CN105714476A - 一种防紫外线聚丙烯纺粘无纺布及其制备方法 - Google Patents
一种防紫外线聚丙烯纺粘无纺布及其制备方法 Download PDFInfo
- Publication number
- CN105714476A CN105714476A CN201510595813.4A CN201510595813A CN105714476A CN 105714476 A CN105714476 A CN 105714476A CN 201510595813 A CN201510595813 A CN 201510595813A CN 105714476 A CN105714476 A CN 105714476A
- Authority
- CN
- China
- Prior art keywords
- ultraviolet
- woven fabrics
- coupling agent
- antioxidant
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防紫外线聚丙烯纺粘无纺布及其制备方法，防紫外线聚丙烯纺粘无纺布由以下重量比的成分组成：聚丙烯100份、紫外线吸收剂0.2-1.5份、偶联剂0.3-0.8份、抗氧剂0.3-1.0份、硬脂酸锌0.3-1.5份。防紫外线聚丙烯纺粘无纺布的制备方法包括以下步骤：将PP、紫外线吸收剂、偶联剂、抗氧剂、硬脂酸锌按比例进行混合、搅拌，得到混合均匀的颗粒状产品，将颗粒状产品经熔融挤出，制得无纺布成品。本发明的制成的无纺布成品添加了紫外线吸收剂，除了具备聚丙烯纺粘无纺布的优异性能，还具有良好的吸收紫外线效果。
Description
技术领域
本发明涉及一种防紫外线聚丙烯纺粘无纺布及其制备方法，属于无纺布材料技术领域。
背景技术
紫外线(ultravioletrays简称UV)分为长波紫外线(UV-A，320～400nm)、中波紫外线(UV-B，280～320nm)和短波紫外线(UV-C,200～280nm)。紫外线在日光中约占6%，其中UV-A的比例较大，UV-B比例较小，UV-B的作用是UV-A的1000倍。一般地讲，UV-C波长较短，在空气中已被吸收，不能达到地球表面，但由于近年来空气中含氟量的提高，到达地面的紫外线B和C也随之增加。纺织品紫外线吸收整理的原理是在纤维、纱线或织物上添加紫外线吸收剂，这类物质能吸收紫外线，并将其转换为低能量的热能或波长较短的电磁波，从而达到防紫外线辐射的目的。
本发明提供了一种防紫外线聚丙烯纺粘无纺布及其制备方法，本发明的制成的无纺布成品添加了紫外线吸收剂，除了具备聚丙烯纺粘无纺布的优异性能，还具有良好的吸收紫外线效果，因此本发明的是很有必要的。
发明内容
本发明目的是补充现有技术，而提供一种防紫外线聚丙烯纺粘无纺布及其制备方法。
为了实现上述目的，本发明的技术方案如下：
一种防紫外线聚丙烯纺粘无纺布及其制备方法，其特征在于，以重量份数计，由以下重量比的成分组成：聚丙烯100份、紫外线吸收剂0.2-1.5份、偶联剂0.3-0.8份、抗氧剂0.3-1.0份、硬脂酸锌0.3-1.5份。
所述PP为熔融指数为24-40的纤维级PP。
所述紫外线吸收剂为二苯甲酮类化合物。
所述偶联剂为钛酸酯类偶联剂或者铝酸酯类偶联剂。
所述抗氧剂为抗氧剂1010。
一种防紫外线聚丙烯纺粘无纺布的制备方法，包括以下步骤：将PP、紫外线吸收剂、偶联剂、抗氧剂、硬脂酸锌按比例进行混合、搅拌，得到混合均匀的颗粒状产品，将颗粒状产品经熔融挤出，制得无纺布成品。
本发明的有益效果如下：
