CN105482530A - Internal wall paint and preparation method thereof - Google Patents
Internal wall paint and preparation method thereof Download PDFInfo
- Publication number
- CN105482530A CN105482530A CN201511015783.1A CN201511015783A CN105482530A CN 105482530 A CN105482530 A CN 105482530A CN 201511015783 A CN201511015783 A CN 201511015783A CN 105482530 A CN105482530 A CN 105482530A
- Authority
- CN
- China
- Prior art keywords
- parts
- carry out
- formula ratio
- latex
- butadiene resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an internal wall paint which is prepared from the following raw materials in parts by weight: 2.5-7.4 parts of diethylene glycol, 5-10 parts of starch, 5-10 parts of titanium white, 20-25 parts of latex, 3-7 parts of ammonia water, 2.5-4.7 parts of lauraldehyde, 7.5-8.7 parts of deionized water, 3.4-7.2 parts of diphenethyl diphenol polyethenoxy ether, 3.4-6.2 parts of pentaerythritol oleate and 3.5-7 parts of butadiene resin film former. Compared with the existing product, the latex emulsion is added, so the internal wall is healthy and environment-friendly, and is convenient to use; by adding the titanium white and lauraldehyde, the internal wall paint is convenient for transportation and storage, and is environment-friendly and nontoxic since no preservative is added; and by adding the diphenethyl diphenol polyethenoxy ether, pentaerythritol oleate and butadiene resin film former, the internal wall paint has high drying rate, and can endurably reserve aroma and purify air.
Description
Technical field
The present invention relates to a kind of interior wall coating and preparation method thereof, belong to building material field.
Background technology
At present, the kind of the coating used in daily finishing is a lot, emulsion paint is one of current most popular wall decoration material, along with improving constantly of standard of living, people also just increase the requirement of finishing material thereupon, and existing coating variety is various, and what have is unfavorable for construction, some performances can not be satisfied the demand, and what also have is larger to the injury of human body.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provides a kind of interior wall coating and preparation method thereof, solves the defect of currently available products, energy-conserving and environment-protective.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of interior wall coating, is made up of the raw material of following parts by weight: Diethylene Glycol 2.5-7.4 part, starch 5-10 part, titanium dioxide 5-10 part, latex 20-25 part, ammoniacal liquor 3-7 part, lauric aldehyde 2.5-4.7 part, deionized water 7.5-8.7 part, diphenylethyl diphenol Soxylat A 25-7 3.4-7.2 part, PETO 3.4-6.2 part and butadiene resin membrane-forming agent 3.5-7 part.
Optimize, above-mentioned interior wall coating, is made up of the raw material of following parts by weight: Diethylene Glycol 4.7 parts, starch 8 parts, titanium dioxide 8 parts, latex 22 parts, ammoniacal liquor 4.7 parts, lauric aldehyde 3.2 parts, deionized water 7.9 parts, diphenylethyl diphenol Soxylat A 25-7 5.6 parts, PETO 4.5 parts and butadiene resin membrane-forming agent 4.6 parts.
A preparation method for interior wall coating, comprises the following steps:
1) take Diethylene Glycol and starch by above-mentioned formula ratio, after adding deionized water, one piece is placed in reactor, is heated to 50-60 DEG C, is incubated and leaves standstill 2-3 hour after 1-2 hour stirs;
2) titanium dioxide of formula ratio and latex are added reactor, carry out dispersion with 500-600r/min and stir 15-20min, be then heated to 65-70 DEG C;
3) mixed emulsion is cooled to 15-20 DEG C, takes ammoniacal liquor and lauric aldehyde by formula ratio, add in the mixture in previous step, carry out dispersion with 400-500r/min and stir 20-25min;
4) take diphenylethyl diphenol Soxylat A 25-7 and the PETO of formula ratio, carry out dispersion with 500-600r/min and stir 10-15min, mixed emulsion is put into the sealed vessel that safety valve is housed and carry out ageing, leave standstill 3-4 days;
5) take butadiene resin membrane-forming agent, put into the mixture of previous step through ripening, be heated to 42-45 DEG C, be cooled to room temperature after insulation 20-30min, then pack, stamp, inspection, gets product.
