CN105542934A - Smart phone glass cover plate grinding fluid and preparation method and method of application thereof - Google Patents
Smart phone glass cover plate grinding fluid and preparation method and method of application thereof Download PDFInfo
- Publication number
- CN105542934A CN105542934A CN201510999410.6A CN201510999410A CN105542934A CN 105542934 A CN105542934 A CN 105542934A CN 201510999410 A CN201510999410 A CN 201510999410A CN 105542934 A CN105542934 A CN 105542934A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- grinding fluid
- glass cover
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to smart phone glass cover plate grinding fluid. The grinding fluid is prepared from the following raw materials in parts by weight: 1-5 parts of organic acid, 4-10 parts of waterborne extreme pressure lubricant, 10-20 parts of polyether, 3-6 parts of boric acid, 1-5 parts of ionic quaternary ammonium salt settling agent, 2-10 parts of organic amine, 1-5 parts of carboxylate-based compound anti-rust agent, 1-5 parts of mono-butyl-ether coupling agent, 0.1-1 part of hard water resistant agent, 0.01-0.1 part of antifoaming agent and other functional additives and 40-60 parts of tap water. The smart phone glass cover plate grinding fluid has superior cooling performance and corrosion resistance, and can be used circularly for a long time; the anti-rust performance is good, and corrosion on a machine does not exists; the product has small odor, is free from pollution, has high operation performance, does not cause injury to skin of staff and is not allergic, and the health and safety of operating personnel are ensured effectively.
Description
Technical field
The present invention relates to a kind of grinding fluid preparation method and using method of glass processing lubricating area, particularly a kind of preparation method of smart mobile phone glass cover-plate grinding fluid and using method thereof.
Background technology
Along with the development of modern society, the application of display screen, mobile phone glass cover plate, touch-screen and the first-class opticglass of optical frames is more and more extensive, the demand of cleaning agent for optical glass not only increases day by day, also has higher requirement to the cleaning performance of clean-out system and environmental-protecting performance simultaneously.The clean-out system that can be used for cleaning opticglass sold in the market is liquid ceanser, P contained compound is added in capital, as potassium pyrophosphate, trisodium phosphate and tertiary sodium phosphate etc., reason is that the cleaning performance of phosphorus system class clean-out system is good, but phosphoric causes day by day serious pollution to environment, also a very large difficult problem is caused to the discharge after enterprise's cleaning.This product is phosphorus element-containing not, adopts environment-friendly type cleaning additive, has Lower alrali content, not etching glass, pollution-free, good work, to employee's skin zero damage, and the effective health and safety ensureing operator.
Summary of the invention
The present invention seeks to overcome on market that existing cleaning agent for optical glass alkalinity is high, seriously polluted, cleaning force is not high, product surface is seriously dirty, the shortcomings such as yield rate is low, provide anticorrosive water base cleaning agent for optical glass of a kind of high-cleanness, high and preparation method thereof and using method.This glass cleaner is applicable to the cleaning of workshop section before and after the silk-screens such as simple glass, opticglass, sheet glass, camera eyeglass, glasses lens, hand-set lid, sapphire glass.
The present invention discloses the anticorrosive water base cleaning agent for optical glass of a kind of high-cleanness, high, and the raw material of described smart mobile phone glass cover-plate grinding fluid comprises following component by weight: 1-5 part organic acid, 4-10 part water-based extreme pressure lubricant, 10-20 part polyethers, 3-6 part boric acid, 1-5 part ionic quaternary ammonium salt sinking agent, 2-10 part organic amine, 1-5 part carboxylate group mixture rust-preventive agent, 1-5 part monobutyl ether couplant, the anti-hard water agent of 0.1-1 part, 0.01-0.1 part defoamer and other functional additive, 40-60 part tap water.
Concrete, described monobutyl ether couplant is diethylene glycol monobutyl ether, described carboxylate group mixture rust-preventive agent adopts dicarboxylate base complex, described organic amine is one or more in trolamine, thanomin, α-amino isopropyl alcohol, described anti-hard water agent is EDETATE SODIUM, and other functional additive described comprises one or more the mixture in rust-preventive agent, antioxidant, water-soluble extreme pressure lubricant.
