CN105670076A - Wood-plastic material produced from discarded packages as well as production equipment and production method of wood plastic material - Google Patents
Wood-plastic material produced from discarded packages as well as production equipment and production method of wood plastic material Download PDFInfo
- Publication number
- CN105670076A CN105670076A CN201610057325.2A CN201610057325A CN105670076A CN 105670076 A CN105670076 A CN 105670076A CN 201610057325 A CN201610057325 A CN 201610057325A CN 105670076 A CN105670076 A CN 105670076A
- Authority
- CN
- China
- Prior art keywords
- wood
- plastic
- packing material
- discarded
- plastic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wood-plastic material produced from discarded packages as well as production equipment and a production method of the wood plastic material. The wood plastic material comprises raw materials in parts by weight as follows: 10-20 parts of discarded package recycled materials, 20-30 parts of crushed wood-plastic materials, 50-80 parts of plastic particles, 60-80 parts of plant fiber, 10-20 parts of inorganic pigment filler, 5-10 parts of a compatilizer, 2-4 parts of a lubricating agent and 1-2 parts of a functional aid. The discarded packages are turned into a raw material for a wood plastic profile, the appearance, the physical and chemical property and other aspects all meet the requirement for the wood plastic performance, waste is turned into wealth, and the economic and social benefits are produced.
Description
Technical field
The present invention relates to Wood-plastic material production technical field, be specifically related to a kind of Wood-plastic material utilizing discarded packing material to produce and production equipment thereof and production method.
Background technology
Along with the progress of society, growth in the living standard, increasing packing material (includes paper bag, paper and plastics compound bag, plastic bag etc.) and is widely used, and is generally landfilled or burning disposal after having used. This kind of processing mode not only contaminated environment, and take substantial amounts of land resource. Especially recently as the development of Industrial-Enterprises in China, express delivery industry, the substantial amounts of discarded packing material of annual generation. Containing plastics in part packing material, plastics belong to macromolecular compound, are not easily decomposed, and are formed " white garbage ". The packaging burning of substantial amounts of stationery can form " haze ", causes environmental pollution, affects human health.
Wood-plastic material, as a kind of building material, has begun to a large amount of use, is accepted by market gradually. The raw material of Wood-plastic material is the sponge such as plastics and wood bamboo, and these sponges are directly or indirectly from nature material, and how solving raw material problem and not destroying the forest reserves is also a new environmental protection trend.
Summary of the invention
It is an object of the invention to, it is provided that a kind of using discarded packing material as Wood-plastic material raw materials for production, process problem and wood and mould the Wood-plastic material of raw materials for production problem and production equipment thereof and production method solving discarded packing material.
A kind of Wood-plastic material utilizing discarded packing material to produce provided by the invention, including the raw material of following weight portion:
Discarded wrap pages to be reclaimed material 10-20 part, wood mould broken material 20-30 part, plastic pellet 50-80 part, Plant fiber's 60-80 part, inorganic pigment filler 10-20 part, compatilizer 5-10 part, lubricant 2-4 part, function additive 1-2 part.
Wherein, plastic pellet is one or both mixture of PP, PE.
Wherein, Plant fiber is one or both mixture of wood powder, bamboo powder.
Wherein, inorganic pigment filler is iron oxide red, iron oxide yellow, calcium carbonate, one or both mixture of Pulvis Talci.
Wherein, compatilizer is Research of Grafting Malaic Anhydride Onto Polyethylene, ethylene-acrylic acid copolymer, one or several mixture of polypropylene grafted maleic anhydride.
Wherein, lubricant is Tissuemat E, paraffin, stearic acid, zinc stearate, ethylene bis stearic acid amide, one or several mixture of organosilicon.
Wherein, function additive includes antioxidant, UV absorbent.
The production equipment of a kind of Wood-plastic material utilizing discarded packing material to produce provided by the invention, including the shredder connected successively, flour mill, blanking type batch mixer and high-speed mixer.
The production method of a kind of Wood-plastic material utilizing discarded packing material to produce provided by the invention, includes operations described below step successively:
(1), discarded packing material roguing, pulverizing: after discarded wrap pages to be reclaimed, remove impurity therein, put in shredder and pulverize, be ground into the fragment of 1-2 centimetre of size;
(2), fragment grinds: is put into by fragment in flour mill and grinds, by chopped fiber, prepares into cotton-shaped packing material fiber material;
(3), impact, disperse: cotton-shaped packing material fiber material, wood are moulded broken material and put in blanking type batch mixer, cotton-shaped packing material fiber material is moulded broken material by wood and is impacted, make cotton-shaped packing material fiber material dispersed, become discarded wrap pages to be reclaimed material;
(4), dispensing mixing: weigh various raw material respectively by above-mentioned weight portion, put into and mix in high-speed mixer to 120-125 DEG C of discharging to cold mixed, be cooled to discharging when 50-60 DEG C.
