CN101955676A - Plastic wood composite material and preparation method - Google Patents

Plastic wood composite material and preparation method Download PDF

Info

Publication number
CN101955676A
CN101955676A CN2010101963446A CN201010196344A CN101955676A CN 101955676 A CN101955676 A CN 101955676A CN 2010101963446 A CN2010101963446 A CN 2010101963446A CN 201010196344 A CN201010196344 A CN 201010196344A CN 101955676 A CN101955676 A CN 101955676A
Authority
CN
China
Prior art keywords
plastic composite
parts
wood plastic
wood
waste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010101963446A
Other languages
Chinese (zh)
Inventor
姚文俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU TONGJIANG MACHINERY MANUFACTURING Co Ltd
Original Assignee
CHANGSHU TONGJIANG MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU TONGJIANG MACHINERY MANUFACTURING Co Ltd filed Critical CHANGSHU TONGJIANG MACHINERY MANUFACTURING Co Ltd
Priority to CN2010101963446A priority Critical patent/CN101955676A/en
Publication of CN101955676A publication Critical patent/CN101955676A/en
Pending legal-status Critical Current

Abstract

The invention relates to a plastic wood composite material which comprises the following raw materials in parts by weight: 15-30 parts of waste plastics, 70-85 parts of waste physical fibers, 1-5 parts of lubricant, 1-2 parts of tackifier, 2-5 parts of compatibilizer, 1-3 parts of anti-aging agent and 5-10 parts of flame retardant. The compositions are treated by procedures of mixing, stirring, extruding and pressure molding to obtain a finished product. In the invention, the waste plastics and the waste physical fibers are composited to form an advantageous plastic wood composite material which can be recycled by 100 percent, and has the advantages of low cost, good surface finish and good comprehensive properties such as the mechanical property, the heat resistance, the weatherability and the like.

