CN101042016A - Method for making novel PVC edge banding strip - Google Patents
Method for making novel PVC edge banding strip Download PDFInfo
- Publication number
- CN101042016A CN101042016A CN 200710027806 CN200710027806A CN101042016A CN 101042016 A CN101042016 A CN 101042016A CN 200710027806 CN200710027806 CN 200710027806 CN 200710027806 A CN200710027806 A CN 200710027806A CN 101042016 A CN101042016 A CN 101042016A
- Authority
- CN
- China
- Prior art keywords
- edge banding
- preparation
- banding strip
- strip according
- novel pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
It relates to a new PVC sealing strip that comprises the basic material, pattern layer and transparent protective film, with the material for making the basic material composed of PVC, CaCO3, flexibilizer, PVC processing and character change agent, stabilizer, inner lubricant, outer lubricant, elasticizer, coupling agent, antistatic agent, with quick speed due to the extrusion molding, and free from discoloration through the usage of printing method.
Description
Technical field:
The present invention relates to PVC edge sealing bar manufacture technology field, the preparation method of refering in particular to a kind of novel PVC edge banding strip.
Background technology:
At present; edge sealing bar commonly used in the home decoration generally divides log edge sealing bar and conventional P VC edge sealing bar; log edge sealing bar is made simple; but cost costliness; its raw material is mainly derived from the log skin of trees, and in recent years, various countries are in order to protect forest resources; the felling of restriction forest makes that the raw material sources of log edge sealing bar are restricted.For this reason; people expect replacing the log skin as the main material of making the edge sealing bar with PVC; traditional way is to utilize the base material of PVC as the edge sealing bar; stick the thin layer that has various patterns at substrate surface then; then stick the PVC protective film of layer of transparent on the patterned layer surface; at last by heating; pressuring method is with base material; patterned layer and the compacting of PVC protective film; this traditional PVC edge sealing bar is because the defective that manufacture craft exists; make its protective film come off easily; lose protection to patterned layer; make patterned layer be destroyed, lose original aesthetic feeling.
Summary of the invention:
Purpose of the present invention is exactly the preparation method that a kind of novel PVC edge banding strip is provided at the deficiency of prior art existence.
To achieve these goals, the technical solution used in the present invention is: it comprises the making of base material, patterned layer and transparent protective film, makes base material earlier, and the raw material of making base material comprises PVC, CaCO
3, flexibilizer, PVC modifier, stabilizing agent, interior lubrication prescription, outer lubrication prescription, plasticizing agent, coupling agent and antistatic additive, the weight proportion of its raw material is PVC61～70%, CaCO
317%～26%, flexibilizer 4.5%～6%, PVC modifier 0.8%～20%, stabilizing agent 1.8%～4%, interior lubrication prescription 0.25%～0.6%, outer lubrication prescription 0.1%～0.3%, plasticizing agent 0.8%～2.3%, coupling agent 0.5%～0.8%, antistatic additive 0.03%～0.05%;
Above-mentioned raw materials put in the mixing equipment stir, mixing speed remains on 740～1480 rev/mins, and mixing time was controlled at 15～20 minutes, and temperature remains on 90～135 ℃;
After stirring is finished, said mixture is put into cold burden equipment cool off, cold burden is crossed range request the action of stirring, and mixing speed remains on 1300～1440 rev/mins, and mixing time was controlled at 15～20 minutes, and temperature remains on 40～50 ℃;
Above-mentioned cooled mixture is put into extrusion equipment, make the barrel temperature of extrusion equipment remain on 160 ℃～190 ℃, extruded velocity remains on 3～4kg/min, and mixture is at last by the base material of the molding die extruding sheet of extrusion equipment, so far, base material completes;
At the substrate surface printing pattern layer of making, last at the transparent diaphragm of patterned layer surface printing.
Described flexibilizer haloflex.
Described this PVC modifier is an acrylate.
Described stabilizing agent is a dibasic lead phosphite salt.
Lubrication prescription is the unrighted acid pentaerythritol resin in described.
Described outer lubrication prescription is an OPE.
Described plasticizing agent is an epoxidized soybean oil.
Described coupling agent is a chlorinated paraffin wax.