The present invention, compared with existing product, adds latex emulsion, not only health environment-friendly but also easy to use; Add titanium dioxide and lauric aldehyde, transport and storage conveniently, and do not add any sanitas, environment-protecting asepsis; Add diphenylethyl diphenol Soxylat A 25-7, PETO and butadiene resin membrane-forming agent, rate of drying is fast, can also leave fragrance enduringly, purify air.
Embodiment
embodiment 1
The present invention is a kind of interior wall coating, is made up of the raw material of following parts by weight: Diethylene Glycol 2.5 parts, starch 5 parts, titanium dioxide 5 parts, latex 20 parts, ammoniacal liquor 3 parts, lauric aldehyde 2.5 parts, deionized water 7.5 parts, diphenylethyl diphenol Soxylat A 25-7 3.4 parts, PETO 3.4 parts and butadiene resin membrane-forming agent 3.5 parts.
A preparation method for interior wall coating, comprises the following steps:
1) take Diethylene Glycol and starch by above-mentioned formula ratio, after adding deionized water, one piece is placed in reactor, is heated to 50 DEG C, is incubated and leaves standstill 2 hours after 1 hour stirs;
2) titanium dioxide of formula ratio and latex are added reactor, carry out dispersion with 500r/min and stir 15min, be then heated to 65 DEG C;
3) mixed emulsion is cooled to 15 DEG C, takes ammoniacal liquor and lauric aldehyde by formula ratio, add in the mixture in previous step, carry out dispersion with 400r/min and stir 20min;
4) take diphenylethyl diphenol Soxylat A 25-7 and the PETO of formula ratio, carry out dispersion with 500r/min and stir 10min, mixed emulsion is put into the sealed vessel that safety valve is housed and carry out ageing, leave standstill 3 days;
5) take butadiene resin membrane-forming agent, put into the mixture of previous step through ripening, be heated to 42 DEG C, be cooled to room temperature after insulation 20min, then pack, stamp, inspection, gets product.
embodiment 2
The present invention is a kind of interior wall coating, is made up of the raw material of following parts by weight: Diethylene Glycol 7.4 parts, starch 10 parts, titanium dioxide 10 parts, latex 25 parts, ammoniacal liquor 7 parts, lauric aldehyde 4.7 parts, deionized water 8.7 parts, diphenylethyl diphenol Soxylat A 25-7 7.2 parts, PETO 6.2 parts and butadiene resin membrane-forming agent 7 parts.
A preparation method for interior wall coating, comprises the following steps:
1) take Diethylene Glycol and starch by above-mentioned formula ratio, after adding deionized water, one piece is placed in reactor, is heated to 60 DEG C, is incubated and leaves standstill 3 hours after 2 hours stir;
2) titanium dioxide of formula ratio and latex are added reactor, carry out dispersion with 600r/min and stir 20min, be then heated to 70 DEG C;
3) mixed emulsion is cooled to 20 DEG C, takes ammoniacal liquor and lauric aldehyde by formula ratio, add in the mixture in previous step, carry out dispersion with 500r/min and stir 25min;
4) take diphenylethyl diphenol Soxylat A 25-7 and the PETO of formula ratio, carry out dispersion with 600r/min and stir 15min, mixed emulsion is put into the sealed vessel that safety valve is housed and carry out ageing, leave standstill 4 days;
5) take butadiene resin membrane-forming agent, put into the mixture of previous step through ripening, be heated to 45 DEG C, be cooled to room temperature after insulation 30min, then pack, stamp, inspection, gets product.
embodiment 3
The present invention is a kind of interior wall coating, is made up of the raw material of following parts by weight: Diethylene Glycol 4.7 parts, starch 8 parts, titanium dioxide 8 parts, latex 22 parts, ammoniacal liquor 4.7 parts, lauric aldehyde 3.2 parts, deionized water 7.9 parts, diphenylethyl diphenol Soxylat A 25-7 5.6 parts, PETO 4.5 parts and butadiene resin membrane-forming agent 4.6 parts.