Description

A kind of Wood plastic composite and preparation method
Technical field
The invention belongs to the Wood plastic composite technical field, relating to is a kind of Wood plastic composite and preparation method.
Background technology
Wood materials and steel, cement, plastics also are called four big basic raw materials, and wood materials is unique regenerated.The recoverable amount of China's big footpath level timber seldom at present; do not satisfy the demand in market; in order to solve this crisis; people advocate with steel on the one hand for wood, to mould Dai Mu; non-renewable oil and ore deposit iron resources have been consumed again; but caused the generation of one and another raw material crisis; on the other hand; in the face of tree is few greatly; people glue together use to the small wood small powder with the compound way; just must use a large amount of sizing materials, wherein 90% is urea-formaldehyde glue for this reason, and this is the main source that formaldehyde pollutes in the air.
Owing to lack the thin of a complete plastics recovery regeneration channel and environmental consciousness; also owing to lacking mature and reliable ground technology, the plastics that reclaim being fully utilized with the ground of method mass-producing cost-effectively; " white pollution " problem that plastic waste material causes has become a thorny difficult problem in the Chinese environmental protection cause; plastic working is as an industry, must consider the recycling problem after the institute's product of producing use.
Plastic-wood material arises at the historic moment thus, it is to reclaim plastics, agronomic crop fibre, " three surplus things " is raw material in the wood working, not only meets the performance requriements of Wood plastic composite, can be recycled simultaneously, improved the rate of recovery of plastics, having reduced plastics is the potential hazard of environment, has reduced manufacturing cost, improve to reclaim the added value of resource, utilize comprehensive utilization of resources and economize on resources.To protecting forest resources and ecotope, fully recycle resource and the important meaning of making a silk purse out of a sow's ear, can be used for industry or civilian goods such as pallet, building materials, great market capacity is arranged.
External at home, moulding wood development is extrusion moulding than product faster, is extruded quantitative limitation, and the product overwhelming majority is long-pending plate and a bar of leptoprosopy, and moulding wood simultaneously, to melt extrude system viscosity big, and expressing technique is poor, and the energy consumption height is difficult to form slick surface.As Chinese patent CN1786076A, open day is the preparation method who disclosed a kind of plastic-wood material on June 14th, 2006. the laminate structure mineral are pulverized, added coupling agent, make coupling laminate structure mineral powder; Wood powder is added coupling agent while stirring, make the coupling wood powder; With compound wood powder and the plastics that make, auxiliary agent is wanted to mix, and extrudes the wooden compound PP Pipe Compound of moulding promptly in forcing machine, and machine-shaping gets product; Chinese patent CN1912299A, open day is on February 14th, 2007, discloses a kind of plastic wood sheet and preparation method, it is combined into depleted plastics and agronomic crop fibre the novel material of a kind of green, environmental protection.The mechanical property of existing Wood plastic composite, heat-resisting, weathering resistance etc. wait to improve.At these problems, the Wood plastic composite that development research is new has application and vast market prospect widely.
Summary of the invention
In order to overcome above defective, the technical problem to be solved in the present invention is: propose a kind of Wood plastic composite and preparation method, it becomes a kind of matrix material with 100% advantage of recycling with the depleted plastics with refuse reason fiber composite, cheap, smooth finish is good, simultaneously good combination properties such as mechanical property, heat-resisting, weathering resistance.
The technical solution adopted in the present invention is: a kind of Wood plastic composite is characterized in that this Wood plastic composite raw material forms proportioning and comprise: waste or used plastics 15-30 part, discarded physical fiber 70-85 part, lubricant 1-5 part, viscosity increaser 1-2 part, compatilizer 2-5 part, ageing-resistant dose of 1-3 part, fire retardant 5-10 part.
According to another preferred embodiment, a kind of Wood plastic composite comprises that further this Wood plastic composite raw material forms proportioning and comprise: waste or used plastics 25-30 part, discarded physical fiber 80-85 part, lubricant 4-5 part, viscosity increaser 1-2 part, compatilizer 3-5 part, ageing-resistant dose of 2-3 part, fire retardant 8-10 part.
According to another preferred embodiment, a kind of Wood plastic composite comprises that further this Wood plastic composite raw material forms proportioning and comprise: 28 parts of waste or used plastics, 84 parts of discarded physical fibers, 4.5 parts of lubricants, 1.5 parts of viscosity increasers, 4 parts, ageing-resistant dose 2.5 parts of compatilizers, 9 parts of fire retardants.
According to another preferred embodiment, a kind of Wood plastic composite comprises that further described waste or used plastics is one or more mixing in polyvinyl chloride, depleted polyethylene or the depleted polypropylene.
According to another preferred embodiment, a kind of Wood plastic composite comprises that further described discarded physical fiber is one or more in sawmilling, wood shavings, Pericarppium arachidis hypogaeae, the discarded wood powder.
According to another preferred embodiment, a kind of Wood plastic composite comprises that further described lubricant is one or more in paraffin, glycerine, hard ester acid or the calcium stearate.
According to another preferred embodiment, a kind of Wood plastic composite comprises that further described viscosity increaser is a dioctyl phthalate (DOP).
According to another preferred embodiment, a kind of Wood plastic composite comprises that further described compatilizer is one or more in stearic acid and the chlorinatedpolyethylene.
According to another preferred embodiment, a kind of Wood plastic composite further comprises one or more in described fire retardant bromo fire retardant or the hydrated aluminium fire retardant.
The invention also discloses a kind of preparation method of Wood plastic composite, this method comprises the steps:
(1) waste or used plastics is pulverized through film breaking machine, carried out oil removing and abatement processes then, drying, and then be ground into through pulverizer, make particle;
