CN105713268A - Anti-tensile anti-corrosion cable sheath formula and preparing method thereof - Google Patents
Anti-tensile anti-corrosion cable sheath formula and preparing method thereof Download PDFInfo
- Publication number
- CN105713268A CN105713268A CN201610233238.8A CN201610233238A CN105713268A CN 105713268 A CN105713268 A CN 105713268A CN 201610233238 A CN201610233238 A CN 201610233238A CN 105713268 A CN105713268 A CN 105713268A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- raw material
- mixture
- stretch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-tensile anti-corrosion cable sheath formula.The anti-tensile anti-corrosion cable sheath formula comprises, by weight, 6-20 parts of hydrogenated butadiene-acrylonitrile rubber, 2-6 parts of stabilizer, 3-7 parts of plasticizer, 2-6 parts of lubricant, 4-10 parts of nano calcium carbonate powder, 2-8 parts of anti-hydrolysis agent and 3-9 parts of polyethylene glycol.The formula has the advantages that material selection is reasonable, anti-corrosion effect is good, and anti-tensile performance is high.A cable made according to the formula can effectively resist corrosion of strong acid and strong base, and is much longer in service life.
Description
Technical field
The present invention relates to field of cables, particularly relate to a kind of stretch-proof anticorrosion cable cover(ing) formula and preparation method thereof.
Background technology
At present, along with economic develops rapidly, electric wire suffers from being widely applied at industry-by-industry, and electric wire
The most often because of problems such as material selections, during cable makes and uses, it may appear that a lot of problems, it is impossible to
Enough bear higher temperature, inflammable situation occurs, and cable is easy to the feelings that occur being corroded in the environment of strong acid and strong base
Condition, especially in some specific fields, such as Aero-Space, electrical equipment, colliery and oil field, has cable especially
The highest requirement, people are badly in need of solving these problems.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide a kind of stretch-proof anticorrosion cable cover(ing)
Formula and preparation method thereof.
The present invention takes techniques below scheme to realize: a kind of stretch-proof anticorrosion cable cover(ing) formula, by following
Form according to the raw material of weight portion: hydrogenated nitrile-butadiene rubber 6-20 part, stabilizer 2-6 part, plasticizer 3-7 part, lubricant 2-6 part,
Nano-calcium carbonate calcium powder 4-10 part, hydrolysis-resisting agent 2-8 part, Polyethylene Glycol 3-9 part.
Above-mentioned a kind of stretch-proof anticorrosion cable cover(ing) formula, is made up of according to the raw material of weight portion following: hydrogenation fourth
Nitrile rubber 6-18 part, stabilizer 2-4 part, plasticizer 3-5 part, lubricant 2-4 part, nano-calcium carbonate calcium powder 4-8 part, hydrolysis-resisting agent 2-
6 parts, Polyethylene Glycol 3-7 part.
Above-mentioned a kind of stretch-proof anticorrosion cable cover(ing) formula, is made up of according to the raw material of weight portion following: hydrogenation fourth
Nitrile rubber 12 parts, stabilizer 3 parts, plasticizer 4 parts, lubricant 3 parts, nano-calcium carbonate calcium powder 6 parts, hydrolysis-resisting agent 4 parts, Polyethylene Glycol
5 parts.
The preparation method of above-mentioned a kind of stretch-proof anticorrosion cable cover(ing) formula, comprises the steps of:
(1) raw material is weighed according to the weight portion in claim 3, by hydrogenated nitrile-butadiene rubber, stabilizer, plasticizer and nano-calcium carbonate
Calcium powder is put into and is carried out sufficient stir process in batch mixer, makes material mix homogeneously, obtains mixture A；
(2) lubricant, hydrolysis-resisting agent and Polyethylene Glycol are dried at a temperature of 80 DEG C stir process, remove in raw material and contain
Some moisture, and make raw material be sufficiently mixed, obtain mixture B；
(3) mixture A and mixture B is placed in drying device again it is dried process, stirred by agitating device
Mix process, make mixture A and mixture B carry out mixing and pelletize process by screw extruder, obtain finished product C.
The method have the advantages that in sum the present invention have material select rationally, anticorrosion ability good and
The advantages such as stretch-proof performance is good, the cable using this formula to make can effectively be kept out the corrosion of strong acid and strong base, is greatly prolonged
Service life of cable.
