CN105602350A - Plant fiber blending wall clothing and preparation method thereof - Google Patents
Plant fiber blending wall clothing and preparation method thereof Download PDFInfo
- Publication number
- CN105602350A CN105602350A CN201610039718.0A CN201610039718A CN105602350A CN 105602350 A CN105602350 A CN 105602350A CN 201610039718 A CN201610039718 A CN 201610039718A CN 105602350 A CN105602350 A CN 105602350A
- Authority
- CN
- China
- Prior art keywords
- raw material
- preparation
- fibrous raw
- wall clothing
- blending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses plant fiber blending wall clothing and a preparation method thereof. The preparation method comprises three parts including preparation of fiber raw materials, treatment of the fiber raw materials and preparation of the wall clothing, and particularly comprises the following steps: respectively spinning and twisting various natural plant fibers into single yarns; then blending into double strands or a plurality of strands of yarns; cutting into segments serving as the fiber raw materials; wetting the fiber raw materials with water; steaming, boiling, dewatering and drying; and evenly mixing with basic viscose consisting of cotton cellulose and water-soluble vegetable gelatin so as to obtain the plant fiber blending wall clothing. After coating, the wall clothing is flat, fine and smooth in surface and uniform in color distribution, obvious silk yarn interweaving textures can be seen, a wall surface can be attractive, the effect of purifying the environment is good, the quality of an indoor environment can be improved, and the market prospect of the plant fiber blending wall clothing is wide.
Description
Technical field
The invention belongs to metope coating material technical field, be specifically related to a kind of string blending wall clothing and preparation method thereof.
Background technology
Wall surfacing product is generally to adopt paint or wallpaper, but traditional paint coating harmful substance contents is high, large to harm, though adopted in the market water paint, its harmful substance contents reduces, but existing national Specification still can allow a certain amount of free formaldehyde, this makes still need to after ventilating after a while, could live after room wall plastering, and wall pattern color is single, lacks aesthetic feeling; Although the application of wallpaper can be enriched pattern and the color of wall, its cost improves greatly, and service time of a specified duration there will be aging, variable color, be difficult for the problems such as repairing after damaged, meanwhile, wallpaper adhesive used contains formaldehyde more. Wall clothing is the novel decorative material for internal wall of the 3rd class occurring after the decorative material for internal wall such as paint, wallpaper, it processes through special scientific technology taking wood fibre, natural fiber as primary raw material, have attractive in appearance, containing harmful volatile ingredient, texture by force, not easy to crack, construct convenient pollution-free, repair the advantages such as simple and easy, be a kind of environmental protection, green internal wall finishing material.
Summary of the invention
The object of the present invention is to provide a kind of string blending wall clothing and preparation method thereof, it is undertaken after blending as fibrous raw material by the yarn that multiple natural plant fibre is twisted, make gained wall clothing material apply rear surface smooth, fine and smooth, distribution of color is even, and the visible significantly silk thread texture that interweaves, can make metope more attractive in appearance, and it have the effect of better environment purification, can improve indoor environmental quality, market prospects are wide.
For achieving the above object, the present invention adopts following technical scheme:
A kind of string blending wall clothing, its preparation method comprises the preparation of fibrous raw material, the processing of fibrous raw material, three parts of preparation of wall clothing;
Its step is as follows:
(1) preparation of fibrous raw material
1) multiple natural plant fibre is weaved respectively and is twisted single count yarn of diameter 0.5mm-2.5mm, and dye as required different colours; Described natural plant fibre comprises bamboo fibre, wood-fibred, cotton fiber, fibre and soya;
2) various gained single count yarn blending are become to the bifilar or multi-strand yarns of diameter 1mm-5mm;
3) by step 2) gained yarn cuts into the line segment that length is 0.5cm-3cm, obtains fibrous raw material;
(2) fibrous raw material processing
1) gained fibrous raw material water is soaked completely, in 100 DEG C of steam boxs, steam 20-25min;
2) fibrous raw material steaming is cooled to 40 DEG C-50 DEG C, then in boiling water, rolls and boil 12-15min;
3) will roll and boil fibrous raw material centrifugal dehydration 5-10min after treatment;
4) fiber after processed is dried to 30min to fibrous raw material bone dry at 60 DEG C-70 DEG C;
(3) preparation of wall clothing
1) gossypin, water-soluble plant glue are mixed as basic viscose glue by weight 1:1-1:2;
2) fibrous raw material after treatment and basic viscose glue are stirred in mixing equipment after discharging and get final product.
