CN105671738A - 一种复合面料的干燥性测试方法 - Google Patents
一种复合面料的干燥性测试方法 Download PDFInfo
- Publication number
- CN105671738A CN105671738A CN201610139570.8A CN201610139570A CN105671738A CN 105671738 A CN105671738 A CN 105671738A CN 201610139570 A CN201610139570 A CN 201610139570A CN 105671738 A CN105671738 A CN 105671738A
- Authority
- CN
- China
- Prior art keywords
- sample
- fabric
- yarn
- fiber
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种复合面料的干燥性测试方法,其特征在于:所述复合保暖面料包括外层的反射性强的背面织物和内层的反射性弱的正面织物,所述背面织物与正面织物之间设置有保暖层。本发明一种复合保暖面料,正反面分别采用反射性强的背面织物和反射性弱的正面织物制成,可翻转反穿,昼夜温差大的地区,当白天较热时,把反射性强的背面织物的一面穿在外面,达到降温的效果;当晚上较冷时,把反射性弱的深色面来哦的一面穿在外面,达到保温的效果。
Description
技术领域
本发明涉及一种复合面料的干燥性测试方法,属于面料技术领域。
背景技术
传统的面料是一衣一用,根据季节设计,再昼夜温差大的地区,此种面料无法一衣二用,容易太热或受寒,而普通的如羽绒服,棉服等面料产品,多采用人工操作缝纫机进行产品缝制,通过缝纫线迹,形成羽绒或填充物的储存空间,由于产品的特殊性和产品工艺的要求,为保证产品质量和穿着效果,在采用的生产材料和生产工艺等方面有很多要求和限制,尤其在制造材料选用,缝制工艺以及穿着体验方面存在一定的风险。另外,传统的制作面料的所采用的面料为不可以两面使用。
发明内容
本发明的目的在于克服上述不足,提供不再有热量流失管道,保暖性能强的一种复合面料的干燥性测试方法。
本发明的目的是这样实现的:
一种复合面料的干燥性测试方法为:
1)、纱线品种设计:
选用羊毛纤维、竹炭涤纶纤维和聚乳酸纤维,对羊毛纤维、竹炭涤纶纤维和聚乳酸纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
将羊毛纤维、竹炭涤纶纤维和聚乳酸纤维复精梳制成毛条;
3)、纺纱工艺:
经前纺-细纱-络筒-并线-倍捻-蒸纱制成纱线,其中制得细纱其支数为81Nm,捻度780Z捻/米;制得的纱线其为支数80Nm的双股纱,合股捻度810S捻/米;防透明涤纶在经纱与纬纱中的重量百分比含量为30;
4)、后整理工艺:
后整理包括:烧毛-单煮-洗呢-双煮-烘呢-光触媒加工液浸轧-烘呢-TEFLON三防整理-焙烘-熟修-刷毛-剪毛-刷毛-给湿-罐蒸,另外,光触媒加工液的用量30g/l—50g/l,轧液率75%—85%,在光触媒加工液的使用时保持车25m/min—30m/min,温度120℃—135℃,TEFLON三防整理加工的轧液75-85%,车速保持18-22m/min,温度160-180℃,最后制得的面料规格为:纱支96/2-100/2Nm,总紧度145-165,经密615-796根/10厘米,纬密400-358根/10厘米,克重340-390克/米;
5)测试干燥性:
步骤一:在40cm通幅的样品上取10cm×20cm的样品两块作为测试试样;
步骤二:将试样放在洗涤仪容器中,加入300ml四氯乙烯作为干洗剂,密封后放到干洗仪中,干洗30min后取出,然后重复洗涤两次;
步骤三:将试样平置于温度20±2℃,湿度65±3%的环境下,平衡12小时后放于天平上称重,称得试样浸前重量;
步骤四:在烧杯中加入试剂500ml(试剂配制方法:499.5ml蒸馏水中加入0.5ml渗透剂FFA),把干洗后的试样置于烧杯中充分吸湿1分钟;
步骤五:将吸湿后的试样沿长度方向一折为二挂于凉衣架,将挂有试样的凉衣架置于温度20±2℃,湿度65±3%的环境条件下,并记录时间,每隔30分钟后测量试样重量,直到试样恢复浸前重量为止;
步骤六:记录试样恢复浸前重量的时间,即为面料自然干燥时间。
与现有技术相比,本发明的有益效果是:
本发明一种复合保暖面料,正反面分别采用反射性强的背面织物和反射性弱的正面织物制成,可翻转反穿,昼夜温差大的地区,当白天较热时,把反射性强的背面织物的一面穿在外面,达到降温的效果;当晚上较冷时,把反射性弱的深色面来哦的一面穿在外面,达到保温的效果。