Described antistatic additive is white carbon black.
Because base material adopts extrusion equipment to make, and makes manufacturing speed fast, patterned layer and diaphragm adopt mode of printing to make, and make patterned layer and diaphragm to combine with base material securely, the phenomenon of decolouring can not occur.
The specific embodiment:
A present invention wherein embodiment is to be with weight: PVC 70kg, CaCO
318.9kg, the raw material of flexibilizer 5.3kg, PVC modifier 1.5kg, stabilizing agent 1.2kg, interior lubrication prescription 0.5kg, outer lubrication prescription 0.3kg, plasticizing agent 1.2kg, coupling agent 0.7kg, antistatic additive 0.4kg puts in the mixing equipment and stirs, mixing speed remains on 1400 rev/mins, mixing time was controlled at 15 minutes, and temperature remains on 130 ℃;
After stirring is finished, said mixture is put into cold burden equipment cool off, cold burden is crossed range request the action of stirring, and mixing speed remains on 1400 rev/mins, and mixing time was controlled at 15 minutes, and temperature remains on 45 ℃;
Above-mentioned cooled mixture is put into extrusion equipment, make the barrel temperature of extrusion equipment remain on 180 ℃, extruded velocity remains on 4kg/min, and mixture is at last by the base material of the molding die extruding sheet of extrusion equipment, so far, base material completes;
At the substrate surface printing pattern layer of making, last at the transparent diaphragm of patterned layer surface printing.
Described flexibilizer, PVC modifier, stabilizing agent, interior lubrication prescription, outer lubrication prescription, plasticizing agent, coupling agent, antistatic additive, be respectively haloflex, acrylate, dibasic lead phosphite salt, unrighted acid pentaerythritol resin, OPE, epoxidized soybean oil, chlorinated paraffin wax, white carbon black.
Certainly, the example of the above is a preferred embodiments of the present invention, is not to be used for limiting practical range of the present invention, so all equivalences of doing according to described prescription of the present patent application claim and principle change or modify, and all should be included in the present patent application claim.
Claims (9)
1, the preparation method of novel PVC edge banding strip, the making that it comprises base material, patterned layer and transparent protective film is characterized in that: make base material earlier, the raw material of making base material comprises PVC, CaCO
3, flexibilizer, PVC modifier, stabilizing agent, interior lubrication prescription, outer lubrication prescription, plasticizing agent, coupling agent and antistatic additive, the weight proportion of its raw material is PVC61～70%, CaCO
317%～26%, flexibilizer 4.5%～6%, PVC modifier 0.8%～20%, stabilizing agent 1.8%～4%, interior lubrication prescription 0.25%～0.6%, outer lubrication prescription 0.1%～0.3%, plasticizing agent 0.8%～2.3%, coupling agent 0.5%～0.8%, antistatic additive 0.03%～0.05%;
Above-mentioned raw materials put in the mixing equipment stir, mixing speed remains on 740～1480 rev/mins, and mixing time was controlled at 15～20 minutes, and temperature remains on 90～135 ℃;
After stirring is finished, said mixture is put into cold burden equipment cool off, cold burden is crossed range request the action of stirring, and mixing speed remains on 1300～1440 rev/mins, and mixing time was controlled at 15～20 minutes, and temperature remains on 40～50 ℃;
Above-mentioned cooled mixture is put into extrusion equipment, make the barrel temperature of extrusion equipment remain on 160 ℃～190 ℃, extruded velocity remains on 3～4kg/min, and mixture is at last by the base material of the molding die extruding sheet of extrusion equipment, so far, base material completes;
At the substrate surface printing pattern layer of making, last at the transparent diaphragm of patterned layer surface printing.
2, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described flexibilizer haloflex.
3, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described this PVC modifier is an acrylate.
4, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described stabilizing agent is a dibasic lead phosphite salt.
5, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: lubrication prescription is the unrighted acid pentaerythritol resin in described.
6, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described outer lubrication prescription is an OPE.
7, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described plasticizing agent is an epoxidized soybean oil.
8, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described coupling agent is a chlorinated paraffin wax.
9, the preparation method of novel PVC edge banding strip according to claim 1 is characterized in that: described antistatic additive is white carbon black.