CN110194022A - A kind of sand sculpture process product and preparation method thereof - Google Patents
A kind of sand sculpture process product and preparation method thereof Download PDFInfo
- Publication number
- CN110194022A CN110194022A CN201910518378.3A CN201910518378A CN110194022A CN 110194022 A CN110194022 A CN 110194022A CN 201910518378 A CN201910518378 A CN 201910518378A CN 110194022 A CN110194022 A CN 110194022A
- Authority
- CN
- China
- Prior art keywords
- sand
- silica gel
- mother matrix
- molding
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sand sculpture process product and preparation method thereof, include the following steps: S1, modeling: production pre-manufactured model;Making material uses plasticine, gypsum, mud of making pottery, the nuisanceless finished-product material such as 3D printer, by a figure by position grouping molding;By the way that using pinching, the gimmicks such as engraving mould 3 D stereo mother matrix by hand;S2, molding: making material uses silica gel, and mother matrix bottom is placed in the papery of projected area, reserves the gap of 50mm in wooden or metallic box and between outer rim and the edge of the prefabricated mother matrix, bezel height is the 1/3 of mother matrix.Then in the prefabricated uniform brushing release agent of master surfaces, perfusion silica gel forms it into thin film at the top of mother matrix again, and the present invention mixes with drift-sand by using burning colorful sand and carries out note film, bright in luster, weatherability is strong, wear-resisting acid and alkali-resistance, good visual effect are high-grade beautiful, make full use of drift-sand, so that cost of material is low, production process is simple, convenient for operation.
Description
Technical field
The present invention relates to sand carving correlative technology field, specially a kind of sand sculpture process product and preparation method thereof.
Background technique
Sand carving is a kind of sculpture art, is sand drift product and to solidify, then chisels and carves into the skill of various moulding
Art, large-scale combined sand carving can sufficiently show the big scale of construction moulding of sand carving, and each unit sand carving in large-scale combined sand carving surrounds one
A theme will make sand carving works have stronger interesting plot and interest, enhance the cultural connotation of works.
But existing sand sculpture process product production method has the disadvantage in that production process complexity, is not easy to operate, at
The visual effect of product is general, and weatherability and resistance to acid and alkali are bad, and cost of material is high, needs to improve.
Summary of the invention
The purpose of the present invention is to provide a kind of sand sculpture process product and preparation method thereof, to solve to mention in above-mentioned background technique
The production process arrived is complicated, is not easy to operate, the visual effect of finished product is general, and weatherability and resistance to acid and alkali are bad, and raw material
Problem at high cost.
To achieve the above object, the invention provides the following technical scheme: a kind of sand sculpture process product and preparation method thereof, including
Following steps:
S1, modeling: production pre-manufactured model;Making material use plasticine, gypsum, make pottery mud, 3D printer etc. it is nuisanceless at
One figure is grouped molding by position by product material;By the way that using pinching, the gimmicks such as engraving mould 3 D stereo mother matrix by hand;
S2, molding: making material uses silica gel, and mother matrix bottom is placed in the papery of projected area, wooden or metallic
Box in and between outer rim and the edge of the prefabricated mother matrix reserve 50mm gap, bezel height be mother matrix 1/3, add
The purpose of frame is to prevent silica gel slime flux;Then in the prefabricated uniform brushing release agent of master surfaces, then the perfusion at the top of mother matrix
Silica gel forms it into thin film, dips 5 times formation silica gel of silica-gel coating with brush again after film silica gel is consolidated to no flowing
Mold;
S3, slurrying: being weighed the burning colorful sand or drift-sand of different colours by different colours respectively, by weighed burning colorful sand
It is uniformly mixed with adhesive respectively and meets 3 D stereo sculpture mortar;
S4, injection molding: by the mortar made by mold obtained by the grouping of three-dimensional graph mold respectively disposable injection
It is interior;
S5, solidification: oven isothermal curing stands the figure mold after injection molding under oven constant temperature (30-45 DEG C)
1.5h-3h。
S6, demoulding: it can be demoulded after 1.5h-3h;It is 16h-24h that the time, which is fully cured,;
S7, post-production: will demould gained finished product and polish, and local characteristic desert surprise stone is pasted and used in combination after polishing,
Finished product bone carving, finished product woodcarving, finished product silver carving, finished product coral, livestock fur etc. are decorated with adhesive.
