CN110157228A - A kind of powdery textured coating and its construction method - Google Patents
A kind of powdery textured coating and its construction method Download PDFInfo
- Publication number
- CN110157228A CN110157228A CN201910391830.4A CN201910391830A CN110157228A CN 110157228 A CN110157228 A CN 110157228A CN 201910391830 A CN201910391830 A CN 201910391830A CN 110157228 A CN110157228 A CN 110157228A
- Authority
- CN
- China
- Prior art keywords
- powdery
- parts
- textured coating
- powder
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to sculpture technical field of coatings, more particularly to a kind of powdery textured coating and its construction method, aim to solve the problem that the performances such as textured coating cold-hot cyclicity, alkali resistance, weatherability are poor, storage, transport are inconvenient, and the problem of higher cost, technical points are: being made of 3-5 parts of rubber powder by weight the following raw material, 30-40 parts of cement, 35-42 parts of filler, 10-12 parts of fiber, 5-8 parts of mineral powder, 1-2 parts of auxiliary agent；The rubber powder includes redispersible latex powder, hydroxypropyl methyl cellulose and the polyvinyl alcohol that weight proportion is 15:5:4, and the viscosity of the hydroxypropyl methyl cellulose is 100000mPas；The cement includes that the portland cement that weight proportion is 1:2-3 and beach are husky, and the partial size of the beach sand is not more than 0.2mm.Powdery sculpture coating prepared by the present invention is easy to use, and bond strength is high, has good alkali resistance and weatherability, and its is at low cost, suitable for being widely popularized.
Description
Technical field
The present invention relates to sculpture technical field of coatings, and in particular to a kind of powdery textured coating and its construction method.
Background technique
Sculpture, which refers to, to be moulded, for beautifying city or carve for commemoration meaning with certain implied meaning, symbol or pictograph
Visual article and souvenir.Sculpture is one kind of plastic arts, is also known as carved, and is carving, carves, the general name of three kinds of method for creating of modeling, refers to
With various plastic materials (such as gypsum, resin, clay) or hard material (such as timber, stone, metal, the jade that can carve, can carve
Block, agate, aluminium, glass reinforced plastic, sandstone, copper etc.), visual, the artistic image that can touch with certain space are createed, so as to reflection
Social life, the aesthetic method of art of expression man, Aesthetic Emotion, aesthetic ideal art.Carving substance is reduced by carving, carving
Material, modeling then increase plastic materials and qualities by heap to achieve the purpose that creation of art.
Textured coating belongs to a kind of three-dimensional Multi wall architectural coatings, and level distinctness is presented, and the strong decorative pattern of tactile sensation has
Excellent cohesion and good water resistance, alkali resistance and weatherability, is widely used in the protection of all kinds of building inner-outer walls
And decoration.
Textured coating currently on the market mainly coheres the cold-resistant thermal cycle of such product based on material with synthetic resin emulsion
Property, the performances such as alkali resistance, weatherability it is poor, storage, transport are inconvenient, and higher cost.
Therefore, in view of the above-mentioned problems, the invention proposes further solutions.
Summary of the invention
Therefore, the technical problem to be solved in the present invention is that overcoming textured coating cold-hot cyclicity, resistance in the prior art
The performances such as alkalinity, weatherability are poor, and storage, transport are inconvenient, and the defect of higher cost, to provide a kind of powdery embossment
Coating and its construction method.
Above-mentioned technical purpose of the invention has the technical scheme that
A kind of powdery textured coating is made of by weight the following raw material:
3-5 parts of rubber powder, 30-40 parts of cement, 35-42 parts of filler, 10-12 parts of fiber, 5-8 parts of mineral powder, 1-2 parts of auxiliary agent；
The rubber powder includes redispersible latex powder, hydroxypropyl methyl cellulose and the poly- second that weight proportion is 15:5:4
Enol, the viscosity of the hydroxypropyl methyl cellulose are 100000mPas；
The cement includes that the portland cement that weight proportion is 1:2-3 and beach are husky, and the partial size of the beach sand is not more than
0.2mm。
Optionally, the filler is talcum powder.