Concrete, the raw material of described smart mobile phone glass cover-plate grinding fluid comprises following component according to components by weight percent: 2 parts of organic acids, 6 parts of water-based extreme pressure lubricants, 20 parts of polyethers, 3 parts of boric acid, 1 part of quaternary ammonium salts sinking agent, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer surplus are that tap water adds to 100.
The present invention also discloses a kind of preparation method of above-mentioned smart mobile phone glass cover-plate grinding fluid, described preparation method comprises: by weight by organic amine, water-based extreme pressure lubricant, boric acid, polyethers, carboxylate group mixture rust-preventive agent adds in tap water successively, within after mixing uniform stirring 10-30 minute, extremely dissolve completely, add monobutyl ether coupler, ionic quaternary amine sinking agent, anti-hard water agent and defoamer more by weight successively, be stirred to homogeneous transparent.
The present invention also discloses a kind of using method of above-mentioned smart mobile phone glass cover-plate grinding fluid, and described using method comprises: smart mobile phone glass cover-plate grinding fluid and water are doubly diluted use by 1:10 ~ 1:30.
Concrete, smart mobile phone glass cover-plate grinding fluid and water are doubly diluted use by 1:20.
Beneficial effect of the present invention is: for the water-based grinding fluid of above-mentioned mobile phone glass cover plate, its lubricating fluid has excellent oilness, rust-preventing characteristic and perviousness and glass abrasive dust settling property, not containing chlorine, phosphorus, sulphur and the material such as nitrite, phenol, be not easy to raw bacterium smelly, this ground finish lubricating fluid of Long Term Contact, can not cause a skin inflammation and skin irritation; Liquid waste disposal is easy, decreases and pollutes and discharge, and be watered dilution and use, use cost is low.
Embodiment
The present invention is further elaborated below:
A kind of smart mobile phone glass cover-plate grinding fluid in the present embodiment, is characterized in that: grinding fluid raw material comprises following component by weight: 1-5 part organic acid, 4-10 part water-based extreme pressure lubricant, 10-20 part polyethers, 3-6 part boric acid, 1-5 part ionic quaternary ammonium salt sinking agent, 2-10 part organic amine, 1-5 part carboxylate group mixture rust-preventive agent, 1-5 part monobutyl ether couplant, the anti-hard water agent of 0.1-1 part, 0.01-0.1 part defoamer and other functional additive, 40-60 part tap water.
Monobutyl ether couplant is diethylene glycol monobutyl ether, carboxylate group mixture rust-preventive agent adopts dicarboxylate base complex, organic amine is one or more in trolamine, thanomin, α-amino isopropyl alcohol, anti-hard water agent is EDETATE SODIUM, and other described functional additive comprises one or more the mixture in rust-preventive agent, antioxidant, water-soluble extreme pressure lubricant;
Preferably, grinding fluid raw material comprises following component by weight: 2 parts of organic acids, 6 parts of water-based extreme pressure lubricants, 20 parts of polyethers, 3 parts of boric acid, 1 part of quaternary ammonium salts sinking agent, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer surplus are that tap water adds to 100;
The invention still further relates to the preparation method of above-mentioned smart mobile phone glass cover-plate grinding fluid, this preparation method comprises: by weight by organic amine, water-based extreme pressure lubricant, polyethers, carboxylate group mixture rust-preventive agent adds in tap water successively, within after mixing uniform stirring 10-30 minute, extremely dissolve completely, add monobutyl ether coupler, ionic quaternary amine sinking agent, anti-hard water agent and defoamer more by weight successively, be stirred to homogeneous transparent, gained clear solution is that complete synthesis aqueous machining fluid is used in the processing of mobile phone glass cover plate.
The invention still further relates to the using method of above-mentioned smart mobile phone glass cover-plate grinding fluid, this using method comprises: smart mobile phone glass cover-plate grinding fluid and water are doubly diluted use by 1:10 ~ 1:30.