Wherein, plastic pellet, it is possible to adopt the waste plastic particle reclaimed as raw material, strengthen the utilization rate to garbage further, economize on resources and avoid by the brought environmental pollution of waste plastic.
Wherein, after step (4); can the Wood-plastic material being successfully prepared be put in comminutor; comminutor is open parallel double-screw extruder; expressing technique condition is: barrel zone temperature is: 140-180 DEG C; screw speed is 200-400rpm, and Wood-plastic material is prepared into graininess, it is simple to transport and use.
When manufacturing Wood-plastic profiles, Wood-plastic material granule is put in Wood-plastic profiles forming machine, can be prepared by section bar, Wood-plastic profiles forming machine is conical double-screw Wood-plastic profiles extruder, barrel zone temperature is: 160-200 DEG C, and screw speed is 10-25rpm, the cooled sizing of section bar of molding, fixed length cutting, mould installation method by wood, after assembling, namely prepare finished product.
In the present invention, by the combination of the equipment such as shredder, flour mill, mixer, make the packing material (such as coated paper envelope, paper and plastics compound bag etc.) discarded become can in Wood-plastic material production process operable reclaimed materials. Due to different on composition of paper fiber and the wood fiber, very easily reunite, consider the feasibility of economy and processing, paper fiber is not individually continued to be processed into grinding by this method, but by the blending with broken material, utilize the friction of storeroom, isolation so that paper fiber can be moulded in production technology at the wood of existing maturation and apply, and every physicochemical property is attained by every wood and moulds performance requirement.
The present invention has innovated compared with moulding production technology with normal wood in technique, the efficient shearing of shredder, the powerful grinding of flour mill and the dispersion isolation features of mixer is carried out process combination, solves the problem that paper coma wadding cannot use. Discarded packing material becomes the raw material of Wood-plastic profiles, and the everyway such as outward appearance, physicochemical property reaches every wood and moulds performance requirement, it is achieved turn waste into wealth, and produces economic and social benefit.
Accompanying drawing explanation
Fig. 1 is the schematic flow sheet that in the present invention, Wood-plastic material produces.
Detailed description of the invention
Below in conjunction with specific embodiment, invention is described in further detail.
Embodiment 1
A kind of Wood-plastic material utilizing discarded packing material to produce, including the raw material of following weight portion:
Discarded 30 parts of wrap pages to be reclaimed material, 50 parts of Recycled HDPE particle, wood powder 50 parts, Pulvis Talci 20 parts, silane coupler 3 parts, Research of Grafting Malaic Anhydride Onto Polyethylene 6 parts, zinc stearate 3 parts, ethylene bis stearic acid amide 3 parts, antioxidant 1010 0.5 part, UV absorbent UV5310.5 part.
Wherein, silane coupler model is A-174, Nanjing dawn Chemical Co., Ltd. produce.
Wherein, Research of Grafting Malaic Anhydride Onto Polyethylene model is HAD-14, Mount Huang Bei Nuo Science and Technology Ltd. produce.
Wherein, antioxidant 1010 is produced by Xuzhou ten thousand and chemical industry company limited.
Wherein, UV absorbent UV531 is produced by Nantong Chemical Co., Ltd. of Kingcon Thailand.
Referring to Fig. 1, the production equipment of a kind of Wood-plastic material utilizing discarded packing material to produce provided by the invention, including the shredder 1 connected successively, flour mill 2, blanking type batch mixer 3 and high-speed mixer 4.
The production method of a kind of Wood-plastic material utilizing discarded packing material to produce, includes operations described below step successively:
(1), discarded packing material roguing, pulverizing: after discarded wrap pages to be reclaimed, remove impurity therein, put in shredder 1 and pulverize, be ground into the fragment of 1 centimetre of size;
(2), fragment grinds: is put into by fragment in flour mill 2 and grinds, by chopped fiber, prepares into cotton-shaped packing material fiber material;
(3), impact, disperse: putting in blanking type batch mixer 3 by cotton-shaped packing material fiber material, broken material, cotton-shaped packing material fiber material is impacted by broken material, makes cotton-shaped packing material fiber material dispersed, becomes discarded wrap pages to be reclaimed material;
(4), dispensing mixing: weigh various raw material respectively by above-mentioned weight portion, after cotton-shaped packing material fiber material is warming up to 105 DEG C, add above-mentioned raw materials, mixed to 120 DEG C of dischargings to cold mixed by high-speed mixer 4, be cooled to 50 DEG C of dischargings;
(5), pelletize: by screw conveyer, the compound obtained by step (4) is sent into comminutor, and comminutor is open parallel double-screw extruder, and expressing technique condition is: barrel zone temperature is: 140 DEG C, and screw speed is 300rpm;
(6), molding: the pellet produced by comminutor prepares section bar by Wood-plastic profiles forming machine, and Wood-plastic profiles forming machine is conical double-screw Wood-plastic profiles extruder, and barrel zone temperature is: 160 DEG C, and screw speed is 10rpm;
(7), cutting: the section bar cooling and shaping of molding, as required fixed length cutting;
(8), assemble: mould installation method by wood, assemble various section bar.
