CN105695994A - Nano-ceramic technology for inner wall of stainless steel - Google Patents
Nano-ceramic technology for inner wall of stainless steel Download PDFInfo
- Publication number
- CN105695994A CN105695994A CN201610124873.2A CN201610124873A CN105695994A CN 105695994 A CN105695994 A CN 105695994A CN 201610124873 A CN201610124873 A CN 201610124873A CN 105695994 A CN105695994 A CN 105695994A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel
- nano
- inwall
- wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nano-ceramic technology for the inner wall of stainless steel. The nano-ceramic technology specifically comprises the steps of steel body manufacturing, sand blasting, cleaning, inner wall spraying, drying and curing. The whole manufacturing process of nano ceramic on the inner wall of the stainless steel can be completed through the steps. Stainless steel products made through the technology are high in ability to resist acid and alkalis and can contain acid-alkaline products or food. In addition, because the stainless steel products made through the technology are not liable to oxidation, cleaning of the stainless steel products is convenient, and objects can be contained more healthily.
Description
Technical field
The present invention relates to a kind of stainless steel cup processing technology, specifically a kind of rustless steel inwall Nano ceramic technique。
Background technology
Utilizing the nano ceramic material that nanotechnology is developed is utilize nano-powder that existing pottery is modified, by adding in pottery or generating nano-scale particle, whisker, wafer fiber etc., make crystal grain, crystal boundary and the combination between them all reach nanometer level, make the intensity of material, toughness and superplasticity increase substantially。Which overcome many deficiencies of engineering ceramics, and the performances such as the mechanics of material, electricity, calorifics, magnetooptics are produced material impact, for replacing the application of engineering ceramics to open up frontier。
Stainless steel products has wide range of applications, and particularly in making on water tumbler, has the status that can not be substituted especially, but in actually used process, stainless steel product easily reacts with saline and alkaline, and is easily generated the dirt being difficult to clean, and is therefore not very convenient to use。
Summary of the invention
It is an object of the invention to provide a kind of rustless steel inwall Nano ceramic technique, with the problem solving to propose in above-mentioned background technology。
For achieving the above object, the present invention provides following technical scheme:
A kind of rustless steel inwall Nano ceramic technique, it specifically includes following steps:
1) steel system is made, and is made the bottle of stainless steel cup by metal working process;
2) sandblasting, by material mixing such as quartz, Anhydrite and china clay, and is uniformly sprayed on the inwall of steel body by sandblasting machine;
3) clean, sandblasting position unnecessary in step 2 is carried out;
4) inner-wall spraying, carries out inner-wall spraying to position irregular in step 3;
5) dry, the steel body after carrying out inner-wall spraying in step 4 is dried;
6) solidifying, the steel body after drying is carried out hot setting, its solidification temperature is 800 DEG C-820 DEG C。
As the further scheme of the present invention: the drying temperature in step 5 is 300 DEG C-350 DEG C。
Compared with prior art, the invention has the beneficial effects as follows: the stainless steel product that the present invention makes, entirety has good antiacid alkali ability, entirety can hold soda acid goods and can also hold food, owing to entirety will not produce oxidation, therefore entirety is convenient to clean, and holds article more healthy simultaneously。
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments。Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain under not making creative work premise, broadly fall into the scope of protection of the invention。
In the embodiment of the present invention 1, a kind of rustless steel inwall Nano ceramic technique, it specifically includes following steps:
1) steel system is made, and is made the bottle of stainless steel cup by metal working process;
2) sandblasting, by material mixing such as quartz, Anhydrite and china clay, and is uniformly sprayed on the inwall of steel body by sandblasting machine;
3) clean, sandblasting position unnecessary in step 2 is carried out;
4) inner-wall spraying, carries out inner-wall spraying to position irregular in step 3;
5) dry, the steel body after carrying out inner-wall spraying in step 4 is dried;
6) solidifying, the steel body after drying is carried out hot setting, its solidification temperature is 800 DEG C。
Through above-mentioned steps, can completing the making overall process of rustless steel inwall Nano ceramic, total quality is excellent, appearance looks elegant。
In the embodiment of the present invention 2, a kind of rustless steel inwall Nano ceramic technique, it specifically includes following steps:
7) steel system is made, and is made the bottle of stainless steel cup by metal working process;
8) sandblasting, by material mixing such as quartz, Anhydrite and china clay, and is uniformly sprayed on the inwall of steel body by sandblasting machine;
9) clean, sandblasting position unnecessary in step 2 is carried out;
10) inner-wall spraying, carries out inner-wall spraying to position irregular in step 3;
11) dry, the steel body after carrying out inner-wall spraying in step 4 is dried;
12) solidifying, the steel body after drying is carried out hot setting, its solidification temperature is 810 DEG C。
Through above-mentioned steps, can completing the making overall process of rustless steel inwall Nano ceramic, total quality is excellent, appearance looks elegant。
In the embodiment of the present invention 3, a kind of rustless steel inwall Nano ceramic technique, it specifically includes following steps:
1) steel system is made, and is made the bottle of stainless steel cup by metal working process;
2) sandblasting, by material mixing such as quartz, Anhydrite and china clay, and is uniformly sprayed on the inwall of steel body by sandblasting machine;
3) clean, sandblasting position unnecessary in step 2 is carried out;
4) inner-wall spraying, carries out inner-wall spraying to position irregular in step 3;
5) dry, the steel body after carrying out inner-wall spraying in step 4 is dried;
6) solidifying, the steel body after drying is carried out hot setting, its solidification temperature is 820 DEG C。
Through above-mentioned steps, can completing the making overall process of rustless steel inwall Nano ceramic, total quality is excellent, appearance looks elegant
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when without departing substantially from the spirit of the present invention or basic feature, it is possible to realize the present invention in other specific forms。Therefore, no matter from which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the invention rather than described above limits, it is intended that all changes in the implication of the equivalency dropping on claim and scope included in the present invention。
In addition, it is to be understood that, although this specification is been described by according to embodiment, but not each embodiment only comprises an independent technical scheme, this narrating mode of description is only for clarity sake, description should be made as a whole by those skilled in the art, and the technical scheme in each embodiment through appropriately combined, can also form other embodiments that it will be appreciated by those skilled in the art that。
Claims (2)
1. a rustless steel inwall Nano ceramic technique, it is characterised in that it specifically includes following steps:
1) steel system is made, and is made the bottle of stainless steel cup by metal working process;
2) sandblasting, by material mixing such as quartz, Anhydrite and china clay, and is uniformly sprayed on the inwall of steel body by sandblasting machine;
3) clean, sandblasting position unnecessary in step 2 is carried out;
4) inner-wall spraying, carries out inner-wall spraying to position irregular in step 3;
5) dry, the steel body after carrying out inner-wall spraying in step 4 is dried;
6) solidifying, the steel body after drying is carried out hot setting, its solidification temperature is 800 DEG C-820 DEG C。
2. rustless steel inwall Nano ceramic technique according to claim 1, it is characterised in that the drying temperature in step 5 is 300 DEG C-350 DEG C。