CN105625588B - 一种建筑保温外墙施工方法 - Google Patents
一种建筑保温外墙施工方法 Download PDFInfo
- Publication number
- CN105625588B CN105625588B CN201610054076.1A CN201610054076A CN105625588B CN 105625588 B CN105625588 B CN 105625588B CN 201610054076 A CN201610054076 A CN 201610054076A CN 105625588 B CN105625588 B CN 105625588B
- Authority
- CN
- China
- Prior art keywords
- wall
- parts
- construction
- layer
- insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种建筑保温外墙施工方法通过软件分析计算导热系数,优选最佳墙体材料,确保墙体施工前,满足墙体要求隔热施工要求;进行施工前实验,针对不同的材料构成的实体试验模型进行导热和隔音实验,选择最佳墙体材料,可提前预知墙体隔热施工效果,缩减成本同时提高施工可靠性;施工墙体所选聚合砂浆具有防水功能,聚丙烯酸酯树脂能够赋予聚合砂浆层的防水性和粘结强度;由聚苯颗粒和膨胀玻化微珠为保温隔热骨料,聚丙烯酸酯树脂和无机胶结料为粘结剂,互相形成最紧密堆积而使材料密实性好且结构均匀,体积稳定,抗裂性好;采用本技术施工方法,结合隔热涂料层,简化了墙体保温施工程序,缩短施工工期和并可有效降低系统成本。
Description
技术领域
本发明涉及建筑施工方法,更具体的说,是涉及一种建筑保温外墙施工方法。
背景技术
传统的外墙外保温系统由保温层、抗裂防护层、饰面层和固定材料组成,但其施工工序多,施工周期长,使得工程综合成本较高;另外,对于施工工艺要求较高,一旦施工不当,如:基层表面平整度偏差过大、界面处理不符合要求、锚固件的埋设深度不够或锚固数量过多等,会导致保温层的稳定性差或者抗裂防护层的抗裂性能差,从而使得外保温系统无法满足保温隔热的需要,更为严重的是可能会导致外保温系统的开裂甚至脱落。保温材料的选择非常关键,由于目前施工基本通常是直接施工,施工完毕后发现保温效果无法达到施工要求,影响建筑质量,验收无法达标。现有的外墙保温技术有许多不足之处,施工效果如果无法预知,根据有限的施工经验,施工周期长、工程成本高、难以平衡系统的力学性能和保温性能、易开裂、使用寿命短等。
发明内容
本发明针对现有技术的不足,而提供一种建筑保温外墙施工方法。
本发明的一种建筑保温外墙施工方法,所述施工方法包括以下步骤;
步骤一、准备分析,根据墙体的导热施工要求和设计结构,在ANSYS软件中建立对应材料的几何分析模型;对几何分析模型中涉及的材料进行材料属性的确定,划分单元网格,施加外来热源与温差,计算导热系数是否满足墙体施工要求,如果导热系数未满足施工要求,调整墙体材料的属性;
步骤二、施工前实验,根据分析模型构建实体试验模型,针对不同的材料构成的实体试验模型进行导热和隔音实验,选择最佳墙体材料;
步骤三、保温隔音墙体施工;在墙体两侧支模,模板放线完毕后,制取相应内外模板,并通过螺栓拉杆紧固内外模板 ,保证内外模板 相对位置,并做好相应的内外的模板支撑保护措施,对混凝土墙体进行混凝土浇筑;
步骤四、采用水泥砂浆修补混凝土墙体,对混 凝土墙体进行找平,在混 凝土墙体的外层涂刷一层聚合砂浆,所述聚合砂浆由水泥、石英砂、憎水剂、聚丙烯酸酯树脂组成;在聚合砂浆层外未干燥前设置一层保温层,所述保温层由聚苯颗粒和膨胀玻化微珠为保温隔热骨料、聚丙烯酸酯树脂和无机胶结料为粘结剂组成,在保温层外设置防水层,防水层中铺设耐碱玻璃纤维网格布,在防水层外设置隔热涂料层。