Preferably, the molding further includes plate part way: first by prefabricated plate embossment model add papery, it is wooden or
Metallic outer rim, the height of the outer rim are greater than or equal to the height of the prefabricated mother matrix, the outer rim and prefabricated molds
There are the gap 50mm between the edge of type, bezel height is the 1/3 of mother matrix, and the purpose for adding frame is to prevent mold silica gel slime flux, so
Afterwards in pre-manufactured model surface even application release agent, after release agent is dry, silica gel is injected in Xiang Suoshu outer rim;To silica gel solid
Outer rim is removed after chemical conversion type, the mold silica gel of curing molding and the prefabricated mother matrix are separated to come, final gained and figure
Consistent plate embossment mother matrix.
Preferably, the molding specifically includes:
A, 10 parts of the sand for being 80-120 with subject is uniformly mixed and made into 3 D stereo sand with 1 part of adhesive of weight proportion
Slurry;
B, sand is uniformly mixed and made into 3 D stereo sand former material with 5 parts of drift-sand of weight proportion by 5 parts of burning colorful sand
Material.
The present invention provides a kind of sand sculpture process product and preparation method thereof, have it is following the utility model has the advantages that
(1) present invention, which is mixed by using burning colorful sand with drift-sand, carries out note film, and bright in luster, weatherability is strong, wear-resisting
Acid and alkali-resistance, good visual effect is high-grade beautiful, and makes full use of drift-sand, so that cost of material is low, production process is simple, just
In operation.
Specific embodiment
Embodiment 1:
Make pre-manufactured model;Making material uses plasticine, and gypsum, mud of making pottery, the nuisanceless finished-product material such as 3D printer will
One figure is grouped molding by position;By the way that using pinching, the gimmicks such as engraving mould 3 D stereo mother matrix by hand;Making material uses
Mother matrix bottom is placed in the papery of projected area, in wooden or metallic box and outer rim and the preform carrier by silica gel
The gap of 50mm is reserved between the edge of version, bezel height is mother matrix 1/3, and the purpose for adding frame is to prevent silica gel slime flux;Then exist
The uniform brushing release agent of prefabricated master surfaces, then perfusion silica gel forms it into thin film at the top of mother matrix, to thin film silicon
Gelling dips 3 times formation silica gel moulds of silica-gel coating with brush again after consolidating to no flowing;Weigh different face respectively by different colours
The burning colorful sand or drift-sand of color, weighed burning colorful sand is uniformly mixed with adhesive respectively and meets 3 D stereo sculpture
Mortar;10 parts of the sand for being 80-120 with subject is uniformly mixed and made into 3 D stereo mortar with 1 part of adhesive of weight proportion;It is husky
Son is uniformly mixed and made into 3 D stereo sand raw material with 5 parts of drift-sand of weight proportion by 5 parts of burning colorful sand;It is made described
Mortar by the grouping of three-dimensional graph mold respectively disposable injection gained mold;Normal temperature laboratory solidification, after injection molding
The figure mold places constant temperature (30-45 DEG C) in oven, can demould after 1.5h-3h;It is 16h- that the time, which is fully cured,
24h;Gained finished product polishing will be demoulded, combination pastes and uses local characteristic desert surprise stone, finished product bone carving, finished product wood after polishing
Carving, finished product silver carving, finished product coral, livestock fur etc. are decorated with adhesive, keep the finished product finally presented more lively beautiful.
