CN105602350B - String blending wall clothing and preparation method thereof - Google Patents
String blending wall clothing and preparation method thereof Download PDFInfo
- Publication number
- CN105602350B CN105602350B CN201610039718.0A CN201610039718A CN105602350B CN 105602350 B CN105602350 B CN 105602350B CN 201610039718 A CN201610039718 A CN 201610039718A CN 105602350 B CN105602350 B CN 105602350B
- Authority
- CN
- China
- Prior art keywords
- raw material
- fibrous raw
- preparation
- wall clothing
- blending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of string blending wall clothing and preparation method thereof, it includes the preparation of fibrous raw material, the treatment of fibrous raw material, three parts of the preparation of wall clothing, specifically various natural plant fibres are weaved respectively and is twisted single count yarn, again by its blending into bifilar or multi-strand yarns, and line segment is cut into as fibrous raw material, then by after the fibrous raw material water-soaked, after steaming, rolling and boil, be dehydrated, dry, the basic viscose glue constituted with gossypin and water-soluble plant glue is well mixed, and obtains final product the string blending wall clothing.Surfacing, exquisiteness after wall clothing coating, distribution of color is uniform, and visible obvious silk thread intertexture texture, and metope can be made more attractive in appearance, and it has the effect of preferable environment purification, can improve indoor environmental quality, its wide market.
Description
Technical field
The invention belongs to metope coating material technical field, and in particular to a kind of string blending wall clothing and its preparation side
Method.
Background technology
Wall surfacing product is usually to use paint or wallpaper, but traditional paint coating harmful substance contents are high, right
Harm is big, though water paint has been used in the market, the reduction of its harmful substance contents, existing national Specification is still
A certain amount of free formaldehyde can be allowed, this needs for be occupied after divulging information after a while after making room wall plastering
Firmly, and wall pattern color is single, aesthetic feeling is lacked；Although the application of wallpaper can enrich the pattern and color of wall, its cost
Greatly improve, and use time is long that the problems such as be difficult repairing after aging, discoloration, breakage occurs, meanwhile, gluing used by wallpaper
Containing formaldehyde agent more.Wall clothing is the 3rd class Novel interior wall ornament materials occurred after the decorative material for internal wall such as paint, wallpaper,
It is processed as primary raw material with wood fibre, natural fiber through special scientific technology, with it is attractive in appearance, without noxious volatile
Composition, texture is strong, not easy to crack, construct it is convenient it is pollution-free, be a kind of environmental protection, the internal wall finishing of green the advantages of repair simple
Material.
The content of the invention
It is an object of the invention to provide a kind of string blending wall clothing and preparation method thereof, it passes through will be various natural
The yarn that string is twisted is carried out after blending as fibrous raw material, makes surfacing, exquisiteness, face after the material coating of gained wall clothing
Color is evenly distributed, and visible obvious silk thread intertexture texture, and metope can be made more attractive in appearance, and it has the work of preferable environment purification
With indoor environmental quality, wide market can be improved.
To achieve the above object, the present invention is adopted the following technical scheme that：
A kind of string blending wall clothing, its preparation method includes preparation, the treatment of fibrous raw material, the wall clothing of fibrous raw material
Three parts of preparation；
Its step is as follows：
（One）The preparation of fibrous raw material
1）Various natural plant fibres are weaved respectively and is twisted single count yarn of diameter 0.5mm-2.5mm, and as needed
Dye different colours；The natural plant fibre includes bamboo fibre, wood-fibred, cotton fiber, fibre and soya；
2）By the various single count yarn blending of gained into diameter 1mm-5mm bifilar or multi-strand yarns；
3）By step 2）Gained yarn cuts into the line segment that length is 0.5cm-3cm, obtains final product fibrous raw material；
（Two）The treatment of fibrous raw material
1）Gained fibrous raw material water is soaked completely, 20-25min is steamed in 100 DEG C of steam boxs；
2）The fibrous raw material that will be steamed is cooled to 40 DEG C -50 DEG C, then 12-15min is boiled in rolling in boiling water；
3）The fibrous raw material centrifugal dehydration 5-10min after boiling treatment will be rolled；
4）Fiber after dewater treatment is completely dried in 60 DEG C of -70 DEG C of drying 30min to fibrous raw material；
（Three）The preparation of wall clothing
1）By gossypin, water-soluble plant glue by weight 1:1-1:Viscose glue based on 2 mixing；
2）Discharged after fibrous raw material after treatment and basic viscose glue are stirred in mixing equipment and obtained final product.
