CN105602518A - Colorless and transparent environment-friendly handbag spray glue and preparation method thereof - Google Patents
Colorless and transparent environment-friendly handbag spray glue and preparation method thereof Download PDFInfo
- Publication number
- CN105602518A CN105602518A CN201511015563.9A CN201511015563A CN105602518A CN 105602518 A CN105602518 A CN 105602518A CN 201511015563 A CN201511015563 A CN 201511015563A CN 105602518 A CN105602518 A CN 105602518A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue spraying
- environmental protection
- water white
- white transparency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to glue, in particular to colorless and transparent environment-friendly handbag spray glue and a preparation method thereof. The preparation method comprises the following steps: conveying 400 to 600 parts of No.6 solvent oil, 80 to 120 parts of dimethyl acetate and 40 to 60 parts of ethyl acetate to a reaction kettle through an oil conveying pipeline; then, starting a stirrer and stirring at 300 revolutions/minute, and meanwhile, adding 45 to 70 parts of styrene-isoprene-styrene (SIS) segmented copolymer and 25 to 40 parts of styrene-butadiene-styrene (SBS) copolymer; adjusting the speed of the stirrer to 1200 revolutions/minute after charging is finished, and stirring for 2 hours; then adding 70 to 95 parts of tackifying resin, and meanwhile, adding 0.5 to 2 parts of antiager BHT (butylated hydroxytoluene) and stirring; finishing operation after one hour. The spray glue disclosed by the invention has good anti-ageing property, and is resistant to high temperature, colorless and transparent, weak in smell, free of toxic and harmful substances, uniform in contact points on a spray surface, impervious and higher in adhesive force strength. The preparation method disclosed by the invention is simple and easy to operate.
Description
Technical field
The present invention relates to a kind of glue, relate in particular to a kind of water white transparency environmental protection handbag glue spraying for environmental protection handbag and preparation method thereof.
Background technology
At present, the feature such as high temperature resistant poor, ageing-resistant difference of existing handbag glue spraying ubiquity. The existing high temperature resistant temperature of handbag glue spraying on the market only has 50 DEG C of left and right, run into six, seven, August hot weather adhesive surface very easily flicks, cause secondary to come unglued or repeatedly come unglued, and while doing over again because repeatedly glue spraying causes material face heap glue too much to make material distortion, even make material surface infiltration and damage, causing a large amount of losses. Simultaneously, at present existing very easily opaque of handbag glue spraying on the market, the glue above attachment surface can calcification fall off layer as powder, and four limits can be sewed up with motor by businessman sometimes, but middle viscose glue attachment surface comes off, bondingly not firmly cause that handbag face is heaved, out-of-flatness, impact be attractive in appearance; In addition, handbag glue spraying on market is all yellow, color and luster is running into the material of the light colours such as white, pink colour, blueness, because extremely difficult in glue spraying face process, material bound edge will prevent that yellow liquid from oozing out, affect attractive in appearancely, and clean the liquid oozing out, waste of manpower, material resources with cleaning agent.
Summary of the invention
The object of the invention is to overcome deficiency of the prior art, and provide a kind of water white transparency environmental protection handbag glue spraying and preparation method thereof, its ageing-resistant good, high temperature resistant, water white transparency, taste be low, containing poisonous and harmful substances, spray plane contact point-like is even, impermeable, bonding force intensity is higher.
The technical solution adopted in the present invention: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following parts by weight is standby, No. 6 solvent naphtha 400-600 parts, dimethyl carbonate 80-120 part, ethyl acetate 40-60 part, SIS 45-70 part, SBS 25-40 part, tackifying resin 70-95 part, age resistor 0.5-2 part.
Preferably, a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following parts by weight is standby, No. 6 solvent naphtha 450-550 parts, dimethyl carbonate 90-110 part, ethyl acetate 45-60 part, SIS 50-70 part, SBS 30-35 part, tackifying resin 80-95 part, age resistor 1-2 part.
Preferably, a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following parts by weight is standby, 500 parts of No. 6 solvent naphthas, 100 parts of dimethyl carbonates, 50 parts of ethyl acetates, 60 parts of SISs, 30 parts of SBSs, 80 parts of tackifying resins, 1 part, age resistor.
Described tackifying resin is water-white rosin.
Described age resistor is BHT.
A preparation method for above-mentioned water white transparency environmental protection handbag glue spraying, it comprises the following steps:
Step a, according to above-mentioned parts by weight, No. 6 solvent naphthas, dimethyl carbonate, ethyl acetates are joined in reactor, and open mixer material is stirred, mixer rotating speed is 200-350 rev/min and stirs;
Step b, in stirring, in reactor, add SIS, and SBS, add and mixer rotating speed be adjusted to 1000-1400 rev/min, stirring 1.5-3 hour afterwards;
Step c, material after stirring in step b add tackifying resin, age resistor, continue to stir within 1-2 hour, to obtain water white transparency environmental protection handbag glue spraying.