The construction method of described string blending wall clothing is: described string blending wall clothing is stirred after 1:3-1:5 is watered, leave standstill 30min, before use, again stir, be then applied on metope, smearing thickness is 2-5mm, after dry and hard and get final product.
In prior art, due to fibrous raw material and auxiliary material roughly similar in unit volume, weight, the phenomenon that causes fibrous raw material easily to be united, thus cause the fiber skewness as the main material of functional form, affect the realization of the attractive in appearance and material environment friendly performance of body of wall; Meanwhile, due to the exclusiveness between fiber, make traditional wall clothing directly several functionalities fiber type be mixed and to be produced, caused the central bottleneck of wall clothing product processes development. String blending wall clothing of the present invention is by becoming bifilar or multi-strand yarns by direct single count yarn blending, make the fibrous raw material of preparing be yam-like, not only make fibrous raw material present a contrast with auxiliary material from volume, weight, thereby can both realize good being evenly distributed in the middle of production and construction, so that it can reach the most stable effect from outward appearance and function, also solve the problem that the fiber not of the same race that causes because of fiber exclusiveness can not and be deposited, made the raw material of string wall clothing select face greatly to improve.
On the other hand, the adsorption function of traditional plant fiber wall clothing self all builds on string self and has many cracks not of uniform size, fold, can, by the harmful substance in absorbed air, reach the effect purifying the air of a room by the circulation of air. The present invention adopts the treatment process of innovation, utilize the absorption affinity of string, by fibrous raw material water-soaked, make moisture be full of the original crack of string, again by high temperature steam, boil, the operation such as centrifugal dehydration makes that crack increases, fold increases, and changed the structure of wall clothing internal fiber, makes that wall clothing is inner produces more cracks, thereby strengthen the permeability of product, also made product adsorb more free foreign matter and pernicious gas by cross-ventilation. The purifying formaldehyde efficiency of string blending wall clothing material of the present invention can reach more than 88%, simultaneously humidity absorption and release performance be up to state standards more than 2 times, prove that it has good environment purification and humidity conditioning function.
In addition, traditional wall clothing easily runs into because repeatedly constructing in work progress to be smeared and causes the undue situation of disperseing of fiber, has a strong impact on the visual effect of product texture, color aspect. And adopt string blending wall clothing of the present invention to construct, because it has first become fiber yarn by filament blending, can make the tightr of combination between fiber, the resistance to application property of reinforcement material, under 10 dual intensities, construction can not make fiber occur the situation of disperseing yet repeatedly, and the metope texture color after gained applies is clear, can as traditional wall clothing, not occur that texture is fuzzy, the phenomenon of color distortion.
Brief description of the drawings
Fig. 1 is the comparison diagram of gained wood-fibred pattern before and after blending, wherein, and before figure A is blending, after figure B is blending.
Fig. 2 is the electron-microscope scanning figure of fibrous raw material, and wherein, figure A is fibrous raw material before treatment, and figure B is fibrous raw material after treatment.
Fig. 3 is the surperficial comparison diagram of traditional plant fiber wall clothing and string blending wall clothing of the present invention.
Detailed description of the invention
In order to make content of the present invention more be convenient to understand, below in conjunction with detailed description of the invention, technical solutions according to the invention are described further, but the present invention is not limited only to this.
