphalt mixtures modified by epoxy resin
Fat, chitosan quaternary ammonium salt, octadecyldimethylamine, vegetable wax, montmorillonite, laterite, nitric acid ester fiber are scattered using beating crusher
Processing, then be put into ultrasonic disperse instrument and carry out ultrasonic disperse, obtain mixed slurry；By mixed slurry with being manufactured paper with pulp with oblique net paper machine,
Drying, obtains color ink jet printer paper.
Embodiment 7
Color ink jet printer paper is counted including following material by weight：25 parts of cellulose, 20 parts of hemicellulose, lignin
15 parts, 7.5 parts of polyurethane, 3.5 parts of epoxy resin, 2.5 parts of chitosan quaternary ammonium salt, 2.5 parts of octadecyldimethylamine, polyethylene
5 parts of wax, 4.5 parts of montmorillonite, 5 parts of cinnabar, 9.5 parts of soybean fiber, 3.5 parts of neopelex；
It is beaten after cellulose, hemicellulose, lignin, neopelex are mixed, adds wooden polyurethane, ring
Oxygen tree fat, chitosan quaternary ammonium salt, octadecyldimethylamine, Tissuemat E, montmorillonite, cinnabar, soybean fiber are used and beaten
Broken machine decentralized processing, then be put into ultrasonic disperse instrument and carry out ultrasonic disperse, obtain mixed slurry；By mixed slurry inclined wire paper
Machine is manufactured paper with pulp, dried, and obtains color ink jet printer paper.
Absorbency, folding strength, expansion and contraction, opacity are carried out to the obtained writing copy paper of embodiment 1~7 to survey
Examination, the results are shown in Table 1.
The test result of the embodiment 1~7 of table 1
The foregoing description of the disclosed embodiments, enables professional and technical personnel in the field to realize or public to institute using this
The described above for the embodiment opened, enables professional and technical personnel in the field to realize or using the present invention.To these embodiments
A variety of modifications will be apparent for those skilled in the art, and generic principles defined herein can be
In the case of not departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention is not intended to be limited to
The embodiments shown herein, and it is to fit to the most wide model consistent with novel features with principles disclosed herein
Enclose.
Claims (8)
1. a kind of color ink jet printer paper, it is characterised in that include the raw material of following parts by weight：
2. color ink jet printer paper as claimed in claim 1, it is characterised in that the pigment is cinnabar, carbon black, laterite, hero
Huang, peacock green, gamboge, alizarin red, indigo-blue, titanium white, lithopone, lead chromate yellow or barba hispanica.
3. color ink jet printer paper as claimed in claim 1, it is characterised in that the wax be paraffin, Tissuemat E, beeswax or
Vegetable wax.
4. color ink jet printer paper as claimed in claim 1, it is characterised in that the staple fibre is alginate fibre, cuprammonium
Fiber, nitric acid ester fiber or soybean fiber.
5. color ink jet printer paper as claimed in claim 1, it is characterised in that also including antiseptic, the antiseptic is described
Antiseptic includes N- (4- hydroxy 3-methoxybenzene methyls) acrylamides and chitin.
6. color ink jet printer paper as claimed in claim 1, it is characterised in that the surfactant is detergent alkylate sulphur
Sour sodium or triethanolamine soap.
7. color ink jet printer paper as claimed in claim 1, it is characterised in that also including antistatic additive, the antistatic additive
For dodecyldimethylammonium hydroxide inner salt or AEO.
8. a kind of preparation method of color ink jet printer paper as claimed in claim 1, it is characterised in that comprise the following steps：
It is beaten after cellulose, hemicellulose, lignin, surfactant are mixed, adds wooden polyurethane, epoxy resin, shell
Glycan quaternary ammonium salt, octadecyldimethylamine, wax, montmorillonite, pigment, staple fibre use beating crusher decentralized processing, then are put into
Ultrasonic disperse is carried out in ultrasonic disperse instrument, mixed slurry is obtained；By mixed slurry with being manufactured paper with pulp, being dried with oblique net paper machine, coloured silk is obtained
Color Alhue paper.