CN105666309B - Hard alloy workpiece method for fine finishing - Google Patents

Hard alloy workpiece method for fine finishing Download PDF

Info

Publication number
CN105666309B
CN105666309B CN201610060861.8A CN201610060861A CN105666309B CN 105666309 B CN105666309 B CN 105666309B CN 201610060861 A CN201610060861 A CN 201610060861A CN 105666309 B CN105666309 B CN 105666309B
Authority
CN
China
Prior art keywords
workpiece
spreading
grinding
ground
hard alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610060861.8A
Other languages
Chinese (zh)
Other versions
CN105666309A (en
Inventor
唐振荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinghua Jinpeng Alloy Steel Co.,Ltd.
Original Assignee
LIUZHOU ANLONG MACHINERY EQUIPMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU ANLONG MACHINERY EQUIPMENT CO Ltd filed Critical LIUZHOU ANLONG MACHINERY EQUIPMENT CO Ltd
Priority to CN201610060861.8A priority Critical patent/CN105666309B/en
Publication of CN105666309A publication Critical patent/CN105666309A/en
Application granted granted Critical
Publication of CN105666309B publication Critical patent/CN105666309B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of hard alloy workpiece method for fine finishing, it is related to hard alloy workpiece processing technique field;The grinding agent that spreading is mixed into by kerosene and F180 boron carbides on lapping apparatus, workpiece pressurization is ground;The grinding agent that spreading is mixed into by kerosene and F150 boron carbides on lapping apparatus, the workpiece pressurization after step A processing is ground;The bortz powder abrasive pastes of W1.5~W2.5 on embedding good husky grinding tool on spreading by dilution, to workpiece pressure grinding;The bortz powder abrasive pastes of W1 on embedding good husky grinding tool on spreading by dilution, to workpiece pressure grinding;Be packed with the lap tool of polisher lapper granularity be W1~W1.5 sand grains, and on spreading W0.5~W1 bortz powder abrasive pastes, to step D process after workpiece be ground.The present invention can solve low production efficiency during existing hard alloy workpiece finishing, it is impossible to the problem of adapting to the needs produced in enormous quantities.

Description

Hard alloy workpiece method for fine finishing
Technical field
It is especially a kind of that hard alloy workpiece is finished the present invention relates to hard alloy workpiece processing technique field Method.
Background technology
Because Hardmetal materials are harder, so when being ground to hard alloy workpiece, grounds travel(Cream)Selection It is very crucial, more commonly used at present is using material of the boron carbide abrasive material as thick waste attrition process, but such processing There is low production efficiency for method, it is impossible to adapts to the needs produced in enormous quantities.
The content of the invention
It is an object of the invention to provide a kind of hard alloy workpiece method for fine finishing, and it can solve existing hard alloy Low production efficiency when workpiece finishes, it is impossible to the problem of adapting to the needs produced in enormous quantities.
In order to solve the above problems, the technical solution adopted by the present invention is:This hard alloy workpiece method for fine finishing, bag Include following steps:
A, the grinding agent that spreading is mixed into by kerosene and F180 boron carbides on lapping apparatus, workpiece pressurization is ground Mill;This step will be the allowance that next step reserves 0.07~0.1 millimeter;
B, the grinding agent that spreading is mixed into by kerosene and F150 boron carbides on lapping apparatus, to after step A processing Workpiece pressurization is ground;This step will be the allowance that next step reserves 0.03~0.05 millimeter;
C, the bortz powder abrasive pastes of W1.5~W2.5 on embedding good husky grinding tool on spreading by dilution, by step C Workpiece after processing is cleaned, to the workpiece pressure grinding after cleaning;This step to be next step reserve 0.015~ 0.003 millimeter of allowance;
D, the bortz powder abrasive pastes of the W1 on embedding good husky grinding tool on spreading by dilution, after step C is processed Workpiece is cleaned, to the workpiece pressure grinding after cleaning;This step will be that next step is reserved more than 1~1.5 micron of processing Amount;
E, be packed with the lap tool of polisher lapper granularity be W1~W1.5 sand grains, and on spreading W0.5~W1 Buddha's warrior attendant Stone flour abrasive pastes, the workpiece after being processed to step D are ground.
By adopting the above-described technical solution, the present invention is compared with prior art, have an advantageous effect in that:
After the present invention is using boron carbide waste progress preprocessing thick to workpiece, then using bortz powder to workpiece progress finishing Work, the machining accuracy of workpiece can be improved, production efficiency is high, adapts to the needs produced in enormous quantities.
Embodiment
With reference to embodiment, the invention will be further described:
This hard alloy workpiece method for fine finishing, comprises the following steps:
A, the grinding agent that spreading is mixed into by kerosene and F180 boron carbides on lapping apparatus, workpiece pressurization is ground Mill;This step will be the allowance that next step reserves 0.07~0.1 millimeter;
B, the grinding agent that spreading is mixed into by kerosene and F150 boron carbides on lapping apparatus, to after step A processing Workpiece pressurization is ground;This step will be the allowance that next step reserves 0.03~0.05 millimeter;
C, the bortz powder abrasive pastes of W1.5~W2.5 on embedding good husky grinding tool on spreading by dilution, by step C Workpiece after processing is cleaned, to the workpiece pressure grinding after cleaning;This step to be next step reserve 0.015~ 0.003 millimeter of allowance;By the processing of this step, the precision and surface roughness of the geometry of workpiece obtain aobvious The raising of work;
D, the bortz powder abrasive pastes of the W1 on embedding good husky grinding tool on spreading by dilution, after step C is processed Workpiece is cleaned, to the workpiece pressure grinding after cleaning;This step will be that next step is reserved more than 1~1.5 micron of processing Amount;
E, be packed with the lap tool of polisher lapper granularity be W1~W1.5 sand grains, and on spreading W0.5~W1 Buddha's warrior attendant Stone flour abrasive pastes, the workpiece after being processed to step D are ground;After the processing of this step, the surface roughness of workpiece is reachable To 0.8 grade.

Claims (1)

  1. A kind of 1. hard alloy workpiece method for fine finishing, it is characterised in that:Comprise the following steps:
    A, the grinding agent that spreading is mixed into by kerosene and F180 boron carbides on lapping apparatus, workpiece pressurization is ground;This Step will be the allowance that next step reserves 0.07~0.1 millimeter;
    B, the grinding agent that spreading is mixed into by kerosene and F150 boron carbides on lapping apparatus, to the workpiece after step A processing Pressurization is ground;This step will be the allowance that next step reserves 0.03~0.05 millimeter;
    C, the bortz powder abrasive pastes of W1.5~W2.5 on embedding good husky grinding tool on spreading by dilution, step B is processed Workpiece afterwards is cleaned, to the workpiece pressure grinding after cleaning;This step will be that next step reserves 0.015~0.003 milli The allowance of rice;
    D, the bortz powder abrasive pastes of the W1 on embedding good husky grinding tool on spreading by dilution, the workpiece after step C is processed Clean, to the workpiece pressure grinding after cleaning;This step will be the allowance that next step reserves 1~1.5 micron;
    E, be packed with the lap tool of polisher lapper granularity be W1~W1.5 sand grains, and on spreading W0.5~W1 bortz powder Abrasive pastes, the workpiece after being processed to step D are ground.
CN201610060861.8A 2016-01-29 2016-01-29 Hard alloy workpiece method for fine finishing Active CN105666309B (en)