CN106283842A - A kind of moisture absorption paper and preparation method thereof - Google Patents

A kind of moisture absorption paper and preparation method thereof Download PDF

Info

Publication number
CN106283842A
CN106283842A CN201610762218.XA CN201610762218A CN106283842A CN 106283842 A CN106283842 A CN 106283842A CN 201610762218 A CN201610762218 A CN 201610762218A CN 106283842 A CN106283842 A CN 106283842A
Authority
CN
China
Prior art keywords
parts
moisture absorption
paper
absorption paper
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610762218.XA
Other languages
Chinese (zh)
Inventor
楼旭军
冯沾善
冯小义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yiwu Yinan Paper Co Ltd
Original Assignee
Yiwu Yinan Paper Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yiwu Yinan Paper Co Ltd filed Critical Yiwu Yinan Paper Co Ltd
Priority to CN201610762218.XA priority Critical patent/CN106283842A/en
Publication of CN106283842A publication Critical patent/CN106283842A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of moisture absorption paper and preparation method thereof, this moisture absorption paper is made up of following weight composition: meldable fibre 16 55 parts, polyvinyl binding agent 27 parts, reed pulp 33 44 parts, softwood pulp 33 50 parts, Pulvis Talci 3 10 parts, cross-linking agent 13 parts, deionized water 0.1 2 parts, chlorhexidine acetate 13 parts, reinforcing agent 17 parts, dispersion machine 0.7 3 parts and defoamer 2 4.7 parts.The moisture absorption of the present invention made of paper standby time with the addition of reinforcing agent, improve the tensile strength of paper；In preparation process, with the addition of chlorhexidine acetate simultaneously, improve wettability power, make paper more soft comfortable；Use meldable fibre, polyvinyl binding agent, reed pulp and defoamer mixing manufacture, effectively raise smoothness, also make paper be difficult to hair simultaneously.