The construction method of the string blending wall clothing is：By the string blending wall clothing by weight 1:3-1:
5 be watered after stir, stand 30min, it is uniform using being preceding again stirring for, be then applied on metope, smearing thickness is 2-
5mm, obtains final product after dry and hard.
In the prior art, because fibrous raw material is substantially similar in unit volume, weight with auxiliary material, cause fibrous raw material easy
The phenomenon united, so as to cause as the fiber skewness of functional form main material, influences wall attractive in appearance and material environment friendly
The realization of performance；Simultaneously as the exclusiveness between fiber, makes conventional wall clothing directly cannot be mixed into several functionalities fiber type
Row production, result in the bottleneck in the middle of the development of wall clothing product processes.String blending wall clothing of the present invention is by by single branch
The direct blending of yarn makes the fibrous raw material prepared in yam-like into bifilar or multi-strand yarns, not only causes fibrous raw material from body
Product, presented a contrast with auxiliary material in weight, so as to produce and can realize in the middle of constructing it is good be evenly distributed so that its from
Outward appearance and most stable of effect is functionally attained by, also solved because same fiber can not be not simultaneously caused by fiber exclusiveness
The problem deposited, makes the raw material of string wall clothing select face to greatly improve.
On the other hand, the adsorption function of traditional plant fiber wall clothing itself build on string itself exist it is many big
The small crack for differing, fold, the harmful substance in air can will be adsorbed by the circulation of air, reach the effect for purifying the air of a room
Really.The present invention, using the absorption affinity of string, by fibrous raw material water-soaked, fills moisture using the handling process of innovation
The full original crack of string, then is steamed by high temperature, boiled, operation makes crack increase, fold increases, and changes wall for centrifugal dehydration etc.
The structure of clothing internal fiber, makes wall clothing inside produce more cracks, so as to enhance the permeability of product, also makes the product can
More free foreign matter and pernicious gas are adsorbed by cross-ventilation.The purifying formaldehyde of string blending wall clothing material of the present invention
Efficiency up to more than 88%, while more than 2 times that humidity absorption and release performance is up to state standards, it was demonstrated that it has good purification ring
Border and humidity conditioning function.
Additionally, conventional wall clothing is likely to encounter in work progress because construction smearing causes the too scattered feelings of fiber repeatedly
Condition, has a strong impact on the visual effect in terms of product texture, color.And constructed using string blending wall clothing of the present invention,
Because it is first by fiber silk blend into fiber yarn, can make to combine between fiber is even closer, and the resistance to of reinforcement material is applied
Work, the metope texture color constructed repeatedly under 10 dual intensities after will not also making fiber scattered situation, and gained coating occur
It is color clear, will not occur that texture is fuzzy, the phenomenon of color distortion as conventional wall clothing.
Brief description of the drawings
Fig. 1 is the comparison diagram of the front and rear gained wood-fibred pattern of blending, wherein, figure A is for before blending, figure B is for after blending.
Fig. 2 is the electron-microscope scanning figure of fibrous raw material, wherein, figure A is the fibrous raw material of before processing, and figure B is the fibre after treatment
Dimension raw material.
Fig. 3 is the surface comparison diagram of traditional plant fiber wall clothing and string blending wall clothing of the present invention.
Specific embodiment
In order that content of the present invention easily facilitates understanding, with reference to specific embodiment to of the present invention
Technical scheme is described further, but the present invention is not limited only to this.