Embodiment 1
A kind of string blending wall clothing material, its preparation method following steps:
(1) preparation of fibrous raw material
1) 3 weight portion bamboo fibres, 5 weight portion cotton fibers are weaved respectively and are twisted single count yarn of diameter 0.5mm, and dye as required different colours;
2) various gained single count yarn blending are become to the bifilar yarn of diameter 1mm;
3) by step 2) gained yarn cuts into the line segment that length is 0.5cm, obtains fibrous raw material;
(2) processing of fibrous raw material
1) after gained fibrous raw material water is soaked completely, in 100 DEG C of steam boxs, steam 20min, then exhaust, unpacking, takes out fibrous raw material;
2) fibrous raw material steaming is cooled to 40 DEG C, then in boiling water, rolls and boil 15min;
3) will roll and boil fibrous raw material after treatment processed 5min in centrifugal drier;
4) fibrous raw material after processed is taken out, dry 30 minutes to fibrous raw material bone dry in 60 DEG C;
(3) preparation of wall clothing
1) gossypin, water-soluble plant glue are mixed as basic viscose glue by weight 1:1;
2) fibrous raw material after treatment and basic viscose glue are put into mixing equipment, after stirring, discharging packaging gets product.
Embodiment 2
A kind of string blending wall clothing material, its preparation method following steps:
(1) preparation of fibrous raw material
1) 3 weight portion bamboo fibres, 3 weight portion wood-fibreds, 6 weight portion fibre and soyas are weaved respectively and are twisted single count yarn of diameter 1.0mm, and dye as required different colours;
2) various gained single count yarn blending are become to the multi-strand yarns of diameter 2mm;
3) by step 2) gained yarn cuts into the line segment that length is 1cm, obtains fibrous raw material;
(2) processing of fibrous raw material
1) after gained fibrous raw material water is soaked completely, in 100 DEG C of steam boxs, steam 30min, then exhaust, unpacking, takes out fibrous raw material;
2) fibrous raw material steaming is cooled to 45 DEG C, then in boiling water, rolls and boil 13min;
3) will roll and boil fibrous raw material after treatment processed 6min in centrifugal drier;
4) fibrous raw material after processed is taken out, dry 30 minutes to fibrous raw material bone dry in 65 DEG C;
(3) preparation of wall clothing
1) gossypin, water-soluble plant glue are mixed as basic viscose glue by weight 1:1.3;
2) fibrous raw material after treatment and basic viscose glue are put into mixing equipment, after stirring, discharging packaging gets product.
Embodiment 3
A kind of string blending wall clothing material, its preparation method following steps:
(1) preparation of fibrous raw material
1) 3 weight portion bamboo fibres, 3 weight portion cotton fibers, 2 weight portion fibre and soyas are weaved respectively and are twisted single count yarn of diameter 2.5mm, and dye as required different colours;
2) various gained single count yarn blending are become to the multi-strand yarns of diameter 5mm;
3) by step 2) gained yarn cuts into the line segment that length is 3cm, obtains fibrous raw material;
(2) processing of fibrous raw material
1) after gained fibrous raw material water is soaked completely, in 100 DEG C of steam boxs, steam 50min, then exhaust, unpacking, takes out fibrous raw material;
2) fibrous raw material steaming is cooled to 50 DEG C, then in boiling water, rolls and boil 12min;
3) will roll and boil fibrous raw material after treatment processed 10min in centrifugal drier;
4) fibrous raw material after processed is taken out, dry 30 minutes to fibrous raw material bone dry in 70 DEG C.
(3) preparation of wall clothing
1) gossypin, water-soluble plant glue are mixed as basic viscose glue by weight 1:2;
2) fibrous raw material after treatment and basic viscose glue are put into mixing equipment, after stirring, discharging packaging gets product.
Fig. 1 is the comparison diagram of wood-fibred pattern before and after blending, wherein schemes before A is blending, after figure B is blending. As can be seen from the figure, before blending, wood-fibred is cotton-shaped, and loosely organized, texture is in disorder; After blending, wood-fibred yarn is twisted wire shape, compact conformation, clean mark. In the middle of practical application, wall clothing prepared by employing blended material will be considerably beyond the product that adopts the fibrous raw material of not blending to prepare in fibre strength, friction tolerance.