Optionally, the fiber is combination one or more in wollastonite fibre, durafiber and polypropylene fibre.
Optionally, the mineral powder is wollastonite powder.
Optionally, the auxiliary agent is bentonite or attapulgite.
A kind of construction method of powdery textured coating, comprising the following steps:
S1, with roller, spray gun in one layer of sculpture product upper berth putty, take advantage of putty it is not dry when, one layer of alkali-proof glass fibre of paving
Dimension, meanwhile, second layer putty is spread on this basis, and surface is made to reach flat and smooth；
S2, after hour for 24 hours is dry, be polishing to it is smooth, meanwhile, above-mentioned material is sequentially added in powder stirrer, is stirred
It mixes 20-30 minutes, configures powdering sculpture coating, water is added when use and obtains paste, stands 10min, makes after being stirred for
With paste uniform ground is applied on basal plane by spray coating method or the spatula of trowel wiping manipulation；
S3, after coating is completely dried, roller coating alkali-resistant primer, the condition in temperature lower than 5 DEG C or humidity higher than 85% is applied
Work；
After S4, brushing alkali-resistant primer 12h, first of low gloss finishing coat of roller coating is pressed first vertically, rear lateral, then vertical original
Then construct, therewith for 24 hours after, the construction of second finishing coat is carried out, to reduce color difference, pollute, connect raft.
Optionally, the alkali-resistant primer is styrene-acrylic emulsion.
Optionally, the low gloss finishing coat is semi-gloss pure C latex paint.
Technical solution of the present invention has the advantages that
1. powdery textured coating of the invention, can be to hardening by the type of rubber powder, structural form and distribution situation
The structure and performance of polyalcohol cement basis textured coating have an important influence on, and the structure after hardening is mainly by Behavior of Hardened Cement Paste phase and polymerization
Object phase composition, this two-phase passes through inorganic particle together with the water ratio limit of polymer particles intergranular in paint structure, polymer
The existence form and mutually stick that efficiency of the rubber powder in polyalcohol cement basis textured coating depends between polymer glue powder and cement
Knot effect；And inorganic coagulation material and main aggregate of the cement as powdery textured coating, on the one hand material is cohered as the hydraulicity
Material improves the bond strength of coating, while cement and rubber powder adapted, active cation are cooperateed with the hydrophilic anionic in rubber powder
Effect, further improves the water resistance of textured coating；Main aggregate of the another aspect cement as textured coating, can play increasing
Add coating richness, improves the effect of embossment three-dimensional decorative effect.
2. powdery textured coating of the invention, the setting of filler, since textured coating will make facing form uneven, layer
Secondary decorative effect clearly demarcated, three-dimensional sense is strong, if preparing textured coating, sprayability and application property as aggregate only with cement
It is poor；In addition, the specking of textured coating is small, dry dehydration is too fast, influences the formation of embossment intensity.To reduce cost, further
The richness and crack resistance for improving textured coating, reach good stereoscopic effect, certain filler need to be added, with aggregate adjustment one
A reasonable gradation, the comprehensive performance of Lai Tigao textured coating.
3. powdery textured coating of the invention, the setting of fiber guarantee that coating does not generate cracking during drying and moulding
Phenomenon improves coating initial dry cracking resistance.
4. powdery textured coating of the invention, the setting of mineral powder, addition can fill embossment cement slurry inside configuration
Gap and defect, reduce rubber powder filling gap and defect quantity, so that rubber powder is sufficiently wrapped in miberal powder and cement particle surface,
Rubber powder is easier to be connected to reticular structure under lower dosage in this way, to preferably inhibit the formation and extension in crack.