Embodiment 1
A kind of string blending wall clothing material, its preparation method following steps：
（One）The preparation of fibrous raw material
1）3 weight portion bamboo fibres, 5 weight portion cotton fibers are weaved respectively and is twisted single count yarn of diameter 0.5mm, and according to
Need to dye different colours；
2）By the various single count yarn blending of gained into diameter 1mm bifilar yarn；
3）By step 2）Gained yarn cuts into the line segment that length is 0.5cm, obtains final product fibrous raw material；
（Two）The treatment of fibrous raw material
1）After gained fibrous raw material water is soaked completely, in 20min is steamed in 100 DEG C of steam boxs, then it is vented, unpacks,
Take out fibrous raw material；
2）The fibrous raw material that will be steamed is cooled to 40 DEG C, then 15min is boiled in rolling in boiling water；
3）The dewater treatment 5min in centrifugal drier of the fibrous raw material after boiling treatment will be rolled；
4）Fibrous raw material after dewater treatment is taken out, is dried in 60 DEG C 30 minutes and is completely dried to fibrous raw material；
（Three）The preparation of wall clothing
1）By gossypin, water-soluble plant glue by weight 1:Viscose glue based on 1 mixing；
2）Fibrous raw material after treatment and basic viscose glue are put into mixing equipment, the packaging that discharged after stirring is obtained final product into
Product.
Embodiment 2
A kind of string blending wall clothing material, its preparation method following steps：
（One）The preparation of fibrous raw material
1）3 weight portion bamboo fibres, 3 weight portion wood-fibreds, 6 parts by weight of soybean fibers are weaved be twisted diameter 1.0mm respectively
Single count yarn, and dye different colours as needed；
2）By the various single count yarn blending of gained into diameter 2mm multi-strand yarns；
3）By step 2）Gained yarn cuts into the line segment that length is 1cm, obtains final product fibrous raw material；
（Two）The treatment of fibrous raw material
1）After gained fibrous raw material water is soaked completely, in 30min is steamed in 100 DEG C of steam boxs, then it is vented, unpacks,
Take out fibrous raw material；
2）The fibrous raw material that will be steamed is cooled to 45 DEG C, then 13min is boiled in rolling in boiling water；
3）The dewater treatment 6min in centrifugal drier of the fibrous raw material after boiling treatment will be rolled；
4）Fibrous raw material after dewater treatment is taken out, is dried in 65 DEG C 30 minutes and is completely dried to fibrous raw material；
（Three）The preparation of wall clothing
1）By gossypin, water-soluble plant glue by weight 1:Viscose glue based on 1.3 mixing；
2）Fibrous raw material after treatment and basic viscose glue are put into mixing equipment, the packaging that discharged after stirring is obtained final product into
Product.
Embodiment 3
A kind of string blending wall clothing material, its preparation method following steps：
（One）The preparation of fibrous raw material
1）3 weight portion bamboo fibres, 3 weight portion cotton fibers, 2 parts by weight of soybean fibers are weaved be twisted diameter 2.5mm respectively
Single count yarn, and dye different colours as needed；
2）By the various single count yarn blending of gained into diameter 5mm multi-strand yarns；
3）By step 2）Gained yarn cuts into the line segment that length is 3cm, obtains final product fibrous raw material；
（Two）The treatment of fibrous raw material
1）After gained fibrous raw material water is soaked completely, in 50min is steamed in 100 DEG C of steam boxs, then it is vented, unpacks,
Take out fibrous raw material；
2）The fibrous raw material that will be steamed is cooled to 50 DEG C, then 12min is boiled in rolling in boiling water；
3）The dewater treatment 10min in centrifugal drier of the fibrous raw material after boiling treatment will be rolled；
4）Fibrous raw material after dewater treatment is taken out, is dried in 70 DEG C 30 minutes and is completely dried to fibrous raw material.
（Three）The preparation of wall clothing
1）By gossypin, water-soluble plant glue by weight 1:Viscose glue based on 2 mixing；
2）Fibrous raw material after treatment and basic viscose glue are put into mixing equipment, the packaging that discharged after stirring is obtained final product into
Product.
Fig. 1 is the comparison diagram of wood-fibred pattern before and after blending, wherein figure A is for before blending, figure B is for after blending.Can from figure
To find out, wood-fibred is in cotton-shaped before blending, and loosely organized, texture is in disorder；Wood-fibred yarn is in twisted wire shape after blending, and structure is tight
Gather, clean mark.In the middle of practical application, the wall clothing prepared using blended material is remote in fibre strength, friction tolerance
Exceed well over the product prepared using the fibrous raw material of non-blending.
