CN105523075A - 一种防滑方向盘套及其制备工艺 - Google Patents
一种防滑方向盘套及其制备工艺 Download PDFInfo
- Publication number
- CN105523075A CN105523075A CN201511023606.8A CN201511023606A CN105523075A CN 105523075 A CN105523075 A CN 105523075A CN 201511023606 A CN201511023606 A CN 201511023606A CN 105523075 A CN105523075 A CN 105523075A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- raw material
- steering wheel
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防滑方向盘套及其制备工艺，属于汽车内饰用品技术领域。一种防滑方向盘套，由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份配比的原料制成：植绒布80-110份；海绵层由以下按重量份配比的原料制成：PVC树脂60-100份、偏苯三酸酯5-8份、环氧大豆油15-30份、丙烯酸正丁酯1-3份、己二酸二辛酯1-3份、氢氧化镁2-5份。本发明的一种防滑方向盘套，表面立体感强、颜色鲜艳、手感柔和、豪华高贵、华丽温馨、形象逼真、无毒无味、保温防潮、不脱绒、耐摩擦、平整无隙，内部海绵软硬合适、弹性好、强度高、韧性强，制成的方向盘套不但吸震减震、防止打滑，而且美观大方。
Description
技术领域
本发明涉及一种防滑方向盘套及其制备工艺，属于汽车内饰用品技术领域。
背景技术
方向盘套带有很强的装饰性，显得更加时尚，又充满绅士风度，手感舒适，设计典雅大方中不失活力。方向盘套的主要功能是使方向盘免受磨损、防止手出汗打滑、减少吸收震动以及增强车行驶时的反应灵敏度和安全性。按照材质的不同来分类，可以分为长毛绒、毛绒、丝绒、厚布面、仿皮、皮革、潜水布、胶粒、真皮以及高密度羔羊毛加厚真皮里等。但不管是哪种材质的方向盘套，其更主要的作用是增加摩擦力，防止打滑，而且要环保，但现在的大多数方向盘套已经只在美观度方面大做文章，而忽视了安全性。
发明内容
本发明的目的在于解决上述已有技术存在的不足之处，提供一种美观大方、吸汗减震、增加摩擦力的防滑方向盘套及其制备工艺。
本发明是通过以下技术方案实现的：
一种防滑方向盘套，其特殊之处在于由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份配比的原料制成：植绒布80-110份；海绵层由以下按重量份配比的原料制成：PVC树脂60-100份、偏苯三酸酯5-8份、环氧大豆油15-30份、丙烯酸正丁酯1-3份、己二酸二辛酯1-3份、氢氧化镁2-5份、磷酸三甲苯酯1-3份、氯化石蜡3-6份、硅灰石粉10-20份、偶氮二甲酰胺4-7份、四季戊四醇酯1-3份；衬布层由以下按重量份配比的原料制成：无纺布80-110份；
所述一种防滑方向盘套，由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份最优配比的原料制成：植绒布100份；海绵层包括由以下按重量份最优配比的原料制成：PVC树脂80份、偏苯三酸酯6份、环氧大豆油20份、丙烯酸正丁酯2份、己二酸二辛酯2份、氢氧化镁3份、磷酸三甲苯酯2份、氯化石蜡4份、硅灰石粉15份、偶氮二甲酰胺5份、四季戊四醇酯2份；衬布层由以下按重量份最优配比的原料制成：无纺布100份；
一种防滑方向盘套的制备工艺，其特殊之处在于包括以下步骤：
(1)将海绵层所有原料按比例配好，加入到反应釜中，在5000-6000r/min转速下，搅拌6-8秒，得到糊料；
(2)将步骤(1)的糊料涂刮在离型纸上，在温度为180-200℃下塑化发泡，剥离后得到半成品海绵体；
(3)将步骤(2)的半成品海绵体放入模具中，在100-120℃下成形，得到海绵体成品；
(4)将植绒布与海绵体、海绵体与无纺布分别进行火焰复合，干燥切割即可。