本发明的制成的无纺布成品添加了紫外线吸收剂，除了具备聚丙烯纺粘无纺布的优异性能，还具有良好的吸收紫外线效果。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1：
一种防紫外线聚丙烯纺粘无纺布及其制备方法，其特征在于，以重量份数计，由以下重量比的成分组成：聚丙烯100份、紫外线吸收剂0.5份、偶联剂0.4份、抗氧剂0.6份、硬脂酸锌1.0份。
所述PP为熔融指数为24-40的纤维级PP。
所述紫外线吸收剂为二苯甲酮类化合物。
所述偶联剂为钛酸酯类偶联剂。
所述抗氧剂为抗氧剂1010。
一种防紫外线聚丙烯纺粘无纺布的制备方法，包括以下步骤：将PP、紫外线吸收剂、偶联剂、抗氧剂、硬脂酸锌按比例进行混合、充分搅拌至均匀，得到混合均匀的颗粒状产品，将颗粒状产品经熔融挤出，制得无纺布成品。
本发明的制成的无纺布成品添加了紫外线吸收剂，除了具备聚丙烯纺粘无纺布的优异性能，还具有良好的吸收紫外线效果。
实施例2：
一种防紫外线聚丙烯纺粘无纺布及其制备方法，其特征在于，以重量份数计，由以下重量比的成分组成：聚丙烯100份、紫外线吸收剂0.7份、偶联剂0.5份、抗氧剂0.6份、硬脂酸锌1.0份。
所述PP为熔融指数为24-40的纤维级PP。
所述紫外线吸收剂为二苯甲酮类化合物。
所述偶联剂为铝酸酯类偶联剂。
所述抗氧剂为抗氧剂1010。
一种防紫外线聚丙烯纺粘无纺布的制备方法，包括以下步骤：将PP、紫外线吸收剂、偶联剂、抗氧剂、硬脂酸锌按比例进行混合、充分搅拌至均匀，得到混合均匀的颗粒状产品，将颗粒状产品经熔融挤出，制得无纺布成品。
本发明的制成的无纺布成品添加了紫外线吸收剂，除了具备聚丙烯纺粘无纺布的优异性能，还具有良好的吸收紫外线效果。
实施例3：
一种防紫外线聚丙烯纺粘无纺布及其制备方法，其特征在于，以重量份数计，由以下重量比的成分组成：聚丙烯100份、紫外线吸收剂0.8份、偶联剂0.6份、抗氧剂0.6份、硬脂酸锌0.8份。
所述PP为熔融指数为24-40的纤维级PP。
所述紫外线吸收剂为二苯甲酮类化合物。
所述偶联剂为铝酸酯类偶联剂。
所述抗氧剂为抗氧剂1010。
一种防紫外线聚丙烯纺粘无纺布的制备方法，包括以下步骤：将PP、紫外线吸收剂、偶联剂、抗氧剂、硬脂酸锌按比例进行混合、充分搅拌至均匀，得到混合均匀的颗粒状产品，将颗粒状产品经熔融挤出，制得无纺布成品。
本发明的制成的无纺布成品添加了紫外线吸收剂，除了具备聚丙烯纺粘无纺布的优异性能，还具有良好的吸收紫外线效果。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种防紫外线聚丙烯纺粘无纺布及其制备方法，其特征在于，以重量份数计，由以下重量比的成分组成：聚丙烯100份、紫外线吸收剂0.2-1.5份、偶联剂0.3-0.8份、抗氧剂0.3-1.0份、硬脂酸锌0.3-1.5份。
2.根据权利要求1所述的防紫外线聚丙烯纺粘无纺布，其特征在于，所述PP为熔融指数为24-40的纤维级PP。
3.根据权利要求1所述的防紫外线聚丙烯纺粘无纺布，其特征在于，所述紫外线吸收剂为二苯甲酮类化合物。
4.根据权利要求1所述的防紫外线聚丙烯纺粘无纺布，其特征在于，所述偶联剂为钛酸酯类偶联剂或者铝酸酯类偶联剂，具有非常好的水解稳定性。
5.根据权利要求1所述的防紫外线聚丙烯纺粘无纺布，其特征在于，所述抗氧剂为抗氧剂1010。
6.根据权利要求1所述的防紫外线聚丙烯纺粘无纺布的制备方法，其特征在于，包括以下步骤：将PP、紫外线吸收剂、偶联剂、抗氧剂、硬脂酸锌按比例进行混合、搅拌，得到混合均匀的颗粒状产品，将颗粒状产品经熔融挤出，制得无纺布成品。