Fig. 2 is the electron-microscope scanning figure of fibrous raw material, wherein fibrous raw materials of the figure A for before processing, figure B is the fiber after treatment
Raw material.It can be seen that after treatment, plant fibre surface fold, hole are greatly increased.
Fig. 3 is the surface comparison diagram of traditional plant fiber wall clothing and string blending wall clothing of the present invention, and wherein left column is
Traditional plant fiber wall clothing, right column is string blending wall clothing of the present invention.By Fig. 3（A）With Fig. 3（B）Contrast can be seen that
The phenomenon that the visible fiber in surface is united after the construction of traditional plant fiber wall clothing, and string blending wallpaper fiber of the present invention disperses
Uniformly；By Fig. 3（C）With Fig. 3（D）Contrast can be seen that traditional plant fiber wall clothing after constructing repeatedly, due to excessive friction
Surface fiber can be caused to disperse, wear and tear, and string blending wall clothing of the present invention texture after equality strength is constructed remains unchanged clearly
It is clear distinguishable；By Fig. 3（E）With Fig. 3（F）Contrast can be seen that traditional plant fiber wall clothing surface almost without crack, it is and of the invention
There is obvious crack between string blending wall clothing surface texture.
1. purifying formaldehyde effect test
According to JC/T 1074-2008《Room air macerates function coating material purifying property》Specified in method, will this
Inventive embodiments 1-3 gained string blending wall clothing materials are tested, and the results are shown in Table 1.
The purifying formaldehyde effect test result of table 1
From table 1, the clean-up effect of string blending wall clothing PARA FORMALDEHYDE PRILLS(91,95) of the present invention is notable, and clean-up effect is persistently,
Illustrate that it has the effect of good purifying formaldehyde.
2. humid test is adjusted
According to JC/T 2082-2011《Humidity conditioning function interior architecture ornament materials》In regulation to embodiment of the present invention 1-3
Gained string blending wall clothing material carries out humidity experiment, the results are shown in Table 2.
The humidity result of the test of table 2
From table 2, string blending wall clothing of the present invention has excellent humidity, can play regulation indoor humidity
Effect.
Claims (3)
1. a kind of preparation method of string blending wall clothing, it is characterised in that：Preparation, fibrous raw material including fibrous raw material
Treatment, three parts of preparation of wall clothing；
Its step is as follows：
（One）The preparation of fibrous raw material
1）Various natural plant fibres are weaved respectively and is twisted single count yarn of diameter 0.5mm-2.5mm, and dyed as needed
Different colours；
2）By the various single count yarn blending of gained into diameter 1mm-5mm bifilar or multi-strand yarns；
3）By step 2）Gained yarn cuts into the line segment that length is 0.5cm-3cm, obtains final product fibrous raw material；
（Two）The treatment of fibrous raw material
1）Gained fibrous raw material water is soaked completely, 20-25min is steamed in 100 DEG C of steam boxs；
2）The fibrous raw material that will be steamed is cooled to 40 DEG C -50 DEG C, then 12-15min is boiled in rolling in boiling water；
3）The fibrous raw material centrifugal dehydration 5-10min after boiling treatment will be rolled；
4）Fiber after dewater treatment is completely dried in 60 DEG C of -70 DEG C of drying 30min to fibrous raw material；
（Three）The preparation of wall clothing
1）By gossypin, water-soluble plant glue by weight 1:1-1:Viscose glue based on 2 mixing；
2）Discharged after fibrous raw material after treatment and basic viscose glue are stirred in mixing equipment and obtained final product；
The natural plant fibre includes bamboo fibre, wood-fibred, cotton fiber, fibre and soya.
2. string blending wall clothing obtained in a kind of preparation method as claimed in claim 1.
3. string blending wall clothing according to claim 2, it is characterised in that：Its construction method is：The plant is fine
Dimension blending wall clothing is by weight 1:3-1:5 be watered after stir, stand 30min, it is uniform using being preceding again stirring for, then smear
In on metope, smearing thickness is 2-5mm, is obtained final product after dry and hard.