具体实施方式
本发明涉及一种复合保暖面料,复合面料的干燥性测试方法为:
1)、纱线品种设计:
选用羊毛纤维、竹炭涤纶纤维和聚乳酸纤维,对羊毛纤维、竹炭涤纶纤维和聚乳酸纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
将羊毛纤维、竹炭涤纶纤维和聚乳酸纤维复精梳制成毛条;
3)、纺纱工艺:
经前纺-细纱-络筒-并线-倍捻-蒸纱制成纱线,其中制得细纱其支数为81Nm,捻度780Z捻/米;制得的纱线其为支数80Nm的双股纱,合股捻度810S捻/米;防透明涤纶在经纱与纬纱中的重量百分比含量为30;
4)、后整理工艺:
后整理包括:烧毛-单煮-洗呢-双煮-烘呢-光触媒加工液浸轧-烘呢-TEFLON三防整理-焙烘-熟修-刷毛-剪毛-刷毛-给湿-罐蒸,另外,光触媒加工液的用量30g/l—50g/l,轧液率75%—85%,在光触媒加工液的使用时保持车25m/min—30m/min,温度120℃—135℃,TEFLON三防整理加工的轧液75-85%,车速保持18-22m/min,温度160-180℃,最后制得的面料规格为:纱支96/2-100/2Nm,总紧度145-165,经密615-796根/10厘米,纬密400-358根/10厘米,克重340-390克/米;
5)测试干燥性:
步骤一:在40cm通幅的样品上取10cm×20cm的样品两块作为测试试样;
步骤二:将试样放在洗涤仪容器中,加入300ml四氯乙烯作为干洗剂,密封后放到干洗仪中,干洗30min后取出,然后重复洗涤两次;
步骤三:将试样平置于温度20±2℃,湿度65±3%的环境下,平衡12小时后放于天平上称重,称得试样浸前重量;
步骤四:在烧杯中加入试剂500ml(试剂配制方法:499.5ml蒸馏水中加入0.5ml渗透剂FFA),把干洗后的试样置于烧杯中充分吸湿1分钟;
步骤五:将吸湿后的试样沿长度方向一折为二挂于凉衣架,将挂有试样的凉衣架置于温度20±2℃,湿度65±3%的环境条件下,并记录时间,每隔30分钟后测量试样重量,直到试样恢复浸前重量为止;
步骤六:记录试样恢复浸前重量的时间,即为面料自然干燥时间。
Claims (1)
1.一种复合保暖面料,其特征在于:其干燥性测试方法为为:
1)、纱线品种设计:
选用羊毛纤维、竹炭涤纶纤维和聚乳酸纤维,对羊毛纤维、竹炭涤纶纤维和聚乳酸纤维进行抗起球处理、酶处理和柔软处理,抗起球处理选用磷酸酯三氧化二锑混合物作为抗起球剂,磷酸酯三氧化二锑混合物用量为羊毛纤维重量1.5-4%,酶处理系使用蛋白酶进行处理,蛋白酶用量为羊毛纤维重量的0.1-0.2%,柔软处理选用的柔软剂为水溶性有机硅柔软剂,水溶性有机硅柔软剂用量为羊毛纤维重量的6-8%;
2)、复精梳工艺:
将羊毛纤维、竹炭涤纶纤维和聚乳酸纤维复精梳制成毛条;
3)、纺纱工艺:
经前纺-细纱-络筒-并线-倍捻-蒸纱制成纱线,其中制得细纱其支数为81Nm,捻度780Z捻/米;制得的纱线其为支数80Nm的双股纱,合股捻度810S捻/米;防透明涤纶在经纱与纬纱中的重量百分比含量为30;
4)、后整理工艺:
后整理包括:烧毛-单煮-洗呢-双煮-烘呢-光触媒加工液浸轧-烘呢-TEFLON三防整理-焙烘-熟修-刷毛-剪毛-刷毛-给湿-罐蒸,另外,光触媒加工液的用量30g/l—50g/l,轧液率75%—85%,在光触媒加工液的使用时保持车25m/min—30m/min,温度120℃—135℃,TEFLON三防整理加工的轧液75-85%,车速保持18-22m/min,温度160-180℃,最后制得的面料规格为:纱支96/2-100/2Nm,总紧度145-165,经密615-796根/10厘米,纬密400-358根/10厘米,克重340-390克/米;
5)测试干燥性:
步骤一:在40cm通幅的样品上取10cm×20cm的样品两块作为测试试样;
步骤二:将试样放在洗涤仪容器中,加入300ml四氯乙烯作为干洗剂,密封后放到干洗仪中,干洗30min后取出,然后重复洗涤两次;
步骤三:将试样平置于温度20±2℃,湿度65±3%的环境下,平衡12小时后放于天平上称重,称得试样浸前重量;
步骤四:在烧杯中加入试剂500ml(试剂配制方法:499.5ml蒸馏水中加入0.5ml渗透剂FFA),把干洗后的试样置于烧杯中充分吸湿1分钟;
步骤五:将吸湿后的试样沿长度方向一折为二挂于凉衣架,将挂有试样的凉衣架置于温度20±2℃,湿度65±3%的环境条件下,并记录时间,每隔30分钟后测量试样重量,直到试样恢复浸前重量为止;
步骤六:记录试样恢复浸前重量的时间,即为面料自然干燥时间。