CN105671717A - 绿色环保面料及其起泡工艺 - Google Patents
绿色环保面料及其起泡工艺 Download PDFInfo
- Publication number
- CN105671717A CN105671717A CN201610136888.0A CN201610136888A CN105671717A CN 105671717 A CN105671717 A CN 105671717A CN 201610136888 A CN201610136888 A CN 201610136888A CN 105671717 A CN105671717 A CN 105671717A
- Authority
- CN
- China
- Prior art keywords
- sample
- fabric
- fiber
- wool
- wool fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及绿色环保面料及其起泡工艺,其特征在于:它包括外层面料和衬里面料,所述外层面料与衬里面料之间设有一层SEE生态棉。本发明绿色环保面料及其起泡工艺通过外层面料与衬里面料之间增加SEE生态棉,使用面料具有生物降解、节能改排、环保生态等特点,是一种理想的绿色环保保暖面料。
Description
技术领域
本发明涉及绿色环保面料及其起泡工艺,属于面料技术领域。
背景技术
随着时代的发展进步,有关生态、环保、无公害等绿色概念将越来越深入人心。绿色食品已经受到消费者的青睐,随之具有绿色慨念的面料服饰,必将受到高度关注,开发前景非常广阔,同行业的开发竞争将呈现多方位、多层次。然而目前服装面料的保温性能一般,已经不能满足时代的需求。
发明内容
本发明的目的在于克服上述不足,提供保温效果好的绿色环保面料及其起泡工艺。
本发明的目的是这样实现的:
一种绿色环保面料的工艺为:
1)、纱线品种设计:
选用羊毛纤维、羊绒纤维和海藻炭纤维,所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成,所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为:所述兔毛纤维占18%-22%,所述美丽诺超细羊毛纤维占15%-19%,所述安哥拉山羊毛纤维占26%-30%,所述丝光羊毛纤维占29%-41%,对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳;
3)、纺纱工艺:
采用一般公知的纺纱工艺,依次经过头针—二针—三针—四针—粗纱-存放—细纱—蒸纱—自络筒-并线-倍捻—蒸纱工序,制成用于织造精纺面料的纱线,细纱工序采用紧密纺细纱设备;
4)、织造和修补工艺:
采用一般公知的织造和修补工艺,将纱线织造成坯布,并通过修补使得坯布无纺疵和织疵;
5)、后整理工艺:
坯布经过烧毛—平幅洗呢—煮呢—烘呢-高速洗呢-烘呢-增深处理—熟修—中检-刷毛-剪毛—罐蒸-蒸呢-预缩工序,制成精纺面料;
6)测试起泡性:
步骤一:在70cm通幅面料样品上取60cm×60cm的样品两块作为测试试样;
步骤二:将试样平置于温度20±2℃,湿度65±3%的环境条件下平衡2小时;
步骤三:把试样纵向折叠试样,折叠后的试样为30cm(横向)×60cm(纵向)正面朝外放到压烫机上,喷蒸汽10秒,蒸汽压力为6kg,织物受湿热后发生变形、起泡,表面起不同大小或不同密度的折痕或泡泡;
步骤四:喷完蒸汽后,用吸风将面料冷却5秒后将面料取出,将试样的横向一端夹在裤子衣架上,使试样保持自然垂直;
步骤五:将夹有试样的裤子衣架悬挂于温度20±2℃,湿度65±3%的环境下,将平衡后的样品移到自然背光条件下,分别在整烫后1小时后及整烫后24小时后这两个时间段,观察试样外观变化确定试样的起泡等级。
与现有技术相比,本发明的有益效果是:
本发明绿色环保面料及其起泡工艺通过外层面料与衬里面料之间增加SEE生态棉,使用面料具有生物降解、节能改排、环保生态等特点,是一种理想的绿色环保保暖面料。