Detailed description of the invention
A kind of stretch-proof anticorrosion cable cover(ing) formula, is made up of according to the raw material of weight portion following: hydrogenated nitrile-butadiene rubber
6-20 part, stabilizer 2-6 part, plasticizer 3-7 part, lubricant 2-6 part, nano-calcium carbonate calcium powder 4-10 part, hydrolysis-resisting agent 2-8 part,
Polyethylene Glycol 3-9 part.
Above-mentioned a kind of stretch-proof anticorrosion cable cover(ing) formula, is made up of according to the raw material of weight portion following: hydrogenation fourth
Nitrile rubber 6-18 part, stabilizer 2-4 part, plasticizer 3-5 part, lubricant 2-4 part, nano-calcium carbonate calcium powder 4-8 part, hydrolysis-resisting agent 2-
6 parts, Polyethylene Glycol 3-7 part.
Above-mentioned a kind of stretch-proof anticorrosion cable cover(ing) formula, is made up of according to the raw material of weight portion following: hydrogenation fourth
Nitrile rubber 12 parts, stabilizer 3 parts, plasticizer 4 parts, lubricant 3 parts, nano-calcium carbonate calcium powder 6 parts, hydrolysis-resisting agent 4 parts, Polyethylene Glycol
5 parts.
The preparation method of above-mentioned a kind of stretch-proof anticorrosion cable cover(ing) formula, comprises the steps of:
(1) raw material is weighed according to the weight portion in claim 3, by hydrogenated nitrile-butadiene rubber, stabilizer, plasticizer and nano-calcium carbonate
Calcium powder is put into and is carried out sufficient stir process in batch mixer, makes material mix homogeneously, obtains mixture A；
(2) lubricant, hydrolysis-resisting agent and Polyethylene Glycol are dried at a temperature of 80 DEG C stir process, remove in raw material and contain
Some moisture, and make raw material be sufficiently mixed, obtain mixture B；
(3) mixture A and mixture B is placed in drying device again it is dried process, stirred by agitating device
Mix process, make mixture A and mixture B carry out mixing and pelletize process by screw extruder, obtain finished product C.
The present invention has that material selects rationally, anticorrosion ability is good and the advantage such as stretch-proof performance is good, uses this formula system
The corrosion of strong acid and strong base can effectively be kept out by the cable made, and substantially prolongs the service life of cable.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute
The equivalence change done or modification, in the range of being all included in present patent application.
Claims (4)
1. a stretch-proof anticorrosion cable cover(ing) formula, it is characterised in that be made up of according to the raw material of weight portion following: hydrogenation
Nitrile rubber 6-20 part, stabilizer 2-6 part, plasticizer 3-7 part, lubricant 2-6 part, nano-calcium carbonate calcium powder 4-10 part, resistant to hydrolysis
Agent 2-8 part, Polyethylene Glycol 3-9 part.
A kind of stretch-proof anticorrosion cable cover(ing) formula the most according to claim 1, it is characterised in that by following according to weight
The raw material composition of amount part: hydrogenated nitrile-butadiene rubber 6-18 part, stabilizer 2-4 part, plasticizer 3-5 part, lubricant 2-4 part, nano-sized carbon
Acid calcium powder 4-8 part, hydrolysis-resisting agent 2-6 part, Polyethylene Glycol 3-7 part.
A kind of stretch-proof anticorrosion cable cover(ing) formula the most according to claim 1, it is characterised in that by following according to weight
The raw material composition of amount part: hydrogenated nitrile-butadiene rubber 12 parts, stabilizer 3 parts, plasticizer 4 parts, lubricant 3 parts, nano-calcium carbonate calcium powder 6
Part, hydrolysis-resisting agent 4 parts, Polyethylene Glycol 5 parts.
4. a preparation method for a kind of stretch-proof anticorrosion cable cover(ing) formula as described in claim 1-3, its feature exists
In, comprise the steps of:
(1) raw material is weighed according to the weight portion in claim 3, by hydrogenated nitrile-butadiene rubber, stabilizer, plasticizer and nano-calcium carbonate
Calcium powder is put into and is carried out sufficient stir process in batch mixer, makes material mix homogeneously, obtains mixture A；
(2) lubricant, hydrolysis-resisting agent and Polyethylene Glycol are dried at a temperature of 80 DEG C stir process, remove in raw material and contain
Some moisture, and make raw material be sufficiently mixed, obtain mixture B；
(3) mixture A and mixture B is placed in drying device again it is dried process, stirred by agitating device
Mix process, make mixture A and mixture B carry out mixing and pelletize process by screw extruder, obtain finished product C.