CN105541286A - Method for production of magnetized ceramic - Google Patents
Method for production of magnetized ceramic Download PDFInfo
- Publication number
- CN105541286A CN105541286A CN201510953644.7A CN201510953644A CN105541286A CN 105541286 A CN105541286 A CN 105541286A CN 201510953644 A CN201510953644 A CN 201510953644A CN 105541286 A CN105541286 A CN 105541286A
- Authority
- CN
- China
- Prior art keywords
- water
- mud
- magnetized
- ceramic
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a method for production of a magnetized ceramic, the method is characterized in that 350 to 500 mesh ferrous oxide and pottery clay are mixed in the ratio of 1:4 to 5, and fully stirred; a milled slurry material is precipitated; after the precipitation, a supernatant is pumped out, and a precipitate is taken out and placed on a clean ground surface to dry; the dried mud material is put into a mud refining machine for mud refining, meanwhile air in the mud is removed; the refined mud is prepared into a corresponding green body, and dried in a drying room at 40-50 DEG C; and the dried green body is put into a fired ceramic green body for calcination at 700-1200 DEG C for 5-8 hours, and then naturally cooled to obtain the magnetized ceramic. In the firing and forming process of the ceramic, ferroferric oxide is generated from the ferrous oxide at high temperature, and the ferroferric oxide is magnetic. Through the effect of a magnetic field, water becomes magnetic water when being poured into a ceramic pot, and the magnetic water has plant growth promoting effect.
Description
Technical field
The present invention relates to a kind of production method of magnetized ceramic, belong to ceramic technology field.
Background technology
Magnetized water refers to the water that some change in physical properties occurs after the action of a magnetic field.After water is magnetized. the surface tension of water increases, electric conductivity raises, pH value rises, the interior of water molecules can improve, the character of water there occurs change, namely become by the small-micelle water of 6 small molecules set by the macromolecular mass water of more than 13 water molecules set, so activity improves greatly, seepage force, solvency power all have enhancing in various degree.
Magnetized water refers to the water that some change in physical properties occurs after the action of a magnetic field.After water is magnetized. the surface tension of water increases, electric conductivity raises, pH value rises, the interior of water molecules can improve, the character of water there occurs change, namely become by the small-micelle water of 6 small molecules set by the macromolecular mass water of more than 13 water molecules set, so activity improves greatly, seepage force, solvency power all have enhancing in various degree.After water is subject to the action of a magnetic field, water with state of charge change, destroy the electrostatic attraction between water molecules, thus cause the change of the certain physical characteristics in water.In addition, the effect that the impurity in water is subject to magnetic field also can make its state of aggregation change.Meanwhile, make water molecules key generation angle and length variations, hydrogen bond angle is reduced to about 103 degree from 105 degree, makes the character of water there occurs series of physical and chemical transformation.
Magnetized water have " refreshing water ", " magic water ", " water of miracle " title.Before the quincentenary. the Ming Dynasty large physician LI Shi-Zhen just finds that magnetized water has the effect such as " removing sore fistula, longue skin ", " Long Drinks has made us son, establishing-Yang ", " pleasant wine " already.In recent years, much research is pointed out, as long as Healthy People drinks magnetized small-micelle water all the year round, the various functions of health can remain on optimum regime.
Moreover, magnetized water can suppress microorganism and abnormal cell proliferation, more can prevent and treat the disease that some damages vital movement.Such as, as long as suffer from people's long-term drinking magnetized water of diabetes, then coordinate the treatment such as medicine, diet, motion, the state of an illness will be alleviated gradually.This is because magnetized water is alkalescent water. change diabetic subject slant acidity physique is of great benefit to.Diabetic subject should note eating basic foodstuff more during drinking magnetized water, as melon and fruit, vegetables, milk-product, bean product, sea-tangle etc., eats the acidic foods such as chicken, duck, rice, face, oil, fish, meat, egg less.After the conditioning several months like this, the body fluid of health will transform to weakly alkaline.Research finds, O.1 diabetic subject's body fluid improved to weakly alkaline direction by slant acidity, and insulin activity will improve 30%-35%, and this is very important to stabilizing blood sugar.And subset magnetized water can change the metabolism state of cell quickly, more has the function of good activating cells, if pancreas p cell is activated. fundamentally can treat diabetes.Moreover adhere to drinking raw magnetized water for a long time, also can receive good effect of supplemented calcium, calcium is for the metabolism state improving Regular Insulin p cell, and the ability improving Regular Insulin control blood sugar is also very important.In addition, diabetic subject's many drinks magnetized water, also can receive prevention urinary system infection, increases Q volume of blood, improves the effect such as blood circulation and microcirculation.