5. powdery textured coating of the invention, the setting of auxiliary agent should have since powdery textured coating is cement base products
Good water-retaining property and suitable operable time, with the abundant aquation of cement in guarantee system, to can be improved by auxiliary agent
The intensity of embossment, and there is setting time appropriate to guarantee the operating time of textured coating.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1:
A kind of powdery textured coating is made of by weight the following raw material:
3 parts of rubber powder, 30 parts of cement, 35 parts of filler, 10 parts of fiber, 5 parts of mineral powder, 1 part of auxiliary agent；
Type, structural form and the distribution situation of rubber powder can structure to the polyalcohol cement basis textured coating of hardening and
Performance has an important influence on, and the structure after hardening is mainly made of Behavior of Hardened Cement Paste phase and polymer phase, this two-phase in paint structure
Through inorganic particle together with the water ratio limit of polymer particles intergranular, polymer glue powder is in polyalcohol cement basis textured coating
Efficiency depend on existence form between polymer glue powder and cement and mutual cohesive action.And cement is as powdery textured coating
Inorganic coagulation material and main aggregate, on the one hand be used as hydraulicity binding material, improve the bond strength of coating, while cement
With rubber powder adapted, the hydrophilic anionic in active cation and rubber powder acts synergistically, and further improves the resistance to of textured coating
It is aqueous；Main aggregate of the another aspect cement as textured coating can play and increase coating richness, improve embossment stereo decoration
The effect of effect.
Wherein rubber powder includes redispersible latex powder, hydroxypropyl methyl cellulose and the poly- second that weight proportion is 15:5:4
Enol, the viscosity of the hydroxypropyl methyl cellulose are 100000mPas；Cement includes the silicate that weight proportion is 1:2-3
Cement and beach are husky, and the partial size of the beach sand can provide more no more than 0.2mm to prepare cement using beach sand for concrete
Raw material that are inexpensive and not influencing concrete performance.
Since textured coating will make facing form decorative effect uneven, well arranged, that three-dimensional sense is strong, if only adopted
Cement is used to prepare textured coating as aggregate, sprayability and application property are poor；In addition, the specking of textured coating is small, it is dry to lose
Water is too fast, influences the formation of embossment intensity.To reduce cost, the richness and crack resistance of textured coating are further increased, is reached
Certain filler need to be added in good stereoscopic effect, adjust a reasonable gradation, the synthesis of Lai Tigao textured coating with aggregate
Performance.In this embodiment of the invention, filler is talcum powder, and the drying shrinkage crack phenomenon of powdery textured coating can be effectively prevented.
Textured coating belongs to thick coating, it is desirable that has certain thickness, specking can also more just will have preferable solid
Sense, but be easy to crack in the drying process in this way.In order to guarantee that coating does not generate cracking during drying and moulding
Phenomenon, it is also necessary to a certain amount of fiber be added to improve coating initial dry cracking resistance, in this embodiment of the invention, fiber is
One or more combination in wollastonite fibre, durafiber and polypropylene fibre.
It just needs to brush overlay coating after generally drying for 24 hours after spraying textured coating, therefore it is preferable to require textured coating to have
Former intensity and early stage water resistance.Surfactant is attracted on the surface of ultrafine mineral powder, enhances its current potential, thus
Diminishing, dispersion, plasticising, filling and homogenization can be better played in embossment cement slurry, the compound of the two keeps cement floating
The microstructure of carving is finer and close.In this embodiment of the invention, mineral powder is wollastonite powder, and addition can fill embossment cement slurry
The gap of inside configuration and defect reduce the quantity in rubber powder filling gap and defect, rubber powder are made sufficiently to be wrapped in miberal powder and cement
Particle surface, such rubber powder are easier to be connected to reticular structure under lower dosage, to preferably inhibit the formation in crack
With extension.
Powdery textured coating is cement base products, should have good water-retaining property and suitable operable time, to guarantee
The abundant aquation of cement in system to improve the intensity of embossment, and has setting time appropriate to guarantee textured coating
Operating time.So the kind and performance of auxiliary agent are extremely important to physical property, the workability of textured coating.In the present invention
In this embodiment, auxiliary agent is bentonite or attapulgite.
