CN105598328B - 模具钢锻造生产方法 - Google Patents

模具钢锻造生产方法 Download PDF

Info

Publication number
CN105598328B
CN105598328B CN201610030273.XA CN201610030273A CN105598328B CN 105598328 B CN105598328 B CN 105598328B CN 201610030273 A CN201610030273 A CN 201610030273A CN 105598328 B CN105598328 B CN 105598328B
Authority
CN
China
Prior art keywords
forging
time
temperature
fire
mould steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610030273.XA
Other languages
English (en)
Other versions
CN105598328A (zh
Inventor
王永军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sinosteel Xingtai Machinery and Mill Roll Co Ltd
Original Assignee
Sinosteel Xingtai Machinery and Mill Roll Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sinosteel Xingtai Machinery and Mill Roll Co Ltd filed Critical Sinosteel Xingtai Machinery and Mill Roll Co Ltd
Priority to CN201610030273.XA priority Critical patent/CN105598328B/zh
Publication of CN105598328A publication Critical patent/CN105598328A/zh
Application granted granted Critical
Publication of CN105598328B publication Critical patent/CN105598328B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种模具钢锻造生产方法，包括以下步骤，A、对锻造工具进行预热；B、制作模具钢钢锭；C、第一火次，大平台镦粗，采用WHF法拔长，D、第二火次，先压扁方锻造，再修侧面，然后立起镦粗，E、第三至四火次，继续拔扁方锻造，大面与侧面交替生产。大面压下与修侧面交替进行，利用回复再结晶提高金属塑性，防止角裂。优化了锻造方式，端部进砧压下，反向压平，减小轴向拉应力，防止接砧处拉裂。

Description

模具钢锻造生产方法
技术领域
本发明涉及一种模具钢锻造生产方法，尤其是用于H11或H13模具钢的锻造方法。
背景技术
在锻造生产模具钢时，锻造工艺一般采用两次镦拔，上下平砧锻造，采用WHF锻造法，锻造时表面及角部易出现裂纹，造成产品火次增多或者角裂过深导致产品致废。
发明内容
本发明要解决的技术问题是提供一种模具钢锻造生产方法，能够减少模具钢角部的裂纹。
为解决上述技术问题，本发明所采取的技术方案是：
模具钢锻造生产方法，包括以下步骤，
A、对锻造工具进行预热；
B、制作模具钢钢锭；
C、第一火次，加热温度1220℃，锻造时间为30分钟，锻造步骤为直接在大平台上镦粗，镦粗比为2.2以上，然后轴向采用WHF锻造法拔长为正方，每趟压下量20%；
D、第二火次，加热温度1220℃，锻造时间为30分钟，锻造步骤为先压扁方锻造，再修侧面，然后立起镦粗，镦粗比为1.6以上，最后继续修扁方至一定尺寸，预留锻比1.3~1.7；
E、第三至四火次，加热温度1200℃，继续拔扁方锻造，大面与侧面交替生产，锻出近似直角。
本发明的进一步改进在于：步骤A中预热温度为200~250℃，预热时间不小于6小时。
本发明的进一步改进在于：步骤C中采用WHF锻造法拔长为正方，每趟压下量20%。
本发明的进一步改进在于：步骤E锻造成品过程中第一趟压下量为120mm，然后逐趟减小压下量，每趟减少的压下量为30~60mm，最小压下量为20mm。
本发明的进一步改进在于：锻造过程随时进行氧化皮吹扫，防止氧化皮凹坑。
由于采用上述技术方案，本发明所产生的有益效果在于：
本发明一种模具钢锻造生产方法，能够减少模具钢角部的裂纹。大面压下与修侧面交替进行，利用回复再结晶提高金属塑性，防止角裂。优化了锻造方式，端部进砧压下，反向压平,减小轴向拉应力,防止接砧处拉裂。
对锻造工具进行预热可防止工具吸热造成表面温度低，角部散热快温度更低，因塑性差造成角部裂纹。
具体实施方式
模具钢锻造生产方法，包括以下步骤，
A、对锻造工具进行预热；热温度为200~250℃，预热时间不小于6小时。对锻造工具预热可防止工具吸热造成锻造件表面温度低，角部散热快温度更低，因塑性差造成角部裂纹。
B、制作模具钢钢锭。
C、第一火次，加热温度1220℃，终锻温度为860℃，锻造时间为30分钟。锻造的方法是直接在大平台上镦粗，镦粗比为2.2以上，然后轴向采用WHF锻造法拔长为正方，每趟压下量20%。
D、第二火次，加热温度1220℃，终锻温度为860℃，锻造时间为30分钟，锻造步骤为先压扁方锻造，再修侧面，然后立起镦粗，镦粗比为1.6以上，最后继续修扁方至一定尺寸，预留锻比1.3~1.7。拔扁方后立起镦平两端，保证出角长度，提高钢锭出材率，同时在不增加锻造火次的前提下起到二次镦粗作用。
E、根据实际情况判断需要三火次或是四火次，第三火次和第四火次加热温度1200℃，终锻温度为860℃，最后一次火次的锻造时间为40分钟，锻造步骤为拔扁方锻造，大面与侧面交替生产，锻出近似直角。拔扁方锻造时，第一趟压下量为120mm，然后逐趟减小压下量，每趟减少的压下量为30~60mm，最小压下量为20mm。
在锻造过程中钳口夹持处与锻造变形处过渡圆滑，防止有尖角尖棱造成角裂；减小成品火次预留宽度和厚度余量，避免角部变形过大产生裂纹。

Claims (2)

1.模具钢锻造生产方法，其特征在于：包括以下步骤，
A、对锻造工具进行预热；
B、制作模具钢钢锭；
C、第一火次，加热温度1220℃，终锻温度为860℃，锻造时间为30分钟，锻造步骤为直接在大平台上镦粗，镦粗比为2.2以上，然后轴向采用WHF锻造法拔长为正方，每趟压下量20%；
D、第二火次，加热温度1220℃，终锻温度为860℃，锻造时间为30分钟，锻造步骤为先压扁方锻造，再修侧面，然后立起镦粗，镦粗比为1.6以上，最后继续修扁方至一定尺寸，预留锻比1.3～1.7；
E、第三至四火次，加热温度1200℃，终锻温度为860℃，继续拔扁方锻造，大面与侧面交替生产，锻出近似直角；
步骤A中预热温度为200～250℃，预热时间不小于6小时；
步骤E锻造成品过程中第一趟压下量为120mm，然后逐趟减小压下量，每趟减少的压下量为30～60mm，最小压下量为20mm。
2.根据权利要求1所述的模具钢锻造生产方法，其特征在于：锻造过程随时进行氧化皮吹扫,防止氧化皮凹坑。
CN201610030273.XA 2016-01-18 2016-01-18 模具钢锻造生产方法 Active CN105598328B (zh)