For another example. patient with gout mainly increases due to the uric acid concentration in blood, and uric acid crystal increases and amasss in the tissue. as first joint etc. of finger, toe, thus cause the inflammation symptoms such as red, swollen, hot, pain.If gout patients can drink a large amount of magnetized water every day, just can promote uric acid excretion, gout symptom is taken a turn for the better gradually.Its reason is, magnetized water is compared with ortho-water, and its solvency power, metabolism power there occurs very large change. every 100 milliliters of ortho-waters can only dissolve 11.7 milligrams of uric acid, and magnetized water can dissolve 21.3 milligrams of uric acid.So as long as the patient suffering from gout is in a large amount of drinking magnetized water of treatments period, strive that every day, urine remained on 2500 ~ 3000 milliliters, by strengthening uric acid excretion, gout symptom just can reverse recovery from illness in the short period of time.Nowadays, headache is a kind of common symptom, and this illness mainly causes due to the reason such as nervous, tired, to drink.According to the statistical figure display of one, Britain investigation, there is a people of 85% I haven't seen you for ages within 1 year headache once, also have the grownup of 38% can be subjected to the puzzlement of having a headache within fortnight.Generally. headache person, when falling ill, can be disappeared voluntarily after timeout or drinking-water.Research finds. headache patient also can be benefited as diabetic subject from magnetized water.Headache Clinic research finds, drinks the people of 2000 ~ 2500 ml waters (preferably magnetized water) every day, just headache probability can be reduced by 60%.
Relevant expert points out, if people wish, by water prevention and therapy cancer, to be just necessary for the nutritive ingredient that human body provides suitable, eliminates the metabolic mechanism that those may exhaust health nutrition deposit.In addition, the chemical environment meta-alkalescence state of health will also be guaranteed.If health presents acidity, cancer cells will be produced.Scientific research finds, when tap water is hard water, cancer morbidity is just low.Drink water and uncleanly cause cancer, this is that scientist is universally recognized.Do those really contribute to people and prevent the positive thing of cancer from what being on earth in tap water? about the research of this respect, brainstrust concentrates in four factors of water: TDS (in water total dissolved solid), hardness, pH value and silicon-dioxide.Research finds, TDS (in the water total dissolved solid) content of tap water is approximately 300 mg/litre, belong to hard water, and meta-alkalescence (pH value > 7), and the silicon-dioxide containing 15 mg/litre, so, the death toll of cancer will reduce 10% ~ 25%.Separately have scientist to find, the relation between silicon-dioxide and cancer, namely higher containing silicon-dioxide, cancered people is fewer.In addition, this scientist also points out, the pH value meta-alkalescence of tap water is that another reduces the key factor of cancer case fatality rate.Cell tissue lack of water is the universal phenomenon of cancer patient, if make cell draw the sufficient moisture then easy rehabilitation of patient.So drink the water of high TDS and high rigidity, the mortality ratio of heart trouble and cancer patients is just low.Certainly, water, healthy water must have been drunk, i.e. small-micelle water.
If human body magnetic is disorderly, will cause growing blunt, the improper performance of physiological function and all kinds of disease incidence rise, and impact causes autonomic nervous dysfunction the most significantly, cell early ageing. blood stickiness increases, hypostasis thing artery-clogging.And the height of the modern society such as these factors and hypertension, cardiovascular diseases, cerebral apoplexy, chronic fatigue syndrome is fallen ill and is had certain relation.As long as suffer from chronic gastritis, cholecystitis, prostatitis, arthralgic people adhere to drinking magnetized water, just effectively the state of an illness can be improved.Show according to correlative study, magnetized water all has certain effect to the various lithiasis for the treatment of (as gallbladdergallstonecholetithiasis, vesical calculus, urinary stone disease etc.), stomach trouble, hypertension, diabetes and flu etc.
In addition, because magnetized water is small-micelle water, its solvency power is high, seepage force is large, good dispersity. thus every day enough drinking magnetized water, the intraor extracellular body fluid of tissue just can be made sufficient, avoid xerosis cutis, help skin to recover elasticity, make people radiant, be conducive to beauty treatment.Certainly, to make magnetized water obtain best effect to human body beauty treatment, also the time of drinking magnetized water and method to be particular about:
1. preferably after 2 hours after the meal, then drink magnetized water.
Can be described as the best moment of human body make up water among a day early morning because health dormant time still work, a large amount of moisture can be consumed.Morning, drinking-water can make helmet intestines come to life at once, stimulated and wriggled, prevent constipation.The more important thing is, after sleeping for a long time, haemoconcentration increases, and this time keeps the skin wet, and haemoconcentration just can be impelled to reduce rapidly, promotes circulation.So like to be beautiful personage, preferably form the custom of magnetized water of having a drink after rising morning.
Because we can perspire by nature when sleep, run off unconsciously moisture and salinity, and in several hours of sleep, health cannot keep the skin wet again, and why Here it is gets up can feel the reason of dry mouth and tougue morning.So, half an hour before sleeping, moisture and ionogen should be supplied in advance, allow health still maintain equilibrium state in sleep, also can reduce urine concentration simultaneously, and then prevent the generation of calculus generally emerald green.
Finally, also will remind everybody, magnetized water is particularly suitable for drinking raw, and the warm water of indication, namely can be regarded as room temperature water in summer here; As long as room temp is at about 20 DEG C in the winter time, also room temperature magnetized water can be drunk. as room temp is too low, can drink by Wen Houzai a little.Secondly, magnetized water is preferably drunk on an empty stomach, because drink a glass magnetized water on an empty stomach, only stops 2 ~ 3 minutes, just can enter small intestine and be preferentially absorbed into blood in stomach. then just can add to body tissue's cell.So, drink magnetized water before the meal, not only can increase appetite. but also can help digest, penetration enhancement, there is very large benefit to healthy.
