CN105505322A - 一种地下开采用除尘剂的制备方法 - Google Patents
一种地下开采用除尘剂的制备方法 Download PDFInfo
- Publication number
- CN105505322A CN105505322A CN201510952266.0A CN201510952266A CN105505322A CN 105505322 A CN105505322 A CN 105505322A CN 201510952266 A CN201510952266 A CN 201510952266A CN 105505322 A CN105505322 A CN 105505322A
- Authority
- CN
- China
- Prior art keywords
- parts
- reactor
- degree
- fully stir
- whipping temp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公布了一种地下开采用除尘剂的制备方法,其中所述除尘剂包括按照质量份数计的如下原料:十二烷基磺酸钠5-9份、月桂醇聚醚硫酸酯钠5-12份、羧甲基纤维素钠2-5份、五水偏硅酸钠3-6份、蓖麻油聚氧乙烯醚15-20份、聚乙二醇1-3份、杀菌剂5-8份、以及去离子水40-50份。本发明的地下开采用除尘剂的除尘效果良好、扩散均匀,性质稳定除尘效果明显,而且还具有杀菌作用,能够净化地下空气,减少粉尘的危害。
Description
技术领域
本发明涉及一种地下开采用除尘剂的制备方法。
背景技术
地下开采的过程中会出现大量的粉尘,粉尘的大量累积会对人体健康产生影响,使人体呼吸不畅,严重至引起肺部疾病,粉尘密度过高亦会产生安全隐患,会严重影响到现场工作人员的人身安全。目前我国煤矿主要采用的防尘措施有喷雾洒水除尘、通风除尘和除尘设备除尘等。喷雾洒水除尘用水量大、效果差、而且易造成工作面泥泞。通风除尘降尘效果差,尤其是对呼吸尘无明显效果。除尘设备除尘,受条件限制很多地点无法使用,除尘范围小。泡沫除尘属于化学降尘,具有结构简单、耗水量少、降尘率高尤其是对呼吸尘降尘效果好,是地下煤矿除尘的发展方向。目前我国地下开采过程中主要通过洒水和通风来进行除尘,除尘效果均不明显,而我国有关除尘剂的研究甚少。而如何克服现有技术的不足开发出具有优异除尘效果的除沉剂成为亟待解决的技术难题。
发明内容
本发明目的是针对现有技术存在的缺陷提供:一种地下开采用除尘剂的制备方法。
本发明为实现上述目的,采用如下技术方案:一种地下开采用除尘剂的制备方法,包括如下步骤,按重量份数计:
步骤一:将40-50份的去离子水倒入反应釜中,然后依次将5-9份的十二烷基磺酸钠加入到反应釜中,充分搅拌3-5分钟,搅拌温度为21-23度;
步骤二:将5-12份的月桂醇聚醚硫酸酯钠加入到反应釜中,充分搅拌4-6分钟,搅拌温度为22-24度;
步骤三:将15-20份的蓖麻油聚氧乙烯醚加入到反应釜中,充分搅拌5-7分钟,搅拌温度为23-25度;
步骤四:将2-5份的羧甲基纤维素钠和3-6份的五水偏硅酸钠依次加入到反应釜中,充分搅拌10-15分钟,搅拌温度为26-30度;
步骤五:最后依次将1-3份的聚乙二醇和5-8份的杀菌剂加入到反应釜中,充分搅拌5-8分钟,搅拌温度为30-33度;混合均匀即可得本发明的除尘剂。
进一步的,所述杀菌剂由醚菌酯、嘧菌酯、氟嘧菌酯、咪鲜胺、氟菌唑和咯菌腈中的任意两种按1∶2的比例混合而成。
本发明的有益效果:本发明的地下开采用除尘剂的除尘效果良好、扩散均匀,性质稳定除尘效果明显,而且还具有杀菌作用,能够净化地下空气,减少粉尘的危害。
具体实施方式
本发明公开了一种一种地下开采用除尘剂,包括按照质量份数计的如下原料:十二烷基磺酸钠5-9份、月桂醇聚醚硫酸酯钠5-12份、羧甲基纤维素钠2-5份、五水偏硅酸钠3-6份、蓖麻油聚氧乙烯醚15-20份、聚乙二醇1-3份、杀菌剂5-8份、以及去离子水40-50份。
优选的方案是,所述杀菌剂由醚菌酯、嘧菌酯、氟嘧菌酯、咪鲜胺、氟菌唑和咯菌腈中的任意两种按1∶2的比例混合而成。