Preferably, smart mobile phone glass cover-plate grinding fluid and water are doubly diluted use by 1:20, the enforcement of this ratio has good onsite application effect.
Embodiment one
Smart mobile phone glass cover-plate grinding fluid in the present embodiment comprises following component: 2 parts of organic acids, 6 parts of water-based extreme pressure lubricants, 20 parts of polyethers, 3 parts of boric acid, 1 part of quaternary ammonium salts sinking agent, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer surplus are that tap water adds to 100.
In the present embodiment, organic acid is the acid of pungent certain herbaceous plants with big flowers, and can certainly be that the organic acid that other function is close replaces, such as n-caprylic acid etc., there is no impact to the stability of system; Other character can be adopted close for carboxylate group mixture and the approximate rust-preventive agent of character replaces, and has no significant effect the character of product; The water-soluble extreme pressure lubricant that water-based extreme pressure lubricant adopts cutting fluid common, the borate ester additive that preferred triethanolamine borate, thanomin boric acid ester etc. are soluble in water; Polyethers is the simple linear polymer that open loop homopolymerization or copolymerization obtain, and can form the highly stable lubricant film with large adsorptive power and supporting capacity under nearly all lubricating status, has lower frictional coefficient and stronger anti-shear ability; Boric acid is boric acid and borate family derivative, as pH value regulator, sterilizing agent, bacteriostatic preservative etc.; Monobutyl ether couplant is diethylene glycol monobutyl ether, also can adopt the monobutyl ether coupler that other character is approximate, has no significant effect the character of product; Organic amine adopts conventional trolamine, certainly also can adopt chemical property other organic amine akin, as AMP95, MDEA etc.; Ionic ammonium salt sinking agent is polyacrylamide negatively charged ion, also can adopt the sinking agent of other similar functions, quaternary ammonium salt as twin in chain alkyl, polyquaternium or chain alkyl three lives quaternary ammonium salt etc.In the present embodiment, other functional additive is selected to add one or more the mixture comprised in alkaline agent, rust-preventive agent, antioxidant, defoamer and anti-hard water agent as required, functionally has good Under Tendency Influence to it; Defoamer is one or more in silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxyethylene polyoxypropylene glyceryl ether, polydimethylsiloxane; Alkaline agent adopts sodium hydroxide, potassium hydroxide etc., and rust-preventive agent can adopt SA, and antioxidant is T501, and anti-hard water agent adopts EDETATE SODIUM, is the material that general aqueous cutting fluid is conventional.
The raw material of above-mentioned weight part is prepared according to aforesaid preparation method, obtains the water-based grinding fluid of mobile phone glass cover plate.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment in use with water by volume 1:20 doubly dilute use, in glass grinding process from sharp tackle tool, lubrication or cooling.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment, use after being watered dilution by 1:20, its lubricating fluid has excellent oilness, rust-preventing characteristic and perviousness and glass abrasive dust settling property, not containing chlorine, phosphorus, sulphur and the material such as nitrite, phenol, be not easy to raw bacterium smelly, this ground finish lubricating fluid of Long Term Contact, can not cause a skin inflammation and skin irritation; Liquid waste disposal is easy, decreases and pollutes and discharge, and be watered dilution and use, use cost is low; This ground finish liquid indices meets or exceeds GB6144-85 related index, and cutter life is long, and concentrate and change the liquid cycle more than more than 60 days, unit changes the liquid cycle more than more than 30 days.
Embodiment two
Smart mobile phone glass cover-plate grinding fluid in the present embodiment comprises following component: 4 parts of organic acids, 4 parts of water-based extreme pressure lubricants, 20 parts of polyethers, 4 parts of boric acid, 2 parts of quaternary ammonium salts sinking agents, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer surplus are that tap water adds to 100.
