CN105643216A - 静态混合器加工工艺 - Google Patents

静态混合器加工工艺 Download PDF

Info

Publication number
CN105643216A
CN105643216A CN201610204086.9A CN201610204086A CN105643216A CN 105643216 A CN105643216 A CN 105643216A CN 201610204086 A CN201610204086 A CN 201610204086A CN 105643216 A CN105643216 A CN 105643216A
Authority
CN
China
Prior art keywords
static mixer
processing technique
cooling
machining process
unit components
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610204086.9A
Other languages
English (en)
Other versions
CN105643216B (zh
Inventor
郁任磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Metal Containers Co Ltd Wuxi Liyuan
Original Assignee
Metal Containers Co Ltd Wuxi Liyuan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Metal Containers Co Ltd Wuxi Liyuan filed Critical Metal Containers Co Ltd Wuxi Liyuan
Priority to CN201610204086.9A priority Critical patent/CN105643216B/zh
Publication of CN105643216A publication Critical patent/CN105643216A/zh
Application granted granted Critical
Publication of CN105643216B publication Critical patent/CN105643216B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了静态混合器加工工艺，包括如下步骤：1)用数控机将原料制成单元组件，使单元组件的本体饱满一致；2)用点焊机焊接单元组件的中心，使其在螺旋轴方向上连接，形成内部组件；3)将内部组件卡接至圆筒状模具中；4)将模具中浇灌混合物，冷却凝固后取出，由车床加工，磨床精磨磨至所需尺寸，形成内部柱件，放入冷冻柜备用或液氮冷却；5)加热静态混合器的外管至温度220-270℃，通过液压或气压将内部柱件顶入管体内部，形成组合件；6)加热组合件，保持10-30分钟，待混合物融化；7)采用水冷隔绝空气，防止氧化，冷却2-3小时。本发明采用过盈配合装配混合器内管，使得内管与混合器外管实现紧密固定，使得产品混合效果充分均匀，提高产品质量。

Description

静态混合器加工工艺
技术领域
本发明涉及静态混合器领域，尤其设计静态混合器加工工艺。
背景技术
随着技术进入高速发展的时代，人们对产品的质量要求越来越高，而传统静态混合器的加工技术的滞后导致纺织机械“核心”部件的质量停滞不前，产品出现各种瑕疵。
一、传统的静态混合器采用的是修配工艺，这种工艺往往使原材料没有规律的混合，从而使得产品出现感观上的差异。
二、传统的静态混合器卡接不严密，制作工艺繁复，生产产品性能易产生缺陷。
发明内容
本发明针对现有技术的缺陷提供静态混合器加工工艺。
本发明为实现以上目的，采用如下方案：静态混合器加工工艺，包括如下步骤：
1)用数控机将原料制成单元组件，使单元组件的本体饱满一致；
2)用电焊机电焊单元组件的中心，使其在螺旋轴方向上连接，形成内部组件；
3)将内部组件卡接至圆筒状模具中；
4)将模具中浇灌混合物，冷却凝固后取出，由车床加工，磨床精磨磨至所需尺寸，形成内部柱件，放入冷冻柜备用；
5)加热静态混合器的外管至温度220-270℃，通过液压或气压将内部柱件顶入管体内部，形成组合件；
6)加热组合件，保持10-30分钟，待混合物融化；
7)采用水冷隔绝空气，防止氧化，冷却2-3小时。
优选的，所述步骤4)的混合物为锡液和铅液。
优选的，所述锡液和铅液的比例为锡液4份，铅液1份。
优选的，所述步骤5)的最佳温度为250℃。
优选的，所述步骤6)的最佳融化时间为20分钟。
本发明的有益效果：本发明采用过盈配合装配混合器内管，使得内管与混合器外管实现紧密固定，使得产品混合效果充分，提高产品质量。
具体实施方式
以下实施例用于说明本发明，但不用于限制本发明的范围。对本发明方法、步骤或条件所做的修改或替换，均属于本发明的保护范围。
实施例静态混合器加工工艺，包括如下步骤：
1)用数控机将原料制成单元组件，使单元组件的本体饱满一致；
2)用点焊机焊接单元组件的中心，使其在螺旋轴方向上连接，形成内部组件；
3)将内部组件卡接至圆筒状模具中；
4)将模具中浇灌混合物，冷却凝固后取出，由车床加工，磨床精磨磨至所需尺寸，形成内部柱件，放入冷冻柜备用；
5)加热静态混合器的外管至温度220-270℃，通过液压或气压将内部柱件顶入管体内部，形成组合件；
6)加热组合件，保持10-30分钟，待混合物融化；
7)采用水冷隔绝空气，防止氧化，冷却2-3小时。
所述步骤4)的混合物为锡液和铅液。
所述锡液和铅液的比例为锡液83％，铅液17％。
所述步骤5)的最佳温度为250℃。
所述步骤6)的最佳融化时间为20分钟。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (5)

1.静态混合器加工工艺，其特征在于，包括如下步骤：
1)用数控机将原料制成单元组件，使单元组件的本体饱满一致；
2)用点焊机焊接单元组件的中心，使其在螺旋轴方向上连接，形成内部组件；
3)将内部组件卡接至圆筒状模具中；
4)将模具中浇灌混合物，冷却凝固后取出，由车床加工，磨床精磨磨至所需尺寸，形成内部柱件，放入冷冻柜备用；
5)加热静态混合器的外管至温度220-270℃，通过液压或气压将内部柱件顶入管体内部，形成组合件；
6)加热组合件，保持10-30分钟，待混合物融化；
7)采用水冷隔绝空气，防止氧化，冷却2-3小时。
2.根据权利要求1所述的静态混合器加工工艺，其特征在于，所述步骤4)的混合物为锡液和铅液。
3.根据权利要求2所述的静态混合器加工工艺，其特征在于，所述锡液和铅液的比例为锡液4份，铅液1份。
4.根据权利要求1所述的静态混合器加工工艺，其特征在于，所述步骤5)的最佳温度为250℃。
5.根据权利要求1所述的静态混合器加工工艺，其特征在于，所述步骤6)的最佳融化时间为20分钟。
CN201610204086.9A 2016-04-02 2016-04-02 静态混合器加工工艺 Active CN105643216B (zh)