Embodiment 2:
Make pre-manufactured model;Making material is using plate embossment and three-dimensional portion mother matrix;Making material uses silica gel;Plate
Part way: adding papery, wooden or metallic outer rim for prefabricated plate embossment model first, and the height of the outer rim is greater than
Or the height equal to the prefabricated mother matrix, there are the gaps 50mm between the outer rim and the edge of pre-manufactured model, add the mesh of frame
Be to prevent mold silica gel slime flux, then in pre-manufactured model surface even application release agent, after release agent is dry, to described outer
Silica gel is injected in frame;Outer rim is removed after silica gel curing molding, by the mold silica gel of curing molding and the prefabricated mother matrix
It is separated from and, final gained and the consistent plate embossment mother matrix of figure;Three-dimensional portion way: use material: plasticine, gypsum,
Pottery mud, the nuisanceless finished-product material such as 3D printer;By visuals moulding with pinching, the gimmicks such as engraving mould 3 D stereo mother matrix,
Perfusion silica gel forms it into thin film at the top of from mother matrix, dips silica gel with brush again after film silica gel is consolidated to no flowing and applies
5 times formation silica gel mould of layer;The burning colorful sand or drift-sand for weighing different colours respectively by different colours, weighed sintering is color
Sand is uniformly mixed with adhesive respectively meets 3 D stereo sculpture mortar;With subject be 80-120 10 parts of sand and bonding
The weight proportion that 1 part of agent is uniformly mixed and made into 3 D stereo mortar;Sand is matched by 5 parts of burning colorful sand with 5 parts of drift-sand of weight
Than being uniformly mixed and made into 3 D stereo sand raw material;By the mortar made by plate embossment and three-dimensional graph mold
Grouping is respectively in disposable injection gained mold;(30-45 DEG C) of oven constant temperature solidification, the figure mold after injection molding is existed
1.5h-3h is stood under normal temperature laboratory, can be demoulded after 1.5h-3h;It is 16h-24h that the time, which is fully cured,;Demoulding gained is put down
Plate embossment and partial 3-D finished product are polished, and combination is pasted and using local characteristic desert surprise stone, finished product bone carving, finished product wood after polishing
Carving, finished product silver carving, finished product coral, livestock fur etc. are decorated with adhesive;Combine the finished product plane finally presented with three-dimensional
Two-dimentional finished product.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of sand sculpture process product and preparation method thereof, which comprises the steps of:
S1, modeling: production pre-manufactured model;Making material uses plasticine, gypsum, mud of making pottery, the nuisanceless finished product material such as 3D printer
One figure is grouped molding by position by material;By the way that using pinching, the gimmicks such as engraving mould 3 D stereo mother matrix by hand;
S2, molding: making material uses silica gel, and mother matrix bottom is placed in the papery of projected area, wooden or metallic side
The gap of 50mm is reserved in frame and between outer rim and the edge of the prefabricated mother matrix, the purpose for adding frame is to prevent silica gel slime flux;
Then in the prefabricated uniform brushing release agent of master surfaces, then silica gel is perfused at the top of mother matrix and forms it into thin film, to
Film silica gel dips 3 times formation silica gel moulds of silica-gel coating with brush again after consolidating to no flowing;
S3, slurrying: the burning colorful sand or drift-sand of different colours are weighed respectively by different colours, weighed burning colorful sand is distinguished
It is uniformly mixed with adhesive and meets 3 D stereo sculpture mortar;
S4, injection molding: by the mortar made by the grouping of three-dimensional graph mold respectively disposable injection gained mold;
S5, solidification: oven isothermal curing stands the figure mold after injection molding in oven under constant temperature (30-45 DEG C)
1.5h-3h;
S6, demoulding: it can be demoulded after 1.5h-3h;It is 16h-24h that the time, which is fully cured,;
S7, post-production: demoulding gained finished product is polished, and combination is pasted and using local characteristic desert surprise stone, finished product after polishing
Bone carving, finished product woodcarving, finished product silver carving, finished product coral, livestock fur etc. are decorated with adhesive.
2. a kind of sand sculpture process product according to claim 1 and preparation method thereof, which is characterized in that the molding further includes
Plate part way: prefabricated plate embossment model is added into papery, wooden or metallic outer rim, the height of the outer rim first
Height more than or equal to the prefabricated mother matrix adds frame there are the gap 50mm between the outer rim and the edge of pre-manufactured model
Purpose be to prevent mold silica gel slime flux, then in pre-manufactured model surface even application release agent, after release agent is dry, to institute
It states and injects silica gel in outer rim;Remove outer rim after silica gel curing molding, by the mold silica gel of curing molding with it is described prefabricated
Mother matrix, which is separated from, to be come, final gained and the consistent plate embossment mother matrix of figure.
3. a kind of sand sculpture process product according to claim 1 and preparation method thereof, which is characterized in that the molding is specifically wrapped
It includes:
A, 10 parts of the sand for being 80-120 with subject is uniformly mixed and made into 3 D stereo mortar with 1 part of adhesive of weight proportion;
B, sand is uniformly mixed and made into 3 D stereo sand raw material with 5 parts of drift-sand of weight proportion by 5 parts of burning colorful sand.