CN105713493A - 一种改性耐高温防腐防锈油漆 - Google Patents
一种改性耐高温防腐防锈油漆 Download PDFInfo
- Publication number
- CN105713493A CN105713493A CN201610182813.6A CN201610182813A CN105713493A CN 105713493 A CN105713493 A CN 105713493A CN 201610182813 A CN201610182813 A CN 201610182813A CN 105713493 A CN105713493 A CN 105713493A
- Authority
- CN
- China
- Prior art keywords
- parts
- modified
- high temperature
- resin
- alkyd resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种改性耐高温防腐防锈油漆，其原料包括改性醇酸树脂、二丁基二月桂酸锡、苯酐聚酯多元醇、过氧化苯甲酰、硅丙乳液、环氧树脂、二甲苯树脂、改性海泡石粉、硫酸钡、碳化硅、有机膨润土、石墨、云母粉、二甲苯、云母氧化铁、磷酸锌、纳米氧化铝、三聚磷酸铝、氯化石蜡、氯甲基苯乙烯、亚磷酸三苯酯磷酸盐和分散剂。本发明油漆具有优异的耐高温防腐防锈性能。
Description
技术领域
本发明涉及油漆领域，尤其涉及一种改性耐高温防腐防锈油漆。
背景技术
油漆是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的油漆的粉刷好以后不仅会传出一股刺鼻的味道，而且在一定的时间能不容易干，而且在粘性很差，粉刷在金属上，会与金属发生反应使金属氧化生锈。
现有技术中的油漆的耐高温防腐防锈性能无法满足实际生产中的需求，因此亟需发明一种具有优异耐高温防腐防锈性能的油漆。
发明内容
为解决背景技术中存在的技术问题，本发明提出一种改性耐高温防腐防锈油漆，具有优异的耐高温、防腐防锈性能。
9+本发明提出的一种改性耐高温防腐防锈油漆，其原料按重量份包括：改性醇酸树脂80-120份、二丁基二月桂酸锡10-50份、苯酐聚酯多元醇5-15份、过氧化苯甲酰2-8份、硅丙乳液3-9份、环氧树脂1-5份、二甲苯树脂2-6份、改性海泡石粉3-9份、硫酸钡4-12份、碳化硅2-8份、有机膨润土1-5份、石墨2-6份、云母粉1-4份、二甲苯3-6份、云母氧化铁1-4份、磷酸锌2-5份、纳米氧化铝3-6份、三聚磷酸铝1-5份、氯化石蜡2-8份、氯甲基苯乙烯3-9份、亚磷酸三苯酯磷酸盐1-4份、分散剂5-15份。
优选地，改性醇酸树脂的原料按重量份包括：醇酸树脂6-18份、纳米二氧化硅2-8份、乙酸正丁酯3-5份、丙二醇甲醚醋酸酯1-4份、钛酸酯偶联剂TMC-TTS1-4份。
优选地，改性醇酸树脂按如下工艺进行制备：将纳米二氧化硅、乙酸正丁酯和丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散20-40min，然后加入钛酸酯偶联剂TMC-TTS，升温至70-90℃，保温0.5-1.5h，冷却至室温后研磨40-60min得到0.05-0.1mm的物料a；将醇酸树脂和物料a混合均匀，然后放入高速分散机中分散20-30min，接着通过砂磨机进行砂磨40-50min，得到15-25μm的改性聚氨酯。
优选地，改性醇酸树脂、二丁基二月桂酸锡、苯酐聚酯多元醇、过氧化苯甲酰、硅丙乳液、环氧树脂和二甲苯树脂的重量比为85-115：15-45：8-12：3-7：4-8：2-4：3-5。