Fig. 2 is the electron-microscope scanning figure of fibrous raw material, and wherein scheming A is fibrous raw material before treatment, and figure B is fibrous raw material after treatment. As can be seen from the figure, after treatment, string surface folding, hole increase greatly.
Fig. 3 is the surperficial comparison diagram of traditional plant fiber wall clothing and string blending wall clothing of the present invention, and wherein left hurdle is traditional plant fiber wall clothing, and right hurdle is string blending wall clothing of the present invention. Can be found out with the contrast of Fig. 3 (B) by Fig. 3 (A), the phenomenon that the visible fiber in traditional plant fiber wall clothing construction rear surface is united, and string blending wallpaper fiber of the present invention is uniformly dispersed; Can be found out with the contrast of Fig. 3 (D) by Fig. 3 (C), traditional plant fiber wall clothing is after repeatedly constructing, disperse, wear and tear because excessive friction can cause surface fiber, and string blending wall clothing of the present invention is constructed afterwards by equality strength, texture is still clear and legible; Contrast by Fig. 3 (E) and Fig. 3 (F) can find out, traditional plant fiber wall clothing surface is almost without crack, and has obvious crack between string blending wall clothing superficial makings of the present invention.
1. purifying formaldehyde effect test
According to the method for regulation in JC/T1074-2008 " room air macerate function coating material purifying property ", embodiment of the present invention 1-3 gained string blending wall clothing material is tested, the results are shown in Table 1.
Table 1 purifying formaldehyde effect test result
From table 1, the clean-up effect of string blending wall clothing PARA FORMALDEHYDE PRILLS(91,95) of the present invention is remarkable, and clean-up effect is lasting, illustrates that it has the effect of good purifying formaldehyde.
2. regulate humid test
According to the regulation in JC/T2082-2011 " humidity conditioning function interior architecture ornament materials ", embodiment of the present invention 1-3 gained string blending wall clothing material is carried out to humidity test, the results are shown in Table 2.
Table 2 humidity result of the test
From table 2, string blending wall clothing of the present invention has good humidity, can bring into play the effect that regulates indoor humidity.
Claims (4)
1. a preparation method for string blending wall clothing, is characterized in that: comprise the preparation of fibrous raw material, the processing of fibrous raw material, three parts of preparation of wall clothing;
Its step is as follows:
(1) preparation of fibrous raw material
1) multiple natural plant fibre is weaved respectively and is twisted single count yarn of diameter 0.5mm-2.5mm, and dye as required different colours;
2) various gained single count yarn blending are become to the bifilar or multi-strand yarns of diameter 1mm-5mm;
3) by step 2) gained yarn cuts into the line segment that length is 0.5cm-3cm, obtains fibrous raw material;
(2) processing of fibrous raw material
1) gained fibrous raw material water is soaked completely, in 100 DEG C of steam boxs, steam 20-25min;
2) fibrous raw material steaming is cooled to 40 DEG C-50 DEG C, then in boiling water, rolls and boil 12-15min;
3) will roll and boil fibrous raw material centrifugal dehydration 5-10min after treatment;
4) fiber after processed is dried to 30min to fibrous raw material bone dry at 60 DEG C-70 DEG C;
(3) preparation of wall clothing
1) gossypin, water-soluble plant glue are mixed as basic viscose glue by weight 1:1-1:2;
2) fibrous raw material after treatment and basic viscose glue are stirred in mixing equipment after discharging and get final product.
2. the preparation method of string blending wall clothing according to claim 1, is characterized in that: described natural plant fibre comprises bamboo fibre, wood-fibred, cotton fiber, fibre and soya.
3. the string blending wall clothing that preparation method makes as claimed in claim 1.
4. string blending wall clothing according to claim 3, it is characterized in that: its construction method is: described string blending wall clothing is stirred after 1:3-1:5 is watered, leave standstill 30min, before use, again stir, then be applied on metope, smearing thickness is 2-5mm, after dry and hard and get final product.