In addition.Also to give up the custom of not drinking water or drinking water less.In general, the water balance in healthy artificial holder. 2000-2500 milliliter magnetized water should be drunk every day.But the method for drinking water should be worthy of careful study, can not once just drink some or two mouthfuls, or once large mouth crapulence.The best method of drinking water be a small amount of repeatedly, namely drink water and have a meal the same, " thin product are swallowed slowly ", as the water of one glass 300 milliliters, should drink flatly about 1O minute a bite. so just can guarantee that health really absorbs use.
Summary of the invention
Problem to be solved by this invention is to provide a kind of production method that can produce the pottery of magnetized water.
In order to solve the problem, the invention provides a kind of production method of magnetized ceramic, it is characterized in that, comprising the following steps:
Step 1): 350 ~ 500 object iron protoxides are mixed by weight 1: 4 ~ 5 with potter's clay, fully stirs;
Step 2): the material-mud of milled is precipitated; Extract supernatant liquid out after precipitation, and taken out by throw out and be placed on clean ground and dry, the time of drying is 50 ~ 55 days;
Step 3): the pug after drying is put into soil kneader and carries out mud refining, get rid of the air in mud simultaneously;
Step 4): the mud refined is made corresponding base substrate, and dries in the baking room of 40 ~ 50 DEG C;
Step 5): the base substrate after drying is put into firing ceramics base substrate, calcines 5 ~ 8 hours at 700 ~ 1200 DEG C, after naturally cooling, obtain magnetized ceramic goods.
In ceramic sintering moulding process, iron protoxide at high temperature generates Z 250, and Z 250 has magnetic.By the effect in magnetic field, can become magnetic water when being poured into by water in this pottery pot, this magnetic water has promoter action to plant-growth.
Embodiment
For making the present invention become apparent, hereby with preferred embodiment, be described in detail below.
Embodiment 1
A production method for magnetized ceramic, concrete steps are as follows:
Step 1): 350 object iron protoxides are mixed by weight 1: 4 with potter's clay, fully stirs;
Step 2): the material-mud of milled is precipitated; Extract supernatant liquid out after precipitation, and taken out by throw out and be placed on clean ground and dry, the time of drying is 50 days;
Step 3): the pug after drying is put into soil kneader and carries out mud refining, get rid of the air in mud simultaneously;
Step 4): the mud refined is made corresponding base substrate, and dries in the baking room of 40 DEG C;
Step 5): the base substrate after drying is put into firing ceramics base substrate, calcines 5 hours at 1200 DEG C, after naturally cooling, obtain magnetized ceramic goods.
Embodiment 2
A production method for magnetized ceramic, concrete steps are as follows:
Step 1): 500 object iron protoxides are mixed by weight 1: 5 with potter's clay, fully stirs;
Step 2): the material-mud of milled is precipitated; Extract supernatant liquid out after precipitation, and taken out by throw out and be placed on clean ground and dry, the time of drying is 55 days;
Step 3): the pug after drying is put into soil kneader and carries out mud refining, get rid of the air in mud simultaneously;
Step 4): the mud refined is made corresponding base substrate, and dries in the baking room of 50 DEG C;
Step 5): the base substrate after drying is put into firing ceramics base substrate, calcines 8 hours at 700 DEG C, after naturally cooling, obtain magnetized ceramic goods.
Embodiment 3
A production method for magnetized ceramic, concrete steps are as follows:
Step 1): 450 object iron protoxides are mixed by weight 1: 4.5 with potter's clay, fully stirs;
Step 2): the material-mud of milled is precipitated; Extract supernatant liquid out after precipitation, and taken out by throw out and be placed on clean ground and dry, the time of drying is 52 days;
Step 3): the pug after drying is put into soil kneader and carries out mud refining, get rid of the air in mud simultaneously;
Step 4): the mud refined is made corresponding base substrate, and dries in the baking room of 45 DEG C;
Step 5): the base substrate after drying is put into firing ceramics base substrate, calcines 6.5 hours at 1000 DEG C, after naturally cooling, obtain magnetized ceramic goods.
Claims (1)
1. a production method for magnetized ceramic, is characterized in that, comprises the following steps:
Step 1): 350 ~ 500 object iron protoxides are mixed by weight 1: 4 ~ 5 with potter's clay, fully stirs;
Step 2): the material-mud of milled is precipitated; Extract supernatant liquid out after precipitation, and taken out by throw out and be placed on clean ground and dry, the time of drying is 50 ~ 55 days;
Step 3): the pug after drying is put into soil kneader and carries out mud refining, get rid of the air in mud simultaneously;
Step 4): the mud refined is made corresponding base substrate, and dries in the baking room of 40 ~ 50 DEG C;
Step 5): the base substrate after drying is put into firing ceramics base substrate, calcines 5 ~ 8 hours at 700 ~ 1200 DEG C, after naturally cooling, obtain magnetized ceramic goods.