CN105671984A - 一种防反射的气刀涂布式苎麻织物面料 - Google Patents

一种防反射的气刀涂布式苎麻织物面料 Download PDF

Info

Publication number
CN105671984A
CN105671984A CN201610187946.2A CN201610187946A CN105671984A CN 105671984 A CN105671984 A CN 105671984A CN 201610187946 A CN201610187946 A CN 201610187946A CN 105671984 A CN105671984 A CN 105671984A
Authority
CN
China
Prior art keywords
coating
fabric
ramie
hours
air knife
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610187946.2A
Other languages
English (en)
Inventor
陈蓓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGYIN BEIYE TEXTILE Co Ltd
Original Assignee
JIANGYIN BEIYE TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGYIN BEIYE TEXTILE Co Ltd filed Critical JIANGYIN BEIYE TEXTILE Co Ltd
Priority to CN201610187946.2A priority Critical patent/CN105671984A/zh
Publication of CN105671984A publication Critical patent/CN105671984A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种防反射的气刀涂布式苎麻织物面料，是在苎麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、去光剂和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到苎麻基布表面，于80℃环境下烘干0.5小时，于120～135℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。苎麻织物面料表面经涂布材料保护后，织物具有更好的防反射特性，提高了面料的使用品质。

Description

一种防反射的气刀涂布式苎麻织物面料
技术领域
本发明属于苎麻织物面料技术领域，具体涉及一种防反射的气刀涂布苎麻织物面料。
背景技术
苎麻是多年生宿根性草本植物，是重要的纺织纤维作物。也称白叶苎麻。其单纤维长、强度最大，吸湿和散湿快，热传导性能好，脱胶后洁白有丝光，可以纯纺，也可和棉、丝、毛、化纤等混纺，闻名于世的浏阳夏布就是苎麻纤维的手工制品。
在各种麻类纤维中，苎麻纤维最长最细。纤维长度比最高级的棉花还要长两倍到七倍原麻脱胶精制后，纤维外观颜色洁白，有丝样光泽。苎麻纤维构造中的空隙大，透气性好，传热快，吸水多而散湿快，所以穿麻织品具有凉爽感。苎麻纤维强力大而延伸度小。它的强力比棉花大七、八倍。苎麻纤维不容易受霉菌腐蚀和虫蛀，而且轻盈。不断开发苎麻织物面料的新功能是苎麻织物面料发展的趋势。
发明内容
本发明的目的是提供一种防反射的气刀涂布式苎麻织物面料。
本发明解决上述问题所采用的技术方案为：一种防反射的气刀涂布式苎麻织物面料，是在苎麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、去光剂和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到苎麻基布表面，于80℃环境下烘干0.5小时，于120～135℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。
优选地，所述苎麻基布的组织结构采用异面组织，以便于涂层更好的涂布以及面料后期的固化平衡，延长使用寿命。
优选地，异面组织包括选1/2斜纹、1/3斜纹、破斜纹、1/4斜纹或者五枚缎纹组织结构。
与现有技术相比，本发明的优点在于：提供了一种气刀涂布式的防反射苎麻织物面料，经过气刀涂层保护后，使苎麻织物面料具有更好的防反射性能，提高了苎麻织物面料的使用品质。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
实施例1
防反射苎麻织物面料，是在苎麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、去光剂和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至8范围，静置2～4小时，然后采用气刀涂布的方式施加到苎麻基布表面，于80℃环境下烘干0.5小时，于120℃环境下固化1.5小时，最后在自然条件下平衡8小时以上。
本实施例中的苎麻基布的组织结构为1/2斜纹组织结构。
本实施例所得苎麻织物面料具有很好的防反射特性。
实施例2
防反射苎麻织物面料，是在苎麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、去光剂和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5范围，静置2～4小时，然后采用气刀涂布的方式施加到苎麻基布表面，于80℃环境下烘干0.5小时，于130℃环境下固化1小时，最后在自然条件下平衡8小时以上。
本实施例中苎麻基布的组织结构为破斜纹组织结构。
本实施例所得苎麻织物面料具有很好的防反射特性。
实施例3
防反射苎麻织物面料，是在苎麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、去光剂和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到苎麻基布表面，于80℃环境下烘干0.5小时，于120℃环境下固化1小时，最后在自然条件下平衡8小时以上。
本实施例中苎麻基布的组织结构为五枚缎纹组织结构。
本实施例所得苎麻织物面料具有很好的防反射特性。

Claims (3)

1.一种防反射的气刀涂布式苎麻织物面料，其特征在于：是在苎麻基布的外表面采用气刀涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷、去光剂和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用气刀涂布的方式施加到苎麻基布表面，于80℃环境下烘干0.5小时，于120～135℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。
2.根据权利要求1所述的防反射的气刀涂布式苎麻织物面料，其特征在于：所述苎麻基布的组织结构采用异面组织。
3.根据权利要求2所述的防反射的气刀涂布式苎麻织物面料，其特征在于：所述异面组织包括选1/2斜纹、1/3斜纹、破斜纹、1/4斜纹或者五枚缎纹组织结构。
CN201610187946.2A 2016-03-30 2016-03-30 一种防反射的气刀涂布式苎麻织物面料 Pending CN105671984A (zh)