本发明的一种防滑方向盘套，表面立体感强、颜色鲜艳、手感柔和、豪华高贵、华丽温馨、形象逼真、无毒无味、保温防潮、不脱绒、耐摩擦、平整无隙，内部海绵软硬合适、弹性好、强度高、韧性强，制成的方向盘套不但吸震减震、防止打滑，而且美观大方。
具体实施方式
以下给出本发明的具体实施方式，用来对本发明的构成作进一步详细说明。
实施例1
本实施例的一种防滑方向盘套，由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份配比的原料制成：植绒布80份；海绵层由以下按重量份配比的原料制成：PVC树脂60份、偏苯三酸酯5份、环氧大豆油15份、丙烯酸正丁酯1份、己二酸二辛酯1份、氢氧化镁2份、磷酸三甲苯酯1份、氯化石蜡3份、硅灰石粉10份、偶氮二甲酰胺4份、四季戊四醇酯1份；衬布层由以下按重量份配比的原料制成：无纺布80份。
实施例2
本实施例的一种防滑方向盘套，由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份配比的原料制成：植绒布110份；海绵层由以下按重量份配比的原料制成：PVC树脂100份、偏苯三酸酯8份、环氧大豆油30份、丙烯酸正丁酯3份、己二酸二辛酯3份、氢氧化镁5份、磷酸三甲苯酯3份、氯化石蜡6份、硅灰石粉20份、偶氮二甲酰胺7份、四季戊四醇酯3份；衬布层由以下按重量份配比的原料制成：无纺布110份。
实施例3
本实施例的一种防滑方向盘套，由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份最优配比的原料制成：植绒布100份；海绵层包括由以下按重量份最优配比的原料制成：PVC树脂80份、偏苯三酸酯6份、环氧大豆油20份、丙烯酸正丁酯2份、己二酸二辛酯2份、氢氧化镁3份、磷酸三甲苯酯2份、氯化石蜡4份、硅灰石粉15份、偶氮二甲酰胺5份、四季戊四醇酯2份；衬布层由以下按重量份最优配比的原料制成：无纺布100份。
以上实施例的一种防滑方向盘套的制备工艺，包括以下步骤：
(1)将海绵层所有原料按比例配好，加入到反应釜中，在55000r/min转速下，搅拌7秒，得到糊料；
(2)将步骤(1)的糊料涂刮在离型纸上，在温度为200℃下塑化发泡，剥离后得到半成品海绵体；
(3)将步骤(2)的半成品海绵体放入模具中，在110℃下成形，得到海绵体成品；
(4)将植绒布与海绵体、海绵体与无纺布分别进行火焰复合，干燥切割即可。
以上实施例的一种防滑方向盘套，表面立体感强、颜色鲜艳、手感柔和、豪华高贵、华丽温馨、形象逼真、无毒无味、保温防潮、不脱绒、耐摩擦、平整无隙，内部海绵软硬合适、弹性好、强度高、韧性强，制成的方向盘套不但吸震减震、防止打滑，而且美观大方。
Claims (3)
1.一种防滑方向盘套，其特征在于由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份配比的原料制成：植绒布80-110份；海绵层由以下按重量份配比的原料制成：PVC树脂60-100份、偏苯三酸酯5-8份、环氧大豆油15-30份、丙烯酸正丁酯1-3份、己二酸二辛酯1-3份、氢氧化镁2-5份、磷酸三甲苯酯1-3份、氯化石蜡3-6份、硅灰石粉10-20份、偶氮二甲酰胺4-7份、四季戊四醇酯1-3份；衬布层由以下按重量份配比的原料制成：无纺布80-110份。
2.根据权利要求1所述的一种防滑方向盘套，其特征在于由绒布层、海绵层与衬布层通过火焰复合而成，绒布层由以下按重量份最优配比的原料制成：植绒布100份；海绵层包括由以下按重量份最优配比的原料制成：PVC树脂80份、偏苯三酸酯6份、环氧大豆油20份、丙烯酸正丁酯2份、己二酸二辛酯2份、氢氧化镁3份、磷酸三甲苯酯2份、氯化石蜡4份、硅灰石粉15份、偶氮二甲酰胺5份、四季戊四醇酯2份；衬布层由以下按重量份最优配比的原料制成：无纺布100份。
3.权利要求1或2所述一种防滑方向盘套的制备工艺，其特征在于包括以下步骤：
(1)将海绵层所有原料按比例配好，加入到反应釜中，在5000-6000r/min转速下，搅拌6-8秒，得到糊料；
(2)将步骤(1)的糊料涂刮在离型纸上，在温度为180-200℃下塑化发泡，剥离后得到半成品海绵体；
(3)将步骤(2)的半成品海绵体放入模具中，在100-120℃下成形，得到海绵体成品；
(4)将植绒布与海绵体、海绵体与无纺布分别进行火焰复合，干燥切割即可。