优选地，硅丙乳液、环氧树脂、二甲苯树脂、醇酸树脂、纳米二氧化硅、乙酸正丁酯、丙二醇甲醚醋酸酯和钛酸酯偶联剂TMC-TTS的重量比为4-8：2-4：3-5：7-17：3-7：3.5-4.5：2-3：2-3。
优选地，改性醇酸树脂、改性海泡石粉、硫酸钡、碳化硅、有机膨润土、石墨、云母粉、二甲苯、云母氧化铁、磷酸锌、纳米氧化铝和三聚磷酸铝的重量比为85-115：4-8：6-10：3-7：2-4：3-5：2-3：4-5：2-3：3-4：4-5：2-4。
优选地，其原料按重量份包括：改性醇酸树脂85-115份、二丁基二月桂酸锡15-45份、苯酐聚酯多元醇8-12份、过氧化苯甲酰3-7份、硅丙乳液4-8份、环氧树脂2-4份、二甲苯树脂3-5份、改性海泡石粉4-8份、硫酸钡6-10份、碳化硅3-7份、有机膨润土2-4份、石墨3-5份、云母粉2-3份、二甲苯4-5份、云母氧化铁2-3份、磷酸锌3-4份、纳米氧化铝4-5份、三聚磷酸铝2-4份、氯化石蜡3-7份、氯甲基苯乙烯4-8份、亚磷酸三苯酯磷酸盐2-3份、分散剂8-12份。
优选地，其原料按重量份包括：改性醇酸树脂100份、二丁基二月桂酸锡30份、苯酐聚酯多元醇10份、过氧化苯甲酰5份、硅丙乳液6份、环氧树脂3份、二甲苯树脂4份、改性海泡石粉6份、硫酸钡8份、碳化硅5份、有机膨润土3份、石墨4份、云母粉2.5份、二甲苯4.5份、云母氧化铁2.5份、磷酸锌3.5份、纳米氧化铝4.5份、三聚磷酸铝3份、氯化石蜡5份、氯甲基苯乙烯6份、亚磷酸三苯酯磷酸盐2.5份、分散剂10份。
本发明的一种改性耐高温防腐防锈油漆，其原料包括改性醇酸树脂、二丁基二月桂酸锡、苯酐聚酯多元醇、过氧化苯甲酰、硅丙乳液、环氧树脂、二甲苯树脂、改性海泡石粉、硫酸钡、碳化硅、有机膨润土、石墨、云母粉、二甲苯、云母氧化铁、磷酸锌、纳米氧化铝、三聚磷酸铝、氯化石蜡、氯甲基苯乙烯、亚磷酸三苯酯磷酸盐和分散剂。其中以改性醇酸树脂为主料，辅助添加二丁基二月桂酸锡、苯酐聚酯多元醇、过氧化苯甲酰、硅丙乳液、环氧树脂和二甲苯树脂，并合理控制其与主料的配比，有效提高了主料的耐高温防腐防锈性能；添加的改性海泡石粉、硫酸钡、碳化硅、有机膨润土、石墨、云母粉、二甲苯、云母氧化铁、磷酸锌、纳米氧化铝和三聚磷酸铝，并控制其与主料的配比，有效提高了主料的耐高温防锈性能，进一步提高了本发明油漆的耐高温防腐防锈性能；添加的氯化石蜡、氯甲基苯乙烯、亚磷酸三苯酯磷酸盐和分散剂作为助剂，有效提高了主料的综合性能；添加的改性酚醛树脂通过纳米二氧化硅和钛酸酯偶联剂TMC-TTS进行改性，有效提高了本发明油漆的耐高温防腐防锈性能。
具体实施方式
下面结合具体实施例对本发明做出详细说明，应当了解，实施例只用于说明本发明，而不是用于对本发明进行限定，任何在本发明基础上所做的修改、等同替换等均在本发明的保护范围内。
实施例1
本发明提出的一种改性耐高温防腐防锈油漆，其原料按重量份包括：改性醇酸树脂100份、二丁基二月桂酸锡30份、苯酐聚酯多元醇10份、过氧化苯甲酰5份、硅丙乳液6份、环氧树脂3份、二甲苯树脂4份、改性海泡石粉6份、硫酸钡8份、碳化硅5份、有机膨润土3份、石墨4份、云母粉2.5份、二甲苯4.5份、云母氧化铁2.5份、磷酸锌3.5份、纳米氧化铝4.5份、三聚磷酸铝3份、氯化石蜡5份、氯甲基苯乙烯6份、亚磷酸三苯酯磷酸盐2.5份、分散剂10份。
改性醇酸树脂按如下工艺进行制备：按重量份将5份纳米二氧化硅、4份乙酸正丁酯和2.5份丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散30min，然后加入2.5份钛酸酯偶联剂TMC-TTS，升温至80℃，保温1.0h，冷却至室温后研磨50min得到0.075mm的物料a；将12份醇酸树脂和物料a混合均匀，然后放入高速分散机中分散25min，接着通过砂磨机进行砂磨45min，得到20μm的改性聚氨酯。
实施例2
