CN106398268A - Building template produced from reclaimed material and preparation method thereof - Google Patents

Building template produced from reclaimed material and preparation method thereof Download PDF

Info

Publication number
CN106398268A
CN106398268A CN201610783343.9A CN201610783343A CN106398268A CN 106398268 A CN106398268 A CN 106398268A CN 201610783343 A CN201610783343 A CN 201610783343A CN 106398268 A CN106398268 A CN 106398268A
Authority
CN
China
Prior art keywords
weight portion
building wood
wood plastic
plastic boards
abrasive dust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610783343.9A
Other languages
Chinese (zh)
Inventor
赵悦英
杨明
李素坤
王苏
化明志
朱莽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Rays Of Sunlight Industrial Co Ltd
Original Assignee
Shandong Rays Of Sunlight Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Rays Of Sunlight Industrial Co Ltd filed Critical Shandong Rays Of Sunlight Industrial Co Ltd
Priority to CN201610783343.9A priority Critical patent/CN106398268A/en
Publication of CN106398268A publication Critical patent/CN106398268A/en
Pending legal-status Critical Current

Abstract

The invention discloses a building wood-plastic sheet produced from a reclaimed material. The raw materials of the building wood-plastic sheet are composed of a reclaimed milling material, a foaming agent, internal and external lubricants, a flexibilizer, a composite stabilizing agent and a processing aid. The invention also discloses a preparation method for the building wood-plastic sheet. The building wood-plastic sheet uses the reclaimed material, so production cost is low; the building wood-plastic sheet has dimensional stability, surface hardness, strength, toughness and nail-holding power much higher than national standard in China; and the building wood-plastic sheet is high in the frequency of repeated usage, so comprehensive usage cost is lowered.

Description

Building template that a kind of utilization reclaimed materials produces and preparation method thereof
Technical field
The present invention relates to a kind of produce building template formula and preparation method thereof using reclaimed materials.
Background technology
With the raising of people's environmental protection and energy saving consciousness, Bamboo Formwork, plank sheathing, steel form can not meet building completely will Ask, in the urgent need to a kind of new construction material with low cost, high access times.
Wood plastic composite is a kind of new material, be working process is crossed waste and old wood, sawdust, crops straw Stalk, the shell of nut, according to certain ratio, are mixed with thermoplastic and make through high temperature high pressure process, have acid and alkali-resistance, will not Rotten the advantages of.
But existing Bamboo Formwork, plank sheathing, steel form have performance and such as pour that metope is rough, and the aspect such as out-of-flatness has Many defects, service life is short, and production cost is high, the complicated shortcoming of long the production cycle, production process；And size changing rate, Case hardness, intensity, toughness and nail-holding ability aspect also leave the problem of many, and it is low that product reuses number of times.
Content of the invention
It is an object of the invention to, a kind of building template of utilization reclaimed materials production and preparation method thereof, Neng Goudai are provided For traditional architecture template and substantially increase recycling number of times, overcome the problem of the aspects such as plate property aspect, production cost.
The building Wood plastic boards that a kind of utilization reclaimed materials produces, raw material includes：Reclaim abrasive dust material, foaming agent, inside and outside lubrication Agent, toughener, compound stabilizer, processing aid.
The building Wood plastic boards that a kind of utilization reclaimed materials produces, the composition of raw material and weight portion are：Reclaim abrasive dust material：100- 200 weight portions, foaming agent：0.5-2.5 weight portion, inside and outside lubricant agent 1-3 weight portion, toughener：3-10 weight portion, stable composition Agent：1-7 weight portion, processing aid：1-6 weight portion.
The building Wood plastic boards that a kind of utilization reclaimed materials produces,：The composition of raw material and weight portion can also be：Reclaim abrasive dust Material：105-125 weight portion, foaming agent：0.6-1.2 weight portion, inside and outside lubricant agent 1-2 weight portion, toughener：4-6 weight portion, multiple Close stabilizer：2-4 weight portion, processing aid：1-2 weight portion.
Preferably, described recovery abrasive dust material is：Reclaim template abrasive dust and/or plastic-steel abrasive dust.
Preferably, described, be：Double methyl esters and/or phthalate and/or adipic acid；Processing aid is：Double first Ester and/or dibutyl ester and/or styrene；Foaming agent is azo acid amides and/or sodium bicarbonate；Inside and outside lubricant agent is：Tissuemat E and/ Or stearic acid.
Preferably, described compound stabilizer is：Rare earth composite stabilizer and/or the dustless compound stabilizer of metallic soap；Institute The toughener stated is：CPE haloflex wax.
The preparation method of the building Wood plastic boards that above-mentioned utilization reclaimed materials produces, comprises the steps：
(1) by mixing raw materials machine, it is heated to 95～150 DEG C, be cooled to 40～80 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 130～215 DEG C of extrusions, extruder barrel temperature 130～200 DEG C, 135～225 DEG C of mold temperature, 8～30 turns/min of engine speed, 9～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut.
It is also possible that the preparation method building Wood plastic boards that above-mentioned utilization reclaimed materials produces, comprise the steps：
(1) by mixing raw materials machine, it is heated to 110～130 DEG C, be cooled to 50～65 DEG C and put into barrel；；
(2) mixed raw material is added extruder, be heated to 135～185 DEG C of extrusions, extruder barrel temperature 145～185 DEG C, 150～205 DEG C of mold temperature, 10～20 turns/min of engine speed, 15～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut.
It is also possible that the product that step (3) obtains also needs through final treatment techniques.
Preferably, final treatment techniques include but is not limited to be embossed.
Beneficial effects of the present invention：
The present invention is had the advantage that using the building template that reclaimed materials produces：
(1) all using reclaimed materials, low production cost, long the production cycle；
(2) surface skining is smooth, smooth, need not add releasing agent in use, using the surface of wall of this product Flatness is far above conventional template.
(3) product tangent plane is neat, closely knit no abscess, and in size changing rate, case hardness, intensity, toughness and nail-holding ability Aspect is far above national standard, and product reuses number of times height, reduces comprehensive use cost.
(4) waterproof and dampproof it is easy to processing, using after the several years can 100% recovery.
Specific embodiment
The present invention can be expressly understood further by the specific embodiment of invention now given below, but following enforcement Example is not limitation of the invention.Following examples are merely to illustrate technical scheme and unrestricted, this area It will be appreciated by the skilled person that technical scheme can be modified or equivalent, without deviating from skill of the present invention The objective of art scheme and scope, it all should be covered in the middle of scope of the presently claimed invention.
Embodiment 1
The building Wood plastic boards that a kind of utilization reclaimed materials produces, the composition of raw material and weight portion are：Reclaim abrasive dust material：100- 200 weight portions, foaming agent：0.5-2.5 weight portion, inside and outside lubricant agent 1-3 weight portion, toughener：3-10 weight portion, stable composition Agent：1-7 weight portion, processing aid：1-6 weight portion；
Described recovery abrasive dust material is：Template abrasive dust；
Described, be：Adipic acid；Processing aid is：Double methyl esters；Foaming agent is azo acid amides；Inside and outside lubricant agent is：Poly- second Alkene wax；Compound stabilizer is：Rare earth composite stabilizer；Toughener is：CPE haloflex wax；
A kind of preparation method of the building Wood plastic boards that utilization reclaimed materials produces, comprises the steps：
(1) by mixing raw materials machine, it is heated to 95～150 DEG C, be cooled to 40～80 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 130～215 DEG C of extrusions, extruder barrel temperature 130～200 DEG C, 135～225 DEG C of mold temperature, 8～30 turns/min of engine speed, 9～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut.
Embodiment 2
The building Wood plastic boards that a kind of utilization reclaimed materials produces, the composition of raw material and weight portion are：Reclaim abrasive dust material：105- 125 weight portions, foaming agent：0.6-1.2 weight portion, inside and outside lubricant agent 1-2 weight portion, toughener：4-6 weight portion, 4-7 weight Part, compound stabilizer：2-4 weight portion, processing aid：1-2 weight portion；
Described recovery abrasive dust material is：Plastic-steel abrasive dust；
Described, be：Double methyl esters；Processing aid is：Styrene；Foaming agent is sodium bicarbonate；Inside and outside lubricant agent is：Stearic Acid；Described compound stabilizer is：The dustless compound stabilizer of metallic soap；Described toughener is：CPE haloflex wax；
A kind of preparation method of the building Wood plastic boards that utilization reclaimed materials produces, comprises the steps：
(1) by mixing raw materials machine, it is heated to 95～150 DEG C, be cooled to 40～80 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 130～215 DEG C of extrusions, extruder barrel temperature 130～200 DEG C, 135～225 DEG C of mold temperature, 8～30 turns/min of engine speed, 9～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut.
Embodiment 3
The building Wood plastic boards that a kind of utilization reclaimed materials produces, the composition of raw material and weight portion are：Reclaim abrasive dust material：110 Weight portion, foaming agent：0.7 weight portion, inside and outside lubricant agent 1.5 weight portion, toughener：5 weight portions, 5 weight portions, stable composition Agent：3 weight portions, processing aid：1.5 weight portion；
Described recovery abrasive dust material is：Template abrasive dust；
Described, be：Phthalate and adipic acid；Processing aid is：Dibutyl ester and styrene；Foaming agent is even Nitrogen acid amides and sodium bicarbonate；Inside and outside lubricant agent is：Tissuemat E；Described compound stabilizer is：The dustless compound stabilizer of metallic soap； Described toughener is：CPE haloflex wax；
A kind of preparation method of the building Wood plastic boards that utilization reclaimed materials produces, comprises the steps：
(1) by mixing raw materials machine, it is heated to 110～130 DEG C, be cooled to 50～65 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 135～185 DEG C of extrusions, extruder barrel temperature 145～185 DEG C, 150～205 DEG C of mold temperature, 10～20 turns/min of engine speed, 15～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut；
The product that step (3) obtains also needs through final treatment techniques, and final treatment techniques are embossing.
Embodiment 4
The building Wood plastic boards that a kind of utilization reclaimed materials produces, the composition of raw material and weight portion are：Reclaim abrasive dust material：120 Weight portion, foaming agent：1.0 weight portions, inside and outside lubricant agent 1.8 weight portion, toughener：5.5 weight portions, 4.9 weight portions, it is combined steady Determine agent：2.5 weight portions, processing aid：1.8 weight portion；
Described recovery abrasive dust material is：Plastic-steel abrasive dust；
Described, be：Phthalate；Processing aid is：Dibutyl ester；Foaming agent is sodium bicarbonate；Inside and outside lubricant agent For：Tissuemat E；Described compound stabilizer is：The dustless compound stabilizer of metallic soap；Described toughener is：CPE chlorination gathers Ethylene waxes；
A kind of preparation method of building Wood plastic boards, comprises the steps：
(1) by mixing raw materials machine, it is heated to 110～130 DEG C, be cooled to 50～65 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 135～185 DEG C of extrusions, extruder barrel temperature 145～185 DEG C, 150～205 DEG C of mold temperature, 10～20 turns/min of engine speed, 15～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut
The product that step (3) obtains also needs through final treatment techniques, and final treatment techniques are embossing.
Embodiment 5
The building Wood plastic boards that a kind of utilization reclaimed materials produces, the composition of raw material and weight portion are：Reclaim abrasive dust material：100 Weight portion, foaming agent：0.8 weight portion, inside and outside lubricant agent 1.2 weight portion, toughener：4 weight portions, 8 weight portions, stable composition Agent：2 weight portions, processing aid：3 weight portions.；
Described recovery abrasive dust material is：Plastic-steel abrasive dust；
Described, be：Adipic acid；Processing aid is：Dibutyl ester；Foaming agent is azo acid amides；Inside and outside lubricant agent is：Stearic Acid；Described compound stabilizer is：Rare earth composite stabilizer；Described toughener is：CPE haloflex wax；
A kind of preparation method of the building Wood plastic boards that utilization reclaimed materials produces, comprises the steps：
(1) by mixing raw materials machine, it is heated to 100～140 DEG C, be cooled to 45～65 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 130～190 DEG C of extrusions, extruder barrel temperature 140～185 DEG C, 145～208 DEG C of mold temperature, 8～22 turns/min of engine speed, 13～30 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut, both.
The product that step (3) obtains also needs through final treatment techniques, and final treatment techniques are embossing.
Experimental example 1 building template is checked
The building template of this inspection is the sheet material being obtained according to the embodiment of the present invention 3.
Shandong Sheng Li wood moulding Services Co., Ltd survey report
Page totally 2 page 2

Claims (10)

1. the building Wood plastic boards that a kind of utilization reclaimed materials produces, it is characterized by：Raw material includes：Reclaim abrasive dust material, foaming agent, interior External lubricant, toughener, compound stabilizer, processing aid.
2. building Wood plastic boards as claimed in claim 1, it is characterized by：The composition of raw material and weight portion are：Reclaim abrasive dust material： 100-200 weight portion, foaming agent：0.5-2.5 weight portion, inside and outside lubricant agent 1-3 weight portion, toughener：3-10 weight portion, is combined Stabilizer：1-7 weight portion, processing aid：1-6 weight portion.
3. building Wood plastic boards as claimed in claim 2, it is characterized by：The composition of raw material and weight portion are：Reclaim abrasive dust material： 105-125 weight portion, foaming agent：0.6-1.2 weight portion, inside and outside lubricant agent 1-2 weight portion, toughener：4-6 weight portion, is combined Stabilizer：2-4 weight portion, processing aid：1-2 weight portion.
4. described building Wood plastic boards as arbitrary in claims 1 to 3, it is characterized by：Described recovery abrasive dust material is：Template is ground Powder and/or plastic-steel abrasive dust.
5. building Wood plastic boards as claimed in claim 4, it is characterized by：Described processing aid is：Dibutyl ester and/or benzene second Alkene；Foaming agent is：Azo acid amides；Inside and outside lubricant agent is：Tissuemat E and/or stearic acid.
6. building Wood plastic boards as claimed in claim 4, it is characterized by：Described compound stabilizer is：Rare earth stable composition Agent and/or the dustless compound stabilizer of metallic soap；Described toughener is：CPE haloflex wax.
7. as described in claim 5 or 6 building Wood plastic boards preparation method it is characterised in that：Comprise the steps：
(1) by mixing raw materials machine, it is heated to 95～150 DEG C, be cooled to 40～80 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 130～215 DEG C and extrude, 130～200 DEG C of extruder barrel temperature, 135～225 DEG C of mold temperature, 8～30 turns/min of engine speed, 9～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut.
8. as claimed in claim 7 building Wood plastic boards preparation method it is characterised in that：Comprise the steps：
(1) by mixing raw materials machine, it is heated to 110～130 DEG C, be cooled to 50～65 DEG C and put into barrel；
(2) mixed raw material is added extruder, be heated to 135～185 DEG C and extrude, 145～185 DEG C of extruder barrel temperature, 150～205 DEG C of mold temperature, 10～20 turns/min of engine speed, 15～28 turns/min of feeding rotating speed；
(3) through mould molding, cooling and shaping, traction after extruding, cut.
9. as described in claim 3 or 4 building Wood plastic boards preparation method it is characterised in that：The product that step (3) obtains Also need through final treatment techniques.
10. as claimed in claim 6 building Wood plastic boards preparation method it is characterised in that：Final treatment techniques include but It is not limited to be embossed.
CN201610783343.9A 2016-08-31 2016-08-31 Building template produced from reclaimed material and preparation method thereof Pending CN106398268A (en)