A preparation method for interior wall coating, comprises the following steps:
1) take Diethylene Glycol and starch by above-mentioned formula ratio, after adding deionized water, one piece is placed in reactor, is heated to 55 DEG C, is incubated and leaves standstill 2.5 hours after 1.5 hours stir;
2) titanium dioxide of formula ratio and latex are added reactor, carry out dispersion with 550r/min and stir 18min, be then heated to 68 DEG C;
3) mixed emulsion is cooled to 17 DEG C, takes ammoniacal liquor and lauric aldehyde by formula ratio, add in the mixture in previous step, carry out dispersion with 450r/min and stir 22min;
4) take diphenylethyl diphenol Soxylat A 25-7 and the PETO of formula ratio, carry out dispersion with 550r/min and stir 12min, mixed emulsion is put into the sealed vessel that safety valve is housed and carry out ageing, leave standstill 3.5 days;
5) take butadiene resin membrane-forming agent, put into the mixture of previous step through ripening, be heated to 43 DEG C, be cooled to room temperature after insulation 25min, then pack, stamp, inspection, gets product.
The finished product prepared by embodiment 1-3 carries out the test of following table properties, the results are shown in Table 1:
Can find out, indices all conformance with standard of coating of the present invention, have very strong abrasion resistance and wear resistance etc.Compared with existing product, add latex emulsion, not only health environment-friendly but also easy to use; Add titanium dioxide and lauric aldehyde, transport and storage conveniently, and do not add any sanitas, environment-protecting asepsis; Add diphenylethyl diphenol Soxylat A 25-7, PETO and butadiene resin membrane-forming agent, rate of drying is fast, can also leave fragrance enduringly, purify air.
To the above-mentioned explanation of the disclosed embodiments, professional and technical personnel in the field are realized or uses the present invention.To be apparent for those skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (3)
1. an interior wall coating, is characterized in that: be made up of the raw material of following parts by weight: Diethylene Glycol 2.5-7.4 part, starch 5-10 part, titanium dioxide 5-10 part, latex 20-25 part, ammoniacal liquor 3-7 part, lauric aldehyde 2.5-4.7 part, deionized water 7.5-8.7 part, diphenylethyl diphenol Soxylat A 25-7 3.4-7.2 part, PETO 3.4-6.2 part and butadiene resin membrane-forming agent 3.5-7 part.
2. interior wall coating according to claim 1, is characterized in that: be made up of the raw material of following parts by weight: Diethylene Glycol 4.7 parts, starch 8 parts, titanium dioxide 8 parts, latex 22 parts, ammoniacal liquor 4.7 parts, lauric aldehyde 3.2 parts, deionized water 7.9 parts, diphenylethyl diphenol Soxylat A 25-7 5.6 parts, PETO 4.5 parts and butadiene resin membrane-forming agent 4.6 parts.
3. the preparation method of the interior wall coating according to claims 1 or 2, comprises the following steps:
1) take Diethylene Glycol and starch by above-mentioned formula ratio, after adding deionized water, one piece is placed in reactor, is heated to 50-60 DEG C, is incubated and leaves standstill 2-3 hour after 1-2 hour stirs;
2) titanium dioxide of formula ratio and latex are added reactor, carry out dispersion with 500-600r/min and stir 15-20min, be then heated to 65-70 DEG C;
3) mixed emulsion is cooled to 15-20 DEG C, takes ammoniacal liquor and lauric aldehyde by formula ratio, add in the mixture in previous step, carry out dispersion with 400-500r/min and stir 20-25min;
4) take diphenylethyl diphenol Soxylat A 25-7 and the PETO of formula ratio, carry out dispersion with 500-600r/min and stir 10-15min, mixed emulsion is put into the sealed vessel that safety valve is housed and carry out ageing, leave standstill 3-4 days;
5) take butadiene resin membrane-forming agent, put into the mixture of previous step through ripening, be heated to 42-45 DEG C, be cooled to room temperature after insulation 20-30min, then pack, stamp, inspection, gets product.