Description

A kind of moisture absorption paper and preparation method thereof
Technical field
The present invention relates to a kind of moisture absorption paper and preparation method thereof.
Background technology
At present, moisture absorption paper has mostly been used to replace cotton swab to draw liquid and to dip medicine, because inhaling within the hospital The liquid absorption of tide paper is big, capture velocity block.But it is little mostly to there is tensile strength in existing moisture absorption paper, and pliability is poor, smoothness Low, and easily fall hair, the shortcoming that production cost is high simultaneously.
Summary of the invention
The technical problem to be solved is to provide a kind of tensile strength greatly, and pliability is good, and smoothness is high, is difficult to Hair, the moisture absorption paper that production cost is low.
For solving the problems referred to above, the present invention is achieved through the following technical solutions: a kind of moisture absorption paper, this moisture absorption paper is It is made up of following weight composition: meldable fibre 16-55 part, polyvinyl binding agent 2-7 part, reed pulp 33-44 part, softwood pulp 33-50 part, Pulvis Talci 3-10 part, cross-linking agent 1-3 part, deionized water 0.1-2 part, chlorhexidine acetate 1-3 part, reinforcing agent 1-7 part, Dispersion machine 0.7-3 part and defoamer 2-4.7 part.
Another technical problem to be solved by this invention is to provide the preparation method of a kind of moisture absorption paper,
The present invention is achieved through the following technical solutions: the preparation process of described moisture absorption paper is as follows:
1) meldable fibre 16-55 part, polyvinyl binding agent 2-7 part, reed pulp 33-44 part and needlebush are extracted by weight ratio Slurry 33-50 part mix homogeneously adds beater；
2) in the beater of step 1, Pulvis Talci 3-10 part and cross-linking agent 1-3 part are added, making beating dispersion 10-20 minute；
3) deionized water 0.1-2 part, chlorhexidine acetate 1-3 part, reinforcing agent 1-7 part, dispersion are gone in extraction by weight ratio Machine 0.7-3 part and defoamer 2-4.7 part are mixed into solvent；
4) mixed solvent of extraction step 3 and the slurry uniform stirring of step 2；
5) the slurry molding on net paper machine that will obtain in step 4；
6) slurry of molding in step 5 is placed on the drying in oven that temperature is 60 DEG C-70 DEG C and is moisture absorption paper.
Moisture absorption paper of the present invention provides the benefit that: the described moisture absorption made of paper standby time with the addition of reinforcing agent, improve the anti-of paper Zhang Qiangdu；In preparation process, with the addition of chlorhexidine acetate simultaneously, improve wettability power, make paper more soft comfortable；Use Meldable fibre, polyvinyl binding agent, reed pulp and defoamer mixing manufacture, effectively raise smoothness, also makes paper be difficult to simultaneously Fall hair.
Detailed description of the invention
Following example are used for illustrating the present invention, but are not limited to the scope of the present invention.
Embodiment 1
A kind of moisture absorption paper of the present invention, this moisture absorption paper is made up of following weight composition: meldable fibre 16 parts, dimension Synthetic fibre binding agent 2 parts, reed pulp 33 parts, softwood pulp 33 parts, Pulvis Talci 3 parts, cross-linking agent 1 part, deionized water 0.1 part, acetic acid is washed must Safe 1 part, reinforcing agent 1 part, dispersion machine 0.7 part and defoamer 2 parts.
The preparation process of described moisture absorption paper is as follows:
1) extract meldable fibre 16 parts, polyvinyl binding agent 2 parts, reed pulp 33 parts and softwood pulp 33 parts by weight ratio to mix Conjunction is uniformly added into beater；
2) in the beater of step 1, Pulvis Talci 3 parts and cross-linking agent 1 part are added, making beating dispersion 10-20 minute；
3) deionized water 0.1 part, chlorhexidine acetate 1 part, reinforcing agent 1 part, dispersion machine 0.7 part are removed in extraction by weight ratio It is mixed into solvent with defoamer 2 parts；
4) mixed solvent of extraction step 3 and the slurry uniform stirring of step 2；
5) the slurry molding on net paper machine that will obtain in step 4；
6) slurry of molding in step 5 is placed on the drying in oven that temperature is 60 DEG C-70 DEG C and is moisture absorption paper.
Embodiment 2
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 55 Part, polyvinyl binding agent 7 parts, reed pulp 44 parts, softwood pulp 50 parts, Pulvis Talci 10 parts, cross-linking agent 3 parts, deionized water 2 parts, acetic acid Hibitane 3 parts, reinforcing agent 7 parts, dispersion machine 3 parts and defoamer 4.7 parts.
Embodiment 3
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 45 Part, polyvinyl binding agent 5 parts, reed pulp 38 parts, softwood pulp 45 parts, Pulvis Talci 6 parts, cross-linking agent 2 parts, deionized water 1 part, acetic acid are washed Must safe 2 parts, reinforcing agent 4 parts, dispersion machine 2 parts and defoamer 3 parts.
Embodiment 4
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 19 Part, polyvinyl binding agent 3 parts, reed pulp 36 parts, softwood pulp 35 parts, Pulvis Talci 4 parts, cross-linking agent 1.4 parts, deionized water 0.6 part, vinegar Acid hibitane 1.2 parts, reinforcing agent 2 parts, dispersion machine 0.9 part and defoamer 2.7 parts.
Embodiment 5
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 51 Part, polyvinyl binding agent 6 parts, reed pulp 41 parts, softwood pulp 44 parts, Pulvis Talci 8 parts, cross-linking agent 2.6 parts, deionized water 1.7 parts, vinegar Acid hibitane 2.3 parts, reinforcing agent 6 parts, dispersion machine 2.2 parts and defoamer 4.2 parts.
Embodiment 6
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 44 Part, polyvinyl binding agent 3.4 parts, reed pulp 40 parts, softwood pulp 36 parts, Pulvis Talci 5 parts, cross-linking agent 1.9 parts, deionized water 0.8 part, Chlorhexidine acetate 1.4 parts, reinforcing agent 3 parts, dispersion machine 1.3 parts and defoamer 3.3 parts.
Embodiment 7
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 27 Part, polyvinyl binding agent 3.5 parts, reed pulp 35 parts, softwood pulp 47 parts, Pulvis Talci 8.8 parts, cross-linking agent 1.8 parts, deionized water 1.3 Part, chlorhexidine acetate 2 parts, reinforcing agent 3.7 parts, dispersion machine 2.1 parts and defoamer 3.9 parts.
Embodiment 8
Its difference from Example 1 is, this moisture absorption paper is made up of following weight composition: meldable fibre 30 Part, polyvinyl binding agent 5 parts, reed pulp 40 parts, softwood pulp 35 parts, Pulvis Talci 5 parts, cross-linking agent 2 parts, deionized water 1.5 parts, acetic acid Hibitane 2 parts, reinforcing agent 5 parts, dispersion machine 1.5 parts and defoamer 2.5 parts.
The present invention is not limited to above-mentioned preferred forms, anyone draw under the enlightenment of the present invention other any with Product as the present invention is same or like, within all falling within protection scope of the present invention.

Claims (2)

1. a moisture absorption paper, it is characterised in that: this moisture absorption paper is made up of following weight composition: meldable fibre 16-55 Part, polyvinyl binding agent 2-7 part, reed pulp 33-44 part, softwood pulp 33-50 part, Pulvis Talci 3-10 part, cross-linking agent 1-3 part, go from Sub-water 0.1-2 part, chlorhexidine acetate 1-3 part, reinforcing agent 1-7 part, dispersion machine 0.7-3 part and defoamer 2-4.7 part.
2. the preparation method of the moisture absorption paper that one kind is prepared described in claim 1, it is characterised in that: the method comprises the following steps:
1) meldable fibre 16-55 part, polyvinyl binding agent 2-7 part, reed pulp 33-44 part and softwood pulp are extracted by weight ratio 33-50 part mix homogeneously adds beater；
2) in the beater of step 1, Pulvis Talci 3-10 part and cross-linking agent 1-3 part are added, making beating dispersion 10-20 minute；
3) deionized water 0.1-2 part, chlorhexidine acetate 1-3 part, reinforcing agent 1-7 part, dispersion machine are removed in extraction by weight ratio 0.7-3 part and defoamer 2-4.7 part are mixed into solvent；
4) mixed solvent of extraction step 3 and the slurry uniform stirring of step 2；
5) the slurry molding on net paper machine that will obtain in step 4；
6) slurry of molding in step 5 is placed on the drying in oven that temperature is 60 DEG C-70 DEG C and is moisture absorption paper.
CN201610762218.XA 2016-08-30 2016-08-30 A kind of moisture absorption paper and preparation method thereof Pending CN106283842A (en)