In the present embodiment, organic acid is the acid of pungent certain herbaceous plants with big flowers, and can certainly be that the organic acid that other function is close replaces, such as n-caprylic acid etc., there is no impact to the stability of system; Other character can be adopted close for carboxylate group mixture and the approximate rust-preventive agent of character replaces, and has no significant effect the character of product; The water-soluble extreme pressure lubricant that water-based extreme pressure lubricant adopts cutting fluid common, the borate ester additive that preferred triethanolamine borate, thanomin boric acid ester etc. are soluble in water; Polyethers is the simple linear polymer that open loop homopolymerization or copolymerization obtain, and can form the highly stable lubricant film with large adsorptive power and supporting capacity under nearly all lubricating status, has lower frictional coefficient and stronger anti-shear ability; Boric acid is boric acid and borate family derivative, as pH value regulator, sterilizing agent, bacteriostatic preservative etc.; Monobutyl ether couplant is diethylene glycol monobutyl ether, also can adopt the monobutyl ether coupler that other character is approximate, has no significant effect the character of product; Organic amine adopts conventional trolamine, certainly chemical property other organic amine akin can also be adopted, as AMP95, MDEA etc., ionic ammonium salt sinking agent is polyacrylamide negatively charged ion, also the sinking agent of other similar functions can be adopted, quaternary ammonium salt as twin in chain alkyl, polyquaternium or chain alkyl three lives quaternary ammonium salt etc.In the present embodiment, other functional additive is selected to add one or more the mixture comprised in alkaline agent, rust-preventive agent, antioxidant, defoamer and anti-hard water agent as required, functionally has good Under Tendency Influence to it; Defoamer is one or more in silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxyethylene polyoxypropylene glyceryl ether, polydimethylsiloxane; Alkaline agent adopts sodium hydroxide, potassium hydroxide etc., and rust-preventive agent can adopt SA, and antioxidant is T501, and anti-hard water agent adopts EDETATE SODIUM, is the material that general aqueous cutting fluid is conventional.
The raw material of above-mentioned weight part is prepared according to aforesaid preparation method, obtains the water-based grinding fluid of mobile phone glass cover plate.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment in use with water by volume 1:30 doubly dilute use, in glass grinding process from sharp tackle tool, lubrication or cooling.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment, use after being watered dilution by 1:30, its lubricating fluid has excellent oilness, rust-preventing characteristic and perviousness and glass abrasive dust settling property, not containing chlorine, phosphorus, sulphur and the material such as nitrite, phenol, be not easy to raw bacterium smelly, this ground finish lubricating fluid of Long Term Contact, can not cause a skin inflammation and skin irritation; Liquid waste disposal is easy, decreases and pollutes and discharge, and be watered dilution and use, use cost is low; This ground finish liquid indices meets or exceeds GB6144-85 related index, and cutter life is long, and concentrate and change the liquid cycle more than more than 50 days, unit changes the liquid cycle more than more than 20 days.
Embodiment three
Smart mobile phone glass cover-plate grinding fluid in the present embodiment comprises following component: 3 parts of organic acids, 4 parts of water-based extreme pressure lubricants, 20 parts of polyethers, 4 parts of boric acid, 1 part of quaternary ammonium salts sinking agent, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer surplus are that tap water adds to 100.
In the present embodiment, organic acid is the acid of pungent certain herbaceous plants with big flowers, and can certainly be that the organic acid that other function is close replaces, such as n-caprylic acid etc., there is no impact to the stability of system; Other character can be adopted close for carboxylate group mixture and the approximate rust-preventive agent of character replaces, and has no significant effect the character of product; The water-soluble extreme pressure lubricant that water-based extreme pressure lubricant adopts cutting fluid common, the borate ester additive that preferred triethanolamine borate, thanomin boric acid ester etc. are soluble in water; Polyethers is the simple linear polymer that open loop homopolymerization or copolymerization obtain, and can form the highly stable lubricant film with large adsorptive power and supporting capacity under nearly all lubricating status, has lower frictional coefficient and stronger anti-shear ability; Boric acid is boric acid and borate family derivative, as pH value regulator, sterilizing agent, bacteriostatic preservative etc.; Monobutyl ether couplant is diethylene glycol monobutyl ether, also can adopt the monobutyl ether coupler that other character is approximate, has no significant effect the character of product; Organic amine adopts conventional trolamine, certainly chemical property other organic amine akin can also be adopted, as AMP95, MDEA etc., described ionic ammonium salt sinking agent is polyacrylamide negatively charged ion, also the sinking agent of other similar functions can be adopted, quaternary ammonium salt as twin in chain alkyl, polyquaternium or chain alkyl three lives quaternary ammonium salt etc.In the present embodiment, other functional additive is selected to add one or more the mixture comprised in alkaline agent, rust-preventive agent, antioxidant, defoamer and anti-hard water agent as required, functionally has good Under Tendency Influence to it; Defoamer is one or more in silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxyethylene polyoxypropylene glyceryl ether, polydimethylsiloxane; Alkaline agent adopts sodium hydroxide, potassium hydroxide etc., and rust-preventive agent can adopt SA, and antioxidant is T501, and anti-hard water agent adopts EDETATE SODIUM, is the material that general aqueous cutting fluid is conventional.