Embodiment 2
A kind of Wood-plastic material utilizing discarded packing material to produce, including the raw material of following weight portion:
Discarded 40 parts of wrap pages to be reclaimed material, 50 parts of Recycled HDPE particle, wood powder 40 parts, Pulvis Talci 20 parts, silane coupler 3 parts, Research of Grafting Malaic Anhydride Onto Polyethylene 6 parts, zinc stearate 3 parts, ethylene bis stearic acid amide 3 parts, Tissuemat E 0.5 part, antioxidant 1010 0.5 part, UV absorbent UV5310.5 part.
The production method of a kind of Wood-plastic material utilizing discarded packing material to produce, includes operations described below step successively:
(1), discarded packing material roguing, pulverizing: after discarded wrap pages to be reclaimed, remove impurity therein, put in shredder 1 and pulverize, be ground into the fragment of 2 centimetres of sizes;
(2), fragment grinds: is put into by fragment in flour mill 2 and grinds, by chopped fiber, prepares into cotton-shaped packing material fiber material;
(3), impact, disperse: putting in blanking type batch mixer 3 by cotton-shaped packing material fiber material, broken material, cotton-shaped packing material fiber material is impacted by broken material, makes cotton-shaped packing material fiber material dispersed, becomes discarded wrap pages to be reclaimed material;
(4), dispensing mixing: weigh various raw material respectively by above-mentioned weight portion, after cotton-shaped packing material fiber material is warming up to 105 DEG C, add above-mentioned raw materials, mixed to 120 DEG C of dischargings to cold mixed by high-speed mixer 4, be cooled to 50 DEG C of dischargings;
(5), pelletize: by screw conveyer, the compound obtained by step (4) is sent into comminutor, and comminutor is open parallel double-screw extruder, and expressing technique condition is: barrel zone temperature is: 150 DEG C, and screw speed is 300rpm;
(6), molding: the pellet produced by comminutor prepares section bar by Wood-plastic profiles forming machine, and Wood-plastic profiles forming machine is conical double-screw Wood-plastic profiles extruder, and barrel zone temperature is: 170 DEG C, and screw speed is 10rpm;
(7), cutting: the section bar cooling and shaping of molding, as required fixed length cutting;
(8), assemble: mould installation method by wood, assemble various section bar.
Embodiment 3
A kind of Wood-plastic material utilizing discarded packing material to produce, including the raw material of following weight portion:
Discarded 50 parts of wrap pages to be reclaimed material, 50 parts of Recycled HDPE particle, wood powder 30 parts, Pulvis Talci 20 parts, silane coupler 3 parts, Research of Grafting Malaic Anhydride Onto Polyethylene 6 parts, zinc stearate 3 parts, ethylene bis stearic acid amide 3 parts, poly-antioxidant 1010 0.5 part, UV absorbent UV5310.5 part.
The production method of a kind of Wood-plastic material utilizing discarded packing material to produce, includes operations described below step successively:
(1), discarded packing material roguing, pulverizing: after discarded wrap pages to be reclaimed, remove impurity therein, put in shredder 1 and pulverize, be ground into the fragment of 1 centimetre of size;
(2), fragment grinds: is put into by fragment in flour mill 2 and grinds, by chopped fiber, prepares into cotton-shaped packing material fiber material;
(3), impact, disperse: putting in blanking type batch mixer 3 by cotton-shaped packing material fiber material, broken material, cotton-shaped packing material fiber material is impacted by broken material, makes cotton-shaped packing material fiber material dispersed, becomes discarded wrap pages to be reclaimed material;
(4), dispensing mixing: weigh various raw material respectively by above-mentioned weight portion, after cotton-shaped packing material fiber material is warming up to 105 DEG C, add above-mentioned raw materials, mixed to 120 DEG C of dischargings to cold mixed by high-speed mixer 4, be cooled to 50 DEG C of dischargings;
(5), pelletize: by screw conveyer, the compound obtained by step (4) is sent into comminutor, and comminutor is open parallel double-screw extruder, and expressing technique condition is: barrel zone temperature is: 180 DEG C, and screw speed is 300rpm;
(6), molding: the pellet produced by comminutor prepares section bar by Wood-plastic profiles forming machine, and Wood-plastic profiles forming machine is conical double-screw Wood-plastic profiles extruder, and barrel zone temperature is: 180 DEG C, and screw speed is 10rpm;
(7), cutting: the section bar cooling and shaping of molding, as required fixed length cutting;
(8), assemble: mould installation method by wood, assemble various section bar.
