CN105688515A - 一种聚全氟乙丙烯滤网的制备方法 - Google Patents

一种聚全氟乙丙烯滤网的制备方法 Download PDF

Info

Publication number
CN105688515A
CN105688515A CN201610166965.7A CN201610166965A CN105688515A CN 105688515 A CN105688515 A CN 105688515A CN 201610166965 A CN201610166965 A CN 201610166965A CN 105688515 A CN105688515 A CN 105688515A
Authority
CN
China
Prior art keywords
filter screen
propylene
perfluoroethylene
preparation
fluorinated ethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610166965.7A
Other languages
English (en)
Other versions
CN105688515B (zh
Inventor
钟校
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610166965.7A priority Critical patent/CN105688515B/zh
Publication of CN105688515A publication Critical patent/CN105688515A/zh
Application granted granted Critical
Publication of CN105688515B publication Critical patent/CN105688515B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚全氟乙丙烯滤网的制备方法，制备步骤包括熔融、牵引挤出、编织、浸渍、烘干、定型粘合。本发明采用270-372度温度下对聚全氟乙丙烯树脂原料粒子进行5分钟内的高温熔融，使得经牵引挤出织物的线径能达到所需的0.05-0.2mm；通过将滤网粗品经由20%纯净水稀释的聚全氟乙丙烯乳液浸渍，使得由于粘性较小而网孔不被乳液中的颗粒堵住，大大提高了滤网成品的质量，在石油、化工、食品、水处理等领域具有广阔的应用前景。

Description

一种聚全氟乙丙烯滤网的制备方法
技术领域
本发明涉及一种滤网，尤其涉及一种聚全氟乙丙烯滤网的制备方法。
背景技术
聚全氟乙丙烯材料具有一系列优良的使用性能：耐温（负85至200度）、耐强酸强碱、耐恶劣气候，使得其在塑料中具有最佳抗老化寿命；高润滑、不粘性，具有固体材料最小的表面张力而不粘附任何物质；无毒害性，具有生性惰性且阻燃，可广泛地应用于石油、化工、食品、水处理等领域。现有的利用聚全氟乙丙烯材料制备各种滤网制品在制备方法及过程中主要存对如下缺点：一是在聚全氟乙丙烯乳液浸渍滤网粗品工艺过程中，缺少将聚全氟乙丙烯乳液稀释的工艺方法，使得聚全氟乙丙烯乳液浸渍滤网粗品后由于聚全氟乙丙烯乳液粘性太大，聚全氟乙丙烯乳液中的细小颗粒极易堵住滤网粗品的网孔，从而大大影响了制成的滤网成品的质量；二是对熔融温度及熔融时间的控制不够精确，使得经牵引挤出织物的线径达不到所需的要求。
发明内容
本发明解决的技术问题是，克服现有技术的缺陷，提供一种通过由20%纯净水稀释的聚全氟乙丙烯乳液浸渍使得由于粘性较小而网孔不被乳液中的颗粒堵住的聚全氟乙丙烯滤网的制备方法。
为了解决上述技术问题，本发明通过下述技术方案得以解决：
一种聚全氟乙丙烯滤网的制备方法，包括如下制备步骤：
A、熔融：先将聚全氟乙丙烯树脂原料粒子熔融在270-372度；
B、牵引挤出：再将熔融后的聚全氟乙丙烯树脂经牵引挤出织物所需的线径，得到所需的聚全氟乙丙烯纤维丝；
C、编织：又将得到的聚全氟乙丙烯纤维丝经织机编织成滤网粗品；
D、浸渍：先取聚全氟乙丙烯乳液，再往聚全氟乙丙烯乳液中加入20%纯净水将聚全氟乙丙烯乳液稀释，然后将C步骤中得到的滤网粗品浸渍到被20%纯净水稀释后的聚全氟乙丙烯乳液；
E、烘干：再将D步骤中浸渍后的滤网粗品经压辊送入烘箱在270度温度且在1-2秒内进行瞬时烘干；本发明经过实验验证，将烘箱内温度设定在270度对D步骤中浸渍后的滤网粗品经压辊送入烘箱在1-2秒内瞬时烘干，能达到最佳的烘干效果；
F、定型粘合：再将步骤E中烘干后的滤网粗品经特殊的定型设备进行定型使经线与纬线粘合，得到滤网成品。
作为优选，步骤A中的熔融时间为不超过5分钟。
作为优选，步骤B中的线径为0.05-0.2mm。
作为优选，滤网网格数目为20-100目。
本发明由于采用了以上技术方案，具有显著的技术效果：采用270-372度温度下对聚全氟乙丙烯树脂原料粒子进行5分钟内的高温熔融，使得经牵引挤出织物的线径能达到所需的0.05-0.2mm；通过将滤网粗品经由20%纯净水稀释的聚全氟乙丙烯乳液浸渍，使得由于粘性较小而网孔不被乳液中的颗粒堵住，大大提高了滤网成品的质量，在石油、化工、食品、水处理等领域具有广阔的应用前景。
具体实施方式
下面结合实施例对本发明作进一步详细描述。
一种聚全氟乙丙烯滤网的制备方法，包括如下制备步骤：
A、熔融：先将聚全氟乙丙烯树脂原料粒子熔融在270-372度；
B、牵引挤出：再将熔融后的聚全氟乙丙烯树脂经牵引挤出织物所需的线径，得到所需的聚全氟乙丙烯纤维丝；
C、编织：又将得到的聚全氟乙丙烯纤维丝经织机编织成滤网粗品；
D、浸渍：先取聚全氟乙丙烯乳液，再往聚全氟乙丙烯乳液中加入20%纯净水将聚全氟乙丙烯乳液稀释，然后将C步骤中得到的滤网粗品浸渍到被20%纯净水稀释后的聚全氟乙丙烯乳液；
E、烘干：再将D步骤中浸渍后的滤网粗品经压辊送入烘箱在270度温度且在1-2秒内进行瞬时烘干；本发明经过实验验证，将烘箱内温度设定在270度对D步骤中浸渍后的滤网粗品经压辊送入烘箱在1-2秒内瞬时烘干，能达到最佳的烘干效果；
F、定型粘合：再将步骤E中烘干后的滤网粗品经特殊的定型设备进行定型使经线与纬线粘合，得到滤网成品。
其中，步骤A中的熔融时间为不超过5分钟。
其中，步骤B中的线径为0.05-0.2mm。
其中，滤网网格数目为20-100目。
本发明提供的聚全氟乙丙烯滤网的制备方法，采用270-372度温度下对聚全氟乙丙烯树脂原料粒子进行5分钟内的高温熔融，使得经牵引挤出织物的线径能达到所需的0.05-0.2mm；通过将滤网粗品经由20%纯净水稀释的聚全氟乙丙烯乳液浸渍，使得由于粘性较小而网孔不被乳液中的颗粒堵住，大大提高了滤网成品的质量，在石油、化工、食品、水处理等领域具有广阔的应用前景。
总之，以上所述仅为本发明的较佳实施例，凡依本发明申请专利范围所作的均等变化与修饰，皆应属本发明专利的涵盖范围。