The raw material of above-mentioned weight part is prepared according to aforesaid preparation method, obtains the water-based grinding fluid of mobile phone glass cover plate.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment in use with water by volume 1:15 doubly dilute use, in glass grinding process from sharp tackle tool, lubrication or cooling.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment, use after being watered dilution by 1:15, its lubricating fluid has excellent oilness, rust-preventing characteristic and perviousness and glass abrasive dust settling property, not containing chlorine, phosphorus, sulphur and the material such as nitrite, phenol, be not easy to raw bacterium smelly, this ground finish lubricating fluid of Long Term Contact, can not cause a skin inflammation and skin irritation; Liquid waste disposal is easy, decreases and pollutes and discharge, and be watered dilution and use, use cost is low; This ground finish liquid indices meets or exceeds GB6144-85 related index, and cutter life is long, and concentrate and change the liquid cycle more than more than 40 days, unit changes the liquid cycle more than more than 20 days.
Embodiment four
Smart mobile phone glass cover-plate grinding fluid in the present embodiment comprises following component: 2 parts of organic acids, 10 parts of water-based extreme pressure lubricants, 10 parts of polyethers, 3 parts of boric acid, 1 part of quaternary ammonium salts sinking agent, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer surplus are that tap water adds to 100.
In the present embodiment, organic acid is the acid of pungent certain herbaceous plants with big flowers, and can certainly be that the organic acid that other function is close replaces, such as n-caprylic acid etc., there is no impact to the stability of system; Other character can be adopted close for carboxylate group mixture and the approximate rust-preventive agent of character replaces, and has no significant effect the character of product; The water-soluble extreme pressure lubricant that water-based extreme pressure lubricant adopts cutting fluid common, the borate ester additive that preferred triethanolamine borate, thanomin boric acid ester etc. are soluble in water; Polyethers is the simple linear polymer that open loop homopolymerization or copolymerization obtain, and can form the highly stable lubricant film with large adsorptive power and supporting capacity under nearly all lubricating status, has lower frictional coefficient and stronger anti-shear ability; Boric acid is boric acid and borate family derivative, as pH value regulator, sterilizing agent, bacteriostatic preservative etc.; Monobutyl ether couplant is diethylene glycol monobutyl ether, also can adopt the monobutyl ether coupler that other character is approximate, has no significant effect the character of product; Organic amine adopts conventional trolamine, certainly chemical property other organic amine akin can also be adopted, as AMP95, MDEA etc., ionic ammonium salt sinking agent is polyacrylamide negatively charged ion, also the sinking agent of other similar functions can be adopted, quaternary ammonium salt as twin in chain alkyl, polyquaternium or chain alkyl three lives quaternary ammonium salt etc.In the present embodiment, other functional additive is selected to add one or more the mixture comprised in alkaline agent, rust-preventive agent, antioxidant, defoamer and anti-hard water agent as required, functionally has good Under Tendency Influence to it; Defoamer is one or more in silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxyethylene polyoxypropylene glyceryl ether, polydimethylsiloxane; Alkaline agent adopts sodium hydroxide, potassium hydroxide etc., and rust-preventive agent can adopt SA, and antioxidant is T501, and anti-hard water agent adopts EDETATE SODIUM, is the material that general aqueous cutting fluid is conventional.
