CN103937120A - PVC edge sealing material and preparation method thereof - Google Patents
PVC edge sealing material and preparation method thereof Download PDFInfo
- Publication number
- CN103937120A CN103937120A CN201410067129.4A CN201410067129A CN103937120A CN 103937120 A CN103937120 A CN 103937120A CN 201410067129 A CN201410067129 A CN 201410067129A CN 103937120 A CN103937120 A CN 103937120A
- Authority
- CN
- China
- Prior art keywords
- pvc
- parts
- edging material
- powder
- sealing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC edge sealing material. The PVC edge sealing material comprises, by weight, 50-150 parts of PVC powder, 40-60 parts of calcium carbonate, 1-3 parts of an internal lubricant, 1-3 parts of an external lubricant, 3-7 parts of a stabilizer, 6-18 parts of dicapryl phthalate, 1-3 parts of a PVC processing aid, 3-9 parts of chlorinated polyethylene and 1-3 parts of a pigment. The invention also discloses a preparation method of the PVC edge sealing material. The PVC edge sealing material has the advantages of high toughness, high smoothness, beautiful appearance, high strength and corrosion resistance, and passes national detection, so the material has no pollution; and the PVC edge sealing material prepared according to the above raw material proportions also has the advantages of glossy and smooth surface, high wear resistance, strong high temperature resistance, unlikely decoloring and unlikely loss. The preparation method is simple and feasible, and is suitable for large scale production.
Description
Technical field
The present invention relates to decoration material field, be specifically related to a kind of PVC edging material and preparation method thereof.
Background technology
At present, in home decoration, conventional edging material generally divides log edge band and conventional P VC edge band, not only cost is high for these, and mostly added harmful stablizer etc., human body is caused to very large harm, and the PVC edge band surface of selling on the market is at present smooth not, poor toughness, frangibility, and easily fade, thereby the aesthetic feeling of losing
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of PVC edging material.
The technical problem that the present invention also will solve has been to provide the preparation method of above-mentioned PVC edging material.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of PVC edging material, comprises by dry matter weight umber: PVC powder 50-150 part, calcium carbonate 40-60 part, interior lubrication prescription 1-3 part, outer lubrication prescription 1-3 part, stablizer 3-7 part, dioctyl phthalate (DOP) 6-18 part, PVC processing aid 1-3 part, chlorinatedpolyethylene 3-9 part, pigment 1-3 part.
Wherein, above-mentioned interior lubrication prescription is stearic acid.
Wherein, above-mentioned outer lubrication prescription is SEMI-REFINED PARAFFIN WAX.
Wherein, aforementioned stable agent is mercaptan tin octylate 17MOK.
Wherein, above-mentioned PVC processing aid is silicone based processing aid.
Wherein, above-mentioned pigment is one or more in ferric oxide, titanium dioxide, aluminium powder, silver powder or phthalocyanine blue
The preparation method of above-mentioned PVC edging material, the method comprises the steps: 1) PVC powder, calcium carbonate, inside and outside lubrication prescription, stablizer, dioctyl ester, PVC processing aid, chlorinatedpolyethylene, pigment are directly put into stirrer according to said ratio, 1500-1800 rev/min of stirring is heated to 135-150 ℃ simultaneously;
2) powder after stirring is put into tablets press, carry out granulation, produce micelle;
3) micelle adds in plastics extruder, extrusion moulding, and the mould by different model in extrusion machine is controlled width and the thickness of product;
4) by cooling tank, utilize cold water cooling, obtain PVC edging material.
Beneficial effect: toughness of products of the present invention is high, slickness is high, outward appearance is beautiful, intensity is high, corrosion-resistant, detects pollution-free by country, PVC edging material prepared by Raw proportioning of the present invention is not only surperficial glossy, smooth but also wear resisting property is high, heat-resisting ability is strong, and is difficult for decolouring, is difficult for losing.Preparation method's simple possible of the present invention, is applicable to scale operation.
Embodiment
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1
2 parts, 100 parts, PVC powder, 50 parts, calcium carbonate, 2 parts of stearic acid, 2 parts of SEMI-REFINED PARAFFIN WAX, mercaptan tin octylate 17MOK5 part, 12 parts of dioctyl phthalate (DOP)s, 2 parts of silicone based processing aids, 6 parts of chlorinatedpolyethylenees, ferric oxide directly put into stirrer according to said ratio, and 1500 revs/min of stirrings are heated to 135 ℃ simultaneously; Powder after stirring is put into tablets press, carry out granulation, produce micelle; Micelle adds in plastics extruder, extrusion moulding, and the mould by different model in extrusion machine is controlled width and the thickness of product; By cooling tank, utilize cold water cooling, obtain PVC edging material.