Embodiment 4
The density of the present invention, 24h water absorption rate, wood mould four-point bending intensity, bending modulus, simply supported beam non-notch, and impact strength, shore hardness, supine human body all detect according to the standard of GBT29418-2012.
The testing result of embodiment 1-3 is as shown in table 1:
Table 1:
It is good with the compatibility of wood powder, plastic pellet to be can be seen that by modified discarded wrap pages to be reclaimed material by upper table, and the excellent in mechanical performance decided moulded by wood, and water absorption rate is little.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-described embodiment, and all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention. It should be pointed out that, for those skilled in the art, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (10)
1. one kind utilizes the Wood-plastic material that discarded packing material produces, it is characterised in that: include the raw material of following weight portion:
Discarded wrap pages to be reclaimed material 10-20 part, wood mould broken material 20-30 part, plastic pellet 50-80 part, Plant fiber's 60-80 part, inorganic pigment filler 10-20 part, compatilizer 5-10 part, lubricant 2-4 part, function additive 1-2 part.
2. a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 1, it is characterised in that: described plastic pellet is one or both mixture of PP, PE.
3. a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 1, it is characterised in that: described Plant fiber is one or both mixture of wood powder, bamboo powder.
4. a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 1, it is characterised in that: described inorganic pigment filler is iron oxide red, iron oxide yellow, calcium carbonate, one or both mixture of Pulvis Talci.
5. a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 1, it is characterised in that: described compatilizer is Research of Grafting Malaic Anhydride Onto Polyethylene, ethylene-acrylic acid copolymer, one or several mixture of polypropylene grafted maleic anhydride.
6. a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 1, it is characterised in that: described lubricant is Tissuemat E, paraffin, stearic acid, zinc stearate, ethylene bis stearic acid amide, one or several mixture of organosilicon.
7. a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 1, it is characterised in that: described function additive includes antioxidant, UV absorbent.
8. the production equipment of the production a kind of Wood-plastic material utilizing discarded packing material to produce described in claim 1～7 any one, it is characterised in that: include the shredder, flour mill, blanking type batch mixer and the high-speed mixer that connect successively.
9. the production method of the preparation a kind of Wood-plastic material utilizing discarded packing material to produce described in claim 1～7 any one, it is characterised in that: comprise the following steps:
(1), discarded packing material roguing, pulverizing: after discarded wrap pages to be reclaimed, remove impurity therein, put in shredder and pulverize, be ground into the fragment of 1-2 centimetre of size;
(2), fragment grinds: is put into by fragment in flour mill and grinds, by chopped fiber, prepares into cotton-shaped packing material fiber material;
(3), impact, disperse: cotton-shaped packing material fiber material, wood are moulded broken material and put in blanking type batch mixer, cotton-shaped packing material fiber material is moulded broken material by wood and is impacted, make cotton-shaped packing material fiber material dispersed, become discarded wrap pages to be reclaimed material;
(4), dispensing mixing: weigh various raw material respectively by above-mentioned weight portion, put into and mix in high-speed mixer to 120-125 DEG C of discharging to cold mixed, be cooled to discharging when 50-60 DEG C.
10. the production method of a kind of Wood-plastic material utilizing discarded packing material to produce according to claim 9, it is characterised in that: further comprising the steps of:
(5), pelletize: the compound obtained by step (4) is sent into comminutor by screw conveyer, comminutor is open parallel double-screw extruder, expressing technique condition is: barrel zone temperature is: 140-180 DEG C, and screw speed is 200-400rpm;
(6), molding: the pellet produced by comminutor prepares section bar by Wood-plastic profiles forming machine, and Wood-plastic profiles forming machine is conical double-screw Wood-plastic profiles extruder, and barrel zone temperature is: 160-200 DEG C, and screw speed is 10-25rpm;
(7), cutting: the section bar cooling and shaping of molding, as required fixed length cutting;
(8), assemble: mould installation method by wood, assemble various section bar.