本发明提出的一种改性耐高温防腐防锈油漆，其原料按重量份包括：改性醇酸树脂80份、二丁基二月桂酸锡50份、苯酐聚酯多元醇5份、过氧化苯甲酰8份、硅丙乳液3份、环氧树脂5份、二甲苯树脂2份、改性海泡石粉9份、硫酸钡4份、碳化硅8份、有机膨润土1份、石墨6份、云母粉1份、二甲苯6份、云母氧化铁1份、磷酸锌5份、纳米氧化铝3份、三聚磷酸铝5份、氯化石蜡2份、氯甲基苯乙烯9份、亚磷酸三苯酯磷酸盐1份、分散剂15份。
改性醇酸树脂按如下工艺进行制备：按重量份将2份纳米二氧化硅、5份乙酸正丁酯和1份丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散40min，然后加入1份钛酸酯偶联剂TMC-TTS，升温至90℃，保温0.5h，冷却至室温后研磨60min得到0.05mm的物料a；将18份醇酸树脂和物料a混合均匀，然后放入高速分散机中分散20min，接着通过砂磨机进行砂磨50min，得到25μm的改性聚氨酯。
实施例3
本发明提出的一种改性耐高温防腐防锈油漆，其原料按重量份包括：改性醇酸树脂120份、二丁基二月桂酸锡10份、苯酐聚酯多元醇15份、过氧化苯甲酰2份、硅丙乳液9份、环氧树脂1份、二甲苯树脂6份、改性海泡石粉3份、硫酸钡12份、碳化硅2份、有机膨润土5份、石墨2份、云母粉4份、二甲苯3份、云母氧化铁4份、磷酸锌2份、纳米氧化铝6份、三聚磷酸铝1份、氯化石蜡8份、氯甲基苯乙烯3份、亚磷酸三苯酯磷酸盐4份、分散剂5份。
改性醇酸树脂按如下工艺进行制备：按重量份将8份纳米二氧化硅、3份乙酸正丁酯和4份丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散20min，然后加入4份钛酸酯偶联剂TMC-TTS，升温至70℃，保温1.5h，冷却至室温后研磨40min得到0.1mm的物料a；将6份醇酸树脂和物料a混合均匀，然后放入高速分散机中分散30min，接着通过砂磨机进行砂磨40min，得到25μm的改性聚氨酯。
实施例4
本发明提出的一种改性耐高温防腐防锈油漆，其原料按重量份包括：改性醇酸树脂85份、二丁基二月桂酸锡45份、苯酐聚酯多元醇8份、过氧化苯甲酰7份、硅丙乳液4份、环氧树脂4份、二甲苯树脂3份、改性海泡石粉8份、硫酸钡6份、碳化硅7份、有机膨润土2份、石墨5份、云母粉2份、二甲苯5份、云母氧化铁2份、磷酸锌4份、纳米氧化铝4份、三聚磷酸铝4份、氯化石蜡3份、氯甲基苯乙烯8份、亚磷酸三苯酯磷酸盐2份、分散剂12份。
改性醇酸树脂按如下工艺进行制备：按重量份将3份纳米二氧化硅、4.5份乙酸正丁酯和2份丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散35min，然后加入2份钛酸酯偶联剂TMC-TTS，升温至85℃，保温0.8h，冷却至室温后研磨55min得到0.06mm的物料a；将16份醇酸树脂和物料a混合均匀，然后放入高速分散机中分散22min，接着通过砂磨机进行砂磨48min，得到18μm的改性聚氨酯。
实施例5
本发明提出的一种改性耐高温防腐防锈油漆，其原料按重量份包括：改性醇酸树脂115份、二丁基二月桂酸锡15份、苯酐聚酯多元醇12份、过氧化苯甲酰3份、硅丙乳液8份、环氧树脂4份、二甲苯树脂3份、改性海泡石粉8份、硫酸钡6份、碳化硅7份、有机膨润土2份、石墨5份、云母粉2份、二甲苯5份、云母氧化铁2份、磷酸锌4份、纳米氧化铝5份、三聚磷酸铝2份、氯化石蜡7份、氯甲基苯乙烯4份、亚磷酸三苯酯磷酸盐3份、分散剂8份。