所述墙体材料的属性包括厚度、密度比、墙体材料及墙体外层涂料的材料。
所述隔热涂料层由隔热涂料涂刷或喷涂制成;所述隔热涂料由聚苯颗粒、聚丙烯酸酯树脂、丙烯酸己酯、无机胶结料、氯化石蜡 、碳酸钙、过氯乙烯、玻璃空心微珠、羟丙基甲基纤维素、防霉剂、沸石粉、纤维素醚溶液、分散剂、滑石粉、弹性剂、石英砂、水组成。
所述羟丙基甲基纤维素粘度单位为20万mPa·s 。所述玻璃空心微珠的堆积密度为150~200kg/m3 。所述聚苯颗粒的最大颗粒小于5mm。所述沸石粉末采用细度小于120目,能够迅速溶解于水。
本发明的有益效果是:1、通过软件分析计算导热系数,优选最佳墙体材料,确保墙体施工前,满足墙体要求隔热施工要求;
2、进行施工前实验,针对不同的材料构成的实体试验模型进行导热和隔音实验,选择最佳墙体材料,可提前预知墙体隔热施工效果,缩减成本同时提高施工可靠性;
3、施工墙体所选聚合砂浆具有防水功能,聚丙烯酸酯树脂能够赋予聚合砂浆层的防水性和粘结强度;
4、由聚苯颗粒和膨胀玻化微珠为保温隔热骨料,聚丙烯酸酯树脂和无机胶结料为粘结剂,互相形成最紧密堆积而使材料密实性好且结构均匀,体积稳定,抗裂性好;
5、采用本技术施工方法,结合隔热涂料层,简化了墙体保温施工程序,缩短施工工期和并可有效降低系统成本,有效增加各层之间的粘附力,墙体因此具有优异的防护性能。
具体实施方式
下面结合实施例对本发明作进一步说明。
本发明一种建筑保温外墙施工方法,所述施工方法包括以下步骤;
步骤一、准备分析,根据墙体的导热施工要求和设计结构,在ANSYS软件中建立对应材料的几何分析模型;对几何分析模型中涉及的材料进行材料属性的确定,划分单元网格,施加外来热源与温差,计算导热系数是否满足墙体施工要求,如果导热系数未满足施工要求,调整墙体材料的属性;
步骤二、施工前实验,根据分析模型构建实体试验模型,针对不同的材料构成的实体试验模型进行导热和隔音实验,选择最佳墙体材料;
步骤三、保温隔音墙体施工;在墙体两侧支模,模板放线完毕后,制取相应内外模板,并通过螺栓拉杆紧固内外模板 ,保证内外模板 相对位置,并做好相应的内外的模板支撑保护措施,对混凝土墙体进行混凝土浇筑;
步骤四、采用水泥砂浆修补混凝土墙体,对混 凝土墙体进行找平,在混 凝土墙体的外层涂刷一层聚合砂浆,所述聚合砂浆由水泥、石英砂、憎水剂、聚丙烯酸酯树脂组成;在聚合砂浆层外未干燥前设置一层保温层,所述保温层由聚苯颗粒和膨胀玻化微珠为保温隔热骨料、聚丙烯酸酯树脂和无机胶结料为粘结剂组成,在保温层外设置防水层,防水层中铺设耐碱玻璃纤维网格布,在防水层外设置隔热涂料层。
所述墙体材料的属性包括厚度、密度比、墙体材料及墙体外层涂料的材料。
所述隔热涂料层由隔热涂料涂刷或喷涂制成;所述隔热涂料配方比例按重量份计如下:聚苯颗粒50份、聚丙烯酸酯树脂20份、丙烯酸己酯10份、无机胶结料20份、氯化石蜡15份、碳酸钙15份、过氯乙烯15份、玻璃空心微珠20份、羟丙基甲基纤维素15份、防霉剂5份、沸石粉5份、纤维素醚溶液5份、分散剂5份、滑石粉50份、弹性剂10份、石英砂20份、水30份组成。所述羟丙基甲基纤维素粘度单位为20万mPa·s 。所述玻璃空心微珠的堆积密度为150~200kg/m3 。所述聚苯颗粒的最大颗粒小于5mm。所述沸石粉末采用细度小于120目,能够迅速溶解于水。
表一 隔热涂料层性能指标
表二 隔热涂料层反射隔热性能指标
项目 | 技术指标 |
施工性 | 涂刷两道无障碍 |
低温稳定性 | 不变质 |
干燥时间(表干)/ | ≤2h |
涂膜外观 | 正常 |
对比率(白色与浅色) | ≥0.93 |