Beneficial effect of the present invention:
The present invention adopts raw material to be all environmental protection shaped material, not containing poisonous and harmful substance, effectively ensure the security performance of product, glue spraying heat-resisting ability of the present invention is strong, it is high temperature resistant reaches 80-90 DEG C, has effectively solved the phenomenon that the explosion of hot weather adhesive surface is come unglued; And its strong adhesion, crystallization are soon, spray plane can be bonding in aggregates in ten minutes, operable time 2-3 days is smoothly attractive in appearance after laminating; In addition, glue spraying water white transparency of the present invention, solved yellow glue spraying completely in the material that runs into the light colours such as white, pink colour, blueness, because extremely difficult in glue spraying face process, material bound edge will prevent that yellow liquid from oozing out, affect problem attractive in appearance, make it in the time using glue spraying of the present invention to process material, can one-shot forming, clean without re-using cleaning agent the liquid oozing out, avoid the waste of human and material resources, effectively saved material; Meanwhile, the preparation method of glue spraying of the present invention is simple, easy operating.
Detailed description of the invention
Below in conjunction with preferred embodiment, the present invention will be further described.
Embodiment 1: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 400Kg, dimethyl carbonate 80Kg, ethyl acetate 40Kg, SIS 45Kg, SBS 25Kg, tackifying resin 70Kg, age resistor 0.5Kg.
Embodiment 2: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 600Kg, dimethyl carbonate 120Kg, ethyl acetate 60Kg, SIS 70Kg, SBS 40Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 3: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 400Kg, dimethyl carbonate 120Kg, ethyl acetate 40Kg, SIS 70Kg, SBS 40Kg, tackifying resin 70Kg, age resistor 0.5Kg.
Embodiment 4: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 450Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 45Kg, SIS 50Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 5: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 110Kg, ethyl acetate 60Kg, SIS 70Kg, SBS 35Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 6: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 60Kg, SIS 50Kg, SBS 35Kg, tackifying resin 80Kg, age resistor 2Kg.
Embodiment 7: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, dimethyl carbonate 100Kg, ethyl acetate 50Kg, SIS 60Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 8: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 400Kg, dimethyl carbonate 80Kg, ethyl acetate 40Kg, SIS 45Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 9: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 400Kg, dimethyl carbonate 80Kg, ethyl acetate 40Kg, SIS 45Kg, SBS 35Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 10: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 400Kg, dimethyl carbonate 80Kg, ethyl acetate 40Kg, SIS 45Kg, SBS 35Kg, tackifying resin 80Kg, age resistor 2Kg.
Embodiment 11: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 400Kg, dimethyl carbonate 80Kg, ethyl acetate 40Kg, SIS 45Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 12: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 450Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 45Kg, SIS 45Kg, SBS 25Kg, tackifying resin 70Kg, age resistor 0.5Kg.
Embodiment 13: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 110Kg, ethyl acetate 60Kg, SIS 45Kg, SBS 25Kg, tackifying resin 70Kg, age resistor 0.5Kg.
Embodiment 14: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 60Kg, SIS 45Kg, SBS 25Kg, tackifying resin 70Kg, age resistor 0.5Kg.
Embodiment 15: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, dimethyl carbonate 100Kg, ethyl acetate 50Kg, SIS 45Kg, SBS 25Kg, tackifying resin 70Kg, age resistor 0.5Kg.
Embodiment 16: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 600Kg, dimethyl carbonate 120Kg, ethyl acetate 60Kg, SIS 50Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 17: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 600Kg, dimethyl carbonate 120Kg, ethyl acetate 60Kg, SIS 70Kg, SBS 35Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 18: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 600Kg, dimethyl carbonate 120Kg, ethyl acetate 60Kg, SIS 50Kg, SBS 35Kg, tackifying resin 80Kg, age resistor 2Kg.
Embodiment 19: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, dimethyl carbonate 100Kg, ethyl acetate 50Kg, SIS 60Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 20: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 450Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 45Kg, SIS 50Kg, SBS 40Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 21: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 110Kg, ethyl acetate 60Kg, SIS 70Kg, SBS 40Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 22: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 60Kg, SIS 50Kg, SBS 40Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 23: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, dimethyl carbonate 100Kg, ethyl acetate 50Kg, SIS 60Kg, SBS 40Kg, tackifying resin 95Kg, age resistor 2Kg.
Embodiment 24: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 450Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 45Kg, SIS 50Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 25: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, dimethyl carbonate 100Kg, ethyl acetate 45Kg, SIS 50Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 26: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 550Kg, acetic acid dimethyl ester 110Kg, ethyl acetate 60Kg, SIS 60Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg.
Embodiment 27: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 60Kg, SIS 50Kg, SBS 35Kg, tackifying resin 80Kg, age resistor 2Kg.