改性醇酸树脂按如下工艺进行制备：按重量份将7份纳米二氧化硅、3.5份乙酸正丁酯和3份丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散25min，然后加入3份钛酸酯偶联剂TMC-TTS，升温至75℃，保温1.2h，冷却至室温后研磨45min得到0.09mm的物料a；将8份醇酸树脂和物料a混合均匀，然后放入高速分散机中分散28min，接着通过砂磨机进行砂磨42min，得到22μm的改性聚氨酯。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种改性耐高温防腐防锈油漆，其特征在于，其原料按重量份包括：改性醇酸树脂80-120份、二丁基二月桂酸锡10-50份、苯酐聚酯多元醇5-15份、过氧化苯甲酰2-8份、硅丙乳液3-9份、环氧树脂1-5份、二甲苯树脂2-6份、改性海泡石粉3-9份、硫酸钡4-12份、碳化硅2-8份、有机膨润土1-5份、石墨2-6份、云母粉1-4份、二甲苯3-6份、云母氧化铁1-4份、磷酸锌2-5份、纳米氧化铝3-6份、三聚磷酸铝1-5份、氯化石蜡2-8份、氯甲基苯乙烯3-9份、亚磷酸三苯酯磷酸盐1-4份、分散剂5-15份。
2.根据权利要求1所述的改性耐高温防腐防锈油漆，其特征在于，改性醇酸树脂的原料按重量份包括：醇酸树脂6-18份、纳米二氧化硅2-8份、乙酸正丁酯3-5份、丙二醇甲醚醋酸酯1-4份、钛酸酯偶联剂TMC-TTS1-4份。
3.根据权利要求1或2所述的改性耐高温防腐防锈油漆，其特征在于，改性醇酸树脂按如下工艺进行制备：将纳米二氧化硅、乙酸正丁酯和丙二醇甲醚醋酸酯混合均匀，然后放入分散机中分散20-40min，然后加入钛酸酯偶联剂TMC-TTS，升温至70-90℃，保温0.5-1.5h，冷却至室温后研磨40-60min得到0.05-0.1mm的物料a；将醇酸树脂和物料a混合均匀，然后放入高速分散机中分散20-30min，接着通过砂磨机进行砂磨40-50min，得到15-25μm的改性聚氨酯。
4.根据权利要求1-3任一项所述的改性耐高温防腐防锈油漆，其特征在于，改性醇酸树脂、二丁基二月桂酸锡、苯酐聚酯多元醇、过氧化苯甲酰、硅丙乳液、环氧树脂和二甲苯树脂的重量比为85-115：15-45：8-12：3-7：4-8：2-4：3-5。
5.根据权利要求1-4任一项所述的改性耐高温防腐防锈油漆，其特征在于，硅丙乳液、环氧树脂、二甲苯树脂、醇酸树脂、纳米二氧化硅、乙酸正丁酯、丙二醇甲醚醋酸酯和钛酸酯偶联剂TMC-TTS的重量比为4-8：2-4：3-5：7-17：3-7：3.5-4.5：2-3：2-3。
6.根据权利要求1-5任一项所述的改性耐高温防腐防锈油漆，其特征在于，改性醇酸树脂、改性海泡石粉、硫酸钡、碳化硅、有机膨润土、石墨、云母粉、二甲苯、云母氧化铁、磷酸锌、纳米氧化铝和三聚磷酸铝的重量比为85-115：4-8：6-10：3-7：2-4：3-5：2-3：4-5：2-3：3-4：4-5：2-4。
7.根据权利要求1-6任一项所述的改性耐高温防腐防锈油漆，其特征在于，其原料按重量份包括：改性醇酸树脂85-115份、二丁基二月桂酸锡15-45份、苯酐聚酯多元醇8-12份、过氧化苯甲酰3-7份、硅丙乳液4-8份、环氧树脂2-4份、二甲苯树脂3-5份、改性海泡石粉4-8份、硫酸钡6-10份、碳化硅3-7份、有机膨润土2-4份、石墨3-5份、云母粉2-3份、二甲苯4-5份、云母氧化铁2-3份、磷酸锌3-4份、纳米氧化铝4-5份、三聚磷酸铝2-4份、氯化石蜡3-7份、氯甲基苯乙烯4-8份、亚磷酸三苯酯磷酸盐2-3份、分散剂8-12份。
8.根据权利要求1-7任一项所述的改性耐高温防腐防锈油漆，其特征在于，其原料按重量份包括：改性醇酸树脂100份、二丁基二月桂酸锡30份、苯酐聚酯多元醇10份、过氧化苯甲酰5份、硅丙乳液6份、环氧树脂3份、二甲苯树脂4份、改性海泡石粉6份、硫酸钡8份、碳化硅5份、有机膨润土3份、石墨4份、云母粉2.5份、二甲苯4.5份、云母氧化铁2.5份、磷酸锌3.5份、纳米氧化铝4.5份、三聚磷酸铝3份、氯化石蜡5份、氯甲基苯乙烯6份、亚磷酸三苯酯磷酸盐2.5份、分散剂10份。