CN105641733A - Preparation method for compound antibacterial haemostatic wound dressing - Google Patents
Preparation method for compound antibacterial haemostatic wound dressing Download PDFInfo
- Publication number
- CN105641733A CN105641733A CN201511033800.4A CN201511033800A CN105641733A CN 105641733 A CN105641733 A CN 105641733A CN 201511033800 A CN201511033800 A CN 201511033800A CN 105641733 A CN105641733 A CN 105641733A
- Authority
- CN
- China
- Prior art keywords
- solution
- chitosan
- preparation
- chitosan solution
- carboxymethyl chitosan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method for a compound antibacterial haemostatic wound dressing. The preparation method comprises the following steps: preparing chitosan, carboxymethyl chitosan and sodium alginate serving as raw materials into a chitosan solution and a carboxymethyl chitosan solution; adding calcium chloride or an aldehyde cross-linking agent or a plant cross-linking agent and a povidone-iodine antibacterial agent into the chitosan solution or the carboxymethyl chitosan solution or a mixture of the chitosan solution and the carboxymethyl chitosan solution, and mixing uniformly; adding a mixed solution of sodium alginate, sodium hyaluronate and the like into a solution at a stage in which gel is not formed; coating the surface of a fiber water-absorbing cushion or a fiber non-woven fabric with the mixed solution, or placing the fiber water-absorbing cushion or the fiber non-woven fabric into the solution at the stage in which the gel is not formed for full soaking till saturation; performing freeze drying in vacuum to obtain a sponge-shaped solid. The preparation method has the beneficial effects that the antibacterial haemostatic wound dressing prepared according to the method is non-toxic, is free from a thermal source, is high in biocompatibility, and has the advantages of inhibiting growth of bacteria, preventing bacteria from entering a wound surface, promoting skin regeneration, accelerating healing, reducing scars and the like.
Description
Technical field:
The preparation method that the present invention relates to a kind of composite antibacterial bleeding-stopping dressing, belongs to medical antibacterial hemostasis technical field of medical instruments.
Background technology:
Antibacterial anti hemorrhagic is always up hospital surgical frequently problem, is also the difficult problem that is frequently encountered by of daily life. Medical dressing is that a class carries out the interim medical material covered for various wounds, wound surface, and it can make wound exempt from the impact of antibacterial infection and other foeign elements, plays the effect of protection wound, wound surface.
There is following requirement generally for wound dressing: (1) has the softness close with human body skin, when moistening, also can keep certain form and intensity; (2) moist environment of wound surface can be kept, have the ability absorbing wound exudate preferably, and have certain breathability; (3) dressing is nontoxic, the reaction that human body is not harmful to and stimulation and it is necessary to antibacterial can be stoped to enter wound surface in case causing superinfection, it is to avoid Wound contact particle and poisonous pollutant, without thermal source; (4) it is preferably formed with effects such as stopping blooding, relieve the pain, granulation growth and skin regeneration, healing acceleration can be promoted, reduce cicatrix; (5) excellent storage stability, it is desirable to have degradability, environment is not produced to pollute by garbage.
Chitin is the natural macromolecular material extracted the cell wall of the shell from the Crustacean such as shrimp, Eriocheir sinensis and bacterium, algae rudimentary plant, is be only second to cellulosic second largest biologically-derived resource in nature. Chitosan is the product of de-acetyl chitin, is unique alkaline polysaccharide in nature. In general, the N-acetyl group of chitin is sloughed more than 50% and is just properly termed as chitosan. Chitosan is a kind of high molecular polysaccharose substance of pure natural, and the toxicity research of chitosan shows, chitosan is substantially nontoxic, has good safety, good biocompatibility, it is possible to degraded and absorbed. Additionally, chitosan can also suppress various bacteria and the effect of fungus growth. Owing to having the physiologically active of uniqueness and excellence, chitosan application in wound dressing is increasingly becoming its focus in biomaterial is applied.
Calcium alginate is widely used as medical dressing, calcium alginate dressing is in that when wound fluid contacts, exchanged by ion, insoluble calcium alginate is made to form a kind of hydrogel after absorbing big quantity of fluid, there is provided a kind of moist environment for wound, and calcium alginate nonwoven is furnished with good hygroscopicity and hemostatic function.
Summary of the invention:
The preparation method that the present invention provides a kind of composite antibacterial bleeding-stopping dressing, antibacterial anti hemorrhagic dressing prepared by Using such method is nontoxic, and without thermal source, biocompatibility is high;There is bacteria growing inhibiting, stop antibacterial to enter wound surface, promote skin regeneration, healing acceleration, reduce the advantages such as cicatrix.
For reaching above-mentioned purpose, the technical solution used in the present invention is:
The preparation method of a kind of composite antibacterial bleeding-stopping dressing: with chitosan, carboxymethyl chitosan, sodium alginate for raw material, prepare chitosan solution and carboxymethyl chitosan solution. After chitosan solution or carboxymethyl chitosan solution or both solution are added calcium chloride or aldehyde crosslinking agent or plant extract cross-linking agent and betadine antiseptic mixing, the mixed solution of sodium alginate, hyaluronate sodium etc. is added at the solution not forming gel phase, coat fibrous absorbent pad or fabric nonwoven cloth surface, or fibrous absorbent pad or fabric nonwoven cloth be positioned in the solution not forming gel phase be completely soaked to saturated, become spongy solid through vacuum lyophilization.
Described prepare chitosan solution method be: dissolve the chitosan in acetum or 0.3��4% hydrochloric acid solution or 0.5��8% lactic acid solution or 0.5��10% glutamic acid solution or the compound two kinds sour of 0.5��5%, form the chitosan solution of 0.2��10%, 0.01��0.02% betagen solution can be simultaneously introduced.