Comparative example 1
2 parts, 100 parts, PVC powder, 50 parts, calcium carbonate, 2 parts of stearic acid, 2 parts of SEMI-REFINED PARAFFIN WAX, mercaptan tin octylate 17MOK5 part, 6 parts of chlorinatedpolyethylenees, ferric oxide directly put into stirrer according to said ratio, and 1500 revs/min of stirrings are heated to 135 ℃ simultaneously; Powder after stirring is put into tablets press, carry out granulation, produce micelle; Micelle adds in plastics extruder, extrusion moulding, and the mould by different model in extrusion machine is controlled width and the thickness of product; By cooling tank, utilize cold water cooling, obtain PVC edging material.
Embodiment 2
1 part, 50 parts, PVC powder, 40 parts, calcium carbonate, 1 part of stearic acid, 1 part of SEMI-REFINED PARAFFIN WAX, mercaptan tin octylate 17MOK3 part, 6 parts of dioctyl phthalate (DOP)s, 1 part of machine silicon class processing aid, 3 parts of chlorinatedpolyethylenees, titanium dioxide directly put into stirrer according to said ratio, and 1800 revs/min of stirrings are heated to 150 ℃ simultaneously; Powder after stirring is put into tablets press, carry out granulation, produce micelle; Micelle adds in plastics extruder, extrusion moulding, and the mould by different model in extrusion machine is controlled width and the thickness of product; By cooling tank, utilize cold water cooling, obtain PVC edging material.
Embodiment 3
3 parts, 150 parts, PVC powder, 60 parts, calcium carbonate, 3 parts of stearic acid, 3 parts of SEMI-REFINED PARAFFIN WAX, mercaptan tin octylate 17MOK7 part, 18 parts of dioctyl phthalate (DOP)s, 3 parts of PVC processing aids, 9 parts of chlorinatedpolyethylenees, phthalocyanine blue directly put into stirrer according to said ratio, and 1650 revs/min of stirrings are heated to 145 ℃ simultaneously; Powder after stirring is put into tablets press, carry out granulation, produce micelle; Micelle adds in plastics extruder, extrusion moulding, and the mould by different model in extrusion machine is controlled width and the thickness of product; By cooling tank, utilize cold water cooling, obtain PVC edging material.
The test data of the present invention embodiment 1～3 and comparative example is as follows:
Table 1 test performance
| ? | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example |
| Glossiness | Glossy | Glossy | Glossy | Matt |
| Slickness | Smooth surface | Smooth surface | Smooth surface | Surface irregularity |
| Wear resistance (1000g, 300 turn) | 0.02 | 0.025 | 0.022 | 0.045 |
| Tolerable temperature (℃) | 536 | 625 | 636 | 305 |
| Whether decolour | No | No | No | Be |
As can be seen from Table 1, adopt PVC edging material prepared by proportioning of the present invention not only surperficial glossy, smooth but also wear resisting property is high, heat-resisting ability is strong, and is difficult for decolouring, is difficult for losing.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (7)
1. a PVC edging material, it is characterized in that, by dry matter weight umber, comprise: PVC powder 50-150 part, calcium carbonate 40-60 part, interior lubrication prescription 1-3 part, outer lubrication prescription 1-3 part, stablizer 3-7 part, dioctyl phthalate (DOP) 6-18 part, PVC processing aid 1-3 part, chlorinatedpolyethylene 3-9 part, pigment 1-3 part.
2. a kind of PVC edging material according to claim 1, is characterized in that, described interior lubrication prescription is stearic acid.
3. a kind of PVC edging material according to claim 1, is characterized in that, described outer lubrication prescription is SEMI-REFINED PARAFFIN WAX.
4. a kind of PVC edging material according to claim 1, is characterized in that, described stablizer is mercaptan tin octylate 17MOK.
5. a kind of PVC edging material according to claim 1, is characterized in that, described PVC processing aid is silicone based processing aid.
6. a kind of PVC edging material according to claim 1, is characterized in that, described pigment is one or more in ferric oxide, titanium dioxide, aluminium powder, silver powder or phthalocyanine blue.
7. the preparation method of PVC edging material claimed in claim 1, it is characterized in that, the method comprises the steps: 1) PVC powder, calcium carbonate, inside and outside lubrication prescription, stablizer, dioctyl ester, PVC processing aid, chlorinatedpolyethylene, pigment are directly put into stirrer according to said ratio, 1500-1800 rev/min of stirring is heated to 135-150 ℃ simultaneously;
2) powder after stirring is put into tablets press, carry out granulation, produce micelle;
3) micelle adds in plastics extruder, extrusion moulding, and the mould by different model in extrusion machine is controlled width and the thickness of product;
4) by cooling tank, utilize cold water cooling, obtain PVC edging material.