Embodiment 28: a kind of water white transparency environmental protection handbag glue spraying, it is to form by the mixed raw material of following weight kilogram number is standby, No. 6 solvent naphtha 500Kg, acetic acid dimethyl ester 90Kg, ethyl acetate 60Kg, SIS 50Kg, SBS 30Kg, tackifying resin 80Kg, age resistor 1Kg
In the above embodiment of the present invention, age resistor all adopts 2,6-di-tert-butyl-4-methy phenol (BHT), effectively raise the antiageing effect of glue spraying of the present invention, tackifying resin all adopts water-white rosin, effectively raise the resistance to elevated temperatures of glue spraying of the present invention, it is colourless making glue spraying of the present invention, has also improved to a certain extent the transparency of glue spraying of the present invention, makes glue spraying of the present invention environmental protection more.
A preparation method for above-mentioned water white transparency environmental protection handbag glue spraying, it comprises the following steps:
Step a, according to above-mentioned parts by weight, No. 6 solvent naphthas, dimethyl carbonate, ethyl acetates are joined in reactor, and open mixer material is stirred, mixer rotating speed is 200-350 rev/min and stirs;
Step b, in stirring, in reactor, add SIS, and SBS, add and mixer rotating speed be adjusted to 1000-1400 rev/min, stirring 1.5-3 hour afterwards;
Step c, material after stirring in step b add tackifying resin, age resistor, continue to stir within 1-2 hour, to obtain water white transparency environmental protection handbag glue spraying.
First environmental protection handbag glue spraying of the present invention has been removed the most glue sprayings in market aspect solvent completely and is also being continued practical poisonous and harmful solvent as carrene, dichloroethanes, dimethylbenzene etc. using. Secondly on raw-material selecting, be all the SIS by external import, its Performance Ratio is more stable. In colourity, have more the standby market competitiveness than traditional khaki glue spraying, tradition glue spraying is also being used rosin to do tackifier mostly, its open hour only have 2-4 hour, and its bonding back pull be 120N in ageing-resistant ability, traditional handbag glue spraying 3-5 month glue under natural environment just there will be powder phenomenon-tion. And transparent handbag glue spraying of new generation has successfully solved the problem of the open hour deficiency of practical Petropols glue, after sprayed on material, in 2-3 days, still have good cementability, on the bonding dynamics at its initial stage without a bit impact. Bonding back pull reaches especially its aging ability of 160N and has obtained especially huge lifting, and bonding rear glue is aging can reach the 8-9 month. Once release, on market, obtain very large success. In spraying, carry out the spray test at initial stage by air pump spray gun, after spraying, find that this product does not fly a phenomenon, rate of gum output is high, and spraying is fast, is homogeneous point-like, and what sprayed on material was conventional does case and bag, leather surface, canvas, corium, nylon, etc. After tested, do not affecting its overall adhesive effect for different materials. The utility time of glue can reach 2-3 days simultaneously. After bonding, after measurer for pulling force test, find that its pulling force is than the stronger bonding more better effects if of traditional pulling force. Toasting through baking oven, its heat resistance can reach 65 DEG C and continue to toast the phenomenon of not coming unglued for 2 hours.
Claims (6)
1. a water white transparency environmental protection handbag glue spraying, it is characterized in that: it is to form by the mixed raw material of following parts by weight is standby No. 6 solvent naphtha 400-600 parts, acetic acid dimethyl ester 80-120 part, ethyl acetate 40-60 part, SIS 45-70 part, SBS 25-40 part, tackifying resin 70-95 part, age resistor 0.5-2 part.
2. water white transparency environmental protection handbag glue spraying according to claim 1, it is characterized in that: it is to form by the mixed raw material of following parts by weight is standby No. 6 solvent naphtha 450-550 parts, acetic acid dimethyl ester 90-110 part, ethyl acetate 45-60 part, SIS 50-70 part, SBS 30-35 part, tackifying resin 80-95 part, age resistor 1-2 part.
3. water white transparency environmental protection handbag glue spraying according to claim 1, it is characterized in that: it is to form by the mixed raw material of following parts by weight is standby 500 parts of No. 6 solvent naphthas, 100 parts of dimethyl carbonates, 50 parts of ethyl acetates, 60 parts of SISs, 30 parts of SBSs, 80 parts of tackifying resins, 1 part, age resistor.
4. according to the water white transparency environmental protection handbag glue spraying described in claim 1 or 2 or 3, it is characterized in that: described tackifying resin is Petropols or water-white abietic resin.
5. according to the water white transparency environmental protection handbag glue spraying described in claim 1 or 2 or 3, it is characterized in that: described age resistor is BHT.
6. a preparation method for water white transparency environmental protection handbag glue spraying, is characterized in that: it comprises the following steps:
Step a, according to above-mentioned parts by weight, No. 6 solvent naphthas, dimethyl carbonate, ethyl acetates are joined in reactor, and open mixer material is stirred, mixer rotating speed is 200-350 rev/min and stirs;
Step b, in stirring, in reactor, add SIS, and SBS, add and mixer rotating speed be adjusted to 1000-1400 rev/min, stirring 1.5-3 hour afterwards;
Step c, material after stirring in step b add tackifying resin, age resistor, continue to stir within 1-2 hour, to obtain water white transparency environmental protection handbag glue spraying.