具体实施方式
本发明涉及一种绿色环保面料的工艺为:
1)、纱线品种设计:
选用羊毛纤维、羊绒纤维和海藻炭纤维,所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成,所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为:所述兔毛纤维占18%-22%,所述美丽诺超细羊毛纤维占15%-19%,所述安哥拉山羊毛纤维占26%-30%,所述丝光羊毛纤维占29%-41%,对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳;
3)、纺纱工艺:
采用一般公知的纺纱工艺,依次经过头针—二针—三针—四针—粗纱-存放—细纱—蒸纱—自络筒-并线-倍捻—蒸纱工序,制成用于织造精纺面料的纱线,细纱工序采用紧密纺细纱设备;
4)、织造和修补工艺:
采用一般公知的织造和修补工艺,将纱线织造成坯布,并通过修补使得坯布无纺疵和织疵;
5)、后整理工艺:
坯布经过烧毛—平幅洗呢—煮呢—烘呢-高速洗呢-烘呢-增深处理—熟修—中检-刷毛-剪毛—罐蒸-蒸呢-预缩工序,制成精纺面料;
6)测试起泡性:
步骤一:在70cm通幅面料样品上取60cm×60cm的样品两块作为测试试样;
步骤二:将试样平置于温度20±2℃,湿度65±3%的环境条件下平衡2小时;
步骤三:把试样纵向折叠试样,折叠后的试样为30cm(横向)×60cm(纵向)正面朝外放到压烫机上,喷蒸汽10秒,蒸汽压力为6kg,织物受湿热后发生变形、起泡,表面起不同大小或不同密度的折痕或泡泡;
步骤四:喷完蒸汽后,用吸风将面料冷却5秒后将面料取出,将试样的横向一端夹在裤子衣架上,使试样保持自然垂直;
步骤五:将夹有试样的裤子衣架悬挂于温度20±2℃,湿度65±3%的环境下,将平衡后的样品移到自然背光条件下,分别在整烫后1小时后及整烫后24小时后这两个时间段,观察试样外观变化确定试样的起泡等级。
Claims (1)
1.一种绿色环保面料,其特征在于:其工艺为:
1)、纱线品种设计:
选用羊毛纤维、羊绒纤维和海藻炭纤维,所述羊毛纤维由兔毛纤维、美丽诺超细羊毛纤维、安哥拉山羊毛纤维以及丝光羊毛纤维四种纤维混纺编织而成,所述的混纺兔羊毛纤维面料中各成分所占重量百分比分别为:所述兔毛纤维占18%-22%,所述美丽诺超细羊毛纤维占15%-19%,所述安哥拉山羊毛纤维占26%-30%,所述丝光羊毛纤维占29%-41%,对羊毛纤维、羊绒纤维和海藻炭纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
依次经过混条—针梳—精梳—针梳—成条工序完成复精梳;
3)、纺纱工艺:
采用一般公知的纺纱工艺,依次经过头针—二针—三针—四针—粗纱-存放—细纱—蒸纱—自络筒-并线-倍捻—蒸纱工序,制成用于织造精纺面料的纱线,细纱工序采用紧密纺细纱设备;
4)、织造和修补工艺:
采用一般公知的织造和修补工艺,将纱线织造成坯布,并通过修补使得坯布无纺疵和织疵;
5)、后整理工艺:
坯布经过烧毛—平幅洗呢—煮呢—烘呢-高速洗呢-烘呢-增深处理—熟修—中检-刷毛-剪毛—罐蒸-蒸呢-预缩工序,制成精纺面料;
6)测试起泡性:
步骤一:在70cm通幅面料样品上取60cm×60cm的样品两块作为测试试样;
步骤二:将试样平置于温度20±2℃,湿度65±3%的环境条件下平衡2小时;
步骤三:把试样纵向折叠试样,折叠后的试样为30cm(横向)×60cm(纵向)正面朝外放到压烫机上,喷蒸汽10秒,蒸汽压力为6kg,织物受湿热后发生变形、起泡,表面起不同大小或不同密度的折痕或泡泡;
步骤四:喷完蒸汽后,用吸风将面料冷却5秒后将面料取出,将试样的横向一端夹在裤子衣架上,使试样保持自然垂直;
步骤五:将夹有试样的裤子衣架悬挂于温度20±2℃,湿度65±3%的环境下,将平衡后的样品移到自然背光条件下,分别在整烫后1小时后及整烫后24小时后这两个时间段,观察试样外观变化确定试样的起泡等级。