耐水性(96h) | 无异常 |
耐碱性(48 h) | 无异常 |
耐洗刷性 | ≥2000次 |
耐沾污性(5次循环;平状;白色与浅色) | ≤15% |
涂层耐温变性 | 无异常 |
太阳光反射比(白色) | ≥0.80 |
半球发射率 | ≥0.80 |
表三 隔热涂料物理力学性能
表四隔热涂料层的性能指标
项 目 | 指 标 |
施工性 | 施工无障碍 |
干燥时间(表干)/h ≤ | 2 |
涂膜外观 | 正常 |
耐水性 | 96h无异常 |
耐碱性 | 48h无异常 |
附着力/级 ≤ | 1 |
透水性/mL ≤ | 0.3 |
本发明的一种建筑保温外墙施工方法通过软件分析计算导热系数,优选最佳墙体材料,确保墙体施工前,满足墙体要求隔热施工要求;进行施工前实验,针对不同的材料构成的实体试验模型进行导热和隔音实验,选择最佳墙体材料,可提前预知墙体隔热施工效果,缩减成本同时提高施工可靠性;施工墙体所选聚合砂浆具有防水功能,聚丙烯酸酯树脂能够赋予聚合砂浆层的防水性和粘结强度;由聚苯颗粒和膨胀玻化微珠为保温隔热骨料,聚丙烯酸酯树脂和无机胶结料为粘结剂,互相形成最紧密堆积而使材料密实性好且结构均匀,体积稳定,抗裂性好;采用本技术施工方法,结合隔热涂料层,简化了墙体保温施工程序,缩短施工工期和并可有效降低系统成本,有效增加各层之间的粘附力,墙体因此具有优异的防护性能。本专利原料来源方便,生产工艺简单,更重要的是,缩短了施工周期,节约了工程成本,具有良好的应用推广前景。
申请人声明,本发明通过上述实施例来说明本发明的详细方法和方法流程,但本发明并不局限于上述详细方法和方法流程,即不意味着本发明必须依赖上述详细方法和方法流程才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (1)
1.一种建筑保温外墙施工方法,其特征是,所述施工方法包括以下步骤;
步骤一、准备分析,根据墙体的导热施工要求和设计结构,在ANSYS软件中建立对应材料的几何分析模型;对几何分析模型中涉及的材料进行材料属性的确定,划分单元网格,施加外来热源与温差,计算导热系数是否满足墙体施工要求,如果导热系数未满足施工要求,调整墙体材料的属性;
步骤二、施工前实验,根据分析模型构建实体试验模型,针对不同的材料构成的实体试验模型进行导热和隔音实验,选择最佳墙体材料;所述墙体材料的属性包括厚度、密度比、墙体材料及墙体外层涂料的材料;
步骤三、保温隔音墙体施工;在墙体两侧支模,模板放线完毕后,制取相应内外模板,并通过螺栓拉杆紧固内外模板 ,保证内外模板 相对位置,并做好相应的内外的模板支撑保护措施,对混凝土墙体进行混凝土浇筑;
步骤四、采用水泥砂浆修补混凝土墙体,对混 凝土墙体进行找平,在混 凝土墙体的外层涂刷一层聚合砂浆,所述聚合砂浆由水泥、石英砂、憎水剂、聚丙烯酸酯树脂组成;在聚合砂浆层外未干燥前设置一层保温层,所述保温层由聚苯颗粒和膨胀玻化微珠为保温隔热骨料、聚丙烯酸酯树脂和无机胶结料为粘结剂组成,在保温层外设置防水层,防水层中铺设耐碱玻璃纤维网格布,在防水层外设置隔热涂料层;所述隔热涂料层由隔热涂料涂刷或喷涂制成;所述隔热涂料配方比例按重量份计如下,聚苯颗粒50份、聚丙烯酸酯树脂20份、丙烯酸己酯10份、无机胶结料20份、氯化石蜡 15份、碳酸钙15份、过氯乙烯15份、玻璃空心微珠20份、羟丙基甲基纤维素15份、防霉剂5份、沸石粉5份、纤维素醚溶液5份、分散剂5份、滑石粉50份、弹性剂10份、石英砂20份、水30份组成;所述羟丙基甲基纤维素粘度单位为20万mPa·s;所述玻璃空心微珠的堆积密度为150~200kg/m3 ;所述聚苯颗粒的最大颗粒小于5mm;所述沸石粉末采用细度小于120目,能够迅速溶解于水。