The method of described preparation carboxymethyl chitosan solution is: carboxymethyl chitosan is soluble in water, forms the carboxymethyl chitosan solution of 0.2��10%, can be simultaneously introduced 0.01��0.02% betagen solution.
The crosslinking of described chitosan is: takes chitosan solution, presses: add glutaraldehyde or other cross-linking agent at 10: 3, and reaction temperature is 25��70 DEG C, mix homogeneously.
The crosslinking of described carboxymethyl chitosan is: go carboxymethyl chitosan solution, adds calcium chloride or the crosslinking of other aldehyde crosslinking agent by 10:2, and reaction temperature is 25��50 DEG C, mix homogeneously.
The invention has the beneficial effects as follows: antibacterial anti hemorrhagic dressing prepared by Using such method is nontoxic, without thermal source, biocompatibility is high; There is bacteria growing inhibiting, stop antibacterial to enter wound surface, promote skin regeneration, healing acceleration, reduce the advantages such as cicatrix.
Detailed description of the invention:
In order to make those skilled in the art be more fully understood that technical scheme, below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
Taking 5 grams of solid chitosan dry powder, its deacetylation is 75%, molecular weight is 300,000, adds the acetum 100ml of 2%, fully dissolve, be filtered to remove insoluble matter, add glycerol appropriate, it is coated with or is soaked in chitosan needle punched non-woven fabrics surface, lyophilization 72 hours, obtaining spongy solid.
Embodiment 2
Take 3 grams of solid chitosan dry powder, its deacetylation is 85%, molecular weight is 350,000, add the acetum 100ml of 2%, fully dissolve, be filtered to remove insoluble matter, add glutaraldehyde weak solution, add glycerol 3-10ml after stirring mixing 0.5h and continue stirring mixing 0.5h, it is coated with or is soaked in chitin needle punched non-woven fabrics surface, lyophilization 72 hours, obtaining spongy solid.
Embodiment 3
Take 4 grams of solid chitosan dry powder, its deacetylation is 80%, molecular weight is 400,000, add the acetum 100ml of 2%, fully dissolve, be filtered to remove insoluble matter, add formaldehyde weak solution, add glycerol 3-10ml after stirring mixing 0.5h and continue stirring mixing 0.5h, it is coated with or is soaked in calcium alginate needle punched non-woven fabrics surface, lyophilization 72 hours, obtaining spongy solid.
Embodiment 4
Taking 3 grams of solid carboxymethyl chitosan dry powder, its deacetylation is 80%, molecular weight is 500,000, adds water 100ml, fully dissolve, be filtered to remove insoluble matter, add glycerol appropriate, it is coated with or is soaked in calcium alginate needle punched non-woven fabrics surface, lyophilization 72 hours, obtaining spongy solid.
Embodiment 5
Take 2 grams of solid carboxymethyl chitosan dry powder, its deacetylation is 85%, molecular weight is 400,000, add water 100ml, fully dissolve, be filtered to remove insoluble matter, add calcium chloride weak solution appropriate, stirring 0.5h is continued after adding glycerol 3-10ml after stirring 1 hour, it is coated with or is soaked in hydrophilic chitosan viscose fiber needle punched non-woven fabrics surface, lyophilization 72 hours, obtaining spongy solid.
Below being only the preferred embodiment of the present invention, it is noted that above-mentioned preferred implementation is not construed as limitation of the present invention, protection scope of the present invention should be as the criterion with claim limited range. For those skilled in the art, without departing from the spirit and scope of the present invention, it is also possible to make some improvements and modifications and also should be regarded as protection scope of the present invention.
Claims (5)
1. a preparation method for composite antibacterial bleeding-stopping dressing, is characterized in that: with chitosan, carboxymethyl chitosan, sodium alginate for raw material, prepare chitosan solution and carboxymethyl chitosan solution; After chitosan solution or carboxymethyl chitosan solution or both solution are added calcium chloride or aldehyde crosslinking agent or plant extract cross-linking agent and betadine antiseptic mixing, the mixed solution of sodium alginate, hyaluronate sodium is added at the solution not forming gel phase, coat fibrous absorbent pad or fabric nonwoven cloth surface, or fibrous absorbent pad or fabric nonwoven cloth be positioned in the solution not forming gel phase be completely soaked to saturated, become spongy solid through vacuum lyophilization.
2. the preparation method of composite antibacterial bleeding-stopping dressing according to claim 1, it is characterized in that: described prepare chitosan solution method be: dissolve the chitosan in acetum or 0.3��4% hydrochloric acid solution or 0.5��8% lactic acid solution or 0.5��10% glutamic acid solution or the compound two kinds sour of 0.5��5%, form the chitosan solution of 0.2��10%.
3. the preparation method of composite antibacterial bleeding-stopping dressing according to claim 1: it is characterized in that: the method for described preparation carboxymethyl chitosan solution is: carboxymethyl chitosan is soluble in water, form the carboxymethyl chitosan solution of 0.2��10%, consider addition betagen solution simultaneously.
4. the preparation method of composite antibacterial bleeding-stopping dressing according to claim 1, the crosslinking of described chitosan is: takes chitosan solution, presses: add glutaraldehyde or other cross-linking agent at 10: 3, and reaction temperature is 25��70 DEG C, mix homogeneously.
5. the preparation method of composite antibacterial bleeding-stopping dressing according to claim 1, the crosslinking of described carboxymethyl chitosan is: go carboxymethyl chitosan solution, add calcium chloride or the crosslinking of other aldehyde crosslinking agent by 10: 2, reaction temperature is 25��50 DEG C, mix homogeneously.