CN105650158A - 有优良导热性的含复合晶须的颗粒料及其制备方法 - Google Patents
有优良导热性的含复合晶须的颗粒料及其制备方法 Download PDFInfo
- Publication number
- CN105650158A CN105650158A CN201510719831.9A CN201510719831A CN105650158A CN 105650158 A CN105650158 A CN 105650158A CN 201510719831 A CN201510719831 A CN 201510719831A CN 105650158 A CN105650158 A CN 105650158A
- Authority
- CN
- China
- Prior art keywords
- weight part
- weight
- parts
- particles
- containing composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种有优良导热性的含复合晶须的颗粒料及其制备方法。其方法是：将硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50～60℃；熔炼时间为20～30min；塑化粉碎成粒径为8-20目的颗粒，即得本发明产品。使用时将本发明以一定比例掺入刹车片的摩擦片，可有效降低摩擦片的硬度和密实度，可使摩擦片在工作时吸收噪音，提高汽车稳定性、防止落灰，还具备环保、优良的导热性能等优点。
Description
技术领域
本发明涉及一种汽车刹车片中摩擦片的材料及其制备方法，特别是一种有优良导热性的含复合晶须的颗粒料及其制备方法。
背景技术
制动系统是汽车上最重要的安全系统之一，而刹车片是整个制动系统中重要的部件，对汽车制动性能的好坏起决定性作用。刹车片一般由钢板、粘接隔热层和摩擦片构成，刹车时摩擦片被挤压在刹车盘上产生摩擦，将汽车的动能转化为热能，制动时的温度会上升到300～400℃。
现有的刹车片中摩擦片的材料密度普遍较大，可达到2.0-2.3g/cm3、洛氏硬度可达80-120HRB，使用过程中与刹车盘接触时容易产生噪音，并磨损刹车盘；且用于汽车刹车片的摩擦片骨架材料一般使用石棉、钢棉、海泡石纤维、复合矿物棉等，这些配方存在性能不稳定、不环保、落灰等问题；至关重要的，摩擦片中的导热材料其导热性能的好坏直接影响刹车片的质量，并且还会影响刹车片在高温时的制动效果。现有摩擦片中普遍采用的导热材料导热性能较差，在刹车片生产过程中，具体说是在热压过程中摩擦片容易产生局部热膨胀现象，引起摩擦片起泡、变形，降低了刹车片的良品率；在刹车片工作过程中，具体说是在连续刹车的情况下，摩擦片温度迅速上升，容易产生局部热膨胀现象，引起摩擦片起泡、变形，从而与刹车盘抱死。
发明内容
本发明的目的之一是克服现有技术的上述不足，而提供一种有优良导热性的含复合晶须的颗粒料。
实现本发明上述发明目的的技术方案是：一种有优良导热性的含复合晶须的颗粒料，其是采用如下方法制备而成的：
配方中包括：硅藻土10-15重量份、六钛酸钾晶须10-15重量份、碳纤维10-15重量份、F826胶黏剂8-15重量份、纳凯夫纤维7-12重量份、球状白蛭石7-12重量份、硅酸铝空心球7-12重量份、泡沫铁粉5-10重量份、鳞片石墨4-7重量份、丁晴胶粉1-2重量份；
其制备工艺步骤如下：
第一步：按材料含有的组份及各自的重量份数进行配料；
第二步：将原料混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50-60℃；熔炼时间为20-30min；
第三步：将塑化后的材料粉碎成粒径为8-20目的颗粒。
本发明进一步的技术方案是：
配方中包括：硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份。
本发明进一步的技术方案也可以是：
配方中包括：硅藻土15重量份、六钛酸钾晶须15重量份、碳纤维15重量份、F826胶黏剂15重量份、纳凯夫纤维12重量份、球状白蛭石12重量份、硅酸铝空心球12重量份、泡沫铁粉10重量份、鳞片石墨7重量份、丁晴胶粉2重量份。
本发明的目的之二是克服现有技术的上述不足，而提供一种有优良导热性的含复合晶须的颗粒料的制备方法。
实现本发明上述发明目的的技术方案是：一种有优良导热性的含复合晶须的颗粒料的制备方法：
配方中包括：硅藻土10-15重量份、六钛酸钾晶须10-15重量份、碳纤维10-15重量份、F826胶黏剂8-15重量份、纳凯夫纤维7-12重量份、球状白蛭石7-12重量份、硅酸铝空心球7-12重量份、泡沫铁粉5-10重量份、鳞片石墨4-7重量份、丁晴胶粉1-2重量份；
其制备工艺步骤如下：
第一步：按材料含有的组份及各自的重量份数进行配料；
第二步：将原料混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50-60℃；熔炼时间为20-30min；
第三步：将塑化后的材料粉碎成粒径为8-20目的颗粒。
本发明进一步的技术方案是：
配方中包括：硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份。