实施例1:一种地下开采用除尘剂,包括按照质量份数计的如下原料:十二烷基磺酸钠5份、月桂醇聚醚硫酸酯钠5份、羧甲基纤维素钠2份、五水偏硅酸钠3份、蓖麻油聚氧乙烯醚15份、聚乙二醇1份、杀菌剂5份、以及去离子水40份。
上述除尘剂的制备方法如下:按照上述质量配比,
步骤一:将去离子水倒入反应釜中,然后依次将十二烷基磺酸钠加入到反应釜中,充分搅拌3分钟,搅拌温度为21度;
步骤二:将月桂醇聚醚硫酸酯钠加入到反应釜中,充分搅拌4分钟,搅拌温度为22度;
步骤三:将蓖麻油聚氧乙烯醚加入到反应釜中,充分搅拌5分钟,搅拌温度为23度;
步骤四:将羧甲基纤维素钠和五水偏硅酸钠依次加入到反应釜中,充分搅拌10分钟,搅拌温度为26度;
步骤五:最后依次将聚乙二醇和杀菌剂加入到反应釜中,充分搅拌5分钟,搅拌温度为30度;混合均匀即可得本发明的除尘剂。
使用时,将上述除尘剂稀释20倍,用喷雾器喷洒除尘,10立方米平均选2个喷洒点,测试喷洒前后的粉尘浓度,计算全尘降尘率和杀菌率,经过专业设备检测,可得出全尘除尘率为70%以上,杀菌率达60%以上。
实施例2:一种地下开采用除尘剂,包括按照质量份数计的如下原料:十二烷基磺酸钠7份、月桂醇聚醚硫酸酯钠8份、羧甲基纤维素钠3份、五水偏硅酸钠4份、蓖麻油聚氧乙烯醚17份、聚乙二醇2份、杀菌剂6份、以及去离子水45份。
上述除尘剂的制备方法如下:按照上述质量配比,
步骤一:将去离子水倒入反应釜中,然后依次将十二烷基磺酸钠加入到反应釜中,充分搅拌4分钟,搅拌温度为22度;
步骤二:将月桂醇聚醚硫酸酯钠加入到反应釜中,充分搅拌5分钟,搅拌温度为23度;
步骤三:将蓖麻油聚氧乙烯醚加入到反应釜中,充分搅拌6分钟,搅拌温度为24度;
步骤四:将羧甲基纤维素钠和五水偏硅酸钠依次加入到反应釜中,充分搅拌12分钟,搅拌温度为28度;
步骤五:最后依次将聚乙二醇和杀菌剂加入到反应釜中,充分搅拌6分钟,搅拌温度为32度;混合均匀即可得本发明的除尘剂。
使用时,将上述除尘剂稀释22倍,用喷雾器喷洒除尘,10立方米平均选2个喷洒点,测试喷洒前后的粉尘浓度,计算全尘降尘率和杀菌率,经过专业设备检测,可得出全尘除尘率为78%以上,杀菌率达62%以上。
实施例3:一种地下开采用除尘剂,包括按照质量份数计的如下原料:十二烷基磺酸钠9份、月桂醇聚醚硫酸酯钠12份、羧甲基纤维素钠5份、五水偏硅酸钠6份、蓖麻油聚氧乙烯醚20份、聚乙二醇3份、杀菌剂8份、以及去离子水50份。
上述除尘剂的制备方法如下:按照上述质量配比,
步骤一:将去离子水倒入反应釜中,然后依次将十二烷基磺酸钠加入到反应釜中,充分搅拌5分钟,搅拌温度为23度;
步骤二:将月桂醇聚醚硫酸酯钠加入到反应釜中,充分搅拌6分钟,搅拌温度为24度;
步骤三:将蓖麻油聚氧乙烯醚加入到反应釜中,充分搅拌7分钟,搅拌温度为25度;
步骤四:将羧甲基纤维素钠和五水偏硅酸钠依次加入到反应釜中,充分搅拌15分钟,搅拌温度为30度;
步骤五:最后依次将聚乙二醇和杀菌剂加入到反应釜中,充分搅拌8分钟,搅拌温度为33度;混合均匀即可得本发明的除尘剂。
使用时,将上述除尘剂稀释25倍,用喷雾器喷洒除尘,10立方米平均选2个喷洒点,测试喷洒前后的粉尘浓度,计算全尘降尘率和杀菌率,经过专业设备检测,可得出全尘除尘率为85%以上,杀菌率达65%以上。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种地下开采用除尘剂的制备方法,其特征在于,包括如下步骤,按重量份数计:
步骤一:将40-50份的去离子水倒入反应釜中,然后依次将5-9份的十二烷基磺酸钠加入到反应釜中,充分搅拌3-5分钟,搅拌温度为21-23度;
步骤二:将5-12份的月桂醇聚醚硫酸酯钠加入到反应釜中,充分搅拌4-6分钟,搅拌温度为22-24度;
步骤三:将15-20份的蓖麻油聚氧乙烯醚加入到反应釜中,充分搅拌5-7分钟,搅拌温度为23-25度;
步骤四:将2-5份的羧甲基纤维素钠和3-6份的五水偏硅酸钠依次加入到反应釜中,充分搅拌10-15分钟,搅拌温度为26-30度;
步骤五:最后依次将1-3份的聚乙二醇和5-8份的杀菌剂加入到反应釜中,充分搅拌5-8分钟,搅拌温度为30-33度;混合均匀即可得本发明的除尘剂。
2.如权利要求1所述的一种地下开采用除尘剂的制备方法,其特征在于,所述杀菌剂由醚菌酯、嘧菌酯、氟嘧菌酯、咪鲜胺、氟菌唑和咯菌腈中的任意两种按1∶2的比例混合而成。