CN105648437A - Wear-resisting processing method for metal product - Google Patents
Wear-resisting processing method for metal product Download PDFInfo
- Publication number
- CN105648437A CN105648437A CN201610055457.1A CN201610055457A CN105648437A CN 105648437 A CN105648437 A CN 105648437A CN 201610055457 A CN201610055457 A CN 201610055457A CN 105648437 A CN105648437 A CN 105648437A
- Authority
- CN
- China
- Prior art keywords
- metallic article
- metal product
- coating
- wear
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wear-resisting processing method for a metal product. The wear-resisting processing method includes the following technological steps that firstly, cleaning is conducted, wherein the metal product is soaked in a soap solution, and the surface of the metal product is thoroughly cleaned; secondly, surface flattening is conducted, wherein a chemical film coating method is used for coating the surface of the metal product with an environment-friendly metal layer, and then cleaning and airing are conducted; thirdly, coating is conducted, wherein a vacuum film coating method is used for coating the surface of the metal product with a film, and the surface of the coating film is coated with a wear-resisting agent; and fourthly, roasting is conducted, wherein the metal product coated with the wear-resisting agent is put into an oven, the roasted metal product is put into a cooling box to be cooled, and then the finished product can be obtained. The wear-resisting processing method has the beneficial effects that a coating is roasted, the metal product is processed, the phenomenon that the metal product is rusted can be effectively prevented, meanwhile, the performance of the metal product can be more stable in the use process, the smeared wear-resisting agent cannot pollute the environment, and the environment-friendly effect is achieved.
Description
Technical field
The present invention relates to a kind of processing method, particularly relate to the wear resistant processing method of a kind of metallic article.
Background technology
For attractive in appearanceization of metallic article in prior art, traditionally adopt electric plating method that the plated surface last layer of metallic article has the rete of aesthetic. Plating utilizes electrolysis principle to plate the process of other metal or alloy of a thin layer on metallic article exactly, it is the technique of the surface attachment layer of metal film utilizing electrolysis to make metal or other material thus playing and preventing corrosion, improves the effects such as wearability, electric conductivity, reflective and having improved aesthetic appearance.
But, metallic article is carried out coating by existing employing electro-plating method, for obtaining the coating of better quality, electroplating technology need to use the chemical materials of substantial amounts of different toxicity, such as, strong acid, highly basic, heavy metal, cyanide, organic additive etc., in electroplating process, above-mentioned poisonous chemical materials because of volatilization or disappears and the operation such as washes and be discharged in water body or atmospheric environment, and environment causes more serious pollution.
Therefore, for solving the problems referred to above, a kind of new technical scheme of special offer.
Summary of the invention
The present invention provides the wear resistant processing method of a kind of metallic article.
The technical solution used in the present invention is:
The wear resistant processing method of a kind of metallic article, comprises the following steps that:
A, cleaning step: now metallic article is dipped in soap liquation, then surface of metal product is cleaned up;
B, surfacing step: adopt electroless plating, at the plated surface environment protection metal layer of metallic article, be then carried out, dry;
C, plating steps: adopt Vacuum Coating method by the surface coating of metallic article, be coated with antiwear additive in coated surface;
D, baking procedure: put in baking oven by the metallic article coating anti-wear agent, put into the metallic article toasted in cooler bin and cool down, can obtain finished product.
Further, the baking temperature in described baking procedure is 140-160 DEG C, and the time is 5-10 minute.
Further, the thickness being coated with antiwear additive is 1-3mm.
The invention has the beneficial effects as follows: adopting coating baking, metallic article is processed, can effectively prevent the phenomenon that metallic article gets rusty, metallic article in use performance can be made more stable simultaneously, the antiwear additive smeared is free from environmental pollution, has environment protecting.
Detailed description of the invention
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment is only used for explaining the present invention, is not intended that the restriction to protection scope of the present invention.
Embodiment 1
The wear resistant processing method of a kind of metallic article, comprises the following steps that:
A, cleaning step: now metallic article is dipped in soap liquation, then surface of metal product is cleaned up;
B, surfacing step: adopt electroless plating, at the plated surface environment protection metal layer of metallic article, be then carried out, dry;
C, plating steps: adopt Vacuum Coating method by the surface coating of metallic article, be coated with antiwear additive in coated surface, and the thickness of coating antiwear additive is 1mm;
D, baking procedure: put in baking oven by the metallic article coating anti-wear agent, baking temperature is 140 DEG C, and the time is 5 minutes, is put in cooler bin by the metallic article toasted and cools down, can obtain finished product.
Embodiment 2
The wear resistant processing method of a kind of metallic article, comprises the following steps that:
A, cleaning step: now metallic article is dipped in soap liquation, then surface of metal product is cleaned up;
B, surfacing step: adopt electroless plating, at the plated surface environment protection metal layer of metallic article, be then carried out, dry;
C, plating steps: adopt Vacuum Coating method by the surface coating of metallic article, be coated with antiwear additive in coated surface, and the thickness of coating antiwear additive is 12mm;
D, baking procedure: put in baking oven by the metallic article coating anti-wear agent, baking temperature is 150 DEG C, and the time is 7 minutes, is put in cooler bin by the metallic article toasted and cools down, can obtain finished product.
Embodiment 3
The wear resistant processing method of a kind of metallic article, comprises the following steps that:
A, cleaning step: now metallic article is dipped in soap liquation, then surface of metal product is cleaned up;
B, surfacing step: adopt electroless plating, at the plated surface environment protection metal layer of metallic article, be then carried out, dry;
C, plating steps: adopt Vacuum Coating method by the surface coating of metallic article, be coated with antiwear additive in coated surface, and the thickness of coating antiwear additive is 3mm;
D, baking procedure: put in baking oven by the metallic article coating anti-wear agent, baking temperature is 160 DEG C, and the time is 10 minutes, is put in cooler bin by the metallic article toasted and cools down, can obtain finished product.
The invention has the beneficial effects as follows: adopting coating baking, metallic article is processed, can effectively prevent the phenomenon that metallic article gets rusty, metallic article in use performance can be made more stable simultaneously, the antiwear additive smeared is free from environmental pollution, has environment protecting.
The above, be only presently preferred embodiments of the present invention, is not the restriction that the present invention makees any other form, and any amendment that the technical spirit of the foundation present invention is made or equivalent variations, still fall within present invention scope required for protection.
Claims (3)
1. the wear resistant processing method of a metallic article, it is characterised in that: comprise the following steps that:
A, cleaning step: now metallic article is dipped in soap liquation, then surface of metal product is cleaned up;
B, surfacing step: adopt electroless plating, at the plated surface environment protection metal layer of metallic article, be then carried out, dry;
C, plating steps: adopt Vacuum Coating method by the surface coating of metallic article, be coated with antiwear additive in coated surface;
D, baking procedure: put in baking oven by the metallic article coating anti-wear agent, put into the metallic article toasted in cooler bin and cool down, can obtain finished product.
2. the wear resistant processing method of a kind of metallic article according to claim 1, it is characterised in that: the baking temperature in described baking procedure is 140-160 DEG C, and the time is 5-10 minute.
3. the wear resistant processing method of a kind of metallic article according to claim 1, it is characterised in that: the thickness of coating antiwear additive is 1-3mm.