本发明进一步的技术方案也可以是：
配方中包括：硅藻土15重量份、六钛酸钾晶须15重量份、碳纤维15重量份、F826胶黏剂15重量份、纳凯夫纤维12重量份、球状白蛭石12重量份、硅酸铝空心球12重量份、泡沫铁粉10重量份、鳞片石墨7重量份、丁晴胶粉2重量份。
本发明与现有技术相比具有如下优点：
使用时将本发明以一定比例掺入刹车片的摩擦片，可有效降低摩擦片的硬度和密实度，可使摩擦片在工作时吸收噪音，提高汽车稳定性、防止落灰，还具备环保、优良的导热性能等优点。
以下通过具体实施例对本发明作进一步描述。
具体实施方式
实施例1：
一种有优良导热性的含复合晶须的颗粒料，其是采用如下方法制备而成的：
配方中包括：硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份；
其制备工艺步骤如下：
第一步：按材料含有的组份及各自的重量份数进行配料；
第二步：将原料混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50～60℃；熔炼时间为20～30min；
第三步：将塑化后的材料粉碎成粒径为8-20目的颗粒。
实施例2：
一种有优良导热性的含复合晶须的颗粒料，其是采用如下方法制备而成的：
配方中包括：硅藻土15重量份、六钛酸钾晶须15重量份、碳纤维15重量份、F826胶黏剂15重量份、纳凯夫纤维12重量份、球状白蛭石12重量份、硅酸铝空心球12重量份、泡沫铁粉10重量份、鳞片石墨7重量份、丁晴胶粉2重量份；其制备工艺与实施例1相同。
实施例3：
一种有优良导热性的含复合晶须的颗粒料的制备方法，其配方中包括：硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份；
其制备工艺步骤如下：
第一步：按材料含有的组份及各自的重量份数进行配料；
第二步：将原料混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50～60℃；熔炼时间为20～30min；
第三步：将塑化后的材料粉碎成粒径为8-20目的颗粒。
实施例4：
一种有优良导热性的含复合晶须的颗粒料的制备方法，其配方中包括：硅藻土15重量份、六钛酸钾晶须15重量份、碳纤维15重量份、F826胶黏剂15重量份、纳凯夫纤维12重量份、球状白蛭石12重量份、硅酸铝空心球12重量份、泡沫铁粉10重量份、鳞片石墨7重量份、丁晴胶粉2重量份；其制备工艺与实施例3相同。
Claims (6)
1.一种有优良导热性的含复合晶须的颗粒料,其特征是采用如下方法制备而成的：
配方中包括有：硅藻土10-15重量份、六钛酸钾晶须10-15重量份、碳纤维10-15重量份、F826胶黏剂8-15重量份、纳凯夫纤维7-12重量份、球状白蛭石7-12重量份、硅酸铝空心球7-12重量份、泡沫铁粉5-10重量份、鳞片石墨4-7重量份、丁晴胶粉1-2重量份；
其制备工艺步骤如下：
第一步：按材料含有的组份及各自的重量份数进行配料；
第二步：将原料混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50-60℃；熔炼时间为20-30min；
第三步：将塑化后的材料粉碎成粒径为8-20目的颗粒。
2.如权利要求1所述的有优良导热性的含复合晶须的颗粒料，其特征是采用如下方法制备而成的：
配方中包括有：硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份。
3.如权利要求1所述的有优良导热性的含复合晶须的颗粒料，其特征是采用如下方法制备而成的：
配方中包括有：硅藻土15重量份、六钛酸钾晶须15重量份、碳纤维15重量份、F826胶黏剂15重量份、纳凯夫纤维12重量份、球状白蛭石12重量份、硅酸铝空心球12重量份、泡沫铁粉10重量份、鳞片石墨7重量份、丁晴胶粉2重量份。
4.一种有优良导热性的含复合晶须的颗粒料的制备方法，其特征是配方中包括有：硅藻土10-15重量份、六钛酸钾晶须10-15重量份、碳纤维10-15重量份、F826胶黏剂8-15重量份、纳凯夫纤维7-12重量份、球状白蛭石7-12重量份、硅酸铝空心球7-12重量份、泡沫铁粉5-10重量份、鳞片石墨4-7重量份、丁晴胶粉1-2重量份；
其制备工艺步骤如下：
第一步：按材料含有的组份及各自的重量份数进行配料；
第二步：将原料混合均匀，投入双辊橡胶开炼机进行熔炼，使原料熔融并塑化；辊筒表面温度为50-60℃；熔炼时间为20-30min；
第三步：将塑化后的材料粉碎成粒径为8-20目的颗粒。
5.如权利要求4所述的有优良导热性的含复合晶须的颗粒料的制备方法，其特征是配方中包括有：硅藻土10重量份、六钛酸钾晶须10重量份、碳纤维10重量份、F826胶黏剂8重量份、纳凯夫纤维7重量份、球状白蛭石7重量份、硅酸铝空心球7重量份、泡沫铁粉5重量份、鳞片石墨4重量份、丁晴胶粉1重量份。
6.如权利要求4所述的有优良导热性的含复合晶须的颗粒料的制备方法，其特征是配方中包括有：硅藻土15重量份、六钛酸钾晶须15重量份、碳纤维15重量份、F826胶黏剂15重量份、纳凯夫纤维12重量份、球状白蛭石12重量份、硅酸铝空心球12重量份、泡沫铁粉10重量份、鳞片石墨7重量份、丁晴胶粉2重量份。