The raw material of above-mentioned weight part is prepared according to aforesaid preparation method, obtains the water-based grinding fluid of mobile phone glass cover plate.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment in use with water by volume 1:20 doubly dilute use, in glass grinding process from sharp tackle tool, lubrication or cooling.
The water-based grinding fluid of the mobile phone glass cover plate of the present embodiment, use after being watered dilution by 1:20, its lubricating fluid has excellent oilness, rust-preventing characteristic and perviousness and glass abrasive dust settling property, not containing chlorine, phosphorus, sulphur and the material such as nitrite, phenol, be not easy to raw bacterium smelly, this ground finish lubricating fluid of Long Term Contact, can not cause a skin inflammation and skin irritation; Liquid waste disposal is easy, decreases and pollutes and discharge, and be watered dilution and use, use cost is low; This ground finish liquid indices meets or exceeds GB6144-85 related index, and cutter life is long, and concentrate and change the liquid cycle more than more than 60 days, unit changes the liquid cycle more than more than 30 days.
The above embodiment, just preferred embodiment of the present invention, be not limit practical range of the present invention, therefore all equivalences done according to structure, feature and the principle described in the present patent application the scope of the claims change or modify, and all should be included in patent claim of the present invention.
Claims (6)
1. a smart mobile phone glass cover-plate grinding fluid, is characterized in that: the raw material of described smart mobile phone glass cover-plate grinding fluid comprises following component by weight: 1-5 part organic acid, 4-10 part water-based extreme pressure lubricant, 10-20 part polyethers, 3-6 part boric acid, 1-5 part ionic quaternary ammonium salt sinking agent, 2-10 part organic amine, 1-5 part carboxylate group mixture rust-preventive agent, 1-5 part monobutyl ether couplant, the anti-hard water agent of 0.1-1 part, 0.01-0.1 part defoamer and other functional additive, 40-60 part tap water.
2. smart mobile phone glass cover-plate grinding fluid according to claim 1, it is characterized in that: described monobutyl ether couplant is diethylene glycol monobutyl ether, described carboxylate group mixture rust-preventive agent adopts dicarboxylate base complex, described organic amine is one or more in trolamine, thanomin, α-amino isopropyl alcohol, described anti-hard water agent is EDETATE SODIUM, and other functional additive described comprises one or more the mixture in rust-preventive agent, antioxidant, water-soluble extreme pressure lubricant.
3. smart mobile phone glass cover-plate grinding fluid according to claim 2, is characterized in that: the raw material of described smart mobile phone glass cover-plate grinding fluid comprises following component according to components by weight percent: 2 parts of organic acids, 6 parts of water-based extreme pressure lubricants, 20 parts of polyethers, 3 parts of boric acid, 1 part of quaternary ammonium salts sinking agent, 4 parts of organic amines, 1 part of carboxylate group mixture rust-preventive agent, 2 parts of monobutyl ether couplants, 0.3 part of anti-hard water agent, 0.1 part of defoamer, surpluses are that tap water adds to 100.
4. one kind as arbitrary in claim 1-3 as described in the preparation method of smart mobile phone glass cover-plate grinding fluid, it is characterized in that: described preparation method comprises: by weight by organic amine, water-based extreme pressure lubricant, boric acid, polyethers, carboxylate group mixture rust-preventive agent adds in tap water successively, within after mixing uniform stirring 10-30 minute, extremely dissolve completely, add monobutyl ether coupler, ionic quaternary amine sinking agent, anti-hard water agent and defoamer more by weight successively, be stirred to homogeneous transparent.
5. a using method for the smart mobile phone glass cover-plate grinding fluid as described in as arbitrary in claim 1-3, is characterized in that: described using method comprises: smart mobile phone glass cover-plate grinding fluid and water are doubly diluted use by 1:10 ~ 1:30.
6. the using method of smart mobile phone glass cover-plate grinding fluid according to claim 5, is characterized in that: smart mobile phone glass cover-plate grinding fluid and water are doubly diluted use by 1:20.