(2) discarded physical fiber is through the tablets press granulation, and 150 ℃ of oven dry 3h cross the 20-30 mesh sieve, get particle, and moisture controlled is at 1-3%;
(3) handled thing with step (1) and step (2) adds the mixer mixing, adds lubricant, viscosity increaser, compatilizer, ageing-resistant dose and fire retardant simultaneously, and mechanical stirring mixes;
(4) batch mixing being added extrusion machine extrudes;
(5) extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
The invention has the beneficial effects as follows: the present invention recycles the depleted plastics and becomes a kind of matrix material with 100% advantage of recycling with refuse reason fiber depleted plastics with refuse reason fiber composite, cheap, compare with existing plastic-wood material, it is good to have moulding processability, and energy consumption is low, and surface smoothness is good, the mechanical property height, woodiness touch is strong, and is heat-resisting, characteristics such as good combination property such as weathering resistance, matrix material provided by the invention in addition is owing to added fire retardant, oxygen index reaches 25-30%, can be used for material of construction, building template, industrial pallet etc., can be used for the finishing material of indoor and outdoor again, market outlook are wide, and economic benefit is obvious.
Description of drawings
Fig. 1 is the process flow sheet of the preferred embodiments of the present invention.
Embodiment
The present invention is further detailed explanation with preferred embodiment in conjunction with the accompanying drawings now.These accompanying drawings are the synoptic diagram of simplification, basic structure of the present invention only is described in a schematic way, so it only show the formation relevant with the present invention.
Embodiment 1
The waste vinylene chloride plastic of 15kg, discarded sawmilling wood powder fiber, 1kg paraffin, 1kg dioctyl phthalate (DOP), 2kg stearic acid, 1kg titanium dioxide and the 5kg bromo fire retardant of 70kg.
The waste vinylene chloride plastic of 15kg is pulverized through film breaking machine, carried out oil removing and abatement processes then, drying, and then be ground into through pulverizer, make particle; Through the tablets press granulation, 150 ℃ of oven dry 3h cross the 20-30 mesh sieve with the discarded sawmilling wood powder fiber of 70kg, particle, moisture controlled is at 1-3%; Waste vinylene chloride plastic particle and discarded sawmilling wood powder fiber grain are added the mixer mixing, add 1kg paraffin simultaneously, the 1kg dioctyl phthalate (DOP), the 2kg stearic acid, 1kg titanium dioxide and 5kg bromo fire retardant, mechanical stirring mixes; Batch mixing is added extrusion machine to be extruded; Extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
Embodiment 2
The waste polyethylene plastics of 30kg, the discarded wood shavings wood powder fiber of 150kg, the hard ester acid of 3kg, 3kg dioctyl phthalate (DOP), 5kg stearic acid, 4kg titanium dioxide and 15kg bromo fire retardant.
The waste polyethylene plastics of 30kg are pulverized through film breaking machine, carried out oil removing and abatement processes then, drying, and then be ground into through pulverizer, make particle; Through the tablets press granulation, 150 ℃ of oven dry 3h cross the 20-30 mesh sieve with the discarded wood shavings wood powder fiber of 150kg, particle, moisture controlled is at 1-3%; Waste polyethylene plastic grain and discarded wood shavings wood powder fiber grain are added the mixer mixing, add the hard ester acid of 3kg simultaneously, the 3kg dioctyl phthalate (DOP), the 5kg stearic acid, 4kg titanium dioxide and 15kg bromo fire retardant, mechanical stirring mixes; Batch mixing is added extrusion machine to be extruded; Extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
Embodiment 3
The waste polypropylene plastic of 50kg, the discarded Pericarppium arachidis hypogaeae fiber of 165kg, 9kg calcium stearate, 4kg dioctyl phthalate (DOP), 8kg chlorinatedpolyethylene, 5kg titanium dioxide and 18kg bromo fire retardant.
The waste polypropylene plastic of 50kg is pulverized through film breaking machine, carried out oil removing and abatement processes then, drying, and then be ground into through pulverizer, make particle; Through the tablets press granulation, 150 ℃ of oven dry 3h cross the 20-30 mesh sieve with the discarded Pericarppium arachidis hypogaeae fiber of 165kg, particle, moisture controlled is at 1-3%; Waste polypropylene plastic particle and discarded Pericarppium arachidis hypogaeae fiber grain are added the mixer mixing, add the 9kg calcium stearate simultaneously, the 4kg dioctyl phthalate (DOP), the 8kg chlorinatedpolyethylene, 5kg titanium dioxide and 18kg bromo fire retardant, mechanical stirring mixes; Batch mixing is added extrusion machine to be extruded; Extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
Embodiment 4
The waste polypropylene plastic of 100kg, the discarded wood powder fiber of 320kg, 19kg paraffin, 7kg dioctyl phthalate (DOP), 18kg chlorinatedpolyethylene, 11kg titanium dioxide and 36kg bromo fire retardant.
The waste polypropylene plastic of 100kg is pulverized through film breaking machine, carried out oil removing and abatement processes then, drying, and then be ground into through pulverizer, make particle; Through the tablets press granulation, 150 ℃ of oven dry 3h cross the 20-30 mesh sieve with the discarded wood powder fiber of 320kg, particle, moisture controlled is at 1-3%; Waste polypropylene plastic particle and discarded wood powder fiber grain are added the mixer mixing, add 19kg paraffin simultaneously, the 7kg dioctyl phthalate (DOP), the 18kg chlorinatedpolyethylene, 11kg titanium dioxide and 36kg bromo fire retardant, mechanical stirring mixes; Batch mixing is added extrusion machine to be extruded; Extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
Embodiment 5
The waste polyethylene plastics of 140kg, the discarded wood powder fiber of 420kg, 22.5kg paraffin, 7.5kg dioctyl phthalate (DOP), 20kg chlorinatedpolyethylene, 12.5kg titanium dioxide and 45kg bromo fire retardant.
The waste polyethylene plastics of 140kg are pulverized through film breaking machine, carried out oil removing and abatement processes then, drying, and then be ground into through pulverizer, make particle; Through the tablets press granulation, 150 ℃ of oven dry 3h cross the 20-30 mesh sieve with the discarded wood powder fiber of 420kg, particle, moisture controlled is at 1-3%; Waste polyethylene plastic grain and discarded wood powder fiber grain are added the mixer mixing, add 22.5kg paraffin simultaneously, the 7.5kg dioctyl phthalate (DOP), the 20kg chlorinatedpolyethylene, 12.5kg titanium dioxide and 45kg bromo fire retardant, mechanical stirring mixes; Batch mixing is added extrusion machine to be extruded; Extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must determine its technical scope according to the claim scope.

