CN105666953A - 一种聚芳噁二唑纤维纸蜂窝 - Google Patents

一种聚芳噁二唑纤维纸蜂窝 Download PDF

Info

Publication number
CN105666953A
CN105666953A CN201610132731.0A CN201610132731A CN105666953A CN 105666953 A CN105666953 A CN 105666953A CN 201610132731 A CN201610132731 A CN 201610132731A CN 105666953 A CN105666953 A CN 105666953A
Authority
CN
China
Prior art keywords
honeycomb
poly
fibrous paper
virtue diazole
diazole
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610132731.0A
Other languages
English (en)
Inventor
隋广忠
孙达
刘玉
杨虹
王金明
马春花
刘海龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU ARAMICORE COMPOSITE CO Ltd
Original Assignee
SUZHOU ARAMICORE COMPOSITE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU ARAMICORE COMPOSITE CO Ltd filed Critical SUZHOU ARAMICORE COMPOSITE CO Ltd
Priority to CN201610132731.0A priority Critical patent/CN105666953A/zh
Publication of CN105666953A publication Critical patent/CN105666953A/zh
Pending legal-status Critical Current

Abstract

一种聚芳噁二唑纤维纸蜂窝，所述聚芳噁二唑纤维纸蜂窝由聚芳噁二唑纤维纸经涂胶、叠层、利用热压机热压，制成蜂窝叠块；然后将所述蜂窝叠块通过拉伸机拉伸成蜂窝孔格后，在烘箱中高温定型制成白蜂窝块；再将所述白蜂窝块在浸胶机中进行浸胶、固化后即得聚芳噁二唑纤维纸蜂窝。本发明制得的聚芳噁二唑纤维纸蜂窝的力学性能比芳纶纸蜂窝高，密度相近，与芳纶纸蜂窝相比较，在耐热性、尺寸稳定性，有更高的优越性。

