CN105564116A - Sand sculpture handicraft and making technology thereof - Google Patents
Sand sculpture handicraft and making technology thereof Download PDFInfo
- Publication number
- CN105564116A CN105564116A CN201410551743.8A CN201410551743A CN105564116A CN 105564116 A CN105564116 A CN 105564116A CN 201410551743 A CN201410551743 A CN 201410551743A CN 105564116 A CN105564116 A CN 105564116A
- Authority
- CN
- China
- Prior art keywords
- sand
- adhesive
- reinforcing agent
- handicraft
- husky
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a sand sculpture handicraft and a making technology thereof. The sand sculpture handicraft comprises sand with the particle size ranging from 80 meshes to 120 meshes, bonding agent and reinforcing agent. The making technology includes the steps that the components are mixed, shaped and solidified, and the sand sculpture handicraft is obtained. The whole color of the finished product is the natural color of the sand, and the surface is smooth. The sand sculpture handicraft has the advantages of being unique and practical in making technology, high in plasticity and compactibility, attractive, smooth in surface and textured, and having the natural color of the sand.
Description
Technical field
The present invention relates to handicraft, especially a kind of sand-plastic handicraft and manufacture craft thereof.
Background technology
Sand, is distributed widely in desert, seabeach and riverbed etc., except building field, always not for he uses.Husky very difficult shaping, thus utilize and husky make the forming technology product with different-style for raw material, also not good process, the husky craft articles of the utilization that can see only have the method sandblasted on the formative substance such as plastics, gypsum, but, the handicraft made lacks texture, sand easily comes off, poor surface smoothness, unsightly.
Summary of the invention
The object of this invention is to provide a kind of reasonable mixture ratio, plasticity be strong, density good, can keep sand-plastic handicraft and the manufacture craft thereof of husky true qualities.
For achieving the above object, the following technical scheme of Bian of the present invention: a kind of sand-plastic handicraft, component is the sand of granularity between 80-120 order, adhesive, reinforcing agent; Each component proportion is:
Husky: 50-80%
Adhesive: 10-40%
Reinforcing agent: 0-40%
Wherein, reinforcing agent is general water curable type coagulating agent;
By the mixing of above component, moulding, solidify and get final product, finished product entirety color and luster is husky true qualities, smooth surface.
Concrete manufacturing process steps is:
Sand, adhesive, reinforcing agent are fully mixed according to the ratio of 50-80%, 10-40%, 0-40%;
It is closely knit, moulding that mixture puts into mould;
Closely knit good mould is put into saggar and is heated more than 100 minutes in 80-150 ° of C.
Take out mould, after the demoulding and get final product.
The present invention possesses following effect:
Manufacture craft is unique, practical;
Plasticity is strong, and density is good;
Natural, attractive in appearance, the husky true qualities of tool;
Smooth surface, there is texture.
Below in conjunction with embodiment, the present invention is further described.
Embodiment one:
Get the Desert Sand of granularity between 80-120 order 800 grams, 107 100 grams, glue, the reinforcing agent of inorganic salts
:land plaster 100 grams, fully mixes.
It is closely knit moulding that mixture puts into mould.
By closely knit good mould, put into baking oven and heat 100 minutes in 150 ° of C.
After taking out mould, obtain the sand-plastic handicraft that color and luster is husky true qualities, ganoid required style.
Embodiment two:
Get the beach sand of granularity between 80-120 order 600 grams, one in the aqueous type adhesives such as poly-vinyl alcohol solution, Pioloform, polyvinyl acetal solution, pollopas and modified urea-formaldehyde resin glue, 200 grams, one in the silicates reinforcing agents such as cement, white cement, kaolin, diatomite and bentonite, 200 grams, fully mix.
It is closely knit moulding that mixture puts into mould.
By closely knit good mould, put into baking oven and heat 120 minutes in 120 ° of C.
After taking out mould, obtain the sand-plastic handicraft that color and luster is husky true qualities, ganoid required style.
Embodiment three:
Get the Desert Sand of granularity between 80-120 order 500 grams, be furnished with the one in the reaction-ing adhesives such as the epoxy resin of curing agent and plasticizer, modified epoxy, unsaturated-resin, 350 grams, Cornstarch 150 grams, fully mixes.
It is closely knit moulding that mixture puts into mould.
By closely knit good mould, put into baking oven and heat 150 minutes in 100 ° of C.
After taking out mould, obtain the sand-plastic handicraft that color and luster is husky true qualities, ganoid required style.
Claims (5)
1. a sand-plastic handicraft, it is characterized in that component is the sand of granularity between 80-120 order, adhesive, reinforcing agent, each component proportion is:
Husky: 50-80%
Adhesive: 10-50%
Reinforcing agent
:0-40%
Wherein, reinforcing agent is general water curable type coagulating agent;
By the mixing of above component, moulding, solidify and get final product, finished product entirety color and luster is husky true qualities, smooth surface.
2. sand-plastic handicraft as claimed in claim 1, it is characterized in that adhesive is water-soluble and response type two class, aqueous type adhesive is poly-vinyl alcohol solution and Pioloform, polyvinyl acetal solution, pollopas and modified urea-formaldehyde resin, and reaction-ing adhesive is be furnished with the epoxy resin of curing agent and plasticizer, modified epoxy and unsaturated-resin.
3. sand-plastic handicraft as claimed in claim 1, it is characterized in that described reinforcing agent has silicates and inorganic salts, silicates is cement, white cement, kaolin, diatomite and bentonite; Inorganic salts are talcum powder, land plaster, Cornstarch.
4. a manufacture craft for sand-plastic handicraft, concrete steps are:
By sand, adhesive, reinforcing agent according to 50-80%, 10-40%, 0-40%.
5. ratio fully mixes;
It is closely knit, moulding that mixture puts into mould;
Closely knit good mould is put into baking oven and is heated more than 100 minutes in 80-150 ° of C.