Claims (4)

1.一种聚全氟乙丙烯滤网的制备方法，其特征在于：包括如下制备步骤：
A、熔融：先将聚全氟乙丙烯树脂原料粒子熔融在270-372度；
B、牵引挤出：再将熔融后的聚全氟乙丙烯树脂经牵引挤出织物所需的线径，得到所需的聚全氟乙丙烯纤维丝；
C、编织：又将得到的聚全氟乙丙烯纤维丝经织机编织成滤网粗品；
D、浸渍：先取聚全氟乙丙烯乳液，再往聚全氟乙丙烯乳液中加入20%纯净水将聚全氟乙丙烯乳液稀释，然后将C步骤中得到的滤网粗品浸渍到被20%纯净水稀释后的聚全氟乙丙烯乳液；
E、烘干：再将D步骤中浸渍后的滤网粗品经压辊送入烘箱在270度温度且在1-2秒内进行瞬时烘干；
F、定型粘合：再将步骤E中烘干后的滤网粗品经特殊的定型设备进行定型使经线与纬线粘合，得到滤网成品。
2.根据权利要求1所述的一种聚全氟乙丙烯滤网的制备方法，其特征在于：步骤A中的熔融时间为不超过5分钟。
3.根据权利要求1所述的一种聚全氟乙丙烯滤网的制备方法，其特征在于：步骤B中的线径为0.05-0.2mm。
4.根据权利要求1所述的一种聚全氟乙丙烯滤网的制备方法，其特征在于：滤网网格数目为20-100目。
CN201610166965.7A 2016-03-23 2016-03-23 一种聚全氟乙丙烯滤网的制备方法 Expired - Fee Related CN105688515B (zh)