Description

一种聚芳噁二唑纤维纸蜂窝
技术领域
本发明涉及一种聚芳噁二唑纤维纸蜂窝，属于新材料技术领域。
背景技术
纸蜂窝产业是近年来被人们认可的节能环保、低碳经济的新兴产业、朝阳产业。目前在航空航天领域里最常用的是芳纶纸蜂窝，芳纶纸蜂窝的最高使用温度不超过200℃，这使得成品蜂窝芯的耐高温性有限，在某些特殊部位无法使用。此外，芳纶的结构特性使得芳纶具有易吸湿变形等特性，影响蜂窝的使用领域。因此，有必要寻找其他材料的纤维纸制品以替代芳纶纸。
聚芳噁二唑纤维（芳香族聚-1,3,4-噁二唑纤维）分子链中苯环和噁二唑环交替排列，具有优异的耐高温性能、阻燃性能和尺寸稳定性，耐温等级为250℃，在300℃条件下也可以短期使用，瞬间耐温可以达到400℃以上，玻璃化转变温度在440℃以上，极限氧指数在30以上，燃烧时不产生溶滴，少烟，无毒。该纤维具有异常优异的高温尺寸稳定性，250℃下的热收缩率仅为0.6%，300℃下的热收缩率也在1%以内。
发明内容
本发明目的是提供一种聚芳噁二唑纤维纸蜂窝。
为达到上述目的，本发明采用的技术方案是：一种聚芳噁二唑纤维纸蜂窝，所述聚芳噁二唑纤维纸蜂窝由聚芳噁二唑纤维纸经涂胶、叠层、利用热压机热压，制成蜂窝叠块；然后将所述蜂窝叠块通过拉伸机拉伸成蜂窝孔格后，在烘箱中高温定型制成白蜂窝块；再将所述白蜂窝块在浸胶机中进行浸胶、固化后即得聚芳噁二唑纤维纸蜂窝。
优选的技术方案为：所述浸胶使用的浸胶液由聚酰亚胺树脂和酚醛树脂按照5:1~2的体积比例构成。
优选的技术方案为：所述聚芳噁二唑纤维纸的厚度为35~200微米。
优选的技术方案为：所述固化后得到的聚芳噁二唑纤维纸蜂窝的密度20-144kg/m3。
优选的技术方案为：所述蜂窝孔格为正六边形或矩形。
优选的技术方案为：所述聚芳噁二唑纤维纸由聚芳噁二唑纤维经过造纸工艺制得聚芳噁二唑纤维纸。
优选的技术方案为：所述造纸工艺使用的纸浆中含有至少60%体积分数的聚芳噁二唑纤维。
优选的技术方案为：所述聚芳噁二唑纤维的算术平均长度大于或等于0.5毫米。
由于上述技术方案运用，本发明与现有技术相比具有下列优点和效果：
1、本发明制得的聚芳噁二唑纤维纸蜂窝的力学性能比芳纶纸蜂窝高，密度相近，与芳纶纸蜂窝相比较，在耐热性、尺寸稳定性，有更高的优越性。
2、本发明使用的聚酰亚胺树脂赋予纸蜂窝高强度、低吸水率、耐水解、耐辐射、优异绝缘性及耐热氧老化稳定性等特性。
具体实施方式
下面结合实施例对本发明作进一步描述：
实施例：一种聚芳噁二唑纤维纸蜂窝
一种聚芳噁二唑纤维纸蜂窝，所述聚芳噁二唑纤维纸蜂窝由聚芳噁二唑纤维纸经涂胶、叠层、利用热压机热压，制成蜂窝叠块；然后将所述蜂窝叠块通过拉伸机拉伸成蜂窝孔格后，在烘箱中高温定型制成白蜂窝块；再将所述白蜂窝块在浸胶机中进行浸胶、固化后即得聚芳噁二唑纤维纸蜂窝。
优选的实施方式为：所述浸胶使用的浸胶液由聚酰亚胺树脂和酚醛树脂按照5:1~2的体积比例构成。
优选的实施方式为：所述聚芳噁二唑纤维纸的厚度为50微米。
优选的实施方式为：所述固化后得到的聚芳噁二唑纤维纸蜂窝的密度30kg/m3。
优选的实施方式为：所述蜂窝孔格为正六边形或矩形。
优选的实施方式为：所述聚芳噁二唑纤维纸由聚芳噁二唑纤维经过造纸工艺制得聚芳噁二唑纤维纸。
优选的实施方式为：所述造纸工艺使用的纸浆中含有60%体积分数的聚芳噁二唑纤维。
优选的实施方式为：所述聚芳噁二唑纤维的算术平均长度为0.5毫米。
本发明采用聚芳噁二唑纤维制成聚芳噁二唑纤维纸，能够有效保持纤维本身的优异性能，用该类特种纸制成的蜂窝芯能够在保证强度的同时大大降低组件的重量。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。

Claims (8)

1.一种聚芳噁二唑纤维纸蜂窝，其特征在于：所述聚芳噁二唑纤维纸蜂窝由聚芳噁二唑纤维纸经涂胶、叠层、利用热压机热压，制成蜂窝叠块；然后将所述蜂窝叠块通过拉伸机拉伸成蜂窝孔格后，在烘箱中高温定型制成白蜂窝块；再将所述白蜂窝块在浸胶机中进行浸胶、固化后即得聚芳噁二唑纤维纸蜂窝。
2.根据权利要求1所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述浸胶使用的浸胶液由聚酰亚胺树脂和酚醛树脂按照5:1~2的体积比例构成。
3.根据权利要求1所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述聚芳噁二唑纤维纸的厚度为35~200微米。
4.根据权利要求1所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述固化后得到的聚芳噁二唑纤维纸蜂窝的密度20-144kg/m3。
5.根据权利要求1所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述蜂窝孔格为正六边形或矩形。
6.根据权利要求1所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述聚芳噁二唑纤维纸由聚芳噁二唑纤维经过造纸工艺制得聚芳噁二唑纤维纸。
7.根据权利要求6所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述造纸工艺使用的纸浆中含有至少60%体积分数的聚芳噁二唑纤维。
8.根据权利要求6所述的聚芳噁二唑纤维纸蜂窝，其特征在于：所述聚芳噁二唑纤维的算术平均长度大于或等于0.5毫米。
CN201610132731.0A 2016-03-10 2016-03-10 一种聚芳噁二唑纤维纸蜂窝 Pending CN105666953A (zh)