Embodiment 2:
A kind of construction method of powdery textured coating, comprising the following steps:
S1, with roller, spray gun in one layer of sculpture product upper berth putty, the putty of selection is dry-type, by latex powder, modification
Silicate, inorganic filler and various auxiliary agents composition, take advantage of putty it is not dry when, one layer of alkali-resistant glass fibre of paving, meanwhile, it is basic herein
Upper berth second layer putty, makes surface reach flat and smooth；
S2, after hour for 24 hours is dry, be polishing to it is smooth, meanwhile, above-mentioned material is sequentially added in powder stirrer, is stirred
It mixes 20-30 minutes, configures powdering sculpture coating, water is added when use and obtains paste, stands 10min, makes after being stirred for
With paste uniform ground is applied on basal plane by spray coating method or the spatula of trowel wiping manipulation；
S3, after coating is completely dried, roller coating alkali-resistant primer, the condition in temperature lower than 5 DEG C or humidity higher than 85% is applied
Work, wherein alkali-resistant primer is styrene-acrylic emulsion；
After S4, brushing alkali-resistant primer 12h, first of low gloss finishing coat of roller coating is pressed first vertically, rear lateral, then vertical original
Then construct, therewith for 24 hours after, the construction of second finishing coat is carried out, to reduce color difference, pollute, connect raft, wherein low gloss finishing coat
For semi-gloss pure C latex paint.
Obviously, the above embodiments are merely examples for clarifying the description, and does not limit the embodiments.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of variation or
It changes.There is no necessity and possibility to exhaust all the enbodiments.And it is extended from this it is obvious variation or
It changes still within the protection scope of the invention.
Claims (8)
1. a kind of powdery textured coating, which is characterized in that be made of by weight the following raw material:
3-5 parts of rubber powder, 30-40 parts of cement, 35-42 parts of filler, 10-12 parts of fiber, 5-8 parts of mineral powder, 1-2 parts of auxiliary agent；
The rubber powder includes redispersible latex powder, hydroxypropyl methyl cellulose and the polyethylene that weight proportion is 15:5:4
Alcohol, the viscosity of the hydroxypropyl methyl cellulose are 100000mPas；
The cement includes that the portland cement that weight proportion is 1:2-3 and beach are husky, and the partial size of the beach sand is not more than 0.2mm.
2. a kind of powdery textured coating according to claim 1, which is characterized in that the filler is talcum powder.
3. a kind of powdery textured coating according to claim 1, which is characterized in that the fiber is wollastonite fibre, Du
One or more combination in dimension of towing and polypropylene fibre.
4. a kind of powdery textured coating according to claim 1, which is characterized in that the mineral powder is wollastonite powder.
5. a kind of powdery textured coating according to claim 1, which is characterized in that the auxiliary agent is bentonite or concave convex rod
Soil.
6. a kind of construction method of powdery textured coating described in -5 according to claim 1, which is characterized in that including following step
It is rapid:
S1, with roller, spray gun in one layer of sculpture product upper berth putty, take advantage of putty it is not dry when, one layer of alkali-resistant glass fibre of paving, together
When, second layer putty is spread on this basis, and surface is made to reach flat and smooth；
S2, after hour for 24 hours is dry, be polishing to it is smooth, meanwhile, above-mentioned material is sequentially added in powder stirrer, is stirred
20-30 minutes, powdering sculpture coating is configured, water is added when use and obtains paste, stands 10min, is used after being stirred for,
Paste uniform ground is applied on basal plane by spray coating method or the spatula of trowel wiping manipulation；
S3, after coating is completely dried, roller coating alkali-resistant primer, the condition in temperature lower than 5 DEG C or humidity higher than 85% is constructed；
S4, after brushing alkali-resistant primer 12h, first of low gloss finishing coat of roller coating, by first vertical, it is rear laterally, then vertical principle into
Row construction, therewith for 24 hours after, the construction of second finishing coat is carried out, to reduce color difference, pollute, connect raft.
7. a kind of powdery textured coating according to claim 6 and its construction method, which is characterized in that the alkali-resistant primer
For styrene-acrylic emulsion.
8. a kind of powdery textured coating according to claim 6 and its construction method, which is characterized in that the low gloss face
Paint is semi-gloss pure C latex paint.