Claims (10)

1. Wood plastic composite is characterized in that this Wood plastic composite raw material forms proportioning and comprise: waste or used plastics 15-30 part, discarded physical fiber 70-85 part, lubricant 1-5 part, viscosity increaser 1-2 part, compatilizer 2-5 part, ageing-resistant dose of 1-3 part, fire retardant 5-10 part.
2. a kind of Wood plastic composite according to claim 1 is characterized in that this Wood plastic composite raw material forms proportioning and comprise: waste or used plastics 25-30 part, discarded physical fiber 80-85 part, lubricant 4-5 part, viscosity increaser 1-2 part, compatilizer 3-5 part, ageing-resistant dose of 2-3 part, fire retardant 8-10 part.
3. a kind of Wood plastic composite according to claim 1 is characterized in that this Wood plastic composite raw material composition proportioning comprises: 28 parts of waste or used plastics, 84 parts of discarded physical fibers, 4.5 parts of lubricants, 1.5 parts of viscosity increasers, 4 parts, ageing-resistant dose 2.5 parts of compatilizers, 9 parts of fire retardants.
4. a kind of Wood plastic composite according to claim 1 is characterized in that described waste or used plastics is one or more mixing in depleted polyvinyl chloride, depleted polyethylene or the depleted polypropylene.
5. a kind of Wood plastic composite according to claim 1 is characterized in that described discarded physical fiber is one or more in sawmilling, wood shavings, Pericarppium arachidis hypogaeae, the discarded wood powder.
6. a kind of Wood plastic composite according to claim 1 is characterized in that described lubricant is one or more in paraffin, glycerine, hard ester acid or the calcium stearate.
7. a kind of Wood plastic composite according to claim 1 is characterized in that described viscosity increaser is a dioctyl phthalate (DOP).
8. a kind of Wood plastic composite according to claim 1 is characterized in that described compatilizer is one or more in stearic acid and the chlorinatedpolyethylene.
9. a kind of Wood plastic composite according to claim 1 is characterized in that in described fire retardant bromo fire retardant or the hydrated aluminium fire retardant one or more.
10. the preparation method of a Wood plastic composite is characterized in that this method comprises the steps:
(1) waste or used plastics is pulverized through film breaking machine, carried out oil removing and abatement processes, separate, drying, and then be ground into through pulverizer, make particle;
(2) discarded physical fiber is through the tablets press granulation, and 150 ℃ of oven dry 3h cross the 20-30 mesh sieve, get particle, and moisture controlled is at 1-3%;
(3) handled thing with step (1) and step (2) adds the mixer mixing, adds lubricant, viscosity increaser, compatilizer, ageing-resistant dose and fire retardant simultaneously, and mechanical stirring mixes;
(4) batch mixing being added extrusion machine extrudes;
(5) extrudate is put into metal die, extrusion forming, moulding pressure is 10~15MPa, the dwell time is 3~5 minutes, cooling die, die sinking gets composite finished product.
CN2010101963446A 2010-06-09 2010-06-09 Plastic